元素Si对TiAl合金抗氧化性能的影响

研究了元素Si对不同Nb含量TiAl合金抗氧化性能的影响．结果表明，合金中Nb含量越低，Si对合金抗氧化性能的提高作用越明显．主要表现为Si促使二元合金形成连续致密的Al2O3层及使不同Nb含量合金表层氧化物更加均匀细小．因而随Si含量的增加，TiAl合金的氧化增重速率系数降低，氧化速率下降．运用等温氧化增重实验、X射线衍射和扫描电镜等手段对Si的作用进行了分析讨论．     

高速电弧喷涂Fe-Al金属间化合物涂层

采用粉芯丝材和高速电弧喷涂技术(HVAS)制备了Fe-Al金属间化合物涂层,并研究了涂层的显微组织和室温至650℃的滑动摩擦磨损性能.结果表明:Fe-Al涂层的平均成分为Fe-20.0Al-14.1O(摩尔分数,%),主要相是Fe3Al,FeAl,α-Fe,Al2O3及少量Al;涂层具有较高的结合强度和硬度、较低的孔隙率及较高的高温耐磨性;高温下磨损面形成了大面积的氧化物保护层,降低了涂层的摩擦因数,而剥层磨损是涂层的主要磨损机制.涂层中Fe3Al和FeAl金属间化合物相较高的高温强度和硬度能有效地阻碍裂纹的产生、扩展及扁平颗粒的断裂,从而使Fe-Al涂层表现出优异的高温耐磨性.     

Manufacturing a TiAl alloy by high-energy ball milling and subsequent reactive sintering

A TiAl alloy was fabricated by high-energy ball milling and subsequent reactive sintering from the mixed powders of Ti and Al. High-energy ball milling produced a kind of particular composite powders with an extremely fine altemative Ti and Al lamella structure. The composite powders not only possessed good consolidation and densification characteristics, but also resulted in the augment of nucleation rate of α and γ titanium aluminides during solid-phase reactive sintering After a series of processing, pressing, degassing, extrusion, and sintering, the resultant TiAl alloy presented high relative density and refined grain sizes of （α2 ＋ γ） lamella and γ phases. The compressive yield strength of the sintered TiAl reached 600 MPa at 800℃.     

B和C对铸造TiAl基合金宏观和显微组织的影响

对比研究了B和C含量的变化对铸造TiAl基合金宏观和显微组织的影响。结果表明 ，B或C含量的增加均能细化TiAl基合金的晶粒，但二者的作用特点不同。B含量对宏观组织和晶粒尺寸的影响是渐进的，而C对其影响存在一个临界含量。显微观察表明，微量的B就能使合金析出TiB2，随着合金中B含量的增加，硼化物颗粒呈不同的形貌。对于含C合金，当C含量低于临界含量时，在光学尺度上观察不到碳化物相，而当C含量高于临界含量时，合金中生成大量的Ti2AlC碳化物颗粒。讨论了B和C细化TiAl基合金的机制。     

离子束增强沉积氮化硅膜及TiAl抗高温氧化性能的改善

用离子束增强沉积（ＩＢＥＤ）方法在金属间化合物ＴｉＡｌ上合成厚度为０．５，１，和２μｍ的氮化硅薄膜。所形成的薄膜为非晶态，膜与基底间存在混合的过渡区，膜与基底结合紧密用ＡＥＳ，ＸＲＤ和ＸＰＳ研究薄膜的组成和结构，高温循环氧化结果表明，经沉积膜的ＴｉＡｌ试样的抗氧化性能显著提高其中沉积０．５μｍ薄膜的试样表现出极好的抗循环氧化性能由ＳＥＭ及ＥＤＳ分析得出，良好的高温稳定性能、高的膜／基底结合力和形成富Ａｌ２Ｏ３和硅化物的保护层是提高ＴｉＡｌ抗高温氧化性能的主要因素．     

加工TiNi形状记忆丝的新工艺

采用模拟试样研究了Ti/TiAl、Nb/TiAl和NbTi/TiAl 3种复合材料的界面特性。结果表明,爆炸试样的界面反应层厚度远小于热等静压试样的界面反应层厚度。在同一条件下热等静压成型的这3种复合材料,其界面差异明显:Ti/TiAl和NbTi/TiAl试样的界面反应层较厚,界面结合强度较高;Nb/TiAl试样的界面反应层较薄,界面结合强度较低。     

Recent developments in engineering γ—TiAl intermetallics

γ-TiAl based alloys are rapidly being developed for elevated temperature applications,due to their high strength,light mass and good oxidation resistance.However,th disadvantages of TiAl based alloys are low ductility and toughness at room temperature,and poor workability.Grain refinement is one of the most effective ways for improving room temperature tensile properties and hot workability of ordered TiAl based alloys.At present,the majority of research works have focused on alloy modifications through compositional controls,alloying additions,thermo-mechanical processing and production techniques.This article discusses the research status of TiAl based alloys in the aras of microstructure,alloying,processing and applications.     

Friction welding of TiAI intermetallics and structural steel by applying Inconel 718 as interlayer

Inconel 718 with thickness ranged from 0. 1 - 1.7 mm was chosen as interlayer to promote weldability in friction welding of TiAl intermetallics and structural steel such as AIS14140, in which the welded joint presents single fin showing less welding deformation on TiAl side. The correlations between tensile strength and the interlayer thickness were analyzed and fitted to a model. It indicates an optimum interlayer thickness ranged from 0.9 - 1.1 mm where the tensile strength reaches as high as 360 MPa. Otherwise, while the interlayer thickness decreases to 0. 1 mm, brittle compounds of TiC, Al2Ti4C2 and MTC3 are formed in the welded zone so that the tensile strength decays. Thicker interlayer should be also avoided as double joints may occur at TiAl -lnconel 718 and lnconel 718 -AISI 4140, respectively, which lowers the tensile strength to some extent.     

Isothermal oxidation behavior of FeCo–2V intermetallic alloy

Isothermal oxidation behavior and the nature of oxide layer formed during oxidation of FeCo–2V alloy were characterized in the temperature range of 500–600 °C. Oxidation kinetics of the alloy follows a parabolic rate law. SEM and XRD studies indicate the formation of an iron rich outer oxide layer and an inner solute rich layer containing cobalt and vanadium rich oxides. The oxidation mechanism of the FeCo–2V alloy is similar to that of low alloy steels. During the initial stages, preferential oxidation of iron and cobalt occurs at the alloy surface and leads to the formation of a solute rich inner layer. Continued oxidation occurs through oxidation of iron and cobalt at the outer layer and internal oxidation of inner layer. The iron rich oxide layer formed at the surface on oxidation of FeCo alloy is semi-conducting in nature and may not provide the necessary insulating barrier required at the surface to minimize eddy current losses during A.C. applications.