慈竹置换蒸煮对己烯糖醛酸含量的影响

研究了慈竹置换蒸煮过程中预浸渍段、温充段、热充段NaOH用量及硫化度对置换蒸煮和蒸煮过程中己烯糖醛酸(HexA)产生的影响,通过合理控制工艺可降低纸浆中HexA含量,不仅有利于纸浆Kappa值的测定,而且可以减轻对后续ECF漂白的不良影响。研究结果表明:当预浸渍段NaOH用量从2g/L到10g/L变化时,HexA的含量从4.278μmol/g增加到了6.515μmol/g;温充段的NaOH用量对置换蒸煮中HexA含量影响较小,当NaOH用量从5g/L增加到15g/L时,HexA的含量仅降低了0.85μmol/g;热充段NaOH用量对HexA含量的影响最为显著,当热充段NaOH用量从20g/L增加到40g/L时,HexA的含量从14.14μmol/g下降到4.28μmol/g。硫化度对HexA含量影响较小。当预浸渍段NaOH浓度为10g/L、温充段NaOH用量为15g/L、热充段NaOH用量为30g/L,硫化度为23%时,浆料中HexA的含量仅为6.51μmol/g,去除HexA的影响后,浆料卡伯值为12.0,得率为44.21%。     

蔗渣DDS置换蒸煮工艺研究

对蔗渣进行了烧碱法置换蒸煮的研究,探讨了置换蒸煮应用于蔗渣的可行性,研究了总用碱量、温充温度对制浆性能和黑液的影响。结果表明:置换蒸煮可应用于蔗渣原料,相比传统间歇烧碱法蒸煮,置换蒸煮制得的浆得率更高,黏度更高;在总用碱量30%(Na OH计),温充、热充用碱比为3∶2,温充温度120℃、保温50min,热充温度155℃、保温50min时,可以获得卡伯值为14.2、白度为48.4%ISO、黏度为1057m L/g、细浆得率为52.3%的具有较好质量的蔗渣浆。     

双元助剂强化慈竹蒸煮

研究双元蒸煮助剂在慈竹硫酸盐蒸煮过程中的应用。结果表明,添加改性蒽醌对蒸煮的强化脱木素作用效果明显。巴克曼蒸煮渗透剂 A、B、C 分别单独使用时不仅没有强化脱木素作用,而且会使黑液残碱降低、纸浆得率下降。巴克曼蒸煮渗透剂 A、B、C 与改性 AQ 双元复配使用时均可提高蒸煮效果,使得成浆卡伯值下降、细浆得率提高。其中巴克曼蒸煮渗透剂 A 与改性 AQ 双元复配使用时效果最好。改性 AQ 与巴克曼蒸煮渗透剂 A 双元复配使用时:当改性 AQ 用量 0.05%,巴克曼蒸煮渗透剂 A 用量 0.03%,成浆得率提高 1.31%,卡伯值下降 4.0;当改性AQ 用量 0.06%,巴克曼蒸煮渗透剂 A 用量 0.03%,成浆卡伯值降低了 6.4,细浆得率基本不变。     

预处理工艺对慈竹性能影响的研究

针对竹片密度大、蒸煮药液难渗透的问题,研究了慈竹预处理工艺及其对成浆性能的影响.实验结果发现,用热水预浸渍慈竹,当温度80℃、时间30 min时,在保证综纤维素含量基本不变的条件下,竹片中木素脱出率相对较高;用NaOH和Na2S共同预处理,当NaOH浓度10 g/L、Na2S浓度10 g/L、温度80℃、时间30 min时,得到了术素含量低、综纤维素含量适当降解的原料.经预处理和未预处理的慈竹在相同蒸煮工艺条件下成浆,其性能差别明显,经预处理后的成浆得率下降,但卡伯值降低更为显著.     

预水解硫酸盐法溶解浆置换蒸煮技术

简要分析了预水解因子与半纤维素提取率的关系及对置换KP法蒸煮浆料得率、卡伯值、黏度、强度的影响,介绍了预水解置换蒸煮溶解浆生产流程及工艺技术特点。     

预浸渍时间对硫酸盐桦木浆性能的影响

在生产漂白硫酸盐桦木浆的工厂中研究了木片预浸渍时间(5～60min)对浆料性能的影响。蒸煮后浆料的目标卡伯值和白度保持恒定,制浆的其他条件都按工厂的操作条件进行。当浆料卡伯值恒定时,通过分析浆料性能发现,预浸渍时间对预浸段有效碱的消耗量有很大影响,而对总碱的消耗量没有影响;为使浆料达到目标卡伯值,缩短预浸渍时间,则需要更高的蒸煮温度,同时会提高粗渣率;预浸渍时间对浆料黏度、碳水化合物组分以及纤维饱和点的影响不明显,但延长预浸渍时间会破坏一部分纤维;成纸抗张强度和挺度随预浸渍时间的缩短而提高,在抗张指数一定时,撕裂度与预浸渍时间的相关性不显著。     

MODDE分析软件用于桉木硫酸盐法蒸煮的研究

使用MODDE实验设计与分析软件对桉木硫酸盐法蒸煮的主要影响因素进行了研究,蒸煮条件为:有效碱用量17%～23%,硫化度25%～45%,最高温度150～160℃,保温时间45～135min。实验结果显示:有效碱用量、硫化度、温度和时间对成浆性质都有明显影响;蒸煮所得浆料的各项性能很难同时达到最佳。使用MODDE对实验结果进行优化,当目标卡伯值范围在15～25时,最适宜的蒸煮条件为:有效碱用量20%,硫化度45%,最高温度151℃,保温时间99min;MODDE显示该条件下所得浆料的卡伯值、细浆得率、白度和黏度分别为16、48.5%、46.4%和1498mL/g。     

预处理工艺对慈竹原料性能的影响

本刊讯陕西科技大学造纸工程学院李佩燚等人,针对竹片密度大、蒸煮药液难渗透的问题,研究了慈竹预处理工艺及其对成浆性能的影响。实验结果发现,用热水预浸渍慈竹,当温度80℃、时间30min时,在保证综纤维素含量基本不变的条件下,竹片中木素脱出率相对较高;用NaOH和Na2S共同预处理,当NaOH浓度10g·L-1、Na2S浓度10g·L-1、温度80℃、时间30min时,得到了木素含量低、综纤维素含量适当降解的原料。经预处理和未预处理的慈竹在相同蒸煮工艺条件下成浆,其性能差别明显,经预处理后的成浆得率下降,但卡伯值降低更为显著。     

蔗渣两段氧碱制浆的研究

探讨了NaOH用量对蔗渣浸渍和后续氧碱蒸煮制浆的影响,同时,也研究了氧碱制浆过程中氧压、蒽醌用量、蒸煮时间、蒸煮温度及液比等因素对氧碱制浆的影响。研究结果表明,浸渍段NaOH用量分别为4%、8%和14%时,氧碱制浆段NaOH用量为14%可获得较好的制浆效果;当浸渍段NaOH用量分别为6%、10%和12%时,氧碱制浆段NaOH用量为16%可获得较好的制浆效果。研究结果还表明,在相同蒸煮条件下,与蔗渣单段氧碱制浆相比,在获得相同卡伯值和抗碱性（R10）的纸浆时,两段氧碱制浆后纸浆得率更高,即在氧碱制浆前对蔗渣进行浸渍处理,可有效提高细浆得率和抗碱性,同时降低卡伯值。     

竹材热水预抽提对硫酸盐法制浆的影响

以绿竹为原料,采用不同热水预抽提时间以及蒸煮前将热水预抽提液与竹片分离的方法,通过对比KP法制浆黑液残碱含量以及KP浆的卡伯值、得率、黏度含量等探讨了对硫酸盐法制浆性能的影响。结果表明：热水预抽提可以提高竹片蒸煮脱木素效率,达到相同的脱木素程度（相同卡伯值20）可节省约52%的有效碱用量。在预抽提时间80 min时,浆料的最低卡伯值为7.03。另外,预抽提工艺有利于提高纸浆的黏度,同时纸浆的得率也产生了较大的下降。     

碱预浸低温硫酸盐法制备竹浆粕及其抗菌性的研究

为了保留竹子的天然抗菌性,以四川慈竹为原料,利用碱顶浸低温硫酸盐法和常规硫酸盐法制备竹浆,对两种工艺条件下的浆料性质进行对比,探讨了碱预浸低温硫酸盐法蒸煮的最佳工艺条件.结果表明,最佳碱预浸条件为:预浸温度120℃,NaOH用量12％,渗透剂用量1.75％,预浸时间 30 min;预浸后的蒸煮条件:用碱量(以Na2O计)20％,硫化度18％.碱预浸低温硫酸盐法浆粕中α-纤维素含量能够达到91％以上,且较常规硫酸盐法有更好的抗菌性.     

Sulfite-Formaldehyde Pulping and Oxygen Delignification of Wheat Straw

In this study,wheat straw pulp was prepared by sulfiteformaldehyde(SF) pulping combined with oxygen delignification to develop a sustainable methodology for chemical pulping of straw materials.The bleachability of oxygen-delignified SF pulp was also evaluated by hypochlorite bleaching.The results indicated that the Na_2SO_3 charge played an important role in lignin removal during SF pulping as well as oxygen delignification.The efficiency of oxygen delignification of wheat straw SF pulp was markedly high.After the oxygenation stage,the Kappa number decreased by over 50%(the original Kappa number of SF pulp was lower than 30) when the Na OH charge was in the range of 3%~5%.The optimal conditions for preparing bleached pulp via combined SF pulping and oxygen delignification involved the use of 12% of Na_2SO_3 and 3% of Na OH,respectively.Pulp with relatively high brightness,a low Kappa number,as well as an acceptable viscosity could be obtained when oxygen-delignified SF pulp was bleached with hypochlorite under a low active chlorine dosage.     

RDH法和常规KP法蒸煮过程中蒸煮液组成的变化及对比

对RDH(快速置换加热)硫酸盐法和常规KP法蒸煮过程中蒸煮液组成的变化规律进行了研究和对比。结果表明，在RDH硫酸盐法和常规KP法蒸煮过程中，蒸煮液中NaOH和Na2S含量均下降，但蒸煮液硫化度升高。与常规KP法相比，在整个脱木素反应过程中，RDH蒸煮液的有效碱浓度分布较均匀，蒸煮液中Na2S浓度较高，尤其在大量脱木紊的开始阶段(此时蒸煮液中Na2S浓度是常规KP法蒸煮时的2．88倍)，因而RDH法蒸煮能够深度脱除木素。与常规KP法蒸煮废液相比，在废液粘度相近的条件下，RDH法蒸煮废液有较高的固含量，有利于黑液的碱回收。在RDH硫酸盐法蒸煮经过一次完整的循环置换蒸煮周期后，温黑液槽和热黑液槽内的黑液组成基本保持稳定，可为后续进行的连续置换加热蒸煮提供良好的前提条件。     

竹子与马尾松KP法混合蒸煮制浆性能研究

通过竹子、马尾松不同比例的混合蒸煮试验,研究了用碱量、硫化度及竹木配比对制浆性能的影响,并对两种比例的混合浆物理性能进行了测试,结果表明按照一定配比,采用适当的硫酸盐法蒸煮工艺,竹子、马尾松混合蒸煮是可行的,可获得质量良好的木竹混合浆。     

竹、松混合蒸煮的实验

采用KP-AQ法对竹、松混合料片进行蒸煮试验,研究用碱量、硫化度及竹木配比对成浆性能的影响。结果表明,按照一定的竹木配比,采用适当的硫酸盐法蒸煮工艺,竹、松混合蒸煮是可行的,可获得质量良好的松竹混合浆。     

桉木RDH硫酸盐法制浆性能的研究

研究了桉木RDH（快速置换加热）硫酸盐浆的制浆性能，对桉木RDH硫酸盐法制浆时，用碱量、H－因子、白液的硫化度以及在温黑液预处理段温黑液的活性碱浓度和硫化度等蒸煮条件，对最终制浆结果的影响进行了研究。结果表明：与常规硫酸盐法制浆相比，RDH硫酸盐法制浆时的用碱量相对较高（常规KP法和RDH法的用碱量分别为14％和15％，Na2O计），但RDH纸浆的硬度较低（分别为17．0和11．7）；在纸浆达到相似或较低硬度的情况下，RDH法制浆可以缩短蒸煮时间，或在相同的H－因子下，降低纸浆的卡伯值；在一定的范围内提高白液蒸煮段白液的硫化度，可以降低RDH纸浆的卡伯值或提高纸浆的得率，在温黑液预处理段，温黑液的活性碱浓度和硫化度会对RDH纸浆的最终结果产生较大的影响，对纸浆物理性能的分析结果表明，RDH纸浆在低卡伯值条件下也具有较高的强度性能，但与常规硫酸盐浆相比，RDH纸浆的撕裂强度相对较高耐抗张强度相对较低。     

竹子碱法制浆过程中草酸根形成的研究

研究了竹子碱法制浆过程中蒸煮工艺条件对草酸根形成的影响,揭示了蒸煮过程中草酸根的形成与纸浆卡伯值的关系。结果表明,在竹子碱法蒸煮过程中,随着蒸煮反应的进行,草酸根的形成量逐渐增加,提高蒸煮最高温度、增大液比、增加用碱量均会导致草酸根形成量的增加,但当用碱量超过21%时,继续增加用碱量则不会使草酸根的形成量增加。草酸根的形成量随纸浆卡伯值的降低而增加。此外,根据H-因子、用碱量与草酸根形成量的关系,构建了竹子碱法制浆过程中草酸根形成的数学预测模型。该模型的预测准确性较高,可用于竹子碱法制浆过程中草酸根形成的预测。     

绿液预处理杨木硫酸盐法蒸煮脱木素反应历程研究

采用碱回收绿液对杨木木片进行预处理,研究了预处理后硫酸盐法蒸煮过程中脱木素反应历程及NaOH的消耗过程。研究表明,采用绿液预处理后,杨木木片得率为73.1%,木素脱除率为32.54%。预处理后的蒸煮过程中,在初始脱木素段,木素脱除率为14.52%;在大量脱木素段,木素脱除率为42.62%;残余脱木素段,木素脱除率仅为3.41%。这3个阶段的木素脱除率比传统硫酸盐法分别降低了3.55、19.38和9.11个百分点。NaOH几乎全部消耗在蒸煮初期和大量脱木素段,这2个阶段NaOH分别消耗了57.71%和42.29%;Na2S质量浓度在蒸煮初期逐渐减小,蒸煮的中后期又逐渐增大。绿液预处理硫酸盐法蒸煮不仅能提高脱木素选择性,还能提高蒸煮后浆料得率（达到50.8%）,比传统硫酸盐法浆料得率（47.9%）提高2.9个百分点。