退火变脆Fe75Si10B15金属玻璃的脆韧性转变

研究了机械研磨对退火变脆Fe_(75)Si_(10)B_(15)金属玻璃的弛豫过程,晶化行为及脆韧性转变的影响。发现退火变脆的Fe_(75)Si_(10)B_(15)金属玻璃,经不同时间机械研磨,Curie温度T_C逐渐回落,总的弛像焓ΔH_?逐渐回升。在DSC曲线上观察到明显的玻璃转变温度T_(g_1)和一个附加的宽放热峰T_(x_1),随着研磨时间的增加,T_(x_1),T_(x_1),T_C同步降低,与T_(x_1)对应的放热面积ΔH_(x_1)逐渐增大,并在片状粒子表面形成切变带以及与其对应的剪切带,玻璃在退火过程中失掉的韧性逐渐得到恢复。     

六方Co_(2-3)C的形成SCIEI

将50keV碳离子注入纯Co金属膜中,在剂量为2.5×10^(17)/cm^2时,发现了六方结构碳化物。电子衍射结果表明晶格常数a=0.2685nm,c=0.4335nm。当剂量提高到5×10^(17)/cm^2时,六方衍射环仍然存在。而剂量提高到9×10^(17)/cm^2时,衍射环变成具有非晶特征的漫散晕。Auger谱数据表明,形成的六方相成份范围为Co_2-_3C。本文从固体Fermi能来解释Fe,Co和Ni的六方碳化物形成的变化;从能带理论解释热处理方法形成正交Co碳化物的原因。     

镀铬层表面等离子束流加热区视觉信息检测试验

论述了视觉传感技术的特点和研究现状。针对镀铬层固态表面传热及光路特点，选取了普通CCD摄像机，利用固态表面对电弧的反射光和加热工件自身的辐射光，在近红外波段取像的视觉采集方法。结合近红外光谱特点和CCD摄像机的光谱响应度变化趋势，在980nm波长的窗口区域提取到了清晰的视觉图像。分析了镀铬层固态表面等离子束流加热区图像的成像机理，在对加热区图像特征进行分析的基础上对图像进行了处理，提取出了有效信息。     

垂直侵彻钢靶过程中钨合金壳体破坏机理研究

进行了钨合金壳体垂直侵彻45钢靶板的实验，成功地获得钨合金壳体侵彻钢靶板时变形破坏演变的完整过程。通过对回收的钨合金壳体微组织结构的观察与分析，发现钨合金壳体的主要破坏机制是危险截面区域形成绝热剪切带；其次，内腔前端区域发生粘结相撕裂。建立了壳体侵彻过程危险截面区域失效演变的3个阶段：绝热剪切带的形成、带内微裂纹的萌生和剪切裂纹的扩展。材料的失效方式与壳体存在应力集中区域密切相关，只有在壳体的结构设计中尽可能降低局部的应力集中系数，钨合金材料才能既可以发挥优异的侵彻性能，又可以保证侵彻过程完整性的要求，从而实现工程应用和军事应用。     

内生枝晶增塑锆基块体金属玻璃复合材料

利用熔体水淬法制备了内生bcc β-Zr固溶体增塑的Zr56．2Ti13.8Nb5．0Cu6．9Ni5．6Be12．5块体金属玻璃基体复合材料．β相呈发达的树枝状，体积分数约为30％．室温单轴压缩时，复合材料失效前的纯塑性应变达到10．2％，并具有2．0％的弹性应变极限和1788MPa的极限断裂强度．显微观察表明，压缩变形后的试样表面均匀分布着大量波浪形剪切带．     

a-C:F:H films prepared by PECVD

Fluorinated amorphous hydrogenated a-C:F:H carbon thin films were deposited using radio frequency plasma enhanced chemical vapor deposition(RF-PECVD) reactor with CF4 and CH4 as source gases and were annealed in a N2 atmosphere. The properties of these films were evaluated by FTIR spectrometry, UV-VIS spectrophotometry and single-wavelength spectroscopic ellipsometry. A correspondence relativity connection between the deposition rate and technology was found. The chemical bonding structures and the content of CHx and CFx in the films are transformed and the optical band gap decreases monotonically with increasing temperature after annealing.The dielectric constant is increased with decreasing content of F in the films and the optical band gap is decreased with decreasing the content of H in the film.     

Hot compression deformation behavior of MB26 magnesium alloy

The flow stress features of MB26 magnesium alloy were studied by isothermal compression at 300-450 ℃ and strain rate of 0.001^-1 s J with Gleeble 1500 thermal simulator. In addition, the deformation activation energy Q was calculated. The results show that the strain rate and deformation temperature have obvious effect on the true stress. The peak value of flow stress becomes larger with increasing strain rate at the same temperature, and gets smaller with the increasing deformation temperature at the same strain rate. The alloy shows partial dynamic recrystallization. The flow stress of MB26 magnesium alloy during high temperature deformation can be represented by Zener-Hollomon parameter including the Arrhemius term. The temperatt, re range of 350-400℃ is suggested for hot-forming of this alloy.     

超高纯铁素体不锈钢在3．5％NaCl中的腐蚀疲劳的裂纹萌生

本文利用三电极技术研究了超高纯铁素体不锈钢Ｆｅ－２６Ｃｒ－１Ｍｏ在３．５％ＮａＣｌ水溶液转化体系中，低周腐蚀疲劳的裂纹萌生行为．在静态点蚀电位以下，形变诱发点蚀出现，但是点蚀在本文的研究体系不是导致裂纹萌生的原因．在低应变速率下，裂纹沿晶内的驻留滑移带萌生，且沿滑移带的电化学溶解加快了裂纹萌生．在高应变速率下，裂纹在晶界萌生，且沿晶界有点蚀实验结果表明，电化学溶解加速了裂纹萌生，点蚀在此钝化体系中不是裂纹萌生的机制．应变速率影响裂纹萌生方式．     

纳米压痕形变过程的分子动力学模拟

根据EAM多体势，利用分子动力学方法模拟了Ni压头压入Al基体的纳米压痕全过程．包括压头接近和离开基体时的原子组态；压入和上升时的载荷一位移曲线以及位错的发射和形变带的产生和变化；同时模拟了纳米尺度的应力弛豫行为．结果表明，当压头尚未接触基体时就能吸引基体原子，通过缩颈而互相连接．当压入应力Ts为1．9MPa时，基体Al开始发射位错；当分切应力Td=6．4MPa时，出现形变带．压头上升过程出现反向的拉应力，使基体反向屈服，在卸载过程中基体残留位错的组态不断改变．当压头上升离开基体后能拉着基体通过缩颈而相连，当压头和基体分离后仍粘有基体原子．在纳米尺度也存在应力弛豫现象，其原因是热激活引起的位错发射和运动．