为解决电镀砂轮磨削加工中容屑空间不足的问题，采用点胶微粘接的方法制备了磨料有序排布的电镀砂轮，分析了磨料粘接效果和镀层力学性能。通过SEM分析了磨料/镀层/导电胶的结合界面，并进行了干磨削试验。研究结果表明，直径约为磨料粒径40%的胶点可粘接住磨料，单个胶点上粘接多颗磨料的占比小于6%；双脉冲电镀工艺制备的镀层显微硬度大于500HV，表层残余应力小于100MPa，磨料/镀层/导电胶之间的界面贴合紧密，无明显缺陷；砂轮在磨削时没有出现磨料脱落现象。     

Effect of partial replacement of geopolymer binder materials on the fresh and mechanical properties: A review

The growth of demand for concrete raises concerns about the consumption of natural resources and ordinary Portland cement. Geopolymer composites show promise as a sustainable alternative for conventional cement concrete. Considering the wide range of potential geopolymer composites applications (including suitability for transportation infrastructure, underwater applications, repair and rehabilitation of structures as well as recent developments in 3D printing), the desired fresh and mechanical properties of the geopolymer composite may vary between applications: for example, rapid setting can be a merit for certain applications and a demerit for others. Therefore, the desired fresh and mechanical properties (e.g., workability, setting time, compressive strength, etc.) can be controlled for a given geopolymer source material through its partial substitution by natural or by-product materials. Recognizing the critical role of various replacement materials in enhancing the potential applications of geopolymer composites, the present review was undertaken to quantify and understand the effect of partial replacement by fly ash, metakaolin, kaolin, red mud, slag, ordinary Portland cement, and silica fume on the setting time, workability, compressive strength and flexural strength of various source materials addressed in the literature. The review also provides insights into research gaps in the field to promote future research.     

对“垃圾衍生燃料”RDF之探析

当前,我国水泥工业在可燃废弃物应用技术方面都还处于一家一户、自制自用、效率极低的初级阶段。发达国家的替代燃料:“垃圾衍生燃料”RDF、“固体回收燃料”SRF、“次煤”Subcoal和“纸塑垃圾衍生燃料”RPF制成的原材料都是可燃废弃物,只是处理工艺技术不同或者由垃圾中分拣出的可燃废弃物不同,制成颗粒状衍生燃料的品质不同,这些都可以替代部分甚或替代全部化石燃料在水泥窑炉中应用。我国大力发展“替代燃料”产业,有助于水泥工业消纳更多的“可燃废弃物”,为改善环境尤其是城镇环境和面貌,为我国的节能减排和绿色高质量发展发挥更大的作用。     

Hydraulic reactivity and cement formation of baghdadite

In this study, the hydraulic reactivity and cement formation of baghdadite (Ca₃ZrSi₂O₉) was investigated. The material was synthesized by sintering a mixture of CaCO₃, SiO₂, and ZrO₂ and then mechanically activated using a planetary mill. This leads to a decrease in particle and crystallite size and a partial amorphization of baghdadite as shown by X-ray powder diffraction (XRD) and laser diffraction measurements. Baghdadite cements were formed by the addition of water at a powder to liquid ratio of 2.0 g/ml. Maximum compressive strengths were found to be ~2 MPa after 3-day setting for a 24-h ground material. Inductively coupled plasma mass spectrometry (ICP-MS) measurements showed an incongruent dissolution profile of set cements with a preferred dissolution of calcium and only marginal release of zirconium ions. Cement formation occurs under alkaline conditions, whereas the unground raw powder leads to a pH of 11.9 during setting, while prolonged grinding increased pH values to approximately 12.3.     

Enhancement in the osteogenesis and angiogenesis of calcium phosphate cement by incorporating magnesium-containing silicates

Based on the good osteogenic and angiogenic effects of silicon and magnesium elements, three types of micro-nano magnesium-containing silicates (MS), including akermanite (Ake, Ca₂MgSi₂O₇), diopside (Dio, CaMgSi₂O₆) and forsterite (For, Mg₂SiO₄), were incorporated into calcium phosphate cement (CPC) to improve its osteogenic and angiogenic performances for clinical application. In this present work, the physicochemical properties, osteogenesis and angiogenesis of MS/CPCs (Ake/CPCs, Dio/CPCs and For/CPCs) were investigated systematically and comparatively. The results showed that all MS/CPCs had good biomineralization and significantly stimulated the osteogenic differentiation of mBMSCs and angiogenic differentiation of HUVECs, respectively. Besides, the stimulating effects were related to not only the category of MS, but also the content of MS. The For/CPCs had a good angiogenic property but their initial setting times were beyond 60 min. The Dio/CPCs showed the lowest biological performance among the three groups of MS/CPCs due to the lower ion release (Si and Mg). The Ake was the ideal modifier that could provide CPC with appropriate physicochemical properties, better osteogenesis and angiogenesis. Simultaneously, a higher addition (10 wt%) of akermanite resulted in the best potential to bone regeneration. Taken together, this research provides an effective approach to improve the overall performance of CPC, and 10Ake/CPC is of great promising prospect in bone repair.     

Study on the non-uniform contact during ELID groove grinding

This paper introduces the potential feasibility that ELID (electrolytic in-process dressing) grinding replaces superfinishing in bearing manufacturing, but ELID grinding will bring new challenges. Different regions present distinguish surface profile due to the non-uniform contact in ELID groove grinding. However, few reports explaining the non-uniform contact are available. This article explores the mechanisms of the non-uniform contact during ELID groove grinding. Experiments on the non-uniform contact between bearing raceway and grinding wheel have been carried out under different conditions. The results show that non-uniform contact exists in ELID groove grinding process and it exerts influence on the profile of the raceway surface. Non-uniform contact influences the Rsk and Rku value all the time, but it influences the Ra value occasionally. Improvement strategies of eliminating the non-uniform contact are also discussed based on the experimental study.     

Effect of nanosilica addition on bioactivity and in vivo properties of calcium aluminate cement

This study aims at assessing the influence of nanosilica on the bioactivity and mechanical properties of calcium aluminate cement. For this purpose, nanosilica was applied as a replacement for calcium aluminate cement at 0, 2, 5 and 8 wt%. The main components were analyzed by scanning electron microscope coupled with surface imaging and elemental analysis, fourier transform infrared spectroscopy and X-ray diffraction analysis. To estimate the bioactivity of specimens, hydroxyapatite formation on the surface of cement paste was investigated in the simulated body fluid solution. In addition, in vivo evaluation of calcium aluminate cement was performed in subcutaneous tissue of rats. To investigate the mechanical properties, both compressive and flexural strengths were also measured. The results revealed that by increasing nanosilica up to 8 wt%, the strength enhanced. Moreover all cement paste samples with various amounts of nanosilica represented good bioactivity because of formation of bonelike apatite layer on the surface of specimens within 28 days after soaking in simulated body fluid. In vivo experiments indicated that the cement sample was absorbed by the tissue and there was no infection at the implant site. Based on the in vitro and in vivo results, the specimen with 2 wt% nanosilica represented the highest bioactivity.     

空气炮在解决水泥库出库溜子堵塞中的应用

针对水泥库结块经常堵塞下料溜子的问题,决定在溜子处安装空气炮,将空气炮压缩空气出口稍微上扬,以便于击打堵在下料口的结块。经实际使用,效果良好,改善了生产环境,降低了员工的劳动强度。     

Preparation and characterization of calcium phosphate cement with enhanced tissue adhesion for bone defect repair

Anti-washout and tissue adhesion properties are essential for the clinical application of injectable bone materials. In this study, we prepared calcium phosphate cement (CPC) with anti-washout and tissue adhesion properties and attempted to build covalent bonds between CPC and the amino groups in bone tissue under a self-regulating pH system in the CPC (acidic to basic). The results of push-out tests demonstrated that a significant enhancement (from 6.42 ± 0.76 N to 61.5 ± 4.09 N) in tissue adhesion was obtained with the addition of 6% (w/w) oxidized sodium alginate (OSA) in CPC. The FTIR, XRD, anti-washout test, XPS, pH test, and SEM results suggested that the synergistic effect of OSA-citric acid (CA) led to the formation of a three-dimensional gel network structure in the CPC, and the Schiff base reaction between aldehyde and amino groups induced adhesion between CPC and the bone tissue. Further, the addition of less OSA had no significant negative effect on the hydration properties of CPC. Our work aims to promote the development of injectable bone material in clinical applications.     

郴州某复杂硫化铅锌矿阶段磨浮试验研究

针对郴州某复杂硫化铅锌矿资源的性质特点,采用铅快速浮选后尾矿再磨再选的阶磨阶选工艺,较好地实现了铅锌的高效浮选回收。研究了磨矿方式、捕收剂和调整剂种类及用量等因素对该矿石浮选的影响,确定了最佳浮选条件,通过小型闭路浮选试验,得到了铅品位60.05%、回收率89.63%的铅精矿和锌品位47.01%、回收率88.14%的锌精矿。