核级手动截止阀Ω焊缝凝固缺陷成因研究

采用显微硬度测量、金相和扫描电镜(SEM)观察对不锈钢手动截止阀焊接接头各微区的硬度进行测量;对Ω焊缝、热影响区(HAZ)和母材的显微组织进行观察;对接头的断口形貌进行观测分析。结果表明:接头各区域的硬度分布差异不大,分布较为均匀,而2#试样HAZ的硬度高于1#。Ω焊缝金属柱状晶粗大,晶粒(柱状和胞状晶)的方向性强,晶间存在偏析,焊缝已形成沿晶界开裂。主要原因是:Ω焊缝装配间隙部位在冷却结晶时因液态填充不够,形成缩松、缩孔。在焊接应力/应变场作用下,拉伸应变或应变率超过此时材料的临界塑性和临界应变率时则产生焊接凝固裂纹。     

不锈钢薄板储能焊点焊接头的显微组织与力学性能

对0Cr18Ni9奥氏体不锈钢0.4 mm薄板进行了储能点焊试验,对其接头的显微组织和力学性能进行了分析研究。结果表明:焊接接头由熔核区、热影响区和熔核区向热影响区过渡的熔合区组成;熔核区显微组织由等轴奥氏体组成,由于储能焊极短的焊接时间和大的冷却速率,使熔核区的组织显著细化且具有快速凝固特征,其它区域组织与母材相当;当焊接电压为160 V、电极压力为18 N时,可获得有较高力学性能的焊接接头,其显微硬度为235.32 HV、抗剪强度为156.8 MPa。     

USIBOR1500超高强度淬火钢板点焊性能研究

通过对超高强度淬火钢板USIBOR1500同种材料点焊以及与低碳钢DC04异种材料点焊的两种焊接接头的抗剪强度、宏观形貌以及显微组织的研究与分析,探索了USIBOR1500的点焊性能.结果表明两种点焊接头基本不存在内部和外部缺陷,能够满足实际生产需要,USIBOR1500超高强度淬火钢板具有良好的点焊性能.     

钛和锆对2219铝铜合金焊接接头组织和性能的影响

采用力学性能试验和组织观察的方法,研究了焊丝中添加钛和锆对2219铝铜合金惰性气体保护焊焊接接头显微组织和性能的影响.结果表明:钛和锆的组织细化作用是相容的,增加焊丝中钛和锆的含量,可促使焊缝中的粗大、方向性很强的柱状晶转变为细小的等轴晶;钛和锆同时改善了沿晶界和枝晶间分布的α(Al)-CuAl2共晶分布形态,使其均匀分布;钛和锆可显著提高焊接接头的硬度、抗拉强度和伸长率.     

T92/TP347H异种钢焊接接头的组织结构和力学性能

采用ERNiCr-3和ERNiCrMo-3两种镍基焊丝,GTAW法实现T92/TP347H异种钢管焊接。研究了接头的显微组织结构、熔合区(线)两侧的成分分布和接头的力学性能,以及焊后热处理对接头组织结构及力学性能影响等。结果表明:T92/TP347H异种钢接头T92侧热影响区(HAZ)主要由过热区、粗晶区及细晶区构成;TP347H侧HAZ没有明显晶粒长大的现象,但晶界、晶内有碳化物析出。两种焊丝焊接的T92/TP347H异种钢接头拉伸断裂面位于TP347H侧母材,焊缝强度较高;ERNiCrMo-3焊接接头的强度高于ERNiCr-3焊接接头,但塑、韧性不如后者。750℃,30 min焊后热处理,有助于降低T92侧HAZ硬度,改善接头的综合力学性能。     

焊接电流对不等厚异质高强钢点焊接头组织性能的影响

采用电阻点焊工艺将热处理后1.8mm的22MnB5钢与1.5mm的TRIP590钢实施了焊接处理,并且对点焊后的22MnB5/TRIP590不等厚异质高强钢的点焊试样分别做以拉剪试验、显微硬度测试以及显微组织的观察,分析了焊接电流这一焊接工艺参数对于点焊接头显微组织以及力学性能的影响。     

14NiCrMo10 6V与Q345E钢过渡匹配焊接接头的组织与力学性能

采用E551T1-Ni2药芯焊丝对Q345E钢与14NiCrMo10 6V钢进行焊接,并通过室温拉伸、弯曲、冲击、硬度试验以及金相分析等对焊接接头的力学性能与显微组织进行了研究。结果表明:采用此焊丝可以获得拉伸、弯曲和冲击性能均良好的焊接接头,焊缝硬度在200～250HV之间;焊缝处晶界组织为先共析铁素体、少量无碳贝氏体(从晶界伸向晶内),晶内为针状铁素体与珠光体,个别部位有粒状贝氏体;Q345E钢侧热影响区与焊缝过渡区的组织为沿晶界析出的块状先共析铁素体和向晶内生长的条状铁素体以及少量的珠光体和贝氏体;14NiCrMo10 6V钢侧热影响区与焊缝过渡区的组织为板条状马氏体。     

钛基复合材料TIG焊接接头的显微组织和拉伸性能

采用非熔化极惰性气体钨极保护(TIG)焊技术对非连续增强钛基复合材料进行焊接,研究了焊接接头的显微组织与拉伸性能。结果表明:TIG焊接可较好地实现钛基复合材料的连接,焊缝成形良好,表面均匀洁净,未见微裂纹、气孔等焊接缺陷;接头由焊缝区、热影响区和母材区组成;接头中焊缝区和靠近焊缝的热影响区中β相晶界上分布的增强体TiB具有较高的长径比,细化程度较高,同时焊缝区和靠近焊缝的热影响区中存在大量针状马氏体α′相;接头的抗拉强度为1 137MPa,为母材的92%,断后伸长率为2.20%;接头拉伸时均在母材区断裂,拉伸断口主要呈韧性断裂特征,部分区域呈沿晶断裂特征。     

铁素体不锈钢CMT焊接接头HAZ组织性能研究

针对铁素体不锈钢焊接HAZ晶粒易长大的问题,提出采用小热输入的CMT焊接工艺。通过分析接头HAZ的显微组织、显微硬度和冲击性能,探讨了4003铁素体不锈钢焊接接头HAZ组织和性能,并与常规MIG焊焊接接头试样的组织、性能进行对比。试验结果表明:采用CMT焊接工艺获得的接头HAZ粗晶区宽度为460μm,明显窄于MIG焊接接头的粗晶区宽度545μm;CMT接头强度与MIG焊接接头显微硬度值相近,但CMT接头HAZ冲击韧性较MIG焊接接头试样提高了16.28%。     

热轧410S不锈钢板材钨极氩弧焊焊接接头的组织与性能

通过对热轧410S不锈钢板材手工钨极氩弧焊(TIG)焊接接头的组织观察、无损检测、力学性能和耐晶间腐蚀性能试验,以及铁素体含量和显微硬度的测定,研究了热轧410S不锈钢板材TIG焊接接头的组织与性能。结果表明:采用TIG方法焊接410S不锈钢接头的抗拉强度不低于母材的,而且塑性良好;焊接接头的宏观形貌呈铸造粗大组织,并具有明显的外延生长特性;焊缝组织主要为柱状晶奥氏体+沿柱状晶分布的δ铁素体,δ铁素体体积分数为15%~20%;热影响区的马氏体在焊接热的作用下发生了M→γ→M相变,原处于晶界条带中细小的颗粒状马氏体被黑色的团块状马氏体所替代;该焊接接头的晶间腐蚀倾向按热影响区、母材、焊缝顺序依次降低。     

Minimal Realization of Linear Graph Models for Multi-physics Systems

An engineering system may consist of several different types of components,belonging to such physical"domains"as mechanical,electrical,fluid,and thermal.It is t...     

Quantum Cooperative Robotics and Autonomy

The intersection of Quantum Technologies and Robotics Autonomy is explored in the present paper.The two areas are brought together in establishing an interdisci...     

考虑进油孔有限长滑动轴承油膜力的近似解析解

针对具有进油孔的有限长滑动轴承油膜力求解问题,采用变分原理和分离变量法,求得了有限长滑动轴承油膜压力分布的近似解析表达式。将油膜压力分布的近似解析表达式在油膜存在区域上进行积分,即得到了油膜力。将提出的计算有限长滑动轴承油膜力方法与无限长轴承模型、有限元方法的计算结果进行了比较,发现了提出的方法与有限元方法的计算结果很接近。最后,研究了进油孔位置和进油压力对油膜存在区域、油膜力等的影响,研究结果表明进油孔位置和进油压力对油膜存在区域和油膜力有较大的影响。     

三绕组变压器的双绕组等效建模及在Matpower中的应用

针对实际电网存在着大量的三绕组变压器,但国际上一些著名商业软件,如BPA仿真软件、Matpower这一权威潮流计算开源软件,均只提供双绕组变压器模型,限制了其在具有三绕组变压器的电力系统中的应用的问题,潮流计算是自主开发的电力系统各种应用软件的核心模块,因此依托国际权威开源程序进行二次开发,是一种较好的选择。对Matpower要求的数据格式进行了归纳,对变压器的一般的等值电路及带理想变压器的等值电路和带标幺值的等值电路进行了分析研究,提出了三绕组变压器转换为双绕组等效模型的建模方法,使得原先只适应双绕组变压器的潮流计算软件可以适用于三绕组变压器电网的潮流计算;最后以Matpower软件为例进行了案例计算,并用PSASP仿真软件进行对比验证。研究结果证明,所提出的建模方法是有效的。     

On the Relation of Load to Average Gap in the Contact Between Surfaces with Longitudinal Roughness

A computer simulation model for the contact between longitudinally-oriented rough surfaces has been formulated. This model closely duplicates the actual surf ace contact deformation behavior by taking into account the elastic interactions between the asperities. There were no assumptions made about the shapes, or any deformation behavior of the asperities, except for their obeying the laws of elasticity. The plastic deformations on the high asperity peaks were taken into account by setting a ceiling on their contact pressures at the material hardness value. The simulations used real surface profiles which were digitized from unworn circumferentially ground steel surfaces. Each pair of these profiles was mathematically combined to form an equivalent rough profile pressing against an infinitely rigid flat and having the appropriately adjusted elastic modulus. A total of 28 different pairs of profiles were used in the simulations. Each contacting pair was subjected to 30 different load levels and the local contact pressures and deformations were calculated. The contact simulations yielded some important mathematical relationships between parameters, such as the real area of contact, average gap, and average asperity load through statistical curve fitting. Two analytical functions were generated to relate the average load to average gap and the real area of contact to load.     

电站锅炉模糊风险评价方法研究与应用

针对电站锅炉风险等级评价问题,将模糊综合评价技术应用到电站锅炉风险等级评价中。开展了电站锅炉失效影响因素及模糊评价因素的重要程度分析,建立了一套科学合理适于在线评价的电站锅炉风险评价体系,提出了模糊综合评价技术与改进的模糊层次分析法相结合的模糊风险评价方法,利用改进的模糊层次分析法计算了指标体系中各层指标权重。对某一台电站锅炉的实际运行工况影响子因素进行了模糊风险评价,采用模糊合成算子进行模糊综合运算得到电了站锅炉运行工况影响子因素的评价向量。研究结果表明:电站锅炉的运行工况影响子因素的风险评价等级为第6级,失效可能性等级为小,该电站锅炉运行工况良好。     

Non-monotonic material contrast in scanning ion and scanning electron images

30 keV Ga⁺ focused ion beam induced secondary electron (iSE) imaging was used to determine the relative contrast between several materials. The iSE signal compared from C, Si, Al, Ti, Cr, Ni, Cu, Mo, Ag, and W metal layers does not decrease with an increase in target atomic number Z₂, and shows a non-monotonic relationship between contrast and Z₂. The non-monotonic relationship is attributed to periodic fluctuations of the stopping power and sputter yield inherent to the ion–solid interactions. In addition, material contrast from electron-induced secondary electron (eSE) and backscattered electron (BSE) images using scanning electron microscopy (SEM) also shows non-monotonic contrast as a function of Z₂, following the periodic behavior of the stopping power for electron–solid interactions. A comparison of the iSE and eSE results shows similar relative contrast between the metal layers, and not complementary contrast as conventionally understood. These similarities in the contrast behavior can be attributed to similarities in the periodic and non-monotonic function defined by incident particle–solid interaction theory.     

Application of Feature Extraction through Convolution Neural Networks and SVM Classifier for Robust Grading of Apples

This paper proposes a novel grading method of apples,in an automated grading device that uses convolutional neural networks to extract the size,color,texture,an...     

分布动态载荷识别的抗噪处理

针对正交多项式频域法在用多种响应对矩形薄板进行载荷识别中抗噪性较差的问题,综合运用平均法、矩阵预处理和奇异值截断法等方法对之进行改善,并引入空间映射的思想,将该方法的应用范围拓展为复杂的模型.利用仿真算例,证实了该方法具有较好的抗噪性.     

基于MELTAC-N平台的核电厂安全级DCS环网研究与测试

针对工程实践中环网通讯相关问题的处理缺乏理论基础及国产化安全级DCS平台的开发缺乏成熟经验借鉴问题,对基于MELTAC-N平台核电厂安全级DCS环网的软硬件实现进行了研究。提出了安全级DCS环网双环网冗余设计、光切换开关设计等硬件设计方法,以及以RPR协议为基础,采用全数据收发策略的软件设计方法。在CPR1000安全级DCS平台上对安全级DCS环网的可靠性及实时性进行了评价,并进行了容错能力、响应时间及响应时间稳定性测试验证实验。结果表明,基于MELTAC-N平台安全级DCS环网软硬件设计具有较好的容错能力及响应时间稳定性。