Inconel 690传热管GTAW对接焊接头组织及力学性能研究

对Inconel 690传热管材进行钨极气体保护焊(GTAW)对接焊,采用拉伸试验机、压扁试验机和光学显微镜测试和分析传热管焊接接头,同时利用ANSYS软件开展焊接接头在设计工况失压时的一次应力强度校核。研究结果表明:焊缝中心为树枝胞状晶,熔合线附近为粗大柱状晶。室温时接头的平均抗拉强度为619 MPa,平均屈服强度为292 MPa,350℃时接头平均抗拉强度为475 MPa,平均屈服强度为206 MPa,拉伸接头断裂从熔合区开始贯穿整个焊缝组织,呈塑性断裂。压扁试验和反向压扁试验结果表明管接头完好。通过ANSYS分析可知,设计工况下传热管接头350℃许用应力强度150 MPa限值可满足其一次应力强度要求,且裕量较大。     

Preparation and antifouling performance of thin inorganic ultrafiltration membrane via assisted sol-gel method with different composition of dual additives

A novel TiO₂ thin film was prepared on the ceramic hollow fiber by the sol-gel method using poly(vinylpyrrolidone) (PVP) and polyvinyl alcohol (PVA) as additives. SEM images verified the formation of TiO₂ layer with various thickness using different composition of titania sols. The effect of the PVP and PVA contents on the TiO₂ sol properties, the separation and the antifouling performance of the ultrafiltration membranes were investigated thoroughly. When the contents of PVP and PVA were 1.0 wt% and 0.8 wt%, respectively, the resultant membrane showed a thickness of 0.55 μm with a pure water flux of 255 L m^?2 h^?1. In addition, the adherent foulant bovine serum albumin was applied to evaluate the antifouling performance. During the three fouling-recovery cycles, the flux recovery ratio and the flux decay ratio maintained about 99% and 30%. The BSA flux and rejection were still 169 L m^?2 h^?1 and 96.9% after the cycles, indicating a superior antifouling property.     

Evaluation of anticorrosion and contact resistance behavior of poly(orthophenylenediamine)- coated 316L SS bipolar plate for proton exchange membrane fuel cell

The present work was focused on the corrosion properties and contact resistance behavior of poly(orthophenlyenediamine) (PoPD) coating on 316L SS bipolar plates. To reduce the corrosion rate and increase the interfacial conductivity of 316L SS bipolar plates, PoPD coating was deposited using an electropolymerization technique by the various monomer concentration of orthophenlyenediamine (oPD) on its surface. The presence of 1, 2, 4, 5- tetra substituted benzene nuclei of phenazine units in the polymer coating was confirmed by infrared spectroscopy. X-ray photoelectron spectroscopy analysis has confirmed the (%) of chemical composition in PoPD coating. The results of scanning electron microscopy analysis revealed that the uniform and compact coating with complete cover on 316L SS. The corrosion properties were investigated in 0.5 M H₂SO₄ and 2 ppm HF solution at 80 °C. The polarization test results showed that the PoPD coating reduced the corrosion current density both in the PEMFC anode and cathode environments. The charge transfer resistance values were in the order of 316L SS ? 0.02 M PoPD ? 0.06 M PoPD ? 0.04 M PoPD. A very low interfacial contact resistance and good adhesion strength was observed for 0.04 M PoPD coating. The higher contact angle of 0.04 M PoPD coating explained the hydrophobic property and more benefit of water management in the PEMFC environment. The results of the analysis of total metal ion releases clearly explained that the low level of metal ions released for 0.04 M PoPD coating. The overall studies revealed the PoPD coating with optimized 0.04 M oPD concentration showed best performance and provided more anodic protection to 316L SS bipolar plates.     

High H2 selectivity with low coke formation for methanol steam reforming over Cu/Y1.5Ce0.84Ru0.04O4 catalyst in a microchannel plate reactor

The synthesized novel metal oxides Y_xCe_yRu_zO₄ (x = 1.5, y = 0.84, z = 0.04) which was produced by the sol-gel method was used as a support for Cu active metal on the surface of a microchannel plate reactor in the methanol steam reforming (MSR) process. The prepared catalysts were characterized by X-ray powder diffraction (XRD), BET surface area analysis (S_BET), energy-dispersive X-ray analysis (EDX), field-emission scanning electron microscopy (FE-SEM), X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM), temperature-programmed desorption (NH₃-TPD), and temperature-programmed reduction (H₂-TPR). High methanol conversion (99.5%) and H₂ selectivity (98.7%) and low CO selectivity (1.4%) were achieved for Cu/Y_xCe_yRu_zO₄ coated microchannel reactor at 250 °C. FE-SEM images and TGA curve of the spent catalyst displayed no coke formation on the surface of the catalyst after 32 h on stream at 300 °C. The low reduction temperature of Cu, high BET surface area, and high pore volume of the catalyst are considered imperative factors that cause a better dispersion of copper on the Y_1.5Ce_0.84Ru_0.04O₄ support.     

Effect of metal oxide nanofluids on the performance of passive solar still single slope for two different absorbent plates

This study aims to improve the performances of a solar still single slope using metal oxide nanofluid (Al₂O₃–water, Cu₂O–water, and TiO₂–water). The numerical study was carried out for the climatic conditions of Agadir, Morocco, with different concentrations of nanofluids inside a basin equipped with an absorber plate with two different absorptivities. The numerical study is based on thermal balance equations applied on different solar system components and solved using the Runge Kutta method. The numerical model is validated by comparing our results with the literature available data. A comparison study of the effect of these nanofluids on solar still productivity is done. The results show that the productivity of the solar still using nanoparticles Cu₂O, TiO₂, and Al₂O₃ are 7.38, 7.1, and 7.064 kg m⁻² day⁻¹, respectively. It is obtained that the maximum efficiency of the solar still is found to be 55.27% by using cuprous oxide nanoparticles. Furthermore, an enhancement in solar still productivity of 6.36%, 19.54%, and 33.25% is obtained by dispersing 1%, 3%, and 5% volume fraction of Cu₂O nanoparticles in pure water, respectively compared to the conventional solar. Moreover, the impact of the absorptivity of the absorber plate on the solar still effectiveness is investigated. Two types of coatings are considered to change the absorber plate absorptivity. The results indicate that the efficiencies of the solar system are 58.81% and 51.77% using an absorber plate with 0.95 and 0.85 of absorptivity, respectively.     

基于FLAC3D的破碎围岩巷道支护效果分析

为了解破碎围岩分别采用锚杆支护、锚喷支护以及锚喷+锚索耦合三种支护方式下的支护效果,进而为破碎围岩巷道选择合理的支护方式提供参考。通过借助FLAC^3D软件建立数值模型,分析不同支护条件下的破碎围岩巷道位移量、应力分布以及塑性区的时空演化特征。结果表明,采用锚喷+锚索耦合支护时,可以较好的控制巷道围岩的位移量、减小应力集中效应、缩小塑性区的影响范围。     

Entropy generation minimization on electromagnetohydrodynamic radiative Casson nanofluid flow over a melting Riga plate

Minimizing entropy generation is a technique that helps improve the effectiveness of real processes by studying the associated irreversibility of system performance of nanofluid. This study examines the entropy generation analysis of electromagnetohydrodynamic radiative Casson flow induced by a stretching Riga plate in a non-Darcian porous medium under the influence of internal energy change, Arrhenius activation energy, chemical reaction, and melting heat transfer. The thermophysical features of the fluid are assumed constant in most of the literature. However, this current research bridges this gap by considering viscosity, conductivity, and diffusivity as temperature-dependent variables. Also, the exponential decaying Grinberg term is used as a resistive force in this investigation due to the electromagnetic properties of the Riga plate in the momentum conservation equation. Some suitable dimensionless variables are introduced to remodel the transport equations into unitless ones and then solved numerically by employing Galerkin Weighted Residual Method. Analyses reveal that the Casson parameter declines the fluid velocity, while the existence of the melting parameter has the opposite effect. Also, this article includes some future recommendations.     

微通道板表面羟基化工艺研究北大核心

研究了3种微通道板基底羟基化的方法,测量了羟基化处理后微通道板基底表面水接触角及通道端面的形貌变化,分析了各种方法中微通道板基底的亲水性和腐蚀情况。实验结果表明:氨水双氧水溶液对基体表面的亲水性能提升不大,NaOH溶液对基体有腐蚀作用,经食人鱼溶液处理的基体表面亲水性明显提高且无腐蚀作用。研究了微通道板在食人鱼溶液中的浸泡时间和浸泡温度对表面亲水性的影响。结果表明:随着浸泡温度的增加,微通道板表面水接触角先减小后增大,当温度为80℃时达到极小值,浸泡时间对微通道板表面的亲水性影响不大。最终确定了微通道板表面羟基化工艺:浸泡温度为80℃,静置时间为20~60 min。     

高应力软岩巷道锚注一体化联合支护技术应用

介绍了国家专利注锚剂、中空注浆锚索等产品,以国家能源麦朵山煤矿11采区2煤辅助运输巷为研究对象,采用数值模拟、理论分析、现场测试及井下试验相结合的综合研究方法,对11采区2煤辅助运输巷采用锚注一体联合支护技术,来实现对岩体裂隙注浆,使浆料与岩体结为一体,在围岩与支护体共同作用过程中,实现强岩增荷的作用,维护巷道的稳定性,实现工作面的安全生产。