High-temperature oxidation behavior of monolithic Zr3[Al(Si)]4C6 and its composite incorporating 30vol% ZrB2-SiC: Providing a basis for broadening the service temperature

To provide a basis for the high-temperature oxidation of ultra-high temperature ceramics (UHTCs), the oxidation behavior of Zr₃[Al(Si)]₄C₆ and a novel Zr₃[Al(Si)]₄C₆-ZrB₂-SiC composite at 1500 °C were investigated for the first time. From the calculation results, the oxidation kinetics of the two specimens follow the oxidation dynamic parabolic law. Zr₃[Al(Si)]₄C₆ exhibited a thinner oxide scale and lower oxidation rate than those of the composite under the same conditions. The oxide scale of Zr₃[Al(Si)]₄C₆ exhibited a two-layer structure, while that of the composite exhibited a three-layer structure. Owing to the volatilization of B₂O₃ and the active oxidation of SiC, a porous oxide layer formed in the oxide scale of the composite, resulting in the degradation of its oxidation performance. Furthermore, the cracks and defects in the oxide scale of the composite indicate that the reliability of the oxide scale was poor. The results support the service temperature of the obtained ceramics.     

Eco-friendly and degradable red phosphorus nanoparticles for rapid microbial sterilization under visible light

Pathogens pose a serious challenge to environmental sanitation and a threat to public health.The frequent use of chemicals for sterilization in recent years has not only caused secondary damage to the environment but also increased pathogen resistance to drugs,which further threatens public health.To address this issue,the use of non-chemical antibacterial means has become a new trend for environmental disinfection.In this study,we developed red phosphorus nanoparticles(RPNPs),a safe and degradable photosensitive material with good photocatalytic and photothermal properties.The red phosphorus nanoparticles were prepared using a template method and ultrasonication.Under the irradiation of simulated sunlight for 20 min,the RPNPs exhibited an efficiency of 99.98%in killing Staphylococcus aureus due to their excellent photocatalytic and photothermal abilities.Transmission electron microscopy and ultraviolet–visible spectroscopy revealed that the RPNPs exhibited degradability within eight weeks.Both the RPNPs and their degradation products were nontoxic to fibroblast cells.Therefore,such RPNPs are expected to be used as a new type of low-cost,efficient,degradable,biocompatible,and eco-friendly photosensitive material for environmental disinfection.     

煤矸石粉/聚酯纤维沥青混合料盐冻损伤研究EI北大核心CSCD

针对煤矸石粉替代率50%、聚酯纤维掺量0.4%的沥青混合料,开展盐冻耦合作用(NaCl溶液质量分数为0%、7.0%、13.0%、26.5%,冻融循环次数为0、2、4、6、8)下的半圆弯曲(SCB)试验,分析了盐冻耦合作用对SCB试件内部损伤劣化过程的影响.结果表明:NaCl溶液质量分数为13.0%、冻融循环为8次时,盐冻耦合作用对沥青混合料的侵蚀破坏作用最强,试件内部损伤最严重;在煤矸石粉与矿粉质量比为1∶1、聚酯纤维掺量为0.4%的条件下,沥青混合料能够形成高黏性、致密、厚实的沥青膜以及由纤维形成的三维网状结构,从而显著降低盐冻侵蚀对沥青混合料的损伤.通过Poly2D模型对SCB试件的极限拉应力损伤量进行拟合,拟合系数为0.944.     

传统牦牛酸奶源高产胞外多糖乳酸菌特性及发酵性能

为了研究四川藏区传统牦牛酸奶中高产胞外多糖乳酸菌特性及发酵性能，以本实验室分离出的六株高产胞外多糖乳酸菌为研究对象，以菌株生长量、耐酸性、胆盐耐受力、渗透压耐受力和细胞表面疏水性为指标进行特性研究；以发酵酸奶的凝乳时间、持水力、酸化及后酸化能力、挥发性物质及质构等为指标进行发酵性能研究。菌株的生长曲线表明，6株菌株分别在14 h（218、276、266）、16 h（271、285、231）进入对数生长稳定期，其中编号218的菌株生长量最高，OD值为2.188。耐受性实验结果表明，菌株276具有良好的耐酸能力（P<0.05）；菌株266、218、231耐胆盐的能力较强；6株菌株均具有较好的耐渗透压的能力，其中菌株285对高渗透压的耐受性较强；菌株285和218在两种有机试剂中的疏水性均显著（P<0.05）高于其他菌株，且与十六烷的结合效果较好。发酵试验结果表明，6株菌株所发酵酸奶均在6~8 h内凝固，酸乳在冷藏期间，活菌数均保持在107 CFU/mL以上，均符合发酵剂的标准，其中菌株276的最高为3.22×106 CFU/mL；菌株218发酵制得的酸奶质构特性较好，持水力和酸化能力较其余菌株均最强，分别为60.98%和83 °T；菌株276、266抗后酸化能力较好；菌株231产香性能最优，乙醛含量为24~26 μg/mL，双乙酰含量为1.58~3.73 μg/mL，能够明显改善酸奶的风味。通过综合比较6株高产胞外多糖乳酸菌特性及发酵性能，菌株218为一株性能良好、具有良好稳定性的菌株，可作为乳酸菌发酵剂且具有一定的应用潜力。研究为利用四川藏区传统牦牛酸奶中分离出的高产胞外多糖乳酸菌在发酵乳制品的应用提供理论依据。     

基于慕课堂数据的学生学习行为分析

本文结合慕课堂线上学习数据与线下考试成绩,研究学生在线学习的行为表现与学习效果之间的关联性,所获得的信息能够体现出不同学生群体的特点以及不同学习维度的作用,从而提醒教师适时调整教学策略,持续改进,有助于教师改进教学方法,提高教学质量.     

掺钪AlN材料特性及HBAR器件性能研究

该文基于掺钪AlN薄膜制备了高次谐波体声波谐振器(HBAR),研究了钪(Sc)掺杂浓度对AlN压电薄膜材料特性及器件性能的影响。研究表明,当掺入Sc的摩尔分数从0增加到25%时,压电应力系数e₃₃增加、刚度 下降,导致Al₁-_xSc_xN压电薄膜的机电耦合系数 从5.6%提升至15.8%,从而使HBAR器件的有效机电耦合系数 提升了3倍。同时,当Sc掺杂摩尔分数达25%时,Al₁-_xSc_xN(x为Sc掺杂摩尔分数)压电薄膜的声速下降13%,声学损耗提高,导致HBAR器件的谐振频率和品质因数降低。