以正硅酸乙酯(TEOS)为包覆原料,采用包覆法对金属铝粉进行包覆改性后利用注浆成型制备多孔氧化铝陶瓷,研究了TEOS/Al质量比对铝粉包覆率的影响以及铝粉包覆率、包覆铝粉加入量对多孔氧化铝陶瓷性能的影响。研究结果表明,随着TEOS/Al质量增大,铝粉包覆率逐渐增大,并在TEOS/Al质量比为4:5时趋于100%;随着铝粉包覆率增大,多孔氧化铝陶瓷的显气孔率逐渐增大,烧成线收缩率及抗弯强度逐渐减小,但当TEOS/Al质量比超过4:5,达到5:5时,陶瓷显气孔率减小,烧成收缩率和抗弯强度增大;而随着包覆铝粉加入量提高,多孔氧化铝陶瓷的显气孔率逐渐增大,烧成线收缩率及抗弯强度逐渐减小。     

聚空心球对氧化铝陶瓷性能的影响

研究了聚空心球直接添加或聚空心球作为多孔层对氧化铝陶瓷力学性能的影响。在1200～1550℃烧成温度范围内,随烧成温度升高,Al2O3晶粒长大,聚空心球与基体之间结合力增加,聚空心球在烧成温度为1550℃时变形,试样密度为2.84g/cm3,显气孔率为25.2%,抗压强度和抗弯强度最高。当层状陶瓷的聚空心球多孔层含量为60%（质量分数）,层厚比为5/2时,聚空心球的断裂方式由沿球断裂转变为穿球断裂,机械性能得到提高,断裂韧性最高为5.59MPa.m1/2。     

凝胶注模技术制备高强度多孔氮化硅陶瓷

采用凝胶注模技术和无压烧结工艺制备高孔隙率、高强度多孔氮化硅陶瓷。研究了浆料固相含量对多孔氮化硅陶瓷坯体相对质量损失和收缩率的影响,测定了材料在烧结前后的物相组成,分析了浆料固相含量对多孔氮化硅陶瓷显微结构、孔隙率、弯曲强度及断裂韧性的影响。结果表明:随浆料固相含量增大,坯体相对质量损失率和收缩率减小,烧结后的多孔氮化硅陶瓷孔隙率由65.24%减小到61.19%;而弯曲强度和断裂韧性分别由93.91MPa和1.48MPa·m1/2提高到100.83MPa和1.58MPa·m1/2。长棒状β-Si3N4晶粒无规律的交错搭接和相互咬合是多孔氮化硅陶瓷在保持高孔隙率的同时具有高强度的主要原因。     

CMS和纳米TiO2对氧化铝陶瓷烧结的影响

选用CaO-MgO-SiO2(CMS)和纳米TiO2两种添加剂及其复合来降低氧化铝陶瓷的烧结温度、改善其烧结性能.讨论了烧结助剂配比和掺量、烧结温度对氧化铝陶瓷的相对密度、抗弯强度的影响,利用扫描电子显微镜观察了氧化铝陶瓷的显微结构.研究结果发现:CMS/TiO2质量比为1/1,(CMS+TiO2)质量分数为6%,烧结温度为1450 ℃时,氧化铝陶瓷相对密度为93.07 %,晶粒细小均匀、排列紧密、平均粒径3 μm,抗弯强度达到362.87 MPa.     

La_2O_3增强高性能氧化铝陶瓷制备工艺研究

本文以氧化铝粉、硝酸镧为主要原料,研究了La_2O_3对氧化铝陶瓷显微结构及性能的影响。结果表明:La_2O_3的加入有助于提高氧化铝陶瓷的力学性能,添加0.1wt%La_2O_3的氧化铝陶瓷经1 490℃烧结后具有最佳的力学性能,其抗弯强度和断裂韧性分别达到460.145 MPa、5.26 MPa·m~(1/2),较未添加La_2O_3氧化铝陶瓷的抗弯强度和断裂韧性分别提升了10.67%和1.15%,掺镧氧化铝陶瓷平均晶粒尺寸约为3.5μm,La_2O_3抑制氧化铝陶瓷晶粒长大的效果较为明显。     

多孔Si_3N_4/BN复相陶瓷的常压烧结制备

以微米级Si3N4和h-BN粉末为原料,Yb2O3-Al2O3-Y2O3为烧结助剂,采用常压烧结工艺制备了BN体积含量为25%的多孔Si3N4/25%h-BN复相陶瓷。研究了Yb2O3添加量对Si3N4/25%BN复相陶瓷力学性能的影响,通过X射线衍射和扫描电子显微镜分析了复相陶瓷的物相组成和显微结构。结果表明:随着Yb2O3添加量增加,制备的Si3N4/25%BN复相陶瓷的气孔率逐渐增大,收缩率变小,相对密度减小。Yb2O3添加量为2%(质量分数)时,Si3N4/25%BN复相陶瓷的气孔率为15.1%,相对密度为72.8%;当Yb2O3添加量提高至15%时复相陶瓷的气孔率增加至32.1%,相对密度则降至60.3%。同时随着Yb2O3添加量增加,复相陶瓷的室温抗弯强度先增大后减小,Yb2O3含量为4%时,室温抗弯强度呈现最大值,可达264.3MPa。     

热压烧结细晶粒氧化铝陶瓷(英文)

以沉淀法制各的商业α-Al2O3粉体为原料,自制镁铝硅玻璃为烧结助剂,采用热压烧结工艺低温制备高性能氧化铝陶瓷.用Archimedes法、电子探针和三点弯曲法研究了氧化铝陶瓷的致密化行为、显微结构和力学性能.结果表明:在1400℃烧结的氧化铝陶瓷的相对密度高达98.9%,晶粒细小,平均晶粒尺寸约为0.6μm,晶界上有莫来石相析出,样品的抗弯强度和断裂韧性分别达442MPa和4.7MPa·m1/2.     

环氧树脂含量对激光选区烧结制备多孔煤系高岭土陶瓷性能的影响

目前,我国对煤系高岭土资源的整体深加工技术水平较低,导致了资源浪费和环境污染。本文分别以煅烧煤系高岭土和环氧树脂为原料和粘结剂,利用激光选区烧结工艺制备多孔煤系高岭土陶瓷,研究了环氧树脂含量对多孔煤系高岭土陶瓷性能的影响。研究表明,制备的多孔煤系高岭土陶瓷主要物相为莫来石和方石英,其孔隙分布均匀。随着环氧树脂质量分数从10%增大到25%,多孔煤系高岭土陶瓷素坯的抗弯强度由0.17 MPa增大到0.32 MPa,多孔煤系高岭土陶瓷的抗弯强度由2.81 MPa减小到0.82 MPa,其气孔率由50.37%增大到59.69%。以煤系高岭土为原料,采用激光选区烧结工艺制备多孔陶瓷对煤系高岭土资源的开发利用具有较为重要的意义。     

加入陶瓷空心微珠对氧化铝空心球轻质浇注料性能的影响

为了降低氧化铝空心球轻质浇注料的体积密度并优化其综合性能,在氧化铝空心球轻质浇注料中引入陶瓷空心微珠替代部分高铝矾土粉,研究陶瓷空心微珠加入量(质量分数分别为0、2%、4%、6%和8%)对该浇注料的体积密度、常温强度、热导率、烧后线变化率的影响。结果表明,在氧化铝空心球轻质浇注料中引入陶瓷空心微珠替代部分高铝矾土粉,可以降低氧化铝空心球轻质浇注料的体积密度和热导率,但耐压强度和常温抗折强度也稍有降低。从综合性能来看,氧化铝空心球轻质浇注料中陶瓷空心微珠的最佳加入量为2%~4%(w)。     

烧结工艺对电容式高温压力传感器用氧化铝陶瓷基片的影响

为了研究不同烧结工艺对电容式高温压力传感器用氧化铝陶瓷基片的影响,以纳米α-Al_2O_3为主要原料,加入ZrO_2、MgO和Y_2O_3等粉料作为烧结助剂,采用流延成型、等静压成型和气氛保护无压烧结技术制备了氧化铝陶瓷基片。分别对试样的相对密度、抗弯强度、硬度及断裂韧性进行测试,并利用扫描电镜(SEM)观察其显微组织形貌。结果表明:陶瓷基片的烧结不宜接触O_2,因此在烧结过程中应选用流动高纯N_2对其进行气氛保护。为防止试样烧结后变形翘曲,基片在装载时应适度施加压盖,提高平整度。此陶瓷基片的理想烧结温度约为1550℃,对应试样的相对密度、抗弯强度、硬度及断裂韧性数值分别达到了98.8%、766 MPa、17.2 GPa及4.2 MPa·m~(1/2)。1550℃烧结试样显微组织呈现韧窝状,该结构有助于提高陶瓷基体的致密度及强韧化程度。     

Many Drugs of Abuse May Be Acutely Transformed to Dopamine,Norepinephrine and Epinephrine In Vivo

It is well established that a wide range of drugs of abuse acutely boost the signaling of the sympathetic nervous system and the hypothalamic–pituitary–adrenal (HPA) axis, where norepinephrine and epinephrine are major output molecules. This stimulatory effect is accompanied by such symptoms as elevated heart rate and blood pressure, more rapid breathing, increased body temperature and sweating, and pupillary dilation, as well as the intoxicating or euphoric subjective properties of the drug. While many drugs of abuse are thought to achieve their intoxicating effects by modulating the monoaminergic neurotransmitter systems (i.e., serotonin, norepinephrine, dopamine) by binding to these receptors or otherwise affecting their synaptic signaling, this paper puts forth the hypothesis that many of these drugs are actually acutely converted to catecholamines (dopamine, norepinephrine, epinephrine) in vivo, in addition to transformation to their known metabolites. In this manner, a range of stimulants, opioids, and psychedelics (as well as alcohol) may partially achieve their intoxicating properties, as well as side effects, due to this putative transformation to catecholamines. If this hypothesis is correct, it would alter our understanding of the basic biosynthetic pathways for generating these important signaling molecules, while also modifying our view of the neural substrates underlying substance abuse and dependence, including psychological stress-induced relapse. Importantly, there is a direct way to test the overarching hypothesis: administer (either centrally or peripherally) stable isotope versions of these drugs to model organisms such as rodents (or even to humans) and then use liquid chromatography-mass spectrometry to determine if the labeled drug is converted to labeled catecholamines in brain, blood plasma, or urine samples.     

ICP-MS法测定地球化学样品中As、Cr、Ge、V等18种微量痕量元素的研究

建立了测定地球化学样品中包括As、Cr、Ge、V等18种微量、痕量元素的ICP-MS方法。地化试样用HF-HNO3混酸分解后,以1 1 HNO3溶解干渣。由于制样不使用盐酸,避免了Cl对As、Cr、Ge、V的质谱干扰。用国家一级地球化学标准物质GBW 07309制备溶液优化仪器工作参数,并用于校准。方法测定限(6s)为:0.007~6.4μg/g,精密度(RSD%,n=12)为:29%~9.4%,经过国家一级地球化学标准物质的分析验证,结果与标准值吻合。方法已应用于国土资源调查的试样分析。     

基于ATRP法制备的触角状亲水性羟胺树脂的吸硼性能的研究

以大分子引发剂氯乙酰化聚苯乙烯微球(PS-acyl-Cl)经原子转移自由基聚合(ATRP)法引发丙烯酰胺(AM)和甲基丙烯酸缩水甘油酯(GMA)单体的共聚接枝,制得一种触角状亲水性环氧载体(PS-acyl-g-P(AM-co-GMA)),再经二乙醇胺(DEA)的环氧基开环胺化反应,得到一种含多个-NCH2CH2OH螯合配基的多齿-五元螯合环的触角状亲水性羟胺树脂(PS-acyl-g-P(AM-co-GMA)-DEA)。将此树脂用于硼吸附研究,结果表明,PS-acyl-g-P(AM-co-GMA)-DEA树脂对硼的吸附满足Langmuir方程,为单分子层吸附;饱和吸附量约为37.7 mg·g-1,且树脂5 min即可达到吸附平衡,与其它已报道的吸硼树脂相比,该树脂具有更高的吸附量和吸硼速率。吸附动力学研究表明,树脂吸附硼的过程主要由颗粒扩散过程控制。重复使用5次后该树脂的吸附量基本不变,解吸率均在90%以上,重复使用性能良好。     

工业评述2001～2002年国外塑料工业进展

收集了2001年7月到2002年6月有关国外塑料工业的相关期刊资料,介绍了2001年到2002年国外塑料工业的发展情况,提供了世界各地域塑料原材料的产量及构成比,日本、美国、加拿大、德国、法国、比利时、墨西哥、芬兰、西班牙等国家的树脂产量、消费量及增长率,以及日本、西欧、北美等地区的不同品种塑料原料消费量和增长率统计.按通用热塑性树脂(聚乙烯、聚丙烯、聚苯乙烯、聚氯乙烯、ABS树脂)、工程塑料(尼龙、聚碳酸酯、聚甲醛、热塑性聚酯、聚苯醚)、通用热固性树脂(酚醛、聚氨酯、不饱和树脂、环氧树脂)、特种工程塑料(聚苯硫醚、液晶聚合物、聚醚醚酮)不同品种的顺序,对树脂的产量、消费量及合成工艺、产品应用开发、树脂品种的延伸及应用的进一步扩展等有关技术作了详细的介绍.     

工业生产中物位测量的探讨与研究

在工业生产中常常会遇到常温,常压和一般介质的液位,料位和界面的测量,也会遇到高温,高压,易燃易爆,腐蚀性较强的液位,料位和界面的测量。在工业生产中物位测量有接触式和非接触式测量。但应根据生产工况及技术要求来合理选用。     

Confocal microscope—A valuable tool for examining wood-coating interface

The suitability of confocal laser scanning microscopy (CLSM) in examining a wood-coating interface was evaluated using a clear coating system. A comparison of the images of the wood-clear coating interface obtained using CLSM and light microscopy (LM) showed a marked superiority of CLSM in revealing the details of the physical nature of the interaction between the clear coating and the wood cell walls in the surface layer. The most distinct advantage of CLSM was in its ability to clearly resolve penetration of the coating into very fine cracks in cell walls, details not obtainable with LM. The information presented here demonstrates that CLSM has the potential to greatly enhance our understanding of the physical aspects of an interaction between the wood and coating at the interface.     

不同结构充油溶聚丁苯橡胶/炭黑/白炭黑复合材料的结构与性能

研究了炭黑/白炭黑填充的苯乙烯/乙烯基含量不同的充油溶聚丁苯橡胶(HPR 757 D和Buna VSL 5025-2 HM)的物理机械性能及动态力学性能,观察了填料在硫化胶中的微观分布情况。结果表明,炭黑与白炭黑相互镶嵌地分布在橡胶基质中,形成交织的填料网络。高苯乙烯基含量的HPR 757 D的拉伸强度、撕裂强度及耐磨性能优异,滚动阻力较小,填料与橡胶间的结合力强,填料的分散性较好。用白炭黑等量取代炭黑可以提高胶料的拉伸强度,降低其动态压缩温升。但炭黑/白炭黑的最佳配比与橡胶基质的分子结构有关,主链双键含量越高,白炭黑的用量也随之增多。