Structural and optical properties of CdTe-nanocrystals thin films grown by chemical synthesis

By mans of a chemical synthesis technique stoichiometric CdTe-nanocrystals thin films were prepared on glass substrates at 70 °C. First, Cd(OH)₂ films were deposited on glass substrates, then these films were immersed in a growing solution prepared by dissolution of Te in hydroxymethane sulfinic acid to obtain CdTe. The structural analysis indicates that CdTe thin films have a zinc-blende structure. The average nanocrystal size was 19.4 nm and the thickness of the films 170 nm. The Raman characterization shows the presence of the longitudinal optical mode and their second order mode, which indicates a good crystalline quality. The optical transmittance was less than 5% in the visible region (400–700 nm). The compositional characterization indicates that CdTe films grew with Te excess.     

（S）-噻吗洛尔半水合物的合成及表征

为了开发β受体阻断剂新药（S）-噻吗洛尔半水合物，采用3-吗啉-4-氯-1，2，5-噻二唑为起始原料，经水解反应得到中间体1（3-吗啉-4-羟基-1，2，5-噻二唑）。中间体1与R-环氧氯丙烷发生醚化反应，经后处理及重结晶得到中间体2 {（R）-4-［4-（环氧乙烷-2-基甲氧基）-1，2，5-噻二唑-3-基］吗啉}。中间体2经胺化反应、马来酸成盐及重结晶得到（S）-马来酸噻吗洛尔。（S）-马来酸噻吗洛尔经游离、纯水转晶得到符合药典标准的（S）-噻吗洛尔半水合物，总收率14.05%且e.e.值为99.66%。最终成品经IR、1H-NMR、13C-NMR、MS、TGA、DSC表征，并优化各步反应条件。结果表明:以三乙胺为醚化反应缚酸剂75 ℃反应最佳；以乙醇为胺化反应溶剂46 ℃反应16 h最佳；S-噻吗洛尔的转晶拆分以水作溶剂，比传统不对称合成工艺安全稳定，操作简单，适合工业化生产。     

Design of functionalized α-Fe2O3 (III) films with long-term anti-wetting properties

The design of functional anti-wetting ceramic coatings is always a bottleneck restricting the development of ceramic techniques. This study proposes a liquid phase synthesis method to fabricate α-Fe₂O₃ (III) ceramic powders with promising applications and introduces a facile electrophoretic deposition (EPD) technique to construct the corresponding functionalized hydrophobic films – superhydrophobic functionalized α-Fe₂O₃ ceramic films (SFOFS) with roughly even distribution and a high water contact angle (CA) of 169°±1° – followed by heat posttreatments. The microtopography and crystalline structures of the product were investigated by FESEM, EDX, and XRD techniques. The EPD controllability of SFOFS was studied by adjusting the EPD time and the applied field strengths. In addition, the SFOFS show excellent long-term anti-wetting properties for twenty-four months after undergoing a series of tests, including soaking, water droplet impacting, immersion by droplets with different surface tensions and exposure to different gases and relative humidity conditions, etc. This study substantially helps the design of other kinds of functional anti-wetting films through the proposed convenient method beyond the oxide limit.     

Simultaneous synthesis of a heat exchanger network with multiple utilities using utility substages

Heat exchanger network synthesis (HENS) has progressed by using mathematical programming-based simultaneous methodology. Although various considerations such as non-isothermal mixing and bypass streams are applied to consider real world alternatives in modeling phase, many challenges are faced because of its properties within non-convex mixed-integer nonlinear programming (MINLP). We propose a modified superstructure, which contains a utility substage for use in considering multiple utilities in a simultaneous MINLP model. To improve model size and convergence, fixed utility locations according to temperature and series connections between utilities are suggested. The numbers of constraints, discrete, and continuous variables show that overall model size decreases compared with previous research. Thus, it is possible to expand the feasible search area for reaching the nearest global solution. The model's effectiveness and applications are exemplified by several literature problems, where it is used to deduce a network superior to that of any other reported methodology.     

Flame characteristics of premixed H2-air mixtures explosion venting in a spherical container through a duct

The explosion venting duct can effectively reduce the hazard degree of a gas explosion and conduct the venting energy to the safe area. To investigate the flame quantitative propagation law of explosion venting with a duct, the effects of hydrogen fraction and explosion venting duct length on jet flame propagation characteristics of premixed H₂-air mixtures were analyzed through experiment and simulation. The experiment results under initial conditions of room temperature and 1 atm show that when hydrogen fraction was high enough, part of the unburned hydrogen was mixed with air again to reach an ignitable concentration, resulting in the secondary combustion was easier produced and the duration of the secondary flame increased. With the increase of venting duct length, the flame front distance and propagation velocity increased. Meanwhile, the spatial distribution of pressure field and temperature field, and the propagation process and mechanism of the flame venting with a duct were analyzed using FLUENT software. The variation of the pressure wave and the pressure reflection oscillation law in the explosion venting duct was captured. Therefore, in the industrial explosion venting design with a duct, the hazard caused by the coupling of venting pressure and venting flame under different fractions should be considered comprehensively.     

Combustion synthesis of AlN doped with carbon and oxygen

Carbon-and-oxygen-doped AlN specimens were prepared by combustion synthesis using Al, graphite, and AlN. Graphite addition changed the product color from white to blue. By XRD, the lattice constant increased slightly with increasing carbon content. Blue AlN powder was synthesized with a molar ratio of the diluent AlN of 0.2-0.5 with a fixed graphite content of 0.05. At an AlN molar ratio exceeding 0.6, carbon was not successfully incorporated due to the lower reaction temperature. Calcination at 800°C in air removed residual graphite without changing the crystal structure or product color. Oxygen, nitrogen, and carbon analyses revealed that blue AlN powders contained 0.45-0.54 mass% carbon and 1.4-1.6 mass% oxygen, while the undoped AlN contained 0.021 mass% carbon and 0.94 mass% oxygen. The origin of the white-to-blue color change was investigated via reflection measurements. Blue AlN exhibits an absorption peak at 634 nm (1.96 eV). From first-principles electronic structure calculations, the C-doped AlN and carbon-and-oxygen-doped AlN with a 1:1 ratio could be classified as p-type, whereas the O-doped AlN and 1:3 carbon-and-oxygen-doped AlN were n-type. One reason for the absorption peak at 634 nm may be a transition from the conduction band to an upper unoccupied state. These results suggest the possible control of optical and electronic properties of AlN via carbon-and-oxygen doping.     

Alteration of the Route to Menaquinone towards Isochorismate-Derived Metabolites

Chorismate and isochorismate constitute branch-point intermediates in the biosynthesis of many aromatic metabolites in microorganisms and plants. To obtain unnatural compounds, we modified the route to menaquinone in Escherichia coli. We propose a model for the binding of isochorismate to the active site of MenD ((1R,2S, 5S,6S)-2-succinyl-5-enolpyruvyl-6-hydroxycyclohex-3-ene-1-carboxylate (SEPHCHC) synthase) that explains the outcome of the native reaction with α-ketoglutarate. We have rationally designed variants of MenD for the conversion of several isochorismate analogues. The double-variant Asn117Arg–Leu478Thr preferentially converts (5S,6S)-5,6-dihydroxycyclohexa-1,3-diene-1-carboxylate (2,3-trans-CHD), the hydrolysis product of isochorismate, with a >70-fold higher ratio than that for the wild type. The single-variant Arg107Ile uses (5S,6S)-6-amino-5-hydroxycyclohexa-1,3-diene-1-carboxylate (2,3-trans-CHA) as substrate with >6-fold conversion compared to wild-type MenD. The novel compounds have been made accessible in vivo (up to 5.3 g L⁻¹). Unexpectedly, as the identified residues such as Arg107 are highly conserved (>94 %), some of the designed variations can be found in wild-type SEPHCHC synthases from other bacteria (Arg107Lys, 0.3 %). This raises the question for the possible natural occurrence of as yet unexplored branches of the shikimate pathway.     

Synthesis of Benzophenones and in vitro Evaluation of Their Anticancer Potential in Breast and Prostate Cancer Cells

Breast and prostate cancers are frequently treated with chemotherapy. Several novel chemicals are being reported for this purpose, particularly synthetic and natural benzophenones. This work reports the synthesis of substituted 2-hydroxybenzophenones through 1,4-conjugate addition/intramolecular cycloaddition/dehydration of nitromethane on key intermediate chromones. Structures were extensively studied by means of 2D NMR spectroscopy and single-crystal XRD. Their cytotoxicity was evaluated in vitro in two breast cancer cell lines (MDA-MB-231 and T47-D) and one prostate cancer cell line (PC3). The most potent compound exhibited good cytotoxic effects against the three cancer cell lines (IC₅₀ values ranging from 12.09 to 26.49 μm ) and induced cell-cycle retardation only on prostate cancer cells, which suggested that it might exert cell-type-specific effects.     

Combining molybdenum carbide with ceria overlayers to boost Mo/CeO2 catalyzed ammonia synthesis

The design of an efficient non-noble metal catalyst is of burgeoning interest for ammonia synthesis. Herein, we report a Mo₂C/CeO₂ catalyst that is superior in ammonia synthesis activity. In this catalyst, molybdenum carbide coexisted with the ceria overlayers which is from the ceria support as the strong metal–support interaction. There is a high proportion of low-valent Mo species, as well as high concentration of Ce³⁺ and surface oxygen species. The presence of Mo₂C and CeO₂ overlayers not only leads to enhancement of hydrogen and nitrogen adsorption, but also facilitates the desorption and exchange of adsorbed species with the gaseous reagents. Compared with the Mo/CeO₂ catalyst prepared without carbonization, the Mo₂C/CeO₂ catalyst is more than sevenfold higher in ammonia synthesis rate. This work not only presents an explicit example of designing Mo-based catalyst that is highly efficient for ammonia synthesis by tuning the adsorption and desorption properties of the reactant gases, but opens a perspective for other elements in ammonia synthesis.     

La0.6Sr0.4Co0.2Fe0.8O3-δ nanofiber cathode for intermediate-temperature solid oxide fuel cells by water-based sol-gel electrospinning: Synthesis and electrochemical behaviour

Water-based sol-gel electrospinning is employed to manufacture perovskite oxide La_0.6Sr_0.4Co_0.2Fe_0.8O_3-δ (LSCF) nanofiber cathodes for intermediate-temperature solid oxide fuel cells. LSCF fibrous scaffolds are synthesized through electrospinning of a sol-gel solution employing water as the only solvent. Morphological characterizations demonstrate that the LSCF fibers have highly crystalline structure with uniform elemental distribution. After heat treatment, the average fiber diameter is 250 nm and the porosity of the nanofiber tissue is 37.5 %. The heat treated LSCF nanofibers are applied directly onto a Ce_0.9Gd_0.1O_1.95 (CGO) electrolyte disk to form a symmetrical cell. Electrochemical characterization is carried out through electrochemical impedance spectroscopy (EIS) in the temperature range 550?°C–950?°C, and reproducibility of the electrochemical performance for a series of cells is demonstrated. At 650?°C, the average measured polarization resistance R_p is 1.0 Ω cm². Measured performance decay is 1 % during the first 33?h of operation at 750?°C, followed by an additional 0.7 % over the subsequent 70?h.