以水玻璃为硅源喷雾干燥制备SiC前驱体

以廉价的水玻璃和炭黑为原料,通过制备均匀混合的前驱体,利用碳热还原反应合成出超细SiC粉体。比较研究了前驱体喷雾干燥与搅拌干燥两种制备方法对体系碳热还原反应的影响,重点考察了喷雾干燥制备过程中主要工艺参数对前驱粉体密度及收率的影响。结果表明:喷雾制备的前驱体具有更高的反应活性,在1550℃下反应2h就可使SiO2转化率达到89.4%,搅拌干燥制备的前驱体转化率只有65.2%。喷雾干燥过程中,适当提高进口温度、喷雾头转速并降低料液的固体含量,可获得高收率、高产率的前驱粉体,利于整个制备工艺生产效率及产率的提高。     

木质素-SiO2凝胶前驱体合成纳米SiC的研究

以造纸黑液和硅酸钠为原料,采用溶胶-凝胶法制成木质素-SiO2凝胶,以此作为SiC的前驱体,再经炭化处理和高温碳热还原反应而制备出SiC纳米粉体.该粉体呈球形,粒径70～200nm,且大小均匀.红外光谱分析表明,1100℃时就有SiC生成,1300℃时反应速度快且比较完全.提高碳热还原反应温度有利于前驱体向SiC的转变.     

碳热还原法制备球形SiC微粉

以硅溶胶为硅源,蔗糖为碳源,采用低温碳热还原法合成了SiC微粉.低温处理过程为室温到800℃,升温速率为6℃/min.在低温处理过程中蔗糖-硅溶胶混合前驱体转化为球形碳颗粒和SiO2的混合物.800℃以上的升温速率为15℃/min.低温处理后的反应前驱体在1700℃下反应1h全部转化为β-SiC,产物的颗粒尺寸在1μm左右,为近似球形的颗粒.升高反应温度有利于提高反应速率,缩短反应时间.延长反应时间能增加转化率.     

用煤矸石制备Al2O3-SiC复相粉体的研究

以煤矸石和碳质材料(工业炭黑、活性炭、无烟煤)为主要原料,在流动氩气中碳热还原制备了A l2O3-SiC复相粉体,研究了碳过量数、碳源、反应温度、保温时间、成型压力、添加剂种类及数量等工艺参数对制备的A l2O3-SiC复相粉体的相组成和显微结构的影响。结果表明,反应温度、保温时间及氯化物添加剂对煤矸石碳热还原反应有显著影响。通过优化工艺,以煤矸石为基料,加入适量炭黑,在1 550℃3 h下制备出了w(A l2O3)=58%、w(SiC)=42%的复相粉体,其粒度d50≤5μm;加入适量添加剂,可降低合成温度50℃。     

非水解溶胶-凝胶法结合碳热还原法制备β-SiC粉体

为了用较为简便的方法以及廉价原料制备出β-SiC粉体,采用非水解溶胶-凝胶法,以分析纯的四氯化硅(SiCl4)、正硅酸四乙酯(TEOS)为原料,加入催化剂无水氯化铁(FeCl_3)制备出溶胶,然后转移至反应釜中能制备出SiO_2干凝胶。分别以SiO_2干凝胶或石英砂为硅源,与炭黑混合,SiO_2干凝胶或石英砂与炭黑的质量比为3 2,采用碳热还原技术,在氩气气氛中于1 500℃保温2.5 h制备出SiC粉体。采用FTIR、XRD和SEM测试方法研究凝胶过程以及碳热还原产物。结果表明:原料TEOS经过非水解缩合反应制备出的SiO_2干凝胶活性较高,而后用其制备出物相较为纯净的SiC粉体,其晶粒尺寸细小,粒径均匀,粉体表面存在少量的短晶须。     

原位化学沉积法制备镍包覆碳化硅颗粒复合粉体

以六水合氯化镍为镍源,水合肼为还原剂,在SiC的表面,采用原位化学沉淀法制得包裹均匀的Ni/SiC复合粉体.采用扫描电子显微镜(SEM)、X射线衍射仪(XRD)、傅立叶红外光谱仪(FT-IR)等测试表征手段研究了工艺条件对原位沉积反应的影响.研究发现不同络合反应时间形成的镍肼络合物前驱体和镀镍反应温度可以影响反应速率,从而控制Ni颗粒的沉积速率和包裹效果.对比结果表明:络合反应时间为5 min形成的镍肼络合物前驱体在50℃水浴温度下和络合反应时间为2h得到的镍肼络合物前驱体在60℃水浴温度下得到的复合粉体包裹效果最佳.     

碳热还原法合成硼化锆粉体影响因素探究

以氧化锆(ZrO2)、硼酸(H3 BO3)和碳(C)粉为原料,研究了不同碳粉(活性炭、石墨)与前驱体粒度、温度及保温时间对碳热还原法制备硼化锆(ZrB2)粉体的影响.通过X射线衍射(XRD)分析合成粉体物相,扫描电镜(SEM)观察合成粉体形貌,并通过化学方法分析了合成粉体中的C、O含量.结果表明:以活性炭为碳源合成的粉体形貌呈条棒状,以石墨为碳源合成的粉体形貌呈规则的块状;合成粉体的粒度随前驱体粒度减小而减小,形貌由规则的块状逐渐转变为圆滑的不规则形貌,合成ZrB2粉体最小平均粒度约为1.69μm,产物中C含量随前驱体粒度减小而减少,O含量随前驱体粒度减小而增加,氧含量最低为0.54wt％;碳热还原法合成ZrB2粉体在1500℃下是可行的,但直到1900℃碳热还原反应合成ZrB2才进行完全;碳热还原反应合成ZrB2粉体最佳的反应条件为1900℃保温30 min.     

锆英石碳热还原合成ZrB_2—SiC复合粉体

以锆英石、氧化硼、活性炭为原料,采用碳热还原合成工艺制备了ZrB2—SiC复合粉体,并对合成过程进行了热力学分析。考察了反应温度及原料配比对碳热还原合成ZrB2—SiC复合粉体的物相的组成、含量和显微结构的影响。结果表明:提高反应温度有利于ZrB2—SiC复合粉体的合成,适当过量氧化硼及活性炭有利于ZrB2—SiC复合粉体的合成。合成ZrB2—SiC复合粉体的最优参数为:当ZrSiO4、B2O3和C的摩尔比为1∶2∶12,在1 773K保温3h,可得到几乎纯相的ZrB2—SiC复合粉体。     

微波烧结制备碳化硅粉体的研究

以乙炔炭黑和硅粉为原料,采用微波烧结技术合成制备了粒度不同的碳化硅粉体.研究了反应温度和保温时间对碳化硅粉体产率和粒度的影响.结果表明:在900℃反应30 min,所得产物的主要物相为β-SiC和仍残余少量金属Si.随着反应温度的升高,产物中SiC的含量不断增加,残余金属Si的含量则明显下降.当反应温度升高至1100℃以上时,则得到单相的β-SiC.在1200℃下反应5min,产物中主要物相为SiC,存在着少量未反应的金属Si,当反应时间延长到15 min时,即得到单相的β-SiC.     

碳热还原杂化前驱体合成SiC-TaC纳米复合粉体

以五氯化钽(TaCl5)、正硅酸乙酯(TEOS)和葡萄糖(C6H12O6 H2O)为原料制备了葡萄糖复合凝胶,凝胶经过450℃煅烧得到C-SiO2-Ta2O5杂化前驱体,通过碳热还原前驱体,于1200～1500℃合成了SiC-TaC纳米复合粉体,并用X射线衍射扫描电镜和能谱仪对产物进行表征。结果表明:凝胶中无定型的SiO2和Ta2O5可通过Si—O—Ta键合,均匀分布的Si—O—Ta—C长链使得杂化前驱体内部结合成为牢固的互穿网络结构;TaC于1200℃时得到,而SiC可在1400℃开始合成,反应可在1500℃完成。在不同的钽硅摩尔比下,SiC-TaC纳米复合粉体具有差异性形貌。当钽硅比约为0.02时,SiC与TaC纳米晶粒颗粒分布均匀,同质化明显。随着钽硅比的升高,SiC有从球状转变为纳米线状的趋势。     

Many Drugs of Abuse May Be Acutely Transformed to Dopamine,Norepinephrine and Epinephrine In Vivo

It is well established that a wide range of drugs of abuse acutely boost the signaling of the sympathetic nervous system and the hypothalamic–pituitary–adrenal (HPA) axis, where norepinephrine and epinephrine are major output molecules. This stimulatory effect is accompanied by such symptoms as elevated heart rate and blood pressure, more rapid breathing, increased body temperature and sweating, and pupillary dilation, as well as the intoxicating or euphoric subjective properties of the drug. While many drugs of abuse are thought to achieve their intoxicating effects by modulating the monoaminergic neurotransmitter systems (i.e., serotonin, norepinephrine, dopamine) by binding to these receptors or otherwise affecting their synaptic signaling, this paper puts forth the hypothesis that many of these drugs are actually acutely converted to catecholamines (dopamine, norepinephrine, epinephrine) in vivo, in addition to transformation to their known metabolites. In this manner, a range of stimulants, opioids, and psychedelics (as well as alcohol) may partially achieve their intoxicating properties, as well as side effects, due to this putative transformation to catecholamines. If this hypothesis is correct, it would alter our understanding of the basic biosynthetic pathways for generating these important signaling molecules, while also modifying our view of the neural substrates underlying substance abuse and dependence, including psychological stress-induced relapse. Importantly, there is a direct way to test the overarching hypothesis: administer (either centrally or peripherally) stable isotope versions of these drugs to model organisms such as rodents (or even to humans) and then use liquid chromatography-mass spectrometry to determine if the labeled drug is converted to labeled catecholamines in brain, blood plasma, or urine samples.     

ICP-MS法测定地球化学样品中As、Cr、Ge、V等18种微量痕量元素的研究

建立了测定地球化学样品中包括As、Cr、Ge、V等18种微量、痕量元素的ICP-MS方法。地化试样用HF-HNO3混酸分解后,以1 1 HNO3溶解干渣。由于制样不使用盐酸,避免了Cl对As、Cr、Ge、V的质谱干扰。用国家一级地球化学标准物质GBW 07309制备溶液优化仪器工作参数,并用于校准。方法测定限(6s)为:0.007~6.4μg/g,精密度(RSD%,n=12)为:29%~9.4%,经过国家一级地球化学标准物质的分析验证,结果与标准值吻合。方法已应用于国土资源调查的试样分析。     

基于ATRP法制备的触角状亲水性羟胺树脂的吸硼性能的研究

以大分子引发剂氯乙酰化聚苯乙烯微球(PS-acyl-Cl)经原子转移自由基聚合(ATRP)法引发丙烯酰胺(AM)和甲基丙烯酸缩水甘油酯(GMA)单体的共聚接枝,制得一种触角状亲水性环氧载体(PS-acyl-g-P(AM-co-GMA)),再经二乙醇胺(DEA)的环氧基开环胺化反应,得到一种含多个-NCH2CH2OH螯合配基的多齿-五元螯合环的触角状亲水性羟胺树脂(PS-acyl-g-P(AM-co-GMA)-DEA)。将此树脂用于硼吸附研究,结果表明,PS-acyl-g-P(AM-co-GMA)-DEA树脂对硼的吸附满足Langmuir方程,为单分子层吸附;饱和吸附量约为37.7 mg·g-1,且树脂5 min即可达到吸附平衡,与其它已报道的吸硼树脂相比,该树脂具有更高的吸附量和吸硼速率。吸附动力学研究表明,树脂吸附硼的过程主要由颗粒扩散过程控制。重复使用5次后该树脂的吸附量基本不变,解吸率均在90%以上,重复使用性能良好。     

工业评述2001～2002年国外塑料工业进展

收集了2001年7月到2002年6月有关国外塑料工业的相关期刊资料,介绍了2001年到2002年国外塑料工业的发展情况,提供了世界各地域塑料原材料的产量及构成比,日本、美国、加拿大、德国、法国、比利时、墨西哥、芬兰、西班牙等国家的树脂产量、消费量及增长率,以及日本、西欧、北美等地区的不同品种塑料原料消费量和增长率统计.按通用热塑性树脂(聚乙烯、聚丙烯、聚苯乙烯、聚氯乙烯、ABS树脂)、工程塑料(尼龙、聚碳酸酯、聚甲醛、热塑性聚酯、聚苯醚)、通用热固性树脂(酚醛、聚氨酯、不饱和树脂、环氧树脂)、特种工程塑料(聚苯硫醚、液晶聚合物、聚醚醚酮)不同品种的顺序,对树脂的产量、消费量及合成工艺、产品应用开发、树脂品种的延伸及应用的进一步扩展等有关技术作了详细的介绍.     

工业生产中物位测量的探讨与研究

在工业生产中常常会遇到常温,常压和一般介质的液位,料位和界面的测量,也会遇到高温,高压,易燃易爆,腐蚀性较强的液位,料位和界面的测量。在工业生产中物位测量有接触式和非接触式测量。但应根据生产工况及技术要求来合理选用。     

Confocal microscope—A valuable tool for examining wood-coating interface

The suitability of confocal laser scanning microscopy (CLSM) in examining a wood-coating interface was evaluated using a clear coating system. A comparison of the images of the wood-clear coating interface obtained using CLSM and light microscopy (LM) showed a marked superiority of CLSM in revealing the details of the physical nature of the interaction between the clear coating and the wood cell walls in the surface layer. The most distinct advantage of CLSM was in its ability to clearly resolve penetration of the coating into very fine cracks in cell walls, details not obtainable with LM. The information presented here demonstrates that CLSM has the potential to greatly enhance our understanding of the physical aspects of an interaction between the wood and coating at the interface.     

不同结构充油溶聚丁苯橡胶/炭黑/白炭黑复合材料的结构与性能

研究了炭黑/白炭黑填充的苯乙烯/乙烯基含量不同的充油溶聚丁苯橡胶(HPR 757 D和Buna VSL 5025-2 HM)的物理机械性能及动态力学性能,观察了填料在硫化胶中的微观分布情况。结果表明,炭黑与白炭黑相互镶嵌地分布在橡胶基质中,形成交织的填料网络。高苯乙烯基含量的HPR 757 D的拉伸强度、撕裂强度及耐磨性能优异,滚动阻力较小,填料与橡胶间的结合力强,填料的分散性较好。用白炭黑等量取代炭黑可以提高胶料的拉伸强度,降低其动态压缩温升。但炭黑/白炭黑的最佳配比与橡胶基质的分子结构有关,主链双键含量越高,白炭黑的用量也随之增多。