Rational Designs for Lithium-Sulfur Batteries with Low Electrolyte/Sulfur Ratio

Lithium-sulfur batteries (LSBs) are considered a promising next-generation energy storage device owing to their high theoretical energy density. However, their overall performance is limited by several critical issues such as lithium polysulfide (PS) shuttles, low sulfur utilization, and unstable Li metal anodes. Despite recent huge progress, the electrolyte/sulfur ratio (E/S) used is usually very high (≥20 µL mg⁻¹), which greatly reduces the practical energy density of devices. To push forward LSBs from the lab to the industry, considerable attention is devoted to reducing E/S while ensuring the electrochemical performance. To date, however, few reviews have comprehensively elucidated the possible strategies to achieve that purpose. In this review, recent advances in low E/S cathodes and anodes based on the issues resulting from low E/S and the corresponding solutions are summarized. These will be beneficial for a systematic understanding of the rational design ideas and research trends of low E/S LSBs. In particular, three strategies are proposed for cathodes: preventing PS formation/aggregation to avoid inadequate dissolution, designing multifunctional macroporous networks to address incomplete infiltration, and utilizing an imprison strategy to relieve the adsorption dependence on specific surface area. Finally, the challenges and future prospects for low E/S LSBs are discussed.     

Growth,mechanical properties,and tribological performance of TiAlN/NbN and NbN/TiAlN bilayer coatings

Three different coatings, namely TiAlN, TiAlN (external)/NbN (internal) and NbN (external)/TiAlN (internal), were deposited on cemented carbides by arc ion plating. The comparative investigation conducted in this study elucidates the effect of the NbN layer and coating systems on the growth, mechanical properties, and tribological performance of the coatings. The results showed that the surface of the TiAlN and TiAlN/NbN coatings was smoother when TiAlN served as the external layer. The NbN/TiAlN coating, wherein NbN formed the external layer, had a much rougher but more symmetrical surface. With the introduction of the NbN layer, the increased micro stress induced a lower adhesion strength in the TiAlN/NbN and NbN/TiAlN coatings. The TiAlN/NbN and NbN/TiAlN coatings exhibited higher hardness and hardness/effective elastic modulus (H/E*). During the friction test, when the temperature was elevated to 700 °C, the tribological performance of the monolayer TiAlN coating was the lowest because of the TiO₂-induced breakage of the dense tribo-oxide film. The NbN layer participated in the formation of a NbO_x film at elevated temperatures, which was responsible for the high tribological performance of the two bilayer coatings. When the NbN layer was on the outermost layer and in direct contact with the elevated temperature atmosphere, the NbN/TiAlN coating generated a tribo-oxide film with high integrity, and its coefficient of friction decreased by 27% of that at room temperature. Therefore, the NbN/TiAlN coating exhibited the highest wear resistance at 700 °C.     

P-doped CoSe2 nanoparticles embedded in 3D honeycomb-like carbon network for long cycle-life Na-ion batteries

We report for the first time a Na-ion battery anode material composed of P-doped CoSe2 nanoparticles(P-CoSe2)with the size of 5-20 nm that are uniformly embed in a 3D porous honeycomb-like carbon network.High rate capability and cycling stability are achieved simultaneously.The honeycomb-like carbon network is rationally designed to support high electrical conductivity,rapid Na-ion diffusion as well as the accommodation of the volume expansion from the active P-CoSe2 nanoparticles.In particular,heteroatom P-doping within CoSe2 introduces stronger P-Co bonds and additional P-Se bonds that signif-icantly improve the structure stability of P-CoSe2 for highly stable sodiation/desodiation over long-term cycling.P-doping also improves the electrical conductivity of the CoSe2 nanoparticles,leading to highly elevated electrochemical kinetics to deliver high specific capacities at high current densities.Benefiting from the unique nanostructure and atomic-level P-doping,the P-CoSe2(2∶1)/C anode delivers an excel-lent cycle stability with a specific capacity of 206.9 mA h g-1 achieved at 2000 mA g-1 after 1000 cycles.In addition,this material can be synthesized using a facile pyrolysis and selenization/phosphorization approach.This study provides new opportunities of heteroatom doping as an effective method to improve the cycling stability of Na-ion anode materials.     

TiO2/MXene-Assisted LDI-MS for Urine Metabolic Profiling in Urinary Disease

Cancer remains an intractable medical problem. Rapid diagnosis and identification of cancer are critical to differentiate it from nonmalignant diseases. High-throughput biofluid metabolic analysis has potential for cancer diagnosis. Nevertheless, the present metabolite analysis method does not meet the demand for high-throughput screening of diseases. Herein, a high-throughput, cost-effective, and noninvasive urine metabolic profiling method based on TiO₂/MXene-assisted laser desorption/ionization mass spectrometry (LDI-MS) is presented for the efficient screening of bladder cancer (BC) and nonmalignant urinary disease. Combined with machine learning, TiO₂/MXene-assisted LDI-MS enables high diagnostic accuracy (96.8%) for the classification of patient groups (including 47 BC and 46 ureteral calculus (UC) patients) from healthy controls (113 cases). In addition, BC patients can also be identified from noncancerous UC individuals with an accuracy of 88.3% in the independent test cohort. Furthermore, metabolite variations between BC and UC individuals are investigated based on relative quantification, and related pathways are also discussed. These results suggest that this method, based on urine metabolic patterns, provides a potential tool for rapidly distinguishing urinary diseases and it may pave the way for precision medicine.     

Cyclic thermal shock resistance of h-BN composite ceramics with La2O3–Al2O3–SiO2 addition

The effects of La₂O₃–Al₂O₃–SiO₂ addition on the thermal conductivity, coefficient of thermal expansion (CTE), Young's modulus and cyclic thermal shock resistance of hot-pressed h-BN composite ceramics were investigated. The samples were heated to 1000 °C and then quenched to room temperature with 1–50 cycles, and the residual flexural strength was used to evaluate cyclic thermal shock resistance. h-BN composite ceramics containing 10 vol% La₂O₃–Al₂O₃ and 20 vol% SiO₂ addition exhibited the highest flexural strength, thermal conductivity and relatively low CTE, which were beneficial to the excellent thermal shock resistance. In addition, the viscous amorphous phase of ternary La₂O₃–Al₂O₃–SiO₂ system could accommodate and relax thermal stress contributing to the high thermal shock resistance. Therefore, the residual flexural strength still maintained the value of 234.3 MPa (86.9% of initial strength) after 50 cycles of thermal shock.     

Selective Coating of SnS on the Bio‐Inspired Moth‐Eye Patterned PEDOT:PSS Polymer Films

A new strategy for the selective coating of tin sulfide (SnS) on the surface of moth‐eye patterned (MEP) conducting polymer film is studied by considering the optical properties of the antireflective moth‐eye pattern and flexibility of polymer films. The semiconductor SnS is selectively coated on the surface of MEP microdomes of poly(3,4‐ethylenedioxythiophene) poly(styrene‐sulfonate) (PEDOT:PSS) film. The SnS coated MEP film is obtained by using pore selectively SnS thin layer functionalized polystyrene honeycomb‐patterned porous (HCP) film as a template. Aqueous PEDOT:PSS solution is poured on the SnS functionalized HCP films and detached for the fabrication of SnS coated MEP films. The films show a satisfactory photo‐responsive property under solar stimulated light illumination due to the antireflective MEP structure of PEDOT film and homogenous SnS coating on the surface of the conducting polymer.     

Fabrication and characterizations of Cr3+-doped ZnGa2O4 transparent ceramics with persistent luminescence

0.5 at.% Cr:ZnGa₂O₄ precursor was synthesized by the co-precipitation method with nitrates as raw materials, using ammonium carbonate as the precipitant. Low-agglomerated Cr:ZnGa₂O₄ powders with an average particle size of 43 nm were obtained by calcining the precursor at 900℃ for 4 h. Using the powders as starting materials, 0.5 at.% Cr:ZnGa₂O₄ ceramics with an average grain size of about 515 nm were prepared by presintering at 1150℃ for 5 h in air and HIP post-treatment at 1100℃ for 3 h under 200 MPa Ar. The in-line transmittance of 0.5 at.% Cr:ZnGa₂O₄ ceramics with a thickness of 1.3 mm reaches 59.5% at the wavelength of 700 nm. The Cr:ZnGa₂O₄ ceramics can be effectively excited by visible light and produce persistent luminescence at 700 nm. For Cr:ZnGa₂O₄ transparent ceramics, the brightness of afterglow was larger than 0.32 mcd/m² after 30 min, which is far superior to that of Cr:ZnGa₂O₄ persistent luminescence powders.     

径向不耦合装药爆破效果的数值研究

为了研究径向不耦合条件下爆破效果的影响因素,利用AUTODYN-2D对比不耦合系数、不耦合介质、炸药种类对爆破效果的影响规律。结果表明,与耦合装药相比,径向不耦合装药条件下炮孔压力明显降低。对比水介质和空气介质下的爆破效果可知,水介质不耦合条件下,炸药爆炸能量的传递效率更高。炮孔压力与炸药种类密切相关,TNT产生的炮孔压力最大,但作用时间较短,而ANFO和乳化炸药的作用时间较长。     

Microtubule Destabilizing Sulfonamides as an Alternative to Taxane-Based Chemotherapy

Pan-Gyn cancers entail 1 in 5 cancer cases worldwide, breast cancer being the most commonly diagnosed and responsible for most cancer deaths in women. The high incidence and mortality of these malignancies, together with the handicaps of taxanes—first-line treatments—turn the development of alternative therapeutics into an urgency. Taxanes exhibit low water solubility that require formulations that involve side effects. These drugs are often associated with dose-limiting toxicities and with the appearance of multi-drug resistance (MDR). Here, we propose targeting tubulin with compounds directed to the colchicine site, as their smaller size offer pharmacokinetic advantages and make them less prone to MDR efflux. We have prepared 52 new Microtubule Destabilizing Sulfonamides (MDS) that mostly avoid MDR-mediated resistance and with improved aqueous solubility. The most potent compounds, N-methyl-N-(3,4,5-trimethoxyphenyl-4-methylaminobenzenesulfonamide 38, N-methyl-N-(3,4,5-trimethoxyphenyl-4-methoxy-3-aminobenzenesulfonamide 42, and N-benzyl-N-(3,4,5-trimethoxyphenyl-4-methoxy-3-aminobenzenesulfonamide 45 show nanomolar antiproliferative potencies against ovarian, breast, and cervix carcinoma cells, similar or even better than paclitaxel. Compounds behave as tubulin-binding agents, causing an evident disruption of the microtubule network, in vitro Tubulin Polymerization Inhibition (TPI), and mitotic catastrophe followed by apoptosis. Our results suggest that these novel MDS may be promising alternatives to taxane-based chemotherapy in chemoresistant Pan-Gyn cancers.