利用离心萃取器研究协同萃取分离镍钴

利用离心萃取器研究硫酸体系中P507和P204协同萃取分离镍钴的效果。实验研究表明P507和P204组成的协同萃取体系对镍钴的分离存在正协同效应,在有机相组成为VP507: VP204为3:2; VO：VA为1:1;水相酸度为0.2mol/L,流通量为10L/h,转速为2300r/min,常温条件下,钴的二级逆流萃取率为95.8%%,βCo/Ni为5680。负载有机用2mol/L的H2SO4溶液2级逆流反萃,Co2 的反萃取率为93.5%,反萃液中的钴离子浓度为12.6g/L。     

离心萃取器协同萃取分离镍钴

利用离心萃取器研究硫酸体系中P507和P204协同萃取分离镍钴的效果。结果表明,P507和P204组成的协同萃取体系对镍钴的分离存在正协同效应,在有机相组成VP507∶VP204为3∶2,VO∶VA为1∶1,水相酸度为0.2 mol/L,流通量为10 L/h,转速为2 300 r/min,常温条件下,钴的二级逆流萃取率为95.8%,βCo/Ni为5 680。负载有机相用2 mol/L的H2SO4溶液2级逆流反萃,Co2+的反萃取率为93.5%,反萃液中的钴离子浓度为12.6 g/L。     

氨性溶液中铜镍钴的萃取分离

采用PT5050萃取剂，分离和富集镍矿氨液中的铜、镍、钴。采用2级萃取，溶液中铜、镍的萃取率可达99．5％以上，钴不被萃取，经3级低酸选择性反萃镍，镍的反萃率达99％以上，镍反萃液中铜含量小于0．001g/L，满足电镍生产要求。有机相经高酸（180g/L H2SO4)反萃铜，铜反萃液生产电铜或结晶硫酸铜。用硫化钠沉淀萃余液中的钴，钴的沉淀率大于96％，所得到的钴硫精矿含钴大于40％。     

红土镍矿浸出液中钴、锰、铁的协同萃取

将P204与Cyanex272构成混合萃取剂用于萃取红土镍矿浸出液中的Co、Mn、Fe。系统研究了协同萃取的最优萃取剂比例、水相pH值、萃取平衡时间、萃取温度及反萃的最合适酸浓度。结果表明,有机相比例P204∶Cyanex272∶TBP∶磺化煤油=5∶15∶5∶75,待处理溶液pH值为4.5、萃取温度60℃、平衡时间8min为最佳萃取条件;反萃工序中,采用50g/L的H2SO4溶液反萃钴,110g/L的H2SO4溶液反萃锰,7mol/L的HCl溶液反萃铁可获得较好的反萃效果。     

用N235从大洋多金属结核萃铜余液中萃取钴

研究了用N235从大洋多金属结核熔炼-锈蚀-萃取工艺中所产出的萃铜余液中萃取分离钴的方法。实验结果表明, N235萃取钴效果明显, 负载有机相中的钴能被稀酸反萃完全。采用N235萃取和稀酸反萃方法可以把Co(Ⅱ)、Ni(Ⅱ)分离开。从含钴0.85 g/L的料液中, 按相比V_O/V_A= 1/2, 经四级逆流萃取, 二级反萃可将钴富集到15.20 g/L, 萃余液中含钴0.0055 g/L, 萃余液中Ni/Co高达1 838, 反萃液中Co/Ni =1 520, 产品质量符合优质工业氯化钴质量要求, 钴镍萃取分离效果甚佳, 钴的回收率大于98%。     

Cyanex272在镍钴分离中的应用

研究黑镍除钴渣酸溶后溶液用Cyanex272萃取钴,实现钴、镍的深度分离,并介绍其工业生产应用.试验结果表明混合时间3rnin,Co的萃取率可达98%以上;经2级萃取溶液中的Co2+由4.5降至0.01g/L以下;负载有机相经三级洗涤[Co]/[Ni]达到529.20;通过三级萃取,三级洗涤,钴的萃取率达99.90%以上,镍钴分离系数βCo/Ni为2.50×105;两级反萃使有机相含Co2+降至0.020g/L以下;采用去离子水二级洗涤,Cl-几乎100%被洗掉,不会进入硫酸镍溶液中循环积累.工业实践中黑镍除钴渣酸溶后溶液经P204萃取除铜、铁-Cyanex272萃取分离镍钴-氯化钴溶液草酸沉淀-草酸钴煅烧,产出的精制氧化钴粉达到国家Y1级标准,产出的硫酸镍溶液完全满足生产1#电镍的要求.     

某钼镍钒多金属矿石镍钒浸出液萃钒试验

以P204为萃取剂、硫酸溶液为反萃剂,在室温下对贵州某钼镍钒多金属矿石的镍钒浸出液进行钒的萃取-反萃取试验,确定了萃取时适宜的工艺参数为母液pH=2.5,有机相中P204、TBP、磺化煤油的体积比=20∶5∶75,相比（O/A）=1∶2,萃取时间5 min,反萃取时适宜的工艺参数为硫酸溶液浓度2 mol/L、相比（O/A）=2∶1、反萃时间4 min。在所确定的工艺参数下进行5级萃取-反萃取,钒的总萃取率达98.7%、总反萃率达99.8%、总回收率达98.5%。     

采用LIX984萃取废蚀刻液中铜的研究

针对现有氯化物体系废蚀刻液中铜难以电解回收利用的现状,采用LIX984作为萃取剂,探索其对废蚀刻液中铜的萃取及反萃转型性能.系统考察了萃取剂浓度、料液酸度、萃取时间等对铜萃取的影响,硫酸浓度、反萃时间等对铜反萃的影响,绘制了萃取及反萃等温线并模拟了多级逆流过程。结果表明,采用LIX984萃取铜时,为确保铜萃取回收率,应将废蚀刻液稀释至铜浓度接近0.5mol/L或以下。铜131.24g/L、氯231.6g/L,pH=2.45的废蚀刻液稀释4倍后,可直接采用20%(体积分数)的LIX984按相比O/A=4/1、萃取时间10min、萃取温度25℃条件进行萃取,经过5级逆流萃取,铜萃取率为97.1%,氯萃取率仅0.05%。负载铜有机相采用200g/L的硫酸溶液,按照相比O/A=6/1、反萃时间5min、反萃温度25℃条件进行萃取,经过7级逆流反萃,铜反萃率为98.62%。得到的含铜47.16g/L、氯0.18g/L硫酸铜反萃液可直接用于电解回收,得到满足GB/T 467—1997中产品Cu-CATH2要求的金属铜。     

LIX984对废蚀刻液中铜的萃取及反萃转型性能研究

针对现有氯化物体系废蚀刻液中铜难以电解回收利用的现状,本文采用LIX984作为萃取剂,探索其对废蚀刻液中的铜萃取及反萃转型研究,系统考察了萃取剂浓度、料液酸度、萃取时间等对铜萃取的影响,硫酸浓度、反萃时间等对铜反萃的影响,绘制萃取及反萃等温线并模拟多级逆流过程。研究表明：采用LIX984萃取铜时,为确保铜萃取回收率,应将废蚀刻液稀释至Cu浓度接近0.5 mol/L或以下。文中含Cu 131.24 g/L、Cl 231.6 g/L,pH=2.45的废蚀刻液稀释4倍后,可直接采用20 %(体积分数)的LIX984 按相比O/A=4:1,萃取时间10 min,萃取温度25 ℃,经过5级逆流萃取,Cu萃取率为97.1 %,Cl萃取率仅0.05 %。负载铜有机相采用200 g/L的硫酸溶液,按照相比O/A=6:1,反萃时间5 min,反萃温度25 ℃,经过7级逆流反萃,铜反萃率为98.62 %,并得到含Cu 47.16 g/L、Cl 0.18 g/L的硫酸铜反萃液,可直接用于电解回收,得到的金属铜达到国家标准GB/T467-1997 Cu-CATH2要求。     

2,2'-硫代双对叔辛基苯酚萃取镍的性能

研究2,2'-硫代双对叔辛基苯酚对镍的萃取性能.结果表明,以苯为稀释剂,2,2'-硫代双对叔辛基苯酚的浓度1×10-3mol/L,[Ni2+]=0.1g/L,pH=11,萃取时间t=15min,相比(O/A)=1:1,镍的萃取率可达98.6%.硫酸是适宜的反萃剂,用4mol/L硫酸反萃负载镍的有机相,单级反萃率可达85.6%.     

Cyanex 272萃取分离硫酸钴溶液中镍钴的试验研究

采用Cyanex 272萃取剂从硫酸钴溶液中分离去除镍,在有机相组成为25%Cyanex 272+75%航空煤油(用30%NaOH皂化,皂化率75%)、萃原液pH值4.5～5.0、温度25～35 ℃、相比1.5～2条件下,经5级逆流萃取,混合萃取时间5 min,然后用1 mol/L硫酸溶液4级反萃取获得反萃取液,钴直收率达99.86%,Ni去除率达95.20%,钴镍分离效果较好。反萃取后的硫酸钴溶液中杂质含量很低,Co/Ni比达368 95,可以满足生产精制CoSO₄·7H₂O和电钴的要求。     

Recovery of nickel and cobalt from leach solutions of nickel laterites using a synergistic system consisting of Versatic 10 and Acorga CLX 50

A direct solvent extraction (DSX) process to recover nickel and cobalt from laterite leach solutions is potentially more cost effective compared to the traditional precipitation and re-leaching method. A synergistic solvent extraction (SSX) system consisting of Versatic 10 and Acorga CLX 50 in ShellSol 2046 was studied for DSX nickel and cobalt recovery from a synthetic solution using semi-continuous tests. The effect of pH on the metal distribution profile and metal separation were investigated. It was found that the SSX system can effectively recover nickel and cobalt and separate them from manganese, calcium and magnesium. Over 99% of Ni and Co was extracted using four stages of semi-continuous extraction from the synthetic laterite solution at pH 6.3 and an A/O flowrate ratio of 1:1. More than 80% of the manganese was rejected to the raffinate. The co-extraction of calcium was less than 5% and the co-extraction of magnesium was negligible under these conditions. The co-extracted manganese and calcium were readily scrubbed in three stages semi-continuous scrubbing. The loaded strip liquor with a high concentration of nickel (71.3 g/L Ni) was obtained after two-stage continuous stripping. The final strip solution pH of 3 would be suitable for nickel electrowinning. A conceptual DSX process flowsheet using the SSX system to recover nickel and cobalt from laterite leach solutions after iron removal has been proposed.     

P204-仲辛醇皂化萃取氰化尾渣酸浸液中铁的初步研究

采用P204-仲辛醇皂化萃取体系从金精矿氰化尾渣酸浸液中萃取分离铁, 初步研究其萃取机理, 并考察了萃取体系、P204浓度和料液初始pH值、含铁浓度及加入介质NaCl对Fe(Ⅲ)萃取的影响以及相比(O/A)、H₂SO₄浓度对Fe(Ⅲ)反萃的影响。实验结果表明：P204和仲辛醇对酸浸液中的Fe(Ⅲ)具有一定协同萃取效应, 仲辛醇作为萃取体系中的相转移试剂, 尤其能改善铁的反萃效率。同时, 采用氨水皂化后的萃取体系铁的提取率显著提高。P204、仲辛醇以及260^#溶剂油以1∶1∶2的体积比混合作为萃取体系, 在相比为2的条件下, 调整含铁10.18 g/L的原酸浸液的pH值接近2.0, 经过1级萃取, 萃余液中含铁低于0.25 g/L; 以25%(体积分数)的H₂SO₄反萃, 有机相中的铁基本被反萃完全。通过萃取和反萃, 铁离子溶液中杂质含量大大减少, 尤其是砷的含量。     

硫酸镍钴溶液中萃取除镉的试验研究

研究用萃取法从硫酸镍钴溶液中脱除镉。实验采用10 %N235 + 5 %TBP+85 %煤油的油相为萃取剂，稀硫酸为洗涤剂，氢氧化钠溶液为反萃剂。实验结果表明，萃取的最佳条件是：添加氯化钠的量为18 g/L，油水比为1:2、常温萃取5 min，三级逆流萃取率达99.4 %。反萃的最佳条件是：氢氧化钠溶液浓度为120 g/L、油水比为4:1、常温反萃5 min，反萃率达到98.0 %，实现了镉从硫酸镍钴溶液中脱除的目的。     

大洋多金属结核低温氢还原-湿法冶金联用回收有价金属

以大洋多金属结核为原料, 采用低温氢还原-湿法冶金联用工艺回收有价金属, 湿法冶金过程包括硫酸浸出、M5640萃取铜、针铁矿法除铁、P204萃取除锌、HBL110萃取回收镍。在HBL110萃取回收镍过程中, 考察了平衡pH值、相比O/A等因素对萃取镍的影响, 并绘制了镍萃取与反萃平衡等温线。结果表明, 采用50%HBL110+50%磺化煤油组成的有机相, 经过6级逆流萃取-4级逆流洗涤, 镍萃取率达99.85%, 除钴外, 杂质金属Mn、Ca、Mg、Al基本不被萃取。负载有机相经5级逆流反萃, 镍反萃率达98.53%。     

溶析结晶法制备硫酸钴的实验研究

采用溶析结晶法制备硫酸钴,考察了溶析剂种类、溶析剂用量、溶析剂浓度、溶液初始Co²⁺浓度、结晶温度等参数对硫酸钴结晶率的影响。以乙醇为溶析剂,在溶析剂与硫酸钴溶液体积比为1∶1、溶析剂浓度为95%、溶液初始Co²⁺浓度为120 g/L、结晶温度为25 ℃条件下,硫酸钴结晶率达到98.27%,母液中Co²⁺浓度为1.36 g/L。本方法制备的硫酸钴与蒸发结晶工艺制备的硫酸钴相比,在溶解pH值、水不溶物、磁性物、油分等关键指标方面具有明显优势,满足GB/T 26523-2011《精制硫酸钴》优等品的要求。     

陕西某石煤钒矿酸浸液中钒与铁的分离研究

以陕西某石煤酸浸含钒上清液为原料, 先用石灰乳中和、硫代硫酸钠还原预处理, 采用P204+TBP+磺化煤油萃取体系萃取富集、纯化五氧化二钒浸出液; 采用不同酸度硫酸作反萃剂, 对负载有机相反萃取, 进行钒、铁分离。结果表明: 浸出液经石灰乳中和, 硫代硫酸钠还原, 控制溶液pH=2.5, 溶液电位为-200 mV, 当A/O=2, 经6级逆流萃取, 钒的萃取率达99%以上, 而铁萃取率仅为11%; 反萃剂酸度控制在1.0～1.25 mol/L, O/A=18, 经5级逆流反萃取, 钒的反萃取率可达99%以上, 铁的反萃取率仅为9%。反萃取水相中V₂O₅浓度为75.3 g/L, Fe浓度为1.2 g/L, 反萃水相中钒铁质量比为62.8, 钒铁分离效果较好, 满足后续提钒要求。     

P204-TOPO混合萃取体系从湿法炼锌含铟硫酸锌溶液中萃取回收铟

为解决湿法炼锌硫酸锌溶液中传统溶剂萃取回收铟过程需使用高浓度盐酸反萃,且反萃后贫有机相中夹带氯离子危害湿法炼锌的难题.采用P204-TOPO混合萃取体系从含铟浸出液中选择性萃取铟,载铟有机相采用硫酸反萃,实现无氯体系回收铟.研究发现,混合体系萃取铟过程属于阳离子交换,TOPO与P204发生缔合作用,减弱了P204与铟离...     

高镁低品位铜镍矿氧压硫酸浸出液综合回收研究

针对高镁低品位铜镍矿氧压硫酸浸出液特点,提出“Lix984萃取提铜-MgO中和黄钠铁矾法沉淀除铁-MgO中和沉镍”综合回收工艺。结果表明,采用Lix984可选择性萃取99.79%的铜,其他金属离子基本不萃取,经模拟工业贫铜电解液反萃,铜反萃率达98.13%,得到富铜电解液,可电积制备金属铜; 萃铜余液通过MgO中和黄钠铁矾法沉淀除铁,铁沉淀率达99.20%,镍损失率仅0.60%; 沉铁后液通过MgO中和沉淀回收镍,镍沉淀率为99.91%,并得到镍含量24.13%的氢氧化镍粗产品; 沉镍后的高浓度硫酸镁沉淀后液,可用于回收镁。