Modification of the wood-plastic composite for enhancement of formaldehyde clearance and the 3D printing application

As the formaldehyde is one of the main indoor pollutants, the purpose of this study is to effectively remove indoor formaldehyde pollution by using environmentally friendly 3D printing ornaments. The wood 3D printing filaments cellulose/polylactic acid composite (Cellu/P) was selected as the starting material, and 3-aminopropyltriethoxysilane (APTES) was used for chemical modification to obtain a series of cellulose composite materials with amino groups. The modified composite materials (APTES@Cellu/P) were characterized by Fourier transform infrared, X-ray diffraction, scanning electron microscope, energy dispersive spectroscopy, thermogravimetric analysis, and mechanical tests, and a formaldehyde removal experiment was performed. The feasibility of 3D printing was evaluated, and the process of 3D printing-functionalized customized ornaments was proposed, and then a school emblem was used for modeling, printing, and surface modification. Compared with the commercially traditional activated carbon, 3D printing-customized ornaments of APTES@Cellu/P material has a better formaldehyde removal effect, and can even avoid the secondary pollution that is common to the activated carbon.     

木片筛余物高得率半化学法清洁制浆技术研究

以太阳纸业备料车间木片筛选碎料（筛余物）为原料，对其烧碱法半化学制浆的实验室工艺和生产试验进行了研究。结果表明，筛余物采用半化学法制浆可获得较高得率和环压强度的纸浆，且用碱量对纸浆性能有显著影响。相对8%NaOH （相对于绝干原料）化学预处理，采用14%NaOH化学预处理结合两段浆浓22%的高浓磨浆工艺，所制半化学浆抄造浆张的裂断长和环压指数分别达2.89 km和9.76 N·m/g，是前者的1.9倍和1.2倍，而且优于现用国内OCC废纸浆抄造浆张；生产试验得到的浆张性能指标与实验室相吻合，其中紧度和环压强度分别达到GB/T 13023—2008瓦楞芯（原）纸AA级和A级优等品要求。     

Behavior of Decayed Spruce (Picea abies) during Kraft Pulping

This study indicated that by applying an improved classification system to decayed large-diameter Norway spruce (Picea abies) wood, its use as raw material for kraft pulping without loss of pulp quality could be essentially increased. This is based on the fact that although the cooking yield of decayed spruce material which has been sorted according to these new recommendations is somewhat lower and Kappa number higher than those of sound wood material, the greatest part of the decayed stem (the outer part of the stem) contains long-fiber wood material which produces pulp of good quality. Therefore, large-diameter spruce logs can also be separately used, for example, in the manufacture of reinforcement pulp.     

木粉疏水改性对HDPE基木塑复合材料性能的影响

采用一种操作简便且易于工业推广的方法对木粉进行疏水改性，具体过程为：将3种可热聚合的单体，即甲基丙烯酸甲酯（MMA）、甲基丙烯酸丁酯（BMA）和苯乙烯（St）均匀喷洒在木粉上，经过预热处理后，与配方中其他组分，如高密度聚乙烯（HDPE）和马来酸酐接枝聚乙烯（MAPE）等通过高速混合机混合均匀，采用双螺杆挤出机造粒后，注射制备木塑复合材料（WPC）样条，测试其力学性能。另外，考察了疏水改性对WPC接触角、维卡软化温度、洛氏硬度、吸水性能、热性能的影响规律。结果表明：疏水改性后WPC的接触角增大，木粉和HDPE的界面相容性改善，力学性能得到明显提高。其中，当MMA、BMA和St的添加量为3%时，WPC的力学性能最好，与疏水改性前相比，弯曲强度分别提高了17.3%、26.3%和27.5%，弯曲模量分别提高了24.4%、24.4%和26.0%，冲击强度分别提高了54.7%、57.7%和60.5%。 此外，疏水改性后WPC的维卡软化温度、洛氏硬度、耐水性和耐热性也得到改善。     

Moulded pulp products manufacturing with thermoforming

For an effective optimization of pulp thermoforming and of the moulded pulp products manufactured by this process, a full understanding of the process physics combined with full knowledge of the pressing equipment is necessary. For this reason, in this Addendum, we clarify how the process parameters “Holding time,” “Vacuum time,” “Cycle time,” and “Temperature” were interpreted and subsequently defined for the analysis of the process and product‐related outputs of the thermoforming experiments.     

非常规蛋白基木材胶黏剂研究现状及发展前景

介绍了动物和植物型非常规蛋白资源的种类及其制备蛋白基木材胶黏剂的研究现状和存在的问题,展望了非常规蛋白胶黏剂的发展前景。     

Phosphorylated cellulose/electrospun chitosan nanofibers media for removal of heavy metals from aqueous solutions

Contamination of water resources by toxic heavy metals has significant impacts on environmental and human health. Their removal from aqueous media is essential to ensure water sustainability and to provide safe freshwater availability to population. Electrospun chitosan (CS) nonwoven mats are efficient at removing heavy metals from aqueous media. However, they suffer from low permeability and low-mechanical strength. They are also unable to remove contaminants in a nonselective way. A bilayer sorbent media made of a porous phosphorylated cellulose substrate covered by electrospun CS nanofibers was developed to overcome those weaknesses. The hydrophilic composite shows good water permeability and mechanical strength with appropriate thermal and chemical characteristics. Adsorption tests with Cd(II) indicate that pseudo-second order and Langmuir models best fitted experimental data, with a maximum adsorption capacity of 591 mg/g at 25°C. Adsorption with multielement samples containing Cr(VI), Cu(II), Cd(II), and Pb(II) also reveal their capability to remove them in a selective way. This mechanically resistant, hydrophilic, and permeable adsorbent media was able to capture both cationic and anionic metallic contaminants.     

木质纤维与水泥共同改良软土的力学性能与微观机制分析

通过压实试验、无侧限抗压强度试验和劈裂试验,分析不同木质纤维含量、水泥含量和固化时间对软土力学性能的影响规律,探讨木质纤维、水泥改良软土的微观机制。结果表明,木质纤维的加入对水泥改良软土的击实特性有显著的影响;木质纤维与水泥可有效改善土体的抗压和劈裂抗拉强度,随着木质纤维含量的增加,改良土的抗压和劈裂抗拉强度呈现出明显的“驼峰”现象,并在木质纤维含量为0.25%时最大;木质纤维与水化产物、软土颗粒形成互锁效应,增大了改良土的摩擦力,同时木质纤维还承担一定的拉伸强度,使改良土的劈裂强度增加。