Synthesis of a Fe3O4-rGO-ZnO-catalyzed photo-Fenton system with enhanced photocatalytic performance

In this work, we designed a magnetically-separable Fe₃O₄-rGO-ZnO ternary catalyst, ZnO anchored on the surface of reduced graphene oxide (rGO)-wrapped Fe₃O₄ magnetic nanoparticles, where rGO, as an effective interlayer, can enhance the synergistic effect between ZnO and Fe₃O₄. The effects of three operational parameters, namely irradiation time, hydrogen peroxide dosage, and the catalyst dosage, on the photo-Fenton degradation of methylene blue and methyl orange were investigated. The results showed that the Fe₃O₄-rGO-ZnO had great potential for the destruction of organic compounds from wastewater using the Fenton chemical oxidation method at neutral pH. Repeatability of the photocatalytic activity after 5 cycles showed only a tiny drop in the catalytic efficiency.     

气相色谱法测定焦油中微量苯稠杂环化合物

利用蒸馏分离—气相色谱法技术,建立了同时测定煤焦油中苊、氧芴和芴的分析方法。通过对色谱条件的优化,以甲苯为溶剂,正十二烷为内标物,将煤焦油馏分采用DB-5毛细管柱,对煤焦油中苊、氧芴和芴定量分析。分析结果表明:3种主要成分线性关系良好,相关系数均大于0.9995,加标回收率为95.4%~102.4%,相对标准偏差为2.89%~7.14%。该方法分离效果好,检测结果准确、可靠。     

Synthesis of thermoresponsive copolymer/silica-coated magnetite nanoparticle composite and its application for heavy metal ion recovery

To enhance chemical stability and suppress of aggregation of magnetite nanoparticles (MNPs), which are used as a support for thermoresponsive copolymer immobilization, silica coating of the MNPs is applied via the electrooxidation method. Although the resulting silica coated-MNPs also formed aggregates, the size distribution of the aggregate shifted to smaller size range. Because of that, the surface area available for copolymer immobilization increased approximately 6.7 times at maximum as compared with that of the uncoated MNPs. It contributed to the increase of the amount of the immobilized copolymer on the silica-coated MNPs, which is approximately four times larger than that on the uncoated MNPs. Fe₃O₄ dissolution test confirmed enhancement of chemical stability of MNPs. The thermoresponsive copolymer immobilized on the silica-coated MNPs shows the ability to recycle Cu(II) ion from Cu(II) containing solution by changing temperature with significantly shorter time than those in other thermoresponsive adsorbents in gel form.     

Microstructure and electromagnetic properties of LiFe5O8 ferrite ceramics prepared from wet- and dry-milled powders

The effect of dry and wet ball milling of LiFe₅O₈ ferrite powder on the microstructure and electromagnetic properties of ferrite ceramics was studied using XRD analysis, scanning electron microscopy, dilatometry, thermogravimetry, calorimetry, and measurement of specific magnetization and electrical resistance. The sintering temperature was 1050 °C; the sintering time was 2 h. It was found that ferrite fabricated from dry-milled powder exhibits an ordered α-LiFe₅O₈ phase with bulk density of 91%. Its saturation magnetization and Curie temperature are 55 emu/g and 628°С, respectively. Specific electrical resistance is 4?10⁶ Ω cm. Wet milling in isopropyl alcohol causes formation of a disordered β-LiFe₅O₈ phase. Ceramics produced by this method shows higher bulk density (97%) and low porosity, and an order of magnitude lower resistivity. Its saturation magnetization and Curie temperature are 51 emu/g and 607°С, respectively.     

Deacetylated Cellulose Acetate/Polyurethane Composite Nanofiber Membranes with Highly Efficient Oil/Water Separation and Excellent Mechanical Properties

Nowadays, oil pollution has become more serious, which causes great threats both to the ecological environment and human life. In this study, a novel type of multifunctional deacetylated cellulose acetate/polyurethane (d-M_CA:M_TPU) composite nanofiber membranes for oil/water separation are successfully fabricated by electrospinning, which show super-amphiphilicity in air, super-hydrophilicity in oil, and oleophobicity in water. All the d-M_CA:M_TPU composite nanofiber membranes with different mass ratios can be used as water-removing, oil-removing, and emulsion separation substance only by gravity driving force. The highest separation flux for water and oil reaches up to 37 000 and 74 000 L m⁻² h⁻¹, respectively, and all the separation efficiencies are more than 99%. They have outstanding comprehensive mechanics performance, which can be controlled by simply adjusting the mass ratios. They show excellent antifouling and self-cleaning ability, endowing powerful cyclic stability and reusability. Those results show that d-M_CA:M_TPU composite nanofiber membranes have great application prospects in oil/water separation.     

Influence of the stoichiometry,microstructure, and metallization method on the dielectric properties of 0.94 Na0.5Bi0.5TiO3-0.06 BaTiO3

The morphotropic composition of the lead-free solid solution between Na_0.5Bi_0.5TiO₃ and BaTiO₃ (0.94 Na_0.5Bi_0.5TiO₃-0.06 BaTiO₃ or NBT-6BT) is of particular interest for the next generation of high-temperature capacitors but remains plagued by the diversity of dielectric properties reported in the literature. In order to explain the apparent inconsistencies among the reported dielectric properties of NBT-6BT, we examine the influence of stoichiometry, phase separation, and metallization method. We show that the nominal stoichiometry has a crucial effect, since increasing the nominal Na/Bi ratio increases conductivity and dielectric losses (tan δ). It also increases the real part of the permittivity (ε’) and the frequency dispersion of both ε’ and tan δ, thereby altering the shape of the evolution with temperature of the dielectric properties. Moreover it increases the depolarization temperature (T_d) and decreases the temperature of maximum permittivity (T_m). Phase separation also occurs during the synthesis of NBT-6BT as Na evaporation leads to the formation of secondary Ba-containing phases. We report that these phases can have a positive impact on the dielectric properties: a moderate volume fraction (2.5 to 3.0%) and average grain surface (0.9 to 3.0 µm²) of these secondary Ba-containing phases increase the relative permittivity, decrease the dielectric losses, and increase the insulation resistance. We also show that the metallization method impacts the dielectric properties and therefore may contribute to the differences between various reports. The dielectric properties of NBT-6BT samples are measured during successive heating/cooling cycles and reveal that the permittivity value is lower during the first heating when silver paste, even cured, is used. These three components contribute to explaining the diversity of the reported dielectric properties of NBT-6BT.     

Synthesis,characterization, and visible-light photocatalytic activity of transition metals doped ZTO nanoparticles

Transition metals doping has been proved to be a feasible way for tuning the physical properties on the surface and bulk of nanomaterials and also for the good performance in decontamination of emerging pollutants. In this context, doped samples of zinc tin oxide or zinc stannate nanoparticles (ZTO NPs) by several transition metals were synthesized in order to enhance the optical absorbance with the aims of reducing the band gap and therefore ameliorated their photocatalytic activity. They were characterized by the X-ray diffraction (XRD), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), diffuse reflectance spectroscopy, Raman spectroscopy and photoluminescence. The XRD patterns and the microscopic observations showed the formation of spherical nanoparticles with an average size of about 30 nm and highly pure ZTO phase with an inverse spinel structure. The Raman spectra were dominated by bands relatives to the F2g (2) and A1g symmetries modes of inverse spinel structure. The band gap Eg is estimated to be 3.75 eV for the undoped sample, and 3.67, 3.64, 3.78 and 3.21 eV, for 2% Fe, 2% Mg, 2% Gd, and 2% Mn doped ZTO samples, respectively.Furthermore, the undoped ZTO NPs have the intrinsic problem of recombination of photogenerated charge carriers. We have shown that the reduction of the band gap and oxygen vacancies resulting from the doping effect could be a useful tool for trapping and avoid the recombination of electrons coming from photosensitized rhodamine B (RhB) under visible light irradiation. Owing to the structural advantages and low band gap, 2% Mn doped ZTO NPs, with the kinetic rate constants k of 0.024 min⁻¹, show enhanced performance for the elimination of RhB in aqueous solution compared to undoped and other doped ZTO NPs.     

Effect of atmosphere control on magnetic properties of CaO-Al2O3-SiO2-Fe3O4 glass ceramics

The influences of atmosphere during processes of melting and heat treatment, heat treatment temperature, Fe₃O₄ content and basicity on the magnetic properties of magnetite-based glass ceramics were investigated. For sample containing 20 % Fe₃O₄ melted in different atmospheres, the highest saturation magnetisation was realized in 20vol% air + 80 vol% Ar, due to the fact that ratio of Fe³⁺ to Fe²⁺ in melt obtained in this atmosphere was close to 2. However, it was found that the coercivity of glass ceramics was not affected by the melting atmosphere. A high sintering temperature led to the decrease of saturation magnetisation and the increase of coercivity. As increasing Fe₃O₄ content, the main crystal phase transformed from CaSiO₃ to CaFe_0.6Al_1.3Si_1.08O₆ and finally to magnetite phase, accompanied by the increase of saturation magnetisation and coercivity. In addition, the increase of basicity caused the decrease of saturation magnetisation and the increase of coercivity.     

某微细粒嵌布磁铁矿选矿工艺研究

针对某微细粒磁铁矿进行了全磁选流程和磁选-反浮选流程对比试验研究。结果表明,在最终磨矿细度相当的情况下,2种工艺流程都获得了产率48%左右、TFe品位66%左右、回收率80%左右的铁精矿指标,而采用磁选-反浮选流程的第三段磨矿量比全磁选流程减少了2/3。磁选-反浮选流程具有显著的节能降耗优势。     

Constructing magnetically recoverable CdS/CaFe2O4 P–N heterojunctions for enhanced photoelectrochemical properties towards H2 evolution reaction

A novel CdS/CaFe₂O₄ (CS/CFO) heterogeneous p-n junction was created by thermal deposition of CaFe₂O₄ nanoparticles on CdS rods. The CS/CFO hetero-structured photocatalysts exhibited increasingly efficient visible light harvesting compared to the bare CdS. The CS/CFO composites also presented higher photocurrent and slower decay of photoluminescence, suggesting a better separation of the photo-generated electrons and holes. The photocatalytic H₂ evolution quantity on the optimized CS/CFO composite from water in the presence of ethanol was up to 2200 μmol after 3-h visible light illumination, which is more than twice that of the pristine CdS. The chemical interaction between CdS and CaFe₂O₄ was confirmed by the shifts in the XPS peaks, which made it possible for the charge carriers to transfer across the p-n junction interface. This research highlights the importance of forming an interfacial p-n heterojunction between two semiconductors for efficient charge separation and improved photocatalytic performance.