Triton X-100／Vc／H2O微乳液中纳米金的合成

在Triton X-100/Vc/H2O微乳液中,用0.001 mol·L-1HAuCl4溶液代替组分水,以Vc作还原剂制备纳米金.用紫外-可见光谱和透射电镜进行分析.结果表明,所制备的金纳米粒子的平均粒度在20 nm左右,且粒子的粒度分布范围较窄.无论是在固定0.001 mol.L-1HAuCl4/Vc质量比下改变Triton X-100的含量,还是在固定Triton X-100/0.001 mol·L-1 HAuCl4质量比下改变Vc的含量,所得的金纳米粒子大小与形状都没有明显的变化.初步探讨了在Triton X-100/Vc/H2O微乳液中合成纳米金的机制.     

Au-Pt双金属纳米粒子的制备及其电催化性质

在PEG10000/Vc/HAuCl4体系中,用Vc还原HAuCl4制备金纳米粒子,以所制备的金纳米粒子为晶种,通过控制HAuCl4与H2PtCl6的质量比,制备不同Pt/Au比的双金属纳米粒子,并进一步研究其对H2O2电化学氧化的催化作用。紫外-可见光谱(Uv-vis)、透射电子显微镜(TEM)、选区电子衍射(SAED)、X射线粉末衍射(XRD)等实验结果表明：Au-Pt双金属纳米粒子为面心立方结构的合金。用循环伏安法对Au-Pt双金属纳米粒子修饰的玻碳电极的电化学性能进行测试,结果表明：Au-Pt双金属纳米粒子对H2O2电化学氧化有一定的催化作用。催化效率随Au-Pt双金属粒子中Pt含量的增加而增加。     

从Pd-C催化剂废料制备纳米Pd

从Pd—C催化剂废料回收Pd（N03）2，然后在SDS／Brij30／H20体系O／W微乳液中制备纳米钯。结果表明：制备的钯纳米粒子的粒度在5-200nm之间：使用该体系不需外加还原剂，可直接利用非离子表面活性剂Brij30作为还原剂，简化后续单元操作。并初步探讨了SDS／Brij30／H2O体系O／W微乳液中纳米钯的制备机制。     

反相微乳液中纳米金的可控合成及其机理研究

在AOT/正庚烷/氯金酸反相微乳液中,用水合肼作为还原剂制备了纳米金粒子, 用紫外-可见光谱和透射电镜进行分析,系统地研究了水和表面活性剂摩尔比 (ω=nH2O/nAOT)以及氯金酸浓度对粒径的影响。结果表明, 制备的纳米金粒子粒径在4~12 nm、单分散性好。纳米金粒径与ω值存在线性关系。氯金酸的浓度对粒径的影响比较复杂, 随着浓度增大, 粒径先减小后增大。用FT-IR红外光谱解释了AOT的磺酸基对纳米金粒子表面有强烈的吸附作用,从而对合成的纳米金粒子有着很强的保护作用     

氯金酸的浓度对纳米金形态的影响

采用Zn置换HAuCl4溶液的方法制备了具有不同形貌的纳米金,并研究了HAuCl4溶液的浓度对纳米金形貌的影响.实验结果表明,纳米金的形貌主要取决于HAuCl4溶液的浓度.当HAuCl4溶液的浓度为0.01 mmol/L时,置换反应进行5 min后的产物是金纳米颗粒,其粒径为10～50 nm,24 h后金颗粒的粒径超过100 nm,金颗粒团聚成金花状.当HAuCl4溶液的浓度为1 mmol/L时,金颗粒的粒径为数百纳米,部分金颗粒团聚成金花状.当HAuCl4溶液的浓度为10 mmol/L时,在金颗粒中出现由纳米金片组成的多晶枝晶,多晶枝晶随后通过OA和OR机制转变成单晶枝晶.当HAuCl4溶液的浓度为30 mmol/L时,反应时直接生成金枝晶.因此,通过控制HAuCl4溶液的浓度,可制备具有不同形貌的纳米金.     

高产率纳米铁粉的制备及表征

采用循环水冷却和循环等离子体工作气体的改进方法，制备出纳米铁粉。当电流为500A，气体总压为0．03MPa，电压为32V，氢气含量为50％，风机转速为2400r／min时，铁粉产率可高达6．2g／min，其平均粒径为50nm。粒子大多呈球形，表面光滑，粒子大小均匀，连接成链状。但是有些大颗粒粒径达到微米级，这主要是团聚所致。实验中制备的纳米铁颗粒为层状结构，由内到外依次是Fe-Fe3O4—Fe2O3，Fe3O4和Fe2O3的含量很低，但起到了对纳米粒子的保护作用。     

双氧水改性二氧化钛的光催化性能研究

研究了用微乳法制备纳米二氧化钛粉末的工艺，以及在紫外光照射下，TiO2和H2O2分别以及两者结合对于甲基橙溶液的降解作用。结果表明用微乳法可以制备粒度为23．2nm的纳米TiO2粉末；在紫外光照射下，H2O2可以有效地降解甲基橙溶液；当H2O2浓度从1mmol／L增加到10mmol／L，甲基橙的吸光度直线下降；当H2O2浓度达到10mmol／L时，降解率可以达到99％；TiO2也可以有效地降解甲崔橙溶液，当TiO2的浓度为0．50～0．75g／L时，降解率最大；用H2O2对TiO2进行改性后，可以有效地降解甲基橙溶液，固定TiO2的量为0．5g／L时，当H202浓度为4mmol／L时，甲基橙溶液的吸光度达到最低；当H2O2浓度处于10mmol／L以上时，甲基橙溶液的吸光度却出现无规则的变化。     

葡萄糖溶液中金纳米粒子的光化学合成及其光谱性质研究

研究了在葡萄糖溶液中HAuCl4的光化学还原过程及葡萄糖的含量对最终金纳米粒子形状的影响.当葡萄糖:金离子的质量比小于2g/1.2mg时,可得到各向异性金纳米粒子,其中质量比为0.5g/1.2mg时得到形貌良好的金纳米锥;当质量比在2～7g/1.2mg间变化时,能获得较小尺寸的球形(或类球形)金纳米粒子;而当质量比大于...     

丙酮诱导不同形状的金纳米粒子整形

在HAuCl4-葡萄糖-丙酮体系中,丙酮不仅能起光敏剂、加速光化学还原Au(III)离子的反应,还能诱导已形成的金纳米粒子整形。整形过程伴随着明显的可见/近红外吸收光谱变化,并形成一些全新的纳米结构。实验结果表明,金纳米粒子的整形方式与初始金纳米粒子的形貌密切相关,对于球形的金纳米粒子,整形后形成纳米线;而对于锥形纳米粒子则形成金纳米片。     

微乳法制备氧化锆纳米粉体

以可溶性锆盐溶液—环己烷—聚乙二醇辛基苯醚—正戊醇体系的微乳液反应为基础 ,以氨水为沉淀剂 ,在微乳液中发生化学反应产生凝胶状沉淀 ,经洗涤、焙烧得到超细分散 Zr O2 纳米粒子。本文在微乳液法的基础上加入了一种较新的脱水工艺—共沸蒸馏制备了纳米 Zr O2 粉末。通过比表面积 (BET)、透射电镜 (TEM)、X-射线衍射 (XRD)对样品进行了形态表征和物相分析 ,结果表明通过本方法制备的 Zr O2 纳米粉末尺寸可控制在小于 4 0 nm的范围内 ,并具有良好的分散性。共沸蒸馏能充分地脱去凝胶中残余的水分 ,防止因含水胶体干燥过程引起的粉末硬团聚 ,从而显著地提高了粉末的性能     

In-situ chemical synthesis route for a fiber shaped gold-polyaniline nanocomposite

A facile synthesis route is described for the preparation of a gold-polyaniline nanocomposite material by polymerization of aniline hydrochloride using HAuCl4 as the oxidant. It was found that the oxidative polymerization of aniline hydrochloride leads to the formation of polyaniline with a fiber-like morphology, while the concomitant reduction of HAuCl₄ results in the formation of gold nanoparticles of diameter 2–7 nm. The gold nanoparticles were highly dispersed and stabilized throughout the polyaniline fibers while being in intimate contact with the polymer. The combination formed a uniform metal-polymer composite material.     

Fabrication and characteristics of spindle Fe2O3@Au core/shell particles

The fabrication and characteristics of spindle Fe2O3@Au core/shell particle were investigated, and the effect of the core/shell nanoparticles as the surface enhanced Raman spectroscopy (SERS)-active substrates was studied. By using the seed-catalyzed reduction technique, anisotropic Fe2O3@Au core/shell particles with spindle morphology were successfully prepared. The Fe2O3 particles with spindle morphology were initially prepared as original cores. The Au nanoparticles of 2 nm were attached onto the Fe2O3 particles through organosilane molecules. Uniform Au shell formed onto Fe2O3 core modified by Au nanoparticles through the in-situ reduction of HAuCl4. The shell thickness was controlled through regulating the concentration of HAuCl4 solution. The results of TEM, XRD and UV-vis characterization show that the core/shell particles with the original shape of the Fe2O3 particles are obtained and these surfaces are covered by Au shell completely. The surface enhanced Raman spectrum of the probe molecules adsorbed on these core/shell substrates is strong and the intensity is enhanced with the increase of the thickness of Au shell or the aspect ratio of particles. The spindle Fe2O3@Au core/shell particles exhibit optimum (SERS) activity.     

胶束性质对光化学制备金纳米粒子的影响

研究了阴离子表面活性剂疏水链的长度对光化学制备金纳米粒子的影响。结果发现，疏水链越长，获得的金纳米粒子的尺寸越小；特别是苯环的引入使诱导和自催化现象越加不明显。在十二烷基磺酸钠体系中获得的金纳米粒子的λmax位于540．7nm，TEM表征的平均粒径为47．1nm；十二烷基苯磺酸钠体系的λmax位于526．5nm，平均粒径为6．7nm。探讨了胶束性质对光化学制备金纳米粒子的影响。     

水相法制备小粒径金溶胶

采用柠檬酸三钠还原氯金酸法制备金溶胶.研究了还原剂用量、试剂加入顺序、反应时间、搅拌速度等因素对金溶胶浓度、粒径、形貌和分散性的影响,使用紫外-可见分光光度计和透射电子显微镜对金溶胶的光学特性、粒径、形貌及结构进行表征.结果表明:制备小粒径金溶胶的最优条件为柠檬酸三钠(0.034 mol/L)与氯金酸(0.024 mol/L)溶液体积比为3:1,将氯金酸加入柠檬酸三钠溶液中为宜,反应时间6 min,搅拌速度约650 r/min;在此最优条件下可成功制备出形貌均一、分散性好、稳定性佳的金溶胶,其平均粒径约6～7 nm.     

压电驱动脉动混合可控合成金纳米粒子

在用柠檬酸钠作还原剂还原氯金酸的基础上,提出了一种压电驱动式脉动微混合可控合成金纳米粒子的制备方法。分析了金纳米粒子的合成机理及脉动微混合的工作原理。针对不同的浓度比(Na_3C_6H_5O_7:HAuCl_4)和脉动混合频率设计并开展了相关金纳米粒子可控合成试验,利用紫外可见分光光度计和透射电子显微镜对所得样品的光学特性、粒子粒径、粒子偏差及单分散性进行了表征,分析了浓度比和频率对试验结果的影响。结果表明:利用压电驱动式脉动微混合法,通过控制两相制剂的浓度比和脉动混合频率,一定程度上可以实现金纳米粒子的可控合成。     

单分散近球形和片状金粉的制备及表征

以HAuCl4·4H2O为前驱体,抗坏血酸(VC)为还原剂,线性聚乙烯亚胺(L-PEI)为表面活性剂在水相中制备了单分散的近球形和片状金粉.采用SEM、XRD和激光粒度分析仪对金粉的形貌、粒径、结晶和分散性进行了测试和表征.研究了还原剂和金前驱体的摩尔比、L-PEI浓度、温度及反应溶液的pH对近球形和片状金粉的形貌和粒径大小的影响.给出了制备微米级近球形和片状金粉的反应条件,同时也提出了近球形和片状金粉的成核和晶核生长的可能解释.     

A Novel Approach to Prepare Gold Nanoparticles/ Polyacrylamide Composite Nanofibers

在溶液内,利用聚丙烯酰胺为还原剂制备出了聚丙烯酰胺保护下的Au纳米粒子。聚丙烯酰胺起到双重作用,它是制备金纳米粒子的还原剂;另外,它也是一种很好的金纳米粒子的稳定剂。紫外-可见光谱测试证实了溶液内金纳米粒子的存在,透射电镜观察到制得的纳米纤维内含有金纳米粒子。这种新的路线对于制备其他功能性复合纤维有很好的借鉴作用。