Microstructure and hardness of binary Cr-Ta alloys

The dependances of the microstructure and hardness of the binary Cr-Ta alloys [ Cr-9.0, -9.2, -9.4, -9.6,-9.8, and -13.0 Ta] (mole fraction, %) were investigated. When Ta content of the alloy is less than 9.4%, there are primary dandrite grains of a Cr solid-solution phase existing in the matrix of Cr-Cr2Ta eutectic colonies in the alloy. Moreover, the regular polygon grains of the primary Cr2Ta Laves-phase are surrounded by the Cr-Cr2Ta eutectic colony in the hyper-euteetic Cr-9.4 96 Ta alloys. The scanning electron microphotograph shows that one of the Cr2Ta phase plates of an eutectic colony always connects with the primary Cr2Ta Laves-phase grain in a hyper-eutectic alloy. The eutectic colony size of Cr-Ta alloys decreases with increasing Ta. In addition, the macrohardness of Cr-Ta alloys is influanced by the chemical composition at room temperature. The binary eutectic Cr-Ta alloy presents the lowest hardness on a macrohardness scale.     

TiAl基合金在快速加热循环热处理过程中的结构失稳

观察了快速加热循环热处理过程中发生的4种结构失稳现象：形成二次层片组织、原始层片球化、晶界处非连续粗化、相界形核。通过比较连续加热与等温加热条件下的相转变开始线，探讨了连续加热与等温加热条件下结构失稳机制的异同。提出了快速加热循环热处理过程中避免结构失稳的途径：确保合金成分均匀，使各区域相变温度一致；使最高温度下的保温时间尽可能短。     

Effects of h-BN content on properties of Ni-Cr/h-BN composite

Ni-Cr/h-BN self-lubricating composities were prepared by powder metallurgy (P/M) method. The effects of hexagonal boron nitride (h-BN) content on the mechanical and tribological properties of the Ni-Cr/h-BN composites were investigated. The corresponding frictional models were established to analyze the formation of the lubricant h-BN films on the surfaces of the Ni-Cr/h-BN composites. The results show that, when the content of h-BN increases from 5% to 15% (mass fraction), the bending strength of the Ni-Cr/h-BN composite decreases from 96.670 MPa to 17.319 MPa, and the hardness (HB) decreases from 33 to 14. The friction coefficient of the Ni-Cr/h-BN composite decreases firstly from 0.385 to 0.216, and then increases to 0.284, while the wear rate decreases firstly from 4.14×10⁻⁹ kg/(N·m) to 1.35×10⁻⁹ kg/(N·m), then increases to 2.36×10⁻⁹ kg/(N·m). The best comprehensive mechanical and tribological properties can be obtained between 10% and 12% h-BN addition.     

聚丙烯酰胺凝胶法制备BeO纳米粉体

聚丙烯酰胺凝胶法是一种利用三维网络结构高分子将溶液中的离子包裹形成物理阻隔,制备纳米粉体的方法。本文采该方法成功地制备了BeO纳米粉体。热重分析、X射线衍射仪和扫描电子显微镜的研究表明：煅烧温度为680℃,较传统煅烧温度下降140℃。采用聚丙烯酰胺凝胶法700℃煅烧2h制备的粉体,平均晶粒尺寸为16．5nm;升高煅烧温度,粉体粒度显著增大。900℃煅烧2h制备的粉体,平均粒径为20～30nm。     

退火工艺对Au-20Sn钎料组织的影响

采用叠轧-合金化法制备Au-20Sn钎料,研究合金化退火工艺对Au-20Sn钎料显微组织的影响。结果表明:Au/Sn界面在叠轧过程中形成AuSn4,AuSn2和AuSn三个金属间化合物(IMC)层。在200℃退火时,IMC层的厚度随退火时间的延长而逐渐增大。当退火时间延长至48 h时,IMC层发生转变,Au-20Sn钎料最终形成由ζ相(含Sn 10%～18.5%,原子分数)和δ(AuSn)相组成的均质合金。在250℃退火时,Au/Sn界面扩散速度增大,退火6 h后Au-20Sn钎料组织完全转变成ζ相+δ(AuSn)相。在270℃退火时,IMC层熔化,反应界面转变成为固-液界面,Au-20Sn钎料组织转变为脆性的(ζ’+δ)共晶组织。综合Au-20Sn钎料的性能和生产要求,得到优先退火工艺为250℃退火6 h。     

Hg和Ga元素对Mg阳极材料组织和电化学腐蚀性能的影响(英文)

采用动电位极化、恒电流和交流阻抗测试方法研究了Hg和Ga元素对Mg2%Hg,Mg2%Ga和Mg2%Hg2%Ga合金电化学腐蚀性能的影响,并用扫描电镜、X射线衍射和能谱分析了上述合金的显微组织和腐蚀表面形貌。结果表明:Mg2%Ga合金是固溶体,Mg-2%Hg和Mg-2%Hg2%Ga合金的晶界有白色第二相。Mg-2%Ga合金的平均电位为1.48V,腐蚀电流密度为0.15mA/cm2,电化学活性差,耐腐蚀性能好。Mg-2%Hg-2%Ga合金的平均电位1.848V,腐蚀电流密度为2.136mA/cm2,电化学活性好,耐腐蚀性能差。MgHgGa合金的活化机制是Hg和Ga原子的溶解沉积。     

聚丙烯酰胺凝胶法制备纳米BeO粉体前驱体的热分解过程及结晶机理

采用聚丙烯酰胺凝胶法制备纳米BeO粉体,通过TG-DSC、XRD和SEM等测试手段研究凝胶前驱体的热分解过程和所得粉体的性能,并借助负离子配位多面体生长基元理论分析热分解过程中纳米BeO的结晶机理。结果表明:随着温度的升高,凝胶前驱体内的有机凝胶逐渐分解,同时凝胶前驱体内的硫酸铍盐脱除结晶水;当温度达到600℃左右时,有机凝胶完全分解,得到纳米级的无水硫酸铍;继续升高温度,纳米级的无水硫酸铍分解得到纳米BeO;热分解过程中,纳米硫酸铍通过生长基元Be(SO4)6断键形成纳米BeO,成核过程为受迫状态下的非均匀成核。     

TiAl合金设计与成形方法

介绍了TiAl基金属间化合物的研究背景与应用前景,论述了该类合金的成分设计与组织设计,指出合金元素的加入呈现出少量多元的趋势;分析了该类合金的几种常用成形方法,即精密铸造,粉末冶金和超塑性成形,并指出了各自的优点和缺点。     

无铅易切削镁黄铜的组织与性能

采用熔铸、挤压、拉拔的方法生产出了以镁代铅的环保型易切削黄铜材.对易切削黄铜的微观组织进行了观察,并对其力学、化学和切削性能分别进行了研究.结果表明:镁黄铜晶内和晶间有白色和黑色的球状第二相粒子分布,该粒子为金属间化合物,具有脆而不硬的特点,对提高合金切削性能有利.半硬态镁黄铜的抗拉强度为550 MPa,屈服强度为280 MPa,延伸率为16.30%,断面收缩率为32.4%.从切削过程中切削力的大小以及切屑的形貌、大小可以判断,镁黄铜的切削性能接近于C3604铅黄铜.镁黄铜在酸中和盐中的耐蚀性均较好,比较而言耐盐性要好一些.