PP－g－AA的制备和表征

用熔融接枝方法制备了聚丙烯－ｇ－丙烯酸（ＰＰ－ｇ－ＡＡ）。用光电子能谱，广角Ｘ射线衍射，红外光谱和化学滴定方法对接枝物进行了定性和定量表征。讨论了单体和引发剂浓度对接枝率的影响，确定了用红外光谱法测定接枝物含量的经验公式     

固相缩聚共聚酯的熔融行为和结晶速率研究

通过固相缩聚合成了两种不同结构的高分子量共聚酯，研究了样品的熔融行为和结晶速率。研究发现，共聚酯的熔融峰随着固相聚合温度和时间的变化而与纯ＰＥＴ有明显的差别，共聚酯泊结晶速率与慢于纯ＰＥＴ的结晶速率。     

醇镁还原法一步制取对氯苯胺的研究

醇镁还原法一步制取对氯苯胺是一种新的方法 ,研究发现最佳反应温度为 80℃～ 85℃ ,反应时间为4h ,对氯硝基苯与镁粉的用量 (物质的量比 )为 1∶3,产率为 80 %。     

纺丝组件漏浆原因分析

通过对纺丝组件工艺对比调试,分析了纺丝组件消耗材料对纺丝组件漏浆的影响,指出了纺丝组件漏浆的主要影响因素。     

MB8镁合金薄板的搅拌摩擦焊

针对我国航空航天工业常用的MB8镁合金。采用搅拌摩擦焊工艺进行焊接，对其焊缝的成形特点、组织特征和力学性能进行分析。结果表明，采用搅拌摩擦焊焊接镁合金效果良好。     

Synthesis and characterisation of copolyesters from poly(ethylene terephthalate) and poly(hexamethylene terephthalate)

Copolyesters containing poly(ethylene terephthalate) and poly(hexamethylene terephthalate) (PHT) were prepared by a melt condensation reaction. The copolymers were characterised by infrared spectroscopy and intrinsic viscosity measurements. The density of the copolyesters decreased with increasing percentage of PHT segments in the backbone. Glass transition temperatures (T_g). melting points (T_m) and crystallisation temperatures (T_c) were determined by differential scanning calorimetry. An increase in the percentage of PHT resulted in decrease in T_g, T_m and T_c. The as-prepared copolyesters were crystalline in nature and no exotherm indicative of cold crystallisation was observed. The relative thermal stability of the polymers was evaluated by dynamic thermogravimetry in a nitrogen atmosphere. An increase in percentage of PHT resulted in a decrease in initial decomposition temperature. The rate of crystallisation of the copolymers was studied by small angle light scattering. An increase in percentage of PHT resulted in an increase in the rate of crystallisation.     

熔融-固相缩聚法中固相聚合对聚乳酸合成的影响

以L 乳酸单体为原料 ,熔融 -固相缩聚法合成了聚乳酸 ,重点研究了固相聚合的工艺条件。结果表明 ,绝对压力 60Pa ,氯化亚锡为催化剂 ,分段控温 ,可使聚乳酸的粘均分子量提高到固相聚合反应前的 5 3倍。通过对固相聚合产物的结晶度和熔点的分析 ,探讨了固相聚合的机理。     

Immobilization and activation of vanadium(III) and titanium(III) single‐site catalysts for ethylene polymerization using MgCl2‐based supports

Significant increases in the activity of vanadium(III) amidinate catalysts for ethylene polymerization have been obtained by immobilization on a MgCl₂‐based support prepared by reaction of AlEt₃ with a MgCl₂/ethanol adduct. Catalyst immobilization and activation on this type of support prevents the rapid decay in activity observed under homogeneous polymerization conditions with unsupported catalysts. Stable polymerization activity is also observed with analogous titanium(III) complexes. Polyethylene with narrow molecular weight distribution and spherical particle morphology is obtained without reactor fouling. Copyright © 2005 Society of Chemical Industry     

高镁边缘磷矿制取阻燃剂氢氧化镁的工艺

为解决大量的高镁低磷边缘磷矿废渣堆存对环境的影响,开发了以其为原料制取阻燃剂氢氧化镁工艺.该工艺主要包括酸解磷矿和镁沉淀过程,重点讨论了沉淀氢氧化镁过程中时间、温度、氨镁摩尔比n(NH3/MgO)等多种因素的影响,得到的最佳工艺条件是:反应温度65℃,反应时间80min,n(NH3/MgO)为5∶ 1,镁的沉淀效率为80%.     

服装低密度聚乙烯热熔胶化学粉碎的研究

服装粘合衬布的生产需要低密度聚乙烯热熔胶的微细粉末,介绍了对该热熔胶的化学粉碎技术所进行的实验研究,表明采用适当的助剂种类和用量以及适宜的工艺过程,通过化学粉碎可以得到合格的粉末产品。