AISI 304 stainless steel plates were welded with activated flux tungsten inert gas(A-TIG) method by utilizing self-developed activated flux. It is indicated from the experimental results that for 8 mm-thick AISI 304 stainless steel plate, weld joint of full penetration and one-side welding with good weld appearance can be obtained in a single pass without groove preparation by utilizing A-TIG welding. Moreover, activated flux powders do not cause significant effect on the microstructure of TIG weld and the mechanical properties of A-TIG weld joints are also superior to those of C-TIG(conventional TIG) welding. 相似文献
3.
4.
5.
6.
A-TIG焊是一种采用活性剂来增加焊缝熔深的高效TIG焊接技术。与常规TIG焊相比,A-TIG焊具有焊接效率高、焊缝质量好及成本低等优点。本文先对各氧化物单一组元活性剂对焊缝熔深的影响进行研究,然后采用正交试验设计的方法,以获得符合熔深要求的配方,最后进一步优化活性剂配方,以满足焊缝其他性能要求,如表面成形、显微组织、铁素体含量及硬度。试验结果表明,进行A-TIG焊试验可以一次性焊透8 mm厚的304不锈钢板,同时获得外观良好的焊缝,并能满足其他性能要求。 相似文献
7.
以硝酸银为原料,用N,N二甲基甲酰胺溶剂作还原剂,聚酰胺酸(poly amic acid,PAA)为稳定剂,制备金属银纳米粒子。利用红外光谱分析银纳米粒子的形成对PAA结构的影响;用X射线衍射确定银/PAA复合粉末中银粒子的结晶状态;用紫外可见吸收光谱实时检测不同PAA质量浓度的溶液中纳米粒子的等离子体共振吸收情况;用透射电镜观察银纳米粒子的形状和大小。结果表明:银纳米粒子的生成对PAA的分子结构几乎没有影响;银纳米粒子具有很好的结晶度;紫外可见吸收光谱出现明显的不对称双峰;银纳米粒子长大是奥斯特瓦尔成熟过程,制备的银纳米粒子具有较好的形貌,呈软团聚多晶态。 相似文献
8.
A-TIG焊接是一种采用活性剂来增加焊缝熔深的高效TIG焊接技术。与常规TIG焊相比,A-TIG焊具有焊接效率高、焊缝质量良好及成本低廉等优点。采用A-TIG焊接技术对核电常用的304N2高强度不锈钢管道进行全位置焊接,对焊接接头进行超声波探伤检测、显微组织分析及力学性能测试。试验结果表明,对于不开坡口6 mm厚的304N2高强度不锈钢管采用A-TIG焊接,可实现一次焊透、单面焊双面成形,同时获得外观良好的焊缝,接头显微组织和力学性能均优于常规TIG焊接,且其力学性能均达到标准要求。 相似文献
9.
A-TIG焊是一种采用活性剂来增加焊缝熔深的高效TIG焊技术。与常规TIG焊相比,A-TIG焊具有焊接效率高、焊缝质量优及成本低等优点。根据GB/T 4334—2008采用φ(草酸)10%溶液浸蚀方法,对比奥氏体不锈钢TIG焊和奥氏体不锈钢A-TIG焊接头的耐蚀性。结果表明,A-TIG焊接头比常规TIG焊接头具有更优异的抗草酸腐蚀,同时基于焊缝金属的化学成分分析,A-TIG焊方法在焊接过程中能够显著地降低不锈钢焊缝金属中Cr, Ni, Ti等的损失,从而有效提高A-TIG焊接头的耐蚀性。 相似文献