微量钪Sc对5A01合金性能与显微组织的影响

研究了在5A01合金基础上添加0.2%Sc和0.3%Sc后合金的显微组织、力学性能、腐蚀性能及焊接性能。结果表明,微量Sc的加入,初生Al3Sc或Al3(Sc,Zr)粒子可成为有效的非均质晶核,细化合金的铸态晶粒,次生Al3Sc或Al3(Sc,Zr)粒子能有效地钉扎位错和亚晶界,稳定亚结构并强烈抑制合金的再结晶。因此,微量Sc加入使5A01合金基体强度提高,腐蚀性能和焊接性能与5A01合金相当甚至更好。     

微量Sc及热处理对AA6022合金组织与性能的影响

采用铸造及锻造变形方法制备了含Sc的AA6022铝合金。采用X射线衍射分析、金相显微镜、扫描电镜观察及力学性能测试等方法,研究了微量Sc及时效处理工艺对合金的组织与性能影响。结果表明,添加0.15%～0.30%的Sc能明显细化铸态合金的晶粒,其平均尺寸从323μm降低到31μm。拉伸性能测试显示,自然时效(T4态)后,Sc的添加并未明显提高合金的抗拉强度,但伸长率却明显提高。而经过175℃保温30min的处理后(T4p),Sc的添加并未提高基体合金的强化烘烤效应,反而降低了合金的伸长率。180℃×10h峰时效处理(T6)显示,微量Sc的添加并不会明显提高合金的强度,但却提高了其塑性变形能力。     

Sc微合金化对Al-Zn-Mg-Cu-Zr合金组织性能的影响

采用铸锭冶金法制备了Al-8.0Zn-2.0Mg-1.2Cu-0.15Zr-xSc合金,对合金进行了固溶、时效处理,测试了不同状态下合金的力学性能和电导率,利用光学显微镜、扫描电镜和透射电子显微镜研究了合金不同状态的显微组织。结果表明:添加微量钪形成的一次Al3(Sc,Zr)相可作为异质形核核心,细化合金铸态组织;均匀化退火过程中析出的二次Al3(Sc,Zr)粒子强烈钉扎位错和亚晶界,有效阻碍固溶处理过程中合金的再结晶;含0.30%Sc的Al-Zn-Mg-Cu-Zr合金的抗拉强度和伸长率显著高于不加钪的铝合金,经一般固溶及回归再时效(RRA)处理后含0.30%Sc合金的抗拉强度提高36 MPa、屈服强度提高30 MPa、伸长率提高3.0%;采用470℃×60 min+485℃×60 min强化固溶处理,降低合金固溶态的电导率,将合金固溶态以及T6态的抗拉强度分别提高了79.6 MPa、55.8 MPa。     

添加微量Sc、Zr对超高强铝合金微观结构和性能的影响

采用低频电磁铸造技术制备Al-9Zn-2.8Mg-2.5Cu-x Zr-y Sc（x=0,0.15%,0.15%;y=0,0.05%,0.15%）合金,借助金相显微镜、扫描电镜、透射电镜、力学性能测试等手段分别对其均匀化、热挤压态、固溶态和时效态的组织与性能进行对比分析。结果表明：添加微量Sc和Zr,会在凝固过程中形成初生Al3（Sc,Zr）,可显著细化合金铸态晶粒;均匀化时形成的次生Al3（Sc,Zr）粒子可以强烈钉扎位错和亚晶界,有效抑制变形组织的再结晶,显著提高合金的力学性能。与不含Sc、Zr的合金相比,含0.05%Sc和0.15%Zr的合金经固溶处理和峰值时效处理后其抗拉强度和屈服强度分别提高172 MPa和218 MPa,其强化作用主要来自含Sc、Zr化合物对合金起到的亚结构强化、析出强化和细晶强化。     

铸态Mg-11Al-1.2Zn-(-0.3Sc)合金的显微组织与力学性能

通过熔炼铸造方法,制备了Sc含量为0.3%的Mg-11Al-2Zn合金,采用X射线衍射、金相观察,扫描电镜及力学性能测试,研究了Sc的添加对铸态合金显微组织与力学性能的影响.结果显示,基体合金中添加Sc后,铸态合金的晶粒明显得到细化,Mg17Al12相的形态与分布得到有效改善,显微组织主要由α-Mg基体相、Mg17Al12相及MgAlSc相组成.力学性能显示,Sc的添加使铸态合金的室温抗拉强度提高了23.7%.     

钪对镁-铝-锌合金显微组织与力学性能的影响

通过铸锭冶金及形变热处理工艺,制备了含0.3%Sc的Mg-llAl-1.2Zn(质量分数)合金.采用X射线衍射、金相及扫描电镜观察与拉伸性能测试,研究微量钪在基体合金中的作用与存在形式.结果表明,基体合金中添加0.3%Sc后,合金的晶粒明显得到细化,Mg17Al12相的形态与分布得到有效改善.合金的相组成主要由a-Mg基体相、Mg17Al12相及MgAlSc相组成.同时,0.3%Sc的添加也提高了挤压态合金在室温与高温下抗拉强度,室温时的抗拉强度达到340MPa,而伸长率超过了10%.     

微量元素Sc对ZA27合金组织与性能的影响

试验研究了微量元素Sc对ZA27合金铸态显微组织与力学性能的影响规律。试验结果表明:单独添加合金元素Sc,在Sc的加入量为0.5%时,ZA27合金铸态显微组织细化效果较好,粗大的树枝晶组织转变为均匀、细小的团絮状组织,晶界共晶体组织变得更为细小。合金的铸态抗拉强度和硬度分别达到了495MPa和HB120.2,伸长率达到7.6%。元素Sc在ZA27合金中与Al形成了与基体晶格类型和晶胞尺寸极为相近的Al3Sc粒子,起到了促进异质形核和细晶强化的作用,从而提高了合金的力学性能。     

稀土Sc、Zr对铸造Zn-43Al-1.6Cu合金组织及力学性能的影响

通过力学性能测试、X射线衍射、扫描电镜及能谱分析等手段,研究了复合添加稀土元素Sc、Zr对Zn-43Al- 1.6Cu合金铸态显微组织及力学性能的影响.研究发现:在铸态Zn-43Al-1.6Cu合金中复合添加0.4％Sc、0.1％Zr时,合金显微组织细化效果较好,粗大的树枝晶转变为均匀、细小的团絮状组织,合金的抗拉强度达到372.3 MPa,伸长率提高了45.1％;稀土元素Sc、Zr与Zn-43Al- 1.6Cu合金中的Al形成了与α-Al基体晶格类型和晶胞尺寸都极为相近的复杂化合物Al3Sc粒子,促进异质形核,起到细晶强化的作用,从而提高了合金的力学性能.     

Sc对Al-Zn-Mg-Cu-Zr合金铸态组织和力学性能的影响

采用金相显微镜、扫描电镜和能谱分析,研究Sc对Al-9.0Zn-2.5Mg-2.5Cu-0.15Zr合金铸态组织和力学性能的影响。结果表明,添加0.20%-0.60%的Sc,会使合金的铸态组织由粗大的树枝晶变为等轴晶,并使Cu的偏聚减轻,且Sc含量越高,合金铸态组织越细,Sc含量为0.60%的合金铸态组织最细小;随着Sc含量的增加,合金的抗拉强度升高,T6态时,Sc含量为0.60%的合金抗拉强度高达783.9 MPa。从熔体中析出的Al3（Sc,Zr）一次粒子具有与α（Al）基体相同的FCC晶格,晶格常数接近,可有效地细化合金的铸态组织。合金强化机理主要为Al3（Sc,Zr）引起的细晶强化、亚结构强化和沉淀强化。     

微量元素Zr+Sc与凝固速度对铸造Al-Li-Cu-Mg合金组织性能的影响

通过控制微量元素Zr+Sc与凝固速度,对铸造Al-Li-Cu-Mg合金进行熔体处理,研究两种因素对合金微观组织及性能的影响。利用光学显微境、场发射扫描电镜、X射线衍射仪、万用拉伸机等分别对合金的微观组织标定及力学性能进行分析和测试。结果表明：向Al-5Li-4Mg-3.5Cu基础合金中加入Zr+Sc后,合金的铸态晶粒得到明显细化,基体晶粒形貌由树枝状转变为近似等轴晶。向基础合金中加入0.2%Zr+0.4%Sc时达到晶粒细化极值,继续添加Zr+Sc元素则会降低细化效果,恶化合金组织;经过力学性能测试可知,添加0.2%Zr+0.4%Sc的合金的力学性能有了较大的提高,相比于基础合金抗拉强度提高了约48.57%,伸长率提升了27.93%;快速凝固时,添加0.2%Zr+0.4%Sc合金仅有Al2MgLi、Al3Zr、Al3Sc和Al8.9Li1.1相的析出,析出相的数量很少且尺寸极小。     

胫骨生物陶瓷复合材料的微结构增韧机理

扫描电镜观察显示胫骨是一种由羟基磷灰石和胶原蛋白组成的自然生物陶瓷复合材料.羟基磷灰石具有层状的微结构并且平行于骨的表面排列.观察也显示这些羟基磷灰石层又是由许多羟基磷灰石片所组成,这些羟基磷灰石片具有长而薄的形状,也以平行的方式整齐排列.基于在胫骨中观察到的羟基磷灰石片的微结构特征,通过微结构模型分析及实验,研究了羟基磷灰石片平行排列微结构的最大拔出能.结果表明,羟基磷灰石片长而薄的形状以及平行排列方式增加了其最大拔出能,进而提高了骨的断裂韧性.     

Prospects of the Use of Synergetic Approach to Solution of Problems of the Science of Nanomaterials

A synergetic approach to solution of problems of self-controlled synthesis of nanostructures and creation of self-organizing nanotechnologies is considered in connection with the superproblem of creation of materials with functional properties resembling those of biosystems. __________ Translated from Metallovedenie i Termicheskaya Obrabotka Metallov, No. 7, pp. 55 – 61, July, 2005.     

Kinetics of the oxidation of metals — Influence of self-diffusion of metal

The importance of the self-diffusion of a metal during its oxidation by a gas is treated for the cases of nonstoichiometric oxides having either interstitial cation or cation vacancies. We have established a general relationship for the reaction rate when a mixed diffusion process occurs. From this relationship, we have shown that the pressure dependence can be different, according to whether the rate-determining process is the self-diffusion through the metal or through the product.     

Features of formation of the structure in production of blanks of disks of heat-resistant nickel alloys

Conclusions To provide a high level of mechanical properties in wrought blanks of cast ÉP741NP and ÉP962 alloys it is necessary to form controlled structures. A necklace-type structure formed in homogenizing isostatic treatment, subsequent thermomechanical working including alternation of the operations of deformation in the (+)-area and recrystallization anneals, and final heat treatment is preferable. The temperature conditions of all stages of thermomechanical working are strictly controlled, especially the final operation of deformation and heating for hardening. To eliminate hardening cracks and distortions it is necessary to use molten salts at t=600°C as quenchants. The use of multiple production operations makes it possible to significantly reduce the structural inhomogeneity related to inhertance of the original dendritic structure. However, the structure of the final semifinished product is nevertheless characterized by a difference in occurrence of the processes of polygonization and recrystallization between the former dendritic cells and the interdendritic spaces in deformation and heat treatment.To obtain structurally homogeneous blanks for gas turbine engine parts it is necessary to use basically new methods of remelting such as vacuum double electrode remelting and electron beam remelting with an intermediate vessel.Translated from Metallovedenie i Termicheskaya Obrabotka Metallov, No. 12, pp. 25–29, December, 1991.     

Ab-initio calculation of enthalpies of formation of intermetallic compounds and enthalpies of mixing of solid solutions

A large number of ab-initio calculations of energies of formation of intermetallic compounds have been performed in the last 15 years. The currently used methods are listed. The paper presents a review of the aluminium based compounds which have been studied. Comparisons of calculated and experimental enthalpies of formation are provided for aluminim-3d and-4d transition metal alloys at equiatomic composition. The modelling of the enthalpies of mixing of solid solutions based on a given lattice is described.     

试论洋务派教师聘任的思想

洋务派在洋务学堂的办学活动中,为了解决西学专业学科的教学困难,采用了聘请外籍教师的应急措施.他们以真才实学,合同制管理作为主导思想,并认为这种解决师资的途径只是权宜之计,并非久远.从客观上看,洋务派的教师聘任思想有深刻的历史影响.     

面向零件形状的计算机图形库的开发

论述了CAD技术中参数化设计的三种建模方法，重点介绍了基于特征的参数化建模原理。在此基础上，分析机械设计中的机构结构，归纳出其零件的几何特征构成。设计了机构CAD图形库，并提出了该图形库生成步骤和人机交互界面。