纳米碳化钒/碳化铬的微波辅助合成及应用

以微米级氧化钒(V_2O_5)、氧化铬(Cr_2O_3)和纳米碳黑为原料,采用机械合金化及微波辅助加热法制备了纳米碳化钒/碳化铬复合粉末。利用XRD、XPS、TG-DSC、SEM、TEM和BET对产物进行了分析表征。结果表明,纳米碳化钒/碳化铬复合粉末的最佳合成条件为:碳的质量分数为35%,反应温度为900℃,保温时间为1 h。在该条件下的反应产物主要由V_3Cr_2C_5、Cr_2VC_2和Cr_3C_2组成,颗粒为球形或类球形,分散性较好,无明显团聚现象,平均颗粒尺寸约为50 nm,复合粉末的比表面积为115.53 m~2/g。添加纳米碳化钒/碳化铬复合粉末可以提高陶瓷结合剂cBN磨具的力学性能和磨削效率,并且对磨具有减摩作用,降低磨具的损耗。     

碳热还原氮化法合成氮化钒/氮化铬复合粉末的研究

以纳米V2O5、纳米Cr2O3和纳米碳黑为原料,经过干燥、球磨混料后,在流动氮气气氛中焙烧得到了氮化钒/氮化铬复合粉末。利用XRD、TG-DSC、SEM、BET和TEM对合成产物进行了分析。结果表明：在1200 ℃、2 h条件下,可制备出平均晶粒尺寸为40 nm的VN/CrN复合粉末。复合粉末主要由VN、CrN和VCrN2组成。这3种物质均为面心立方结构,空间群均属于Fm3m。将复合粉末作为添加剂加入到陶瓷磨具结合剂中进行性能测试,结果显示：当w（复合粉末）=0.2%时,可使陶瓷磨具结合剂抗折强度和流动性分别提高约20%和50%。当w（复合粉末）=1.0%时,其抗折强度和流动性均达到最大值。     

纳米碳化钒/铬复合粉末对cBN磨具用陶瓷结合剂性能的影响

为了探索在不同烧结温度下纳米碳化钒/铬复合粉末对cBN磨具用陶瓷结合剂性能的影响,实验选用SiO_2-Na_2O-Al_2O_3-B_2O_3-CaO系统作为基础陶瓷结合剂体系,向陶瓷玻璃料中加入6%质量分数的纳米碳化钒/铬复合粉末并分别在微波烧结炉中以不同温度烧结制得纳米陶瓷结合剂。实验采用LCP-1差热膨胀仪、CMT4504型电子拉伸试验机、Stemi2000-C金相显微镜等测试分析仪器,分别对所得结合剂进行差热分析、抗折强度、显微结构分析等性能检测。实验结果表明:纳米碳化钒/铬复合粉末对结合剂性能有很大影响;加入6%纳米碳化钒/铬复合粉末能使陶瓷结合剂最大抗折强度从18.32MPa(550℃)增大到44.44MPa(600℃);纳米碳化钒/铬可以减小陶瓷结合剂的密度,以700℃的温度烧结时,结合剂密度从2.165g/cm~3减小到1.256g/cm~3;以600℃烧结时,6%纳米碳化钒/铬复合粉末能使结合剂的流动性从145.8%增大为154.8%。     

碳含量对纳米碳化钒制备的影响

以偏钒酸铵和纳米炭黑为原料,采用水溶液前驱体方法制备纳米碳化钒（V8C7）粉末。采用X射线衍射仪（XRD）、扫描电镜（SEM）和热重-差热分析仪（TG—DTA）对反应产物进行表征和分析。结果表明：在24％～28％配碳量范围内,随着碳含量增加,晶粒尺寸逐渐减小,当配碳量为28％时,相组成为单一的V8C7晶粒尺寸达到最小值32．6nm;碳含量为28％时,粉末显示出较好的分散性,主要由直径100nm左右的球形颗粒组成。     

碳热还原氮化法合成氮化钒/氮化铬复合粉末

以纳米V_2O_5、纳米Cr_2O_3和纳米碳黑为原料,经过干燥、球磨混料后,在流动氮气中焙烧,得到了氮化钒/氮化铬(VN/CrN)复合粉末。利用XRD、TG-DSC、SEM、BET和TEM对合成产物进行了表征和测试,考察了反应温度和保温时间对VN/CrN复合粉末的微观结构和性能的影响。结果表明:在1 200℃、保温2 h条件下,可制备出平均晶粒直径为40 nm的VN/CrN复合粉末。该复合粉末主要由VN、CrN和VCrN_2组成,这3种物质均为面心立方结构,空间群均属于Fm3m。复合粉末的比表面积为21.09 m~2/g。将复合粉末作为添加剂加入到陶瓷磨具结合剂中进行性能测试,结果显示:当w(复合粉末)=0.2%时,陶瓷磨具结合剂抗折强度和流动性分别提高约20%和50%;当w(复合粉末)=1.0%时,其抗折强度和流动性均达到最大值115.6 MPa和207.2%。     

V2O5制备VN的还原氮化机理

以V₂O₅粉末为原料,C粉末为还原剂,对碳热还原氮化法制备VN的机理进行研究,重点讨论了配碳量和温度对产物的影响.结果表明,V₂O₅为逐级还原,存在直接和间接还原;配碳量（C/V₂O₅）为28%（ω）时,产物氮含量最高;800¹ 000℃发生碳化反应生成VC_1-x,1000¹200℃同时发生碳化和氮化反应,主要生成V（C,N）;温度超过1 300℃,V（C,N）向VC_1-x转化.随温度升高,产物氮含量逐渐降低,钒含量逐渐升高,产物之间发生团聚甚至熔蚀形成球状,大部分颗粒粒径约为1μm.采用本工艺进行实际生产,产品氮含量>17%,钒含量为79%,碳含量<2%,表观密度约为3.5 g/cm³,符合国家标准.     

纳米碳化钒的制备及其表征分析

笔者以偏钒酸铵和纳米碳黑为原料,先将原料制成前驱体粉末,再在真空碳管炉中进行碳热还原反应,在一定条件下制备纳米碳化钒粉体。偏钒酸铵在150℃左右分解为五氧化二钒、氨气和水,使碳和钒氧化物得到充分混合,因而扩散距离缩短,碳化温度降低,反应时间缩短,晶粒尺寸得到有效控制。主要采用了XRD、SEM等分析手段研究了在不同工艺条件(反应温度、保温时间、配碳量)下对制备纳米碳化钒的影响,通过研究得到以下结论:以纳米碳黑和偏钒酸铵为原料可在1 100℃时制备相成分单一的V_8C_7粉体,粉末颗粒的形貌较规则,粉末粒度较小,呈球形或类球形,粉末颗粒的平均粒度小于100nm。当保温时间达到或接近最佳值(本实验为60min)时,反应才能进行彻底,颗粒的形貌较规则,且形貌细小。当碳含量为28%时,主相为V_8C_7,不含其它杂质相,并且晶格常数最接近理论值。     

煅烧-碱浸法从钒铬还原渣中分离回收钒铬

通过煅烧-碱浸法从钒铬还原渣中分离回收钒铬,考察了煅烧反应过程并探讨了煅烧-碱浸条件对浸出钒的影响。结果表明:煅烧过程中Cr(Ⅲ)和V(Ⅳ)反应生成中间产物CrVO4,随后CrVO4分解为Cr2O3和V2O5;相同浓度条件下,在V2O5浸出效果方面NaOH要优于Na2CO3,提高浸出介质浓度和延长浸出时间有利于V2O5的浸出,而浸出温度对V2O5浸出无明显影响,钒铬还原渣在850℃煅烧1.5 h后经3 mol·L?1 NaOH在90℃浸出1.5 h,滤渣中的Cr2O3质量分数高于96%,钒、铬的浸出率分别为87.3%和小于1%,另外,利用酸性铵盐法能够沉淀滤液中97%的钒。     

溶剂热合成纳米孔状V2O3粉末的研究

采用溶剂热路线合成纳米孔状V2O3粉末，产物用x射线衍射仪和透射电子显微镜进行表征，实验结果显示制备的V2O3粉末呈纳米孔状，颗粒的粒径在几百纳米左右，孔径在5～15nm之间。     

制备Mo2C催化剂的最佳工艺条件及其反应机理

钼酸铵焙烧制备碳化钼前驱体MoO3,以MoO3为钼源、V（H2）/V（CH4）混合气体为碳化介质采用程序升温反应法制备Mo2C催化剂;考察钼酸铵制备MoO3适宜的温度,以及程序升温反应法制备Mo2C的最适V（H2）/V（CH4）比和碳化终温,用XRD表征分析产物。得出制备Mo2C催化剂的最佳工艺条件是：钼酸铵焙烧温度为450℃、V（H2）/V（CH4）为2︰1～4︰1、碳化终温为700℃;其反应机理是：MoO3先被还原为MoO2,MoO2需经历过渡态的单质Mo才能碳化生成Mo2C。     

科技创新与钢铁科技进步

建设创新型国家是我们中华民族的历史责任。“自主创新、重点突破、支撑发展、引领未来”的16字方针应当成为我们未来创新活动的指南。建设创新型国家把自主创新放在首位,并提出了引领未来的高标准要求。钢铁科技创新必须突出重点,抓住创新成果产业化这个关键,支撑起行业和国民经济的发展。     

Orthophosphates and Diphosphates Containing Zinc and Copper and Zinc and Cobalt

Solid solutions of diphosphates of zinc and copper and of zinc and cobalt were synthesized from mixtures of pure diphosphates at temperatures up to 1000°C. Their X-ray diffractometry patterns varied continuously from one end member to the other. Solid solutions of orthophosphates of composition Zn_3−xCox(PO₄)2, with x = 0.4–1.6, were formed at temperatures up to 950°C; all exhibited the structure of γ-Zn₃(PO₄)2. Solid solutions of orthophosphates of composition Zn_3−xCu_x(PO₄)2 exhibited more-complex behavior. At 1000°C and copper contents of 20–80 mol%, a phase that is related to Cu₃(PO₄)2, termed here the "ε-phase," predominated. At 850°–950°C and in the region from 20 mol% to ∼33 mol% of copper, the solid solutions (the "η-phase") adopted the structure of graftonite. At 800°–900°C and 10–15 mol% of copper, the solid solutions exhibited a new structure (the "δ-phase"), which we found to be related to the mineral sarcopside. At temperatures 950°C, the solutions that contained 5–15 mol% of copper (the "β-phase") had the structure of β-Zn₃(PO₄)2, whereas at 800°–850°C, solutions with 5 mol% of copper (the "-phase") exhibited the structure of γ-Zn₃(PO₄)2. Attempts to synthesize Cu⁺ZnPO₄ and Cu⁺Cu²⁺Zn₃(PO₄)3 were unsuccessful.     

油气管道及储运设施安全保障技术发展现状及展望

相比已经完善丰富的开采和勘探技术,油气的运输以及储存却仍然存在不足之处。我国对能源安全提出更加严格要求的同时,对区域经济的发展规划也有足够重视。因此,保障油气管道的安全则成为了我国能源安全战略的重中之重。在阐释油气管道现阶段在储运安全保障技术发展状况的基础上,分析了现存的问题及解决问题的手段,并指出未来可能使用的目标策略,为今后研究者提供一定程度上的借鉴经验。     

膜的污染和劣化及其防治对策

较为系统地介绍了膜污染和劣化的定义和特点,因膜污染和劣化而造成的膜性能变化,以及如何预防、减少或清除膜污染和劣化的一些通用方法。     

防水透气聚氨酯薄膜及涂层的研究和应用

综述几种防水透气聚氨酯薄膜及涂层的结构、防水透气原理及其成型加工工艺。阐述防水透气聚氨酯薄膜及涂层在衣物及医用制品如高档服装、运动服、手术服、伤口敷料及手术巾等方面的应用。指出防水透气聚氨酯薄膜及涂层具有广阔的应用前景。     

SBS和SBS环氧化与顺酐化研究

SBS是(苯乙烯-丁二烯-苯乙烯)三嵌段共聚物，是含有聚苯乙烯玻璃化微区及聚丁二烯连续相的多相聚合物，具有热塑性橡胶的性质。它具有良好的拉伸性能、耐湿性、透气性、溶解性及抗滑性，而被大量用于橡胶制品、粘舍剂及沥青和树脂的改性剂等。其缺点是耐油性差，与极性物质不相容，不粘接等。用环氧化及顺酐化改性可改进这方面的缺点。SBS的环氧化改性多半使用过甲酸或过乙酸在溶液中进行。产物可作为压敏胶、热熔胶、密封胶等，用于粘接极性材料，也可作为耐油热塑性橡胶。SBS的顺酐化改性可在熔融态进行，也可在溶液中进行。产物可用作极性聚合物与非极性聚合物的共混增容剂、胶粘剂及进一步合成离聚体。     

Crystallography and equilibrium solubility for ammonium and potassium orthophosphites and hypophosphites

The composition and solubility properties of eight ammonium and potassium orthophosphites and hypophosphites were determined to evaluate the potential of these classes of materials for increasing the plant nutrient content of liquid fertilizers. Phase relationships for the systems (NH₄)₂O-P₂O₃-H₂O, K₂O-P₂O₃-H₂O, (NH₄)₂O-P₂O-H₂O, and K₂O-P₂O-H₂O were determined along with the crystallographic properties (X-ray and optical) of the solid phases. Toxicity and phosphite response was tested in greenhouse experiments for the compounds.     

VB与Excel数据导入导出的研究与实现

通过引用Excel对象实例和ADO对象,解决VB中的数据与Excel数据导入、导出的问题.     

Tetraalkynylated and Tetraalkenylated Benzenes and Pyridines: Synthesis and Photophysical Properties

Tetra(arylalkynyl)pyridines and tetra(arylalkenyl)pyridines and their benzene analogues were prepared by palladium‐catalyzed cross‐coupling reactions from the commercially available chlorinated substrates in good to excellent yields. The photophysical properties of selected compounds were investigated and compared to each other. Very good fluorescence quantum yields were observed, especially for the pyridine derivatives.     