Mechanical properties,corrosion resistance,and rubber pad forming of cold differential speed-rolled pure titanium for bipolar plates of proton-exchange membrane fuel cells

Due to problems such as pores on surface-treated coatings, the corrosion resistance of pure titanium bipolar plates for proton-exchange membrane fuel cells can be further improved by increasing the corrosion resistance of pure titanium by using differential speed-rolling (DSR); however, these materials have not yet reached the standard requirements of bipolar plates (corrosion current density i_corr＜10³ nA·cm^?2). In this work, the corrosion resistance of pure titanium was improved by optimizing the DSR process while the strength was maintained. The best corrosion resistance of the DSR pure titanium was achieved when the roller speed ratio was 2, while i_corr was 429 nA·cm^?2 in a solution of 0.5 M H₂SO₄ and 2 mg/L HF at room temperature. The formability of the DSR pure titanium for bipolar plates was verified. The optimal holding pressure range was 6.8–7.0 kN.     

Unipolar plasma electrolytic oxidation: Waveform optimisation for corrosion resistance of commercially pure titanium

This study deals with the anodisation of titanium grade 2 in 0.5-M sulphuric acid using a pulsed signal in a unipolar regime. The electrical parameters investigated are voltage, frequency and duty cycle. The use of duty cycles with a high percentage of anodic polarisation (90%), combined with high frequencies (1000 Hz) and the higher voltage tested (220 V), favoured the establishment of a plasma regime involving strong dielectric discharges, allowing the growth of thicker oxides but with rough architecture. The corrosion resistance of the formed film has been characterised by potentiodynamic tests in 0.5-M NaBr for localised corrosion resistance and by immersion tests in 10% v/v sulphuric acid solution for a uniform corrosion assessment. Current–time curves, visual observations and electron microscope analysis (scanning electron microscopy, energy-dispersive X-ray spectroscopy) were the tools selected to provide a correlation between technological parameters and oxide growth mechanism. For localised and uniform corrosion, anodisation at 220 V with a high level of anodic polarisation (90%) and frequency (1000 Hz) was verified to be particularly advantageous.     

Surface treatment of titanium dioxide nanopowder using rotary electrode dielectric barrier discharge reactor

Titanium dioxide (TiO2) nanopowder (P-25;Degussa AG) was treated using dielectric barrier discharge (DBD) in a rotary electrode DBD (RE-DBD) reactor.Its electrical and optical characteristics were investigated during RE-DBD generation.The treated TiO2 nanopowder properties and structures were analyzed using x-ray diffraction (XRD) and Fourier-transform infrared spectroscopy (FTIR).After RE-DBD treatment,XRD measurements indicated that the anatase peak theta positions shifted from 25.3° to 25.1°,which can be attributed to the substitution of new functional groups in the TiO2 lattice.The FTIR results show that hydroxyl groups (OH) at 3400 cm-1 increased considerably.The mechanism used to modify the TiO2 nanopowder surface by air DBD treatment was confirmed from optical emission spectrum measurements.Reactive species,such as OH radical,ozone and atomic oxygen can play key roles in hydroxyl formation on the TiO2 nanopowder surface.     

优化作业方式提高始极片质量

针对某厂铜电解种板工序存在的始极片质量波动较大的问题,从种板系统体积控制和添加剂匹配的角度出发,分析各种因素对始极片质量的影响,做出了相应的改进措施,使种板系统运行更加稳定,始极片质量得到进一步提升。     

轧制与退火对T9S钛合金板材组织与性能的影响

研究了轧制变形量及退火温度对T9S钛合金板材显微组织和室温力学性能的影响。结果表明:增加成品轧制变形量,板材组织破碎更充分,退火后形成等轴α相、拉长α相和晶间β相组织形貌,变形流线比较明显,板材室温强度和硬度升高,伸长率降低,弹性模量增加。随着退火温度升高,板材室温强度和硬度逐渐降低,伸长率逐渐提高,横向弹性模量逐渐减小,纵向弹性模量先增加后减小。经(750~790) ℃×45 min空冷退火处理后的板材可以获得较好的强度和塑性的匹配。     

高强WSTi544221合金组织与性能研究

研究了轧制变形量对WSTi544221合金棒材显微组织和力学性能的影响,并对Φ10 mm规格的棒材进行不同制度的固溶+时效处理,对比了不同热处理状态下棒材的组织和力学性能。结果表明,随着轧制变形量的增大,WSTi544221合金棒材的晶粒细化程度增大,强度逐渐提高,但塑性变化不大。经870℃×1 h/WC+520℃×6 h/AC固溶+时效处理后,强度与塑性可以获得良好匹配,当抗拉强度达到1 610 MPa、屈服强度达到1 531 MPa时,延伸率和断面收缩率可分别保持在12%和43%。     

钛合金表面多磁极耦合旋转磁场光整加工特性

面向激光增材制造钛合金表面的光整加工需求，设计出一种多磁极耦合旋转磁场光整加工装置来研究光整加工特性。基于ANSYS Maxwell仿真软件分析了光整加工装置的磁场强度分布。搭建了实验光整平台，分析了主轴转速、C轴转速和加工间隙对表面质量的影响。结果表明，在主轴转速500 r/min、C轴转速160 r/min和加工间隙0.7 mm的加工条件下，表面粗糙度Ra由5.991 μm下降至0793 μm。扫描电子显微镜(SEM)观测表明，光整后的钛合金表面沉积层消失，表面质量得到显著改善。     

工艺参数对超声辅助脉冲电沉积镍-氮化钛复合镀层的影响

在45钢表面以超声波辅助脉冲电沉积制备Ni-TiN复合镀层。研究了平均阴极电流密度、脉冲占空比、超声功率和TiN粒子(平均直径20~30 nm)添加量对复合镀层的TiN粒子含量和显微硬度的影响。得到较优的工艺参数为:NiSO4ꞏ6H2O 300 g/L,NiCl2ꞏ6H2O 30 g/L,H3BO330 g/L,十二烷基硫酸钠0.3 g/L,TiN 25 g/L,pH 4.1~4.3,温度40°C,平均阴极电流密度4 A/dm2,脉冲占空比40%,脉冲频率1000 Hz,超声功率300 W,机械搅拌速率200 r/min,时间60 min。该条件下所得Ni-TiN复合镀层的TiN质量分数为8.35%,显微硬度为819 HV,表面平整、致密,晶粒尺寸均匀。