煅烧温度对水泥熟料主要矿物形成的影响

选取SP窑硅酸盐水泥熟料、NSP窑硅酸盐水泥熟料和低热水泥熟料在1350℃、1450℃和1500℃三种温度下进行煅烧,对每种熟料在不同温度煅烧下的样品进行XRD定性、定量分析和岩相分析.研究结果表明,高温煅烧后熟料中C3S主要以M1型和M3型存在,R型C3S不明显,未发现T型C3S.此外,煅烧温度的变化对熟料中各矿物晶型和含量影响较大.随温度升高,硅酸盐矿物中C3S总体含量通常提高,C2S含量降低;三种熟料中的C3A都呈减少趋势,而C4AF则呈增加趋势,总矿物在最高温度1500℃时达到最大值.随温度升高,矿物存在不同程度的晶型转变,通常M1型C3S向M3型C3S转变.不同温度下熟料的岩相也不同,比较各熟料岩相分析结果与XRD分析结果相吻合.     

微波煅烧硅酸盐水泥的研究

用微波在1370℃,1400℃,不同生料组成下煅烧了硅酸盐水泥,并与在1450℃的电炉煅烧进行了比较.结果显示:微波煅烧比电炉煅烧的温度至少降低50℃,煅烧时间减少约70%.微波煅烧(1400℃,10min)水化活性优于电炉煅烧(1450℃,30min),强度也提高.同种生料,两种不同煅烧模式得到的熟料中,其四大矿物(C3S,C2S,C3A,C4AF)是相同的,阿利特相结构都属于Ⅲ型和Ⅰ型单斜晶系,但微波煅烧的熟料中硅酸盐矿物(C3S+C2S)总含量提高了约10%,晶体的尺寸较小且比例较高,中间相(C3A+C4AF)的含量降低了约10%,黑色中间相的尺寸有增大趋势.结果还表明,适宜的组成有利于微波烧成硅酸盐水泥,并且其矿物形成过程也不同于电炉煅烧.     

易磨硅酸盐水泥熟料的研究

研究了一种容易粉磨硅酸盐水泥熟料的组成、粉磨特性与物理性能。这种容易粉磨硅酸盐水泥熟料可以在假烧温度低于1400℃的条件下烧成。其矿物组成与普通硅酸盐水泥熟料相同，但具有C3S含量高(＞70％)的特点。在水泥熟料粉磨至比表面积320m^2/kg条件下，容易粉磨硅酸盐水泥熟料需要粉磨4．5min，而普通硅酸盐水泥熟料需要粉磨8min。容易粉磨硅酸盐水泥熟料的3d抗压强度可达37MPa，28d抗压强度可达60MPa。     

白色硅酸盐水泥熟料及结球料的矿物组成分析

白色硅酸盐水泥(简称白水泥)是装饰用的特种水泥。白水泥熟料的石灰饱和系数和通用硅酸盐水泥熟料相差不大,但硅率较高(一般在3.5~5.0),铝率很高。这种低铁、高硅、高饱和比的熟料,要求煅烧温度达　1 500℃以上,为降低烧结温度,在生料中必须加入少量矿化剂,最常用的矿化剂是萤石,其掺量控制在0.5%之内。白水泥熟料矿物组成范围为：C3S (55%~60%),C2S (20%~30%),C3A (12%~14%),C4AF(<1%)。     

高硅酸盐水泥熟料煅烧的试验研究

本文从生料易烧性人手,研究了氟硫复合矿化剂对高硅酸盐矿物含量水泥熟料煅烧的影响.利用XRD及XRF对易烧性较好且C3S含量较高的熟料进行了矿物组成及硫含量分析.研究结果表明:在添加氟硫复合矿化剂的条件下可煅烧获得硅酸盐矿物含量大于90％且C3S含量大于70％的高硅酸盐水泥熟料.熟料中f-CaO含量随饱和比LAD的增加而增加,随助溶剂量QLP的增加逐渐减少,随硫过量系数EC的增加而略微升高.熟料中的主要矿物C3S和C2S形成情况良好.     

磷尾矿作原料在水泥生产中的工业试验分析

为合理开发利用日益剧增的磷尾矿工业废渣,本文将磷尾矿应用于水泥生产中。用磷尾矿取代部分原料配制生料,在工业窑进行了试生产,并通过XRD、TG-DTA、岩相、SEM-DES分析方法,与普通硅酸盐水泥熟料进行对比。结果表明:磷尾矿作为原料制备硅酸盐水泥熟料,可以降低生料中碳酸钙的分解温度;减少熟料中的游离氧化钙含量,显著改善了生料的易烧性。掺磷尾矿熟料晶型形貌较好,MⅠ型的C3S和β-C2S的含量有所增加,这有利于熟料早期和后期强度的提高。磷元素在B矿中的富集最多。但由于磷尾矿本身磷含量波动大且试验工厂工业均化效果不佳,实际生产熟料质量产生一定的波动。     

不同熟料矿物含量的水泥对混凝土部分性能的影响

研究了不同熟料矿物含量的水泥对配制混凝土抗疲劳、抗冲击和耐磨性能的影响。结果表明,当熟料中硅酸盐矿物C2S、C3S含量接近时,随着熟料中Fe2O3含量的增加,C4AF含量增加,C3A含量降低,所配制混凝土在28d和90d龄期的抗疲劳、抗冲击和耐磨性能都依次提高;在保证熟料中适量C3S满足强度要求和熔剂矿物C3A、C4AF含量接近的前提下,低C3S高C2S含量的水泥配制的混凝土抗疲劳、抗冲击和耐磨性能都优于高C3S低C2S含量的水泥配制的混凝土。即：在保证足够C3S含量满足强度要求、熔剂矿物含量为19%～20%时,适当提高C4AF和C2S含量对提高混凝土的上述性能是有益的。     

大冶铜尾矿配制高强低能耗水泥的研究

以大冶铜尾矿和部分纯化学试剂为原料，在实验室配料、煅烧高铁和普通硅酸盐水泥，并用岩相、ＸＲＤ等手段进行分析研究。分析表明，由于大冶铜尾矿中ＳＯ_３含量低，尽管显示一定的矿化作用，但效果不明显。但所配制的水泥，特别是掺尾矿达２４％时配制的高铁水泥，具有早强、后期强度高和煅烧温度低的特点。分析认为是铜尾矿中微量元素固溶于熟料矿物中增加矿物结构缺陷，从而提高熟料矿物的水化活性和熟料强度。     

基于CaO-SiO2-Al2O3-Fe2O3-SO3系统的水泥熟料矿物研究

采用石灰石、硬石膏、粉煤灰、硅石为原料,研究了固定铝硫比（P=3.82）条件下,氧化铝含量为10%时,碱度系数和煅烧温度对CaO-SiO2-Al2O3-Fe2O3-SO3系统水泥熟料矿物烧成的影响。结果表明,碱度系数为1.2,煅烧温度范围为1375~1425℃时制得的水泥为高贝利特硅酸盐水泥;C4A3S分解生成了C3A,而非C12A7;在SO3和C3A存在的条件下,促进C3S在低温下形成,部分C3S在高温下分解为α＇-C2S;水泥熟料的矿物形貌未发生明显的变化。     

钼尾矿制备贝利特水泥熟料早期性能研究

本文以钼尾矿为主要原料制备贝利特水泥熟料.并通过强度、X射线衍射、扫描电镜等测试,研究了原料配比和石膏活化剂掺量对水泥熟料性能的影响.实验结果表明:以质量分数为23.3％钼尾矿、3.4％的河砂和73.3％的石灰石为原料,再添加1.5％的石膏作活化剂,在1350℃下煅烧0.5h制得的贝利特水泥熟料强度最高.钼尾矿的掺加对贝利特水泥熟料主要矿物种类没有影响.加入石膏可促进熟料烧成,且生成了少量硫铝酸钙,使得熟料强度明显增加.     

Many Drugs of Abuse May Be Acutely Transformed to Dopamine,Norepinephrine and Epinephrine In Vivo

It is well established that a wide range of drugs of abuse acutely boost the signaling of the sympathetic nervous system and the hypothalamic–pituitary–adrenal (HPA) axis, where norepinephrine and epinephrine are major output molecules. This stimulatory effect is accompanied by such symptoms as elevated heart rate and blood pressure, more rapid breathing, increased body temperature and sweating, and pupillary dilation, as well as the intoxicating or euphoric subjective properties of the drug. While many drugs of abuse are thought to achieve their intoxicating effects by modulating the monoaminergic neurotransmitter systems (i.e., serotonin, norepinephrine, dopamine) by binding to these receptors or otherwise affecting their synaptic signaling, this paper puts forth the hypothesis that many of these drugs are actually acutely converted to catecholamines (dopamine, norepinephrine, epinephrine) in vivo, in addition to transformation to their known metabolites. In this manner, a range of stimulants, opioids, and psychedelics (as well as alcohol) may partially achieve their intoxicating properties, as well as side effects, due to this putative transformation to catecholamines. If this hypothesis is correct, it would alter our understanding of the basic biosynthetic pathways for generating these important signaling molecules, while also modifying our view of the neural substrates underlying substance abuse and dependence, including psychological stress-induced relapse. Importantly, there is a direct way to test the overarching hypothesis: administer (either centrally or peripherally) stable isotope versions of these drugs to model organisms such as rodents (or even to humans) and then use liquid chromatography-mass spectrometry to determine if the labeled drug is converted to labeled catecholamines in brain, blood plasma, or urine samples.     

ICP-MS法测定地球化学样品中As、Cr、Ge、V等18种微量痕量元素的研究

建立了测定地球化学样品中包括As、Cr、Ge、V等18种微量、痕量元素的ICP-MS方法。地化试样用HF-HNO3混酸分解后,以1 1 HNO3溶解干渣。由于制样不使用盐酸,避免了Cl对As、Cr、Ge、V的质谱干扰。用国家一级地球化学标准物质GBW 07309制备溶液优化仪器工作参数,并用于校准。方法测定限(6s)为:0.007~6.4μg/g,精密度(RSD%,n=12)为:29%~9.4%,经过国家一级地球化学标准物质的分析验证,结果与标准值吻合。方法已应用于国土资源调查的试样分析。     

基于ATRP法制备的触角状亲水性羟胺树脂的吸硼性能的研究

以大分子引发剂氯乙酰化聚苯乙烯微球(PS-acyl-Cl)经原子转移自由基聚合(ATRP)法引发丙烯酰胺(AM)和甲基丙烯酸缩水甘油酯(GMA)单体的共聚接枝,制得一种触角状亲水性环氧载体(PS-acyl-g-P(AM-co-GMA)),再经二乙醇胺(DEA)的环氧基开环胺化反应,得到一种含多个-NCH2CH2OH螯合配基的多齿-五元螯合环的触角状亲水性羟胺树脂(PS-acyl-g-P(AM-co-GMA)-DEA)。将此树脂用于硼吸附研究,结果表明,PS-acyl-g-P(AM-co-GMA)-DEA树脂对硼的吸附满足Langmuir方程,为单分子层吸附;饱和吸附量约为37.7 mg·g-1,且树脂5 min即可达到吸附平衡,与其它已报道的吸硼树脂相比,该树脂具有更高的吸附量和吸硼速率。吸附动力学研究表明,树脂吸附硼的过程主要由颗粒扩散过程控制。重复使用5次后该树脂的吸附量基本不变,解吸率均在90%以上,重复使用性能良好。     

工业评述2001～2002年国外塑料工业进展

收集了2001年7月到2002年6月有关国外塑料工业的相关期刊资料,介绍了2001年到2002年国外塑料工业的发展情况,提供了世界各地域塑料原材料的产量及构成比,日本、美国、加拿大、德国、法国、比利时、墨西哥、芬兰、西班牙等国家的树脂产量、消费量及增长率,以及日本、西欧、北美等地区的不同品种塑料原料消费量和增长率统计.按通用热塑性树脂(聚乙烯、聚丙烯、聚苯乙烯、聚氯乙烯、ABS树脂)、工程塑料(尼龙、聚碳酸酯、聚甲醛、热塑性聚酯、聚苯醚)、通用热固性树脂(酚醛、聚氨酯、不饱和树脂、环氧树脂)、特种工程塑料(聚苯硫醚、液晶聚合物、聚醚醚酮)不同品种的顺序,对树脂的产量、消费量及合成工艺、产品应用开发、树脂品种的延伸及应用的进一步扩展等有关技术作了详细的介绍.     

工业生产中物位测量的探讨与研究

在工业生产中常常会遇到常温,常压和一般介质的液位,料位和界面的测量,也会遇到高温,高压,易燃易爆,腐蚀性较强的液位,料位和界面的测量。在工业生产中物位测量有接触式和非接触式测量。但应根据生产工况及技术要求来合理选用。     

Confocal microscope—A valuable tool for examining wood-coating interface

The suitability of confocal laser scanning microscopy (CLSM) in examining a wood-coating interface was evaluated using a clear coating system. A comparison of the images of the wood-clear coating interface obtained using CLSM and light microscopy (LM) showed a marked superiority of CLSM in revealing the details of the physical nature of the interaction between the clear coating and the wood cell walls in the surface layer. The most distinct advantage of CLSM was in its ability to clearly resolve penetration of the coating into very fine cracks in cell walls, details not obtainable with LM. The information presented here demonstrates that CLSM has the potential to greatly enhance our understanding of the physical aspects of an interaction between the wood and coating at the interface.     

不同结构充油溶聚丁苯橡胶/炭黑/白炭黑复合材料的结构与性能

研究了炭黑/白炭黑填充的苯乙烯/乙烯基含量不同的充油溶聚丁苯橡胶(HPR 757 D和Buna VSL 5025-2 HM)的物理机械性能及动态力学性能,观察了填料在硫化胶中的微观分布情况。结果表明,炭黑与白炭黑相互镶嵌地分布在橡胶基质中,形成交织的填料网络。高苯乙烯基含量的HPR 757 D的拉伸强度、撕裂强度及耐磨性能优异,滚动阻力较小,填料与橡胶间的结合力强,填料的分散性较好。用白炭黑等量取代炭黑可以提高胶料的拉伸强度,降低其动态压缩温升。但炭黑/白炭黑的最佳配比与橡胶基质的分子结构有关,主链双键含量越高,白炭黑的用量也随之增多。