钨掺杂二氧化钒/石墨烯复合物的制备及性能

以氧化石墨烯粉末(GO)、五氧化二钒、草酸和钨酸铵为原料,用水热法制备了一系列钨掺杂二氧化钒/石墨烯复合物,考察了钨掺杂量、氧化石墨烯用量对复合材料的相变温度及导热率的影响。通过XRD、SEM、DSC、FTIR、激光导热系数测量仪对复合材料的结构形貌、相变性能进行了表征。结果表明,石墨烯复合材料的二氧化钒粒子团聚情况得到有效改善,并均匀负载在石墨烯表面。当钨原子百分含量为2.5%、氧化石墨烯含量为4%(以五氧化二钒质量为基准)时,形成的钨掺杂二氧化钒/石墨烯复合物与纯二氧化钒相比,相变温度由66.0℃降低到32.2℃,导热率提升到16.341W/(m·K)。该复合材料能同时满足良好的隔热性与高导热性等要求。     

掺钨VO_2纳米粉体的制备及其热致相变特能的研究

以偏钒酸铵(NH_4VO_3)和偏钨酸铵((NH_4)_6H_2W_(12)O_(40).XH_2O)为分别为钒源和掺杂剂,采用水热法进行掺杂钨(W)离子的二氧化钒(VO_2)粉体的制备,在通有氩气气氛的管式炉中600℃热处理6 h后得到纯净的掺杂W二氧化钒粉体,通过XRD、SEM及XPS分析所制备的掺钨二氧化钒的晶体结构、表面形貌以及组分价态的变化。利用DSC及FTIR检测其相变温度点以及相变前后的红外透过率。结果表明:制备出的掺杂W的VO_2粉末为M型纳米片状粉体,钨元素以W~(6+)形式掺入VO_2晶体,取代晶格中部分V原子。随着W离子的摩尔比的增加,VO_2的相变点明显下降,当掺量为2%时,其相变点降低为43℃,相变前后的红外透过率也发生了显著地下降,最大下降量达到40%。     

石墨烯/聚苯乙烯导热复合材料的制备

以偶氮二异丁脒盐酸盐(AIBA)为引发剂,采用分散聚合的方法合成了表面带正电荷、粒径在600 nm的聚苯乙烯(PS)微球,通过自组装将氧化石墨烯包覆于PS微球表面,用化学还原法将氧化石墨烯还原为石墨烯,制备了石墨烯包覆聚苯乙烯微球的复合分散体和压制成型制备的石墨烯/聚苯乙烯导热复合材料。结果表明,随着初始氧化石墨烯投料量的增大,制备得到的石墨烯/聚苯乙烯复合材料的导热系数逐渐增大,投料量为20%时,复合材料的导热系数达到0.41 W/(m·K),相比纯PS本体提高了116%。     

换热器表面复合涂层耐腐蚀与导热性能

为了提升换热器表面耐腐蚀性且不影响换热器的换热效果，以石墨烯，石墨粉末，环氧树脂等为原料，制备应用于换热器表面的耐腐蚀高导热石墨烯复合涂层。经硫酸腐蚀实验、导热实验、结合强度实验的测试，结果表明：涂层的耐腐蚀性能随石墨烯含量的增加而提升，当石墨烯质量分数达到0.06%时，涂层的腐蚀速率达到最低值0.2338mg/(cm2·h)，其耐腐蚀性能远强于304不锈钢的1.5 mg/(cm2·h)；涂层的导热性能随石墨粉含量的增加而提升，且当石墨质量分数为8%时达到最大值35.848 W/(m·K)；涂层的结合强度达到ASTM等级：5B。     

石墨烯包裹的PMMA微球改性环氧树脂的导热性

利用悬浮聚合法和改进Hummers法分别制得粒径为200~300 nm的聚甲基丙烯酸甲酯(PMMA)微球和氧化石墨烯,再用化学还原方法将氧化石墨烯包裹在PMMA微球上,最后利用氧化石墨烯包裹的PMMA微球对环氧树脂进行改性,制得低氧化石墨烯含量的高导热率环氧树脂复合材料。包裹氧化石墨烯的PMMA微球改性后的环氧树脂复合材料微观形貌测试结果表明,氧化石墨烯包裹的PMMA微球均匀分散在环氧树脂基体中;环氧树脂复合材料的导热性在氧化石墨烯含量为0.1%、0.3%、0.5%、0.7%和1%时,导热率分别由纯环氧树脂的0.19 W/(m·K)提高到0.52、0.99、1.22、1.33和1.42 W/(m·K)。     

新型导热塑料

LNP工程塑料公司新推出一系列导热性复合塑料,称作Konduit复合物。在聚合物基体材料中引入导热添加剂,使塑料制作的排热效率可提高50倍。目前,导热添加剂分2类:1类是陶瓷,加入后达到中等热导率(2 W/m·K);另1类是碳纤维,加入后可达到更高的热导率(10 W/m·K)。产     

形态稳定的Na2SO4·10H2O-Na2HPO4·12H2O共晶盐相变储能材料的制备及热性能提升

在复合相变材料中引入碳纳米纤维(CNFs)提高相变体系的导热系数,以实现相变材料与外界环境进行快速有效的热量交换。本文采用熔融共混法将Na₂SO₄·10H₂O和Na₂HPO₄·12H₂O制备成共晶盐相变材料,借助聚丙烯酸钠构筑三维聚合物网络封装相变材料,利用CNFs提升复合材料的导热系数。通过Raman、XPS等测试方法,研究了CNFs经高能球磨、湿化学氧化处理后,其表面含氧官能团的变化;借助Raman、DSC、Hot disk、TG等测试方法,分析了CNFs对复合材料化学相容性、相变行为、热稳定性、潜热容量、导热系数的影响。结果表明:CNFs经过功能化处理,氧、碳原子比增大至0.140,氧化效果显著;CNFs引入至复合相变材料中,体系内各组分之间存在良好的化学相容性;当CNFs的添加量达到3%(质量分数),复合材料的固、液态导热系数分别达到1.05 W/(m·K)、0.88 W/(m·K),相较于未添加CNFs的复合材料,固、液态导热性能分别提升了69.4%、60.0%;经过1 000次循环试验,复合材料的熔融焓和结晶焓相较循环前分别下降了56.2%、65.3%,相变体系仍然具备一定的储热能力,表明将相变材料嵌入三维网络结构是一种有效的封装策略。     

癸酸-棕榈酸/SiO2复合相变材料的热性能

以SiO2为载体、癸酸-棕榈酸为相变材料,采用溶胶-凝胶法制备癸酸-棕榈酸/SiO2复合相变材料,考察了其储热性能、导热性能、微观形貌和组成结构. 结果表明,当癸酸-棕榈酸掺入量为0.08 mol时,所制材料具有最好的潜热性能,相变温度为20.02~22.08℃,相变焓为44.53~50.51 J/g,适合在建筑领域应用;当癸酸-棕榈酸掺入量为0.06 mol时,材料导热性能最好,导热系数在第一降温阶段为0.211 W/(m×K),相变平台阶段为0.017 W/(m×K),第二降温阶段为0.040 W/(m×K);材料中SiO2与癸酸-棕榈酸仅是物理嵌合,未发生明显的化学作用,癸酸-棕榈酸掺杂过量时明显包裹SiO2,导致复合相变材料潜热性能和导热性能下降.     

石墨改性膨胀珍珠岩相变储热复合材料试验及性能

针对传统暖通用的储热材料导热性能差的问题,用石墨粉改性膨胀珍珠岩相变储热复合材料,并对改性后复合材料的性能进行测试.结果表明:石墨粉添加量为1％的复合相变储热材料储热和导热性能良好,热导率为0.392W/(m?K).以该材料为原材制作的蓄热砖同样发挥出较好的储热作用,热导率可达0.412W/(m?K),养护28d后,力...     

高分子辅助沉积法制备钨掺杂的二氧化钒薄膜

利用高分子辅助沉积法(PAD)制备出钨掺杂二氧化钒(VO_2)薄膜。采用X射线衍射、光电子能谱、扫描电子显微镜、Raman光谱等表征技术对不同含量钨掺杂的VO_2薄膜性能进行了研究。结果表明:利用PAD方法制备的VO_2薄膜质量较好,且钨离子掺杂成功。同时Raman光谱显示,钨掺杂1.0%(摩尔分数)的薄膜在相变过程中出现M2相。电学测试结果显示,钨掺杂的VO_2薄膜相变温度大幅下降,每掺杂0.3%(摩尔分数)的钨离子,相变温度下降10℃,且随着钨掺量的增加,VO_2薄膜的热滞回线宽度减小。     

Many Drugs of Abuse May Be Acutely Transformed to Dopamine,Norepinephrine and Epinephrine In Vivo

It is well established that a wide range of drugs of abuse acutely boost the signaling of the sympathetic nervous system and the hypothalamic–pituitary–adrenal (HPA) axis, where norepinephrine and epinephrine are major output molecules. This stimulatory effect is accompanied by such symptoms as elevated heart rate and blood pressure, more rapid breathing, increased body temperature and sweating, and pupillary dilation, as well as the intoxicating or euphoric subjective properties of the drug. While many drugs of abuse are thought to achieve their intoxicating effects by modulating the monoaminergic neurotransmitter systems (i.e., serotonin, norepinephrine, dopamine) by binding to these receptors or otherwise affecting their synaptic signaling, this paper puts forth the hypothesis that many of these drugs are actually acutely converted to catecholamines (dopamine, norepinephrine, epinephrine) in vivo, in addition to transformation to their known metabolites. In this manner, a range of stimulants, opioids, and psychedelics (as well as alcohol) may partially achieve their intoxicating properties, as well as side effects, due to this putative transformation to catecholamines. If this hypothesis is correct, it would alter our understanding of the basic biosynthetic pathways for generating these important signaling molecules, while also modifying our view of the neural substrates underlying substance abuse and dependence, including psychological stress-induced relapse. Importantly, there is a direct way to test the overarching hypothesis: administer (either centrally or peripherally) stable isotope versions of these drugs to model organisms such as rodents (or even to humans) and then use liquid chromatography-mass spectrometry to determine if the labeled drug is converted to labeled catecholamines in brain, blood plasma, or urine samples.     

ICP-MS法测定地球化学样品中As、Cr、Ge、V等18种微量痕量元素的研究

建立了测定地球化学样品中包括As、Cr、Ge、V等18种微量、痕量元素的ICP-MS方法。地化试样用HF-HNO3混酸分解后,以1 1 HNO3溶解干渣。由于制样不使用盐酸,避免了Cl对As、Cr、Ge、V的质谱干扰。用国家一级地球化学标准物质GBW 07309制备溶液优化仪器工作参数,并用于校准。方法测定限(6s)为:0.007~6.4μg/g,精密度(RSD%,n=12)为:29%~9.4%,经过国家一级地球化学标准物质的分析验证,结果与标准值吻合。方法已应用于国土资源调查的试样分析。     

基于ATRP法制备的触角状亲水性羟胺树脂的吸硼性能的研究

以大分子引发剂氯乙酰化聚苯乙烯微球(PS-acyl-Cl)经原子转移自由基聚合(ATRP)法引发丙烯酰胺(AM)和甲基丙烯酸缩水甘油酯(GMA)单体的共聚接枝,制得一种触角状亲水性环氧载体(PS-acyl-g-P(AM-co-GMA)),再经二乙醇胺(DEA)的环氧基开环胺化反应,得到一种含多个-NCH2CH2OH螯合配基的多齿-五元螯合环的触角状亲水性羟胺树脂(PS-acyl-g-P(AM-co-GMA)-DEA)。将此树脂用于硼吸附研究,结果表明,PS-acyl-g-P(AM-co-GMA)-DEA树脂对硼的吸附满足Langmuir方程,为单分子层吸附;饱和吸附量约为37.7 mg·g-1,且树脂5 min即可达到吸附平衡,与其它已报道的吸硼树脂相比,该树脂具有更高的吸附量和吸硼速率。吸附动力学研究表明,树脂吸附硼的过程主要由颗粒扩散过程控制。重复使用5次后该树脂的吸附量基本不变,解吸率均在90%以上,重复使用性能良好。     

工业评述2001～2002年国外塑料工业进展

收集了2001年7月到2002年6月有关国外塑料工业的相关期刊资料,介绍了2001年到2002年国外塑料工业的发展情况,提供了世界各地域塑料原材料的产量及构成比,日本、美国、加拿大、德国、法国、比利时、墨西哥、芬兰、西班牙等国家的树脂产量、消费量及增长率,以及日本、西欧、北美等地区的不同品种塑料原料消费量和增长率统计.按通用热塑性树脂(聚乙烯、聚丙烯、聚苯乙烯、聚氯乙烯、ABS树脂)、工程塑料(尼龙、聚碳酸酯、聚甲醛、热塑性聚酯、聚苯醚)、通用热固性树脂(酚醛、聚氨酯、不饱和树脂、环氧树脂)、特种工程塑料(聚苯硫醚、液晶聚合物、聚醚醚酮)不同品种的顺序,对树脂的产量、消费量及合成工艺、产品应用开发、树脂品种的延伸及应用的进一步扩展等有关技术作了详细的介绍.     

工业生产中物位测量的探讨与研究

在工业生产中常常会遇到常温,常压和一般介质的液位,料位和界面的测量,也会遇到高温,高压,易燃易爆,腐蚀性较强的液位,料位和界面的测量。在工业生产中物位测量有接触式和非接触式测量。但应根据生产工况及技术要求来合理选用。     

Confocal microscope—A valuable tool for examining wood-coating interface

The suitability of confocal laser scanning microscopy (CLSM) in examining a wood-coating interface was evaluated using a clear coating system. A comparison of the images of the wood-clear coating interface obtained using CLSM and light microscopy (LM) showed a marked superiority of CLSM in revealing the details of the physical nature of the interaction between the clear coating and the wood cell walls in the surface layer. The most distinct advantage of CLSM was in its ability to clearly resolve penetration of the coating into very fine cracks in cell walls, details not obtainable with LM. The information presented here demonstrates that CLSM has the potential to greatly enhance our understanding of the physical aspects of an interaction between the wood and coating at the interface.     

不同结构充油溶聚丁苯橡胶/炭黑/白炭黑复合材料的结构与性能

研究了炭黑/白炭黑填充的苯乙烯/乙烯基含量不同的充油溶聚丁苯橡胶(HPR 757 D和Buna VSL 5025-2 HM)的物理机械性能及动态力学性能,观察了填料在硫化胶中的微观分布情况。结果表明,炭黑与白炭黑相互镶嵌地分布在橡胶基质中,形成交织的填料网络。高苯乙烯基含量的HPR 757 D的拉伸强度、撕裂强度及耐磨性能优异,滚动阻力较小,填料与橡胶间的结合力强,填料的分散性较好。用白炭黑等量取代炭黑可以提高胶料的拉伸强度,降低其动态压缩温升。但炭黑/白炭黑的最佳配比与橡胶基质的分子结构有关,主链双键含量越高,白炭黑的用量也随之增多。