P型单晶硅片在KOH溶液中腐蚀行为的电化学研究

采用电化学极化测量技术研究了p(100)和p(111)硅片在碱性KOH溶液中的腐蚀行为,考察了KOH溶液浓度、温度和硅片表面缝隙等因素对腐蚀行为的影响.结果表明:在室温下当KOH浓度为5～6 mol/L时硅片腐蚀速率最大;随着KOH腐蚀液温度增加,腐蚀速率增大,在50℃左右腐蚀速率增加显著;硅片表面缝隙会加剧硅的局部腐蚀,在同等实验条件下缝隙腐蚀速率比均匀腐蚀快一个数量级.     

电镀规范对Fe—Ni—P合金硬度和耐磨性的影响

研究了不同电镀规范的Ｆｅ－Ｎｉ－Ｐ合金层显微硬度和摩擦学性能。镀液中Ｆｅ／（Ｆｅ＋Ｎｉ）浓度比增大或电流密度增加，镀层的硬度上，耐磨提高；槽液的ＰＨ值或温度增大，镀层的显微硬度下降，耐磨性降低。镀液ＮａＨ２ＰＯ２．Ｈ２Ｏ浓度为５ｇ／Ｌ时，镀层硬度和磨性最高。宜选用的工艺参数为ＰＨ值１．０－１．２，温度６０－７０℃，电流密度１０－２０Ａ／ｄｍ＾２。Ｆｅ－Ｎｉ－Ｐ非晶合金的耐磨性比Ｎｉ－Ｐ非昌合金高２     

镍—钨—磷非晶态合金的电沉积方法及耐蚀性能的研究

研究了Ｎｉ－Ｗ－Ｐ非晶态合金的电沉积方法，讨论了电解液组成、温度及ｐＨ值对镀层结构的影响。由Ｘ射线衍射实验测定了镀层结构和晶粒尺寸，分析了非晶态层的形成规律。及极化曲线分析并比较了电沉积Ｎｉ－Ｐ，Ｎｉ－Ｗ及Ｎｉ－Ｗ－Ｐ非晶态合金镀的腐蚀行为。     

316L不锈钢焊缝的点蚀行为

采用数显恒温水浴锅HH-4静态模拟点腐蚀的试验方法,研究316L奥氏体不锈钢焊缝在不同Cl^-浓度和温度下的三氯化铁溶液中点腐蚀行为,探讨不同的Cl^-浓度和温度变化对焊缝耐蚀性能的影响。结果表明：在三氯化铁溶液中,Cl^-浓度增加、温度升高,316L奥氏体不锈钢焊缝的耐点蚀性能下降,腐蚀速率增加,腐蚀后的表面形貌为不均匀点腐蚀。     

凝汽器铜管氨腐蚀的研究

研究了影响凝汽器铜管氨腐蚀的因素与规律,以确定防止凝汽器氨腐蚀的途径.将HAl77-2A铜管管样在10种氨浓度、两种溶解氧浓度的溶液中浸泡45d,测定溶液的溶解氧变化情况,用失重法、原子吸收法测定铜管管样腐蚀速率;在6种温度、两种溶解氧、4种氨浓度条件下研究温度对铜管腐蚀速率的影响.氨液浓度小于800mg/L时,铜管氨腐蚀轻微,氨液浓度为800～1000mg/L时铜管腐蚀速率明显增大,且随氨液浓度的增大而增加;开口状态下铜管腐蚀速率比闭口时大,温度升高时同一氨液浓度下铜管腐蚀速率增大.凝汽器铜管氨腐蚀主要影响因素是溶解氧与氨液浓度,氨液浓度超过800mg/L后,腐蚀速率随氨浓度、氧含量、温度的增加而增大;用失重法与原子吸收法测定铜管腐蚀速率基本一致.     

化学镀Ni—Cu—P工艺

研究了不同Ｃｕ＾２＋浓度、ｐＨ值及温度条件下的化学镀Ｎｉ－Ｃｕ－Ｐ。结果表明，提高化学镀液温度中在较高的Ｃｕ＾２＋浓度下，可加快化学镀速度，提出镀层中Ｃｕ含量。镀层在较高Ｃｕ量下存在的少量化合物Ｎｉ５Ｐ２能使沉积颗粒细化。含Ｃｕ镀层具有较高硬度。     

烙铁头表面改性对抗高温腐蚀性能的影响

研究了用电镀方法对紫铜烙铁头镀Ｎｉ、镀Ｆｅ或镀Ｎｉ－Ｆｅ－Ｎｉ，使之表面生，在５５０℃温度下进行焊锡（６２％Ｓｎ、３８％Ｐｂ）高温腐蚀实验，探讨了高温腐蚀机理以及延长烙铁头寿命的可行途径。     

电沉积非晶态镍—钼合金及其镀层结构的研究

研究了在柠檬酸盐镀液中实现Ｎｉ，Ｍｏ共沉积的电解条件，获得了含Ｍｏ量为１６．４１％－６１．３５％（ｗｔ）的Ｎｉ－Ｍｏ合金。讨论了金属浓度比、阴极电流密度、ＰＨ值、搅拌、温度等因素对合金成分的影响，考查了所得合金的Ｘ射线衍射结构，认为沉积的Ｎｉ－Ｍｏ合金随着Ｍｏ含量的增加为Ｎｉ基取代型固溶体、过饱和固溶体、非晶态。     

用于微机械器件的电镀Fe—Ni合金薄膜的研究

本文考察了非常规Ｆｅ－Ｎｉ合金电镀中,溶液浓度、电流密度、ＰＨ值和温度等因素对电镀的影响。实验结果表明,Ｆｅ－Ｎｉ合金电镀的异常性是由于Ｆｅ（ＯＨ）２对铁离子和镍离子的还原反应有着不同的阻碍作用和程度。用Ｘ射线平移法对Ｆｅ－Ｎｉ合金镀层的残余应力与电镀参数之间的关系进行了研究,并讨论了薄膜微结构与应力的关系。     

钢芯铝绞线的铝线在NaCl溶液中的腐蚀行为

钢芯铝绞线正常运行温度达80℃,受到环境中盐离子的严重腐蚀。采用Tafel直线外推法、电化学阻抗谱法及加速腐蚀试验法,研究了钢芯铝绞线的铝线在不同浓度NaCl溶液中的腐蚀行为,利用SEM和XRD等表征了其腐蚀表面状态及产物形貌。结果表明:随着NaCl浓度的升高,铝线的自腐蚀电位负移,极化电阻变小,腐蚀速率增大,当NaCl为70 mg/L时腐蚀速率急剧增加,是10 mg/L NaCl时的40倍;腐蚀产物及钢芯表面镀锌层可抑制铝线的腐蚀,铝线腐蚀后的表面出现大量的"麻点"及腐蚀坑,白色的腐蚀产物主要由Zn0.64Al0.36(OH)2(CO3)0.18.0.86H2O组成。     

N80油管钢在CO_2/H_2S水介质中的腐蚀研究

油田设施受产出水和CO2/H2S腐蚀严重.以长庆某天然气井产出水为腐蚀介质,采用失重法研究了不同腐蚀影响因素对N80钢的作用规律.结果表明,随着介质温度的升高,腐蚀速率先增加后降低,并在60℃时达到最大;Cl-的影响与温度具有基本相似的规律,在Cl-含量为30 g/L时腐蚀速率最大;随着pH值的增大,腐蚀速率持续减小,并在pH值为8.0左右时达到最低;随着CO:分压的增大,腐蚀速率呈单调增大趋势;随着H2S分压的增大,腐蚀速率先下降后又缓慢升高.     

2种碱化剂对压水堆二回路结构材料腐蚀行为的影响

为考察碱化剂抑制压水堆二回路结构材料腐蚀的情况,通过腐蚀失重法、电化学极化曲线、扫描电镜(SEM)以及小角XRD分析等方法研究了模拟压水堆二回路水化学环境中分别添加乙醇胺(ETA)和氨水(NH_3·H_2O)_2种碱化剂对A508Ⅲ钢和P22钢2种结构材料的腐蚀行为的影响。结果表明:2种结构材料腐蚀速率均在10~(-1)~10~(-2)mg/(dm~2·h)之间,但在ETA中腐蚀电流密度更小,腐蚀速率也更低。在2种结构材料表面形成的主要腐蚀产物均为Fe_3O_4,SEM观察到在ETA中生成的腐蚀产物较为致密。比较ETA与NH_3·H_2O的物化性能,可知在高温水(280℃)中ETA的挥发性能弱于NH_3·H_2O,因此添加ETA的溶液的pH值更高,pH值的不同决定了2种材料的溶液腐蚀行为的差异。综上所述,二回路结构材料在ETA环境中的耐蚀性能更好。     

Incoloy 825/L360复合管焊接接头耐蚀性研究

目的研究Incoloy 825/L360复合管焊后的焊缝耐蚀性能。方法以Incoloy 825/L360复合管为研究对象,选用Inconel625焊材进行了镍基合金焊缝的焊接,并对焊缝和Incoloy 825母材在质量分数为3.5%的NaCl溶液、6%的FeCl_3溶液中进行电化学试验,并对其耐蚀性进行了对比分析。结果在质量分数为3.5%的NaCl溶液中,不同温度下母材自腐蚀电位均高于焊缝,自腐蚀电流密度均小于焊缝,随着温度的升高,母材的自腐蚀电位和焊缝的自腐蚀电流密度均增加,母材的自腐蚀电流密度变化不明显;在质量分数为6%的FeCl_3溶液中,母材与焊缝的自腐蚀电位整体较高,母材的自腐蚀电流密度高于焊缝,不同温度下焊缝极化曲线均存在明显的钝化平台。结论 Incoloy 825母材和焊缝在两种溶液中的耐蚀性存在一定差异;在质量分数为3.5%的NaCl溶液中,母材腐蚀对温度不敏感,焊缝的腐蚀敏感倾向性随着温度的升高而增大,腐蚀敏感性高于母材;在质量分数为6%的FeCl_3溶液中,不同温度下的焊缝极化曲线均存在明显的钝化平台,腐蚀敏感性低于母材。     

Effect of Copper and Bronze Addition on Corrosion Resistance of Alloyed 316L Stainless Steel Cladded on Plain Carbon Steel by Powder Metallurgy

A sandwich structure with cladding alloyed 316L stainless steel on plain carbon steel was prepared by means of powder metallurgy (PM) processing. Electrolytic Cu and prealloyed bronze (95Cu wt pct, 5Sn wt pct) were added in different contents up to 15% into the surface cladded 316L layers and the effect of alloying concentrations on the corrosion resistance of the 316L cladding layers was studied. The corrosion performances of the cladding samples were studied by immersion tests and potentio-dynamic anodic polarization tests in H_2S0_4 and FeCl_3 solutions. Both 316L and alloyed 316L surface layers with 1.0 mm depth produced by PM cladding had an effect to improve corrosion resistance in H2SO4 and FeCI3 solutions. Small Cu and bronze addition (4%) had a positive effect in H_2SO_4 and FeCl3 solutions. 4% Cu alloyed 316L surface layer produced by PM cladding showed similar anodic polarization behaviour to the 316L cladding layer in H_2SO_4 and FeCl_3 solutions.     

Effect of acetic acids on the corrosion crack growth of 3.5NiCrMoV steels in high temperature water: synergistic interaction between stress corrosion and corrosion fatigue

Stress Corrosion Cracking (SCC) tests (pH: 3 ~ 5) and Corrosion Fatigue (CF) tests (R = 0.2, 0.1 Hz) were conducted to evaluate the effect of acetic acid on the corrosion crack growth behavior in high temperature water at 150°C. Acetic acid significantly influenced the corrosion fatigue cracking behavior of turbine disc steels in high temperature water. The CF crack growth rates of turbine disc steels increase until the organic acid concentration reaches a critical saturation value (between pH 4 and pH 3) because of the crack tip sharpening. Below the critical value of pH, the CF crack growth rates decreases because of the crack tip blunting. The corrosion fatigue crack growth rate is accelerated by the interaction of the fatigue and the stress corrosion in the test environment. The synergistic interaction should be accounted for in the realistic prediction of the corrosion fatigue life of turbine steel (3.5NiCrMoV steels) in high temperature water of acetic acid solution. With the high temperature corrosion fatigue data obtained in this study, it is possible to assess the life of turbine components in high temperature and high pressure.     

化学沉积Ni-Mo-P合金工艺参数对性能的影响

研究了镀液pH值和温度等工艺参数对化学镀Ni Mo P合金镀层耐蚀性和硬度的影响。试验结果表明 ,镀液 pH值升高 ,镀层的沉积速度和硬度升高 ,而耐蚀性下降 ;镀液温度升高 ,镀层的沉积速度升高     

N-芳基-α-氨基苄基膦酸的合成及其缓蚀性能研究

制备了14种膦酸缓蚀剂,其中7种为新报道的化合物。考查了膦酸浓度及溶液pH值对缓蚀性能的影响,分析了膦酸分子结构与缓蚀性能的关系,探讨了膦酸的缓蚀机理。结果表明,在膦酸的浓度低于100mg/L时,随着膦酸浓度的增大,对Q235钢的缓蚀能力明显加强;在高pH值条件下,膦酸的缓蚀效果较好。表面膜分析证实膦酸是一种吸附型的缓蚀剂,苯环上供电子基团有利于形成致密的保护膜。     

检验腐蚀对镍基单晶高温合金高周疲劳性能的影响EI北大核心CSCD

为了研究检验腐蚀对一种镍基单晶高温合金高周疲劳性能的影响,将经过标准热处理的试样置于FeCl 3+HCl+H 2O腐蚀剂中分别腐蚀2次和4次,采用莱卡DCM8共聚焦显微镜和扫描电镜对未腐蚀、2次与4次腐蚀试样的表面形貌进行观察,然后分别测试未腐蚀和4次腐蚀试样760℃与980℃的旋转弯曲疲劳性能。结果表明:未腐蚀试样表面存在纵向且相互平行的由抛光带来的细小抛痕,表面粗糙度低;2次腐蚀后,表面抛痕有所减少,枝晶间区域出现腐蚀坑,表面粗糙度增加;4次腐蚀后,表面抛痕被完全腐蚀掉,腐蚀坑深度和表面粗糙度进一步增加。4次腐蚀会略微降低合金760℃的疲劳性能,但对高应力幅条件下的疲劳寿命影响较大,对低应力幅条件下的疲劳寿命影响较小。4次腐蚀对合金980℃疲劳性能影响很小。     

GH4169高温合金化学铣切表面粗糙度的影响因素

为了满足生产对GH4169高温合金化学铣切加工表面粗糙度的要求,通过单因素试验研究了化铣液的主要成分和化铣工艺参数对GH4169高温合金表面粗糙度的影响。结果表明:随着化铣液中FeCl3和HNO3浓度的升高,表面粗糙度呈下降趋势;当化铣液温度高于50℃时,表面粗糙度在1.4μm以下;HCl,HF浓度均为200 mL/L时,表面粗糙度最小;添加剂SA和SN能够降低表面粗糙度和消除凹槽;随着化铣液中Ni2+浓度的增加,表面粗糙度也随之变大,当Ni2+浓度大于26.95 g/L时,表面粗糙度达到1.6μm以上,不符合加工要求;最佳化铣工艺为200～250 g/L FeCl3,200 mL/L HF,150 mL/L HNO3,200 mL/L HCl,0.2 g/L添加剂SA,0.5 mL/L添加剂SN,温度53℃,该工艺下化铣的GH4169高温合金表面质量良好,无凹槽、沟蚀,表面光洁,粗糙度小于1.6μm,符合生产要求。