A comparative study on structural,morphological and photocatalytic properties of anodically grown ZnO nanowires under varying parameters

Journal of Materials Science: Materials in Electronics - In this study, zinc oxide (ZnO) nanowires (NWs) were successfully produced on Zn plates through electrochemical anodization in potassium...     

The effect of liposome on dyeing mohair/wool blends

The aim of this study was to examine the use of liposome in the dyeing of wool and mohair fibres with acid dyestuffs. Soybean lecithin and cholesterol were used to form the liposome membrane utilised in the dyebath. Liposome production was performed according to the thin lipid layer method (Bangham Method) using a rotary evaporator. Two different forms of liposome were used for dyeing wool and mohair fibres. In its first form, liposome was utilised as an auxiliary agent, where it was added to a conventional dyebath at the beginning of the process. In its second form, dyes were encapsulated with liposome and then used in dyeing. The effects of these two different forms of liposome were compared with conventional dyeing. Dyeing was carried out at depths of shade of 0.5%, 1.0% and 2.0% using three different concentrations of liposome (0.33%, 0.66% and 1.33%). An analysis of K/S values, fastness to washing, and the alkali solubility of fibres was conducted. The fibre samples dyed in the presence of liposome exhibited very good fastness to light (grade 8). The wash fastness test results of the liposomal‐dyed samples were significantly better (grade 4‐5) than for those samples which were conventionally dyed. In the presence of liposome, the tensile strength of fibres was 20 gf, whereas it was 11 gf without liposomes.     

Study and evaluation of abrasive water jet turning process performance on AA5083

In this study, the effect of processing parameters on surface roughness and macro surface characteristics was analyzed during the machining of Ø30 mm and 300 mm aluminum alloy AA5083 abrasive water jets. As the processing parameters (up to 10 mm min⁻¹, 15 mm min⁻¹, 20 mm min⁻¹ and 25 mm min⁻¹), abrasive flow rate (50 g min⁻¹, 150 g min⁻¹, 250 g min⁻¹ and 350 g min⁻¹), the lathe chuck rotational speed (25 min⁻¹, 50 min⁻¹, 75 min⁻¹ and 100 min⁻¹) and the nozzle approach distance (2 mm, 5 mm, 8 mm and 11 mm) were used in experiments. In experimental studies, the pump pressure (360 MPa) was used as a constant, in the form of an abrasive Garnet (100 mesh), and the nozzle diameter as 0.76 mm. According to the findings, the best results in terms of surface roughness were obtained as a result of turning speed and abrasive flow rate. When the macro surface characteristics were examined, it was found that the lathe chuck rotational speed increased, the rate of nozzle progression was low, the rate of abrasive flow was high and the nozzle approach distance was lower and the smoother surfaces were obtained.     

Decay and termite resistance of plywood treated with various fire retardants

This study evaluated the ability of white and brown rot fungi and termites to decompose fire retardant-treated (FRT) or untreated-plywood by measuring mass loss. Plywood was manufactured using Ekaba (Tetraberlinia bifoliolata Harms.) veneers which were previously treated with either boric acid, borax, mono-ammonium phosphate (MAP), or di-ammonium phosphate (DAP). Plywood specimens were then subjected to fungal decay resistance tests performed according to Japanese Industrial Standard (JIS) A-9201 method using a brown-rot fungus, Fomitopsis palustris (Berkeley et Curtis) Murrill and a white-rot fungus, Trametes versicolor (L. ex Fr.) Quel. The specimens were also assayed against the subterranean termite, Coptotermes formosanus Shiraki to determine termite resistance. Boron and phosphorus chemicals used in the study increased the resistance of plywood panels against both fungal and termite attack. Plywood panels treated with boric acid and borax resulted in less mass losses when compared to MAP and DAP-treated specimens in decay and termite resistance tests.     

Investigation of the Equivalence of National Dew-Point Temperature Realizations in the ?50?°C to +?20?°C Range

In the field of humidity quantities, the first CIPM key comparison, CCT-K6 is at its end. The corresponding European regional key comparison, EUROMET.T-K6, was completed in early 2008, about 4?years after the starting initial measurements in the project. In total, 24 NMIs from different countries took part in the comparison. This number includes 22 EURAMET countries, and Russia and South Africa. The comparison covered the dew-point temperature range from ?50?°C to +20?°C. It was carried out in three parallel loops, each with two chilled mirror hygrometers as transfer standards in each loop. The comparison scheme was designed to ensure high quality results with evenly spread workload for the participants. It is shown that the standard uncertainty due to the long-term instability was smaller than 0.008?°C in all loops. The standard uncertainties due to links between the loops were found to be smaller than 0.025?°C at ?50?°C and 0.010?°C elsewhere. Conclusions on the equivalence of the dew-point temperature standards are drawn on the basis of calculated bilateral degrees of equivalence and deviations from the EURAMET comparison reference values (ERV). Taking into account 16 different primary dew-point realizations and 8 secondary realizations, the results demonstrate the equivalence of a large number of laboratories at an uncertainty level that is better than achieved in other multilateral comparisons so far in the humidity field.     

The role of particle size of particulate nano-zinc oxide wood preservatives on termite mortality and leach resistance

Historically most residential wood preservatives were aqueous soluble metal formulations, but recently metals ground to submicron size and dispersed in water to give particulate formulations have gained importance. In this study, the specific role nano-zinc oxide (ZnO) particle size and leach resistance plays in termite mortality resulting from exposure to particulate ZnO-treated wood was investigated. Southern yellow pine (SYP) sapwood impregnated with three concentrations of two particle sizes (30 and 70 nm) of ZnO were compared to wood treated with soluble zinc sulphate (ZnSO₄) preservative for leach resistance and termite resistance. Less than four percent leached from the particulate nano-ZnO-treated specimens, while 13 to 25% of the zinc sulphate leached from the soluble treated wood. Nano-ZnO was essentially non-leachable from wood treated with 5% formulation for the 30-nm particle size. In a no-choice laboratory test, eastern subterranean termites (Reticulitermes flavipes) consumed less than 10% of the leached nano-ZnO-treated wood with 93 to 100% mortality in all treatment concentrations. In contrast, termites consumed 10 to 12% of the leached ZnSO₄-treated wood, but with lower mortality: 29% in the 1% treatment group and less than 10% (5 and 8%, respectively) in the group of wood blocks treated with 2.5 and 5.0% ZnSO₄. We conclude that termites were repelled from consuming wood treated with nano-ZnO, but when consumed it was more toxic to eastern subterranean termites than wood treated with the soluble metal oxide formulation. There were no differences in leaching or termite mortality between the two particle sizes of nano-ZnO.     

Thermal degradation characteristic of Tetra Pak panel boards under inert atmosphere

hermal degradation characteristics of Tetra Pak panel boards (TPPB) can be useful to improve usage of such panels as an alternative to wood-based products such as plywood, fiberboard, and particleboard. In the study, samples from the TPBBs manufactured from waste Tetra Pak packages (WTPP) were heated in a nitrogen atmosphere at different heating rates (10, 15 and 20 °C/min) using a thermal analysis system. The Coats-Redfern kinetic model was applied to calculate kinetic parameters. The degradation rate equations were then established. In addition, the kinetic compensation effect (KCE) was used to correlate the pre-exponential factor (k _o ) with activation energy (E _a ) and the existence of the KCE was accepted. TG-FT/IR analyses were applied to the TPPB degradation and then the FT-IR stack plot was used to analyze gas products (CO₂, CH₄, HCOOH, and CH₃OH). Infrared vibrational frequencies and the micro, crystal structure of the TPPBs were investigated by Fourier transform infrared spectroscopy (FT-IR), Scanning electron microscope (SEM) and X-Ray diffraction analysis (XRD), respectively.     

Termite Resistance of MDF Panels Treated with Various Boron Compounds

In this study, the effects of various boron compounds on the termite resistance of MDF panels were evaluated. Either borax (BX), boric acid (BA), zinc borate (ZB), or sodium perborate tetrahydrate (SPT) were added to urea-formaldehyde (UF) resin at target contents of 1%, 1.5%, 2% and 2.5% based on dry fiber weight. The panels were then manufactured using 12% urea-formaldehyde resin and 1% NH₄Cl. MDF samples from the panels were tested against the subterranean termites, Coptotermes formosanus Shiraki. Laboratory termite resistance tests showed that all samples containing boron compounds had greater resistance against termite attack compared to untreated MDF samples. At the second and third weeks of exposure, nearly 100% termite mortalities were recorded in all boron compound treated samples. The highest termite mortalities were determined in the samples with either BA or BX. Also, it was found that SPT showed notable performance on the termite mortality. As chemical loadings increased, termite mortalities increased, and at the same time the weight losses of the samples decreased.     

Antioxidant and anticholinesterase evaluation of selected Turkish Salvia species

Since Salvia species (Lamiaceae) have been recorded to be used against memory loss in European folk medicine, we herein examined in vitro anticholinesterase and antioxidant activities of 56 extracts prepared with petroleum ether, chloroform, ethyl acetate and methanol obtained from 14 Salvia species (Salvia albimaculata Hedge and Hub, Salvia aucheri Bentham var. canescens Boiss and Heldr, Salvia candidissima Vahl. ssp. occidentalis, Salvia ceratophylla L., Salvia cryptantha Montbret and Bentham, Salvia cyanescens Boiss and Bal., Salvia frigida Boiss, Salvia forskahlei L., Salvia halophilaHedge, Salvia migrostegia Boiss and Bal., Salvia multicaulis Vahl., Salvia sclarea L., Salvia syriaca L., Salvia verticillata L. ssp. amasiaca) growing in Turkey. The antioxidant activities were assessed by both chemical and enzymatic methods against 1,1-diphenyl-2-picrylhydrazyl (DPPH) radical-scavenging and xanthine/xanthine oxidase (XO) system generated superoxide anion radical inhibition. Anticholinesterase effect of the extracts was tested against both acetylcholinesterase (AChE) and butyrylcholinesterase (BChE) at concentrations of 0.2 and 1 mg/ml using a microplate-reader assay based on the Ellman method. Most of the extracts did not show any activity against AChE at 0.2 mg/ml, while the chloroform extracts had noticeable inhibition against BChE between 47.7% and 74.7%. The most active extracts at 1 mg/ml for AChE inhibition were observed to be petroleum ether extract of Salvia albimaculata (89.4%) and chloroform extract of Salvia cyanescens (80.2%), whereas ethyl acetate extracts of Salvia frigida and Salvia migrostegia, chloroform extracts of Salvia candidissima ssp. occidentalis and Salvia ceratophylla, as well as petroleum ether extract of Salvia cyanescens were found to inhibit potently BChE (92.2%, 89.6%, 91.1%, 91.3%, and 91.8%, respectively). Particularly, the ethyl acetate and methanol extracts were observed to be highly active against both DPPH and XO. Our data indicates that nonpolar extracts of Salvia species for anticholinesterase activity and the polar extracts for antioxidant activity are worth further phytochemical evaluation for identifying their active components.