New horizon in mechanochemistry—high-temperature,high-pressure mechanical synthesis in a planetary ball mill—with magnesium hydride synthesis as an example

A new route of materials synthesis, namely, high-temperature, high-pressure reactive planetary ball milling (HTPRM), is presented. HTPRM allows for the mechanosynthesis of materials at fully controlled temperatures of up to 450 °C and pressures of up to 100 bar of hydrogen. As an example of this application, a successful synthesis of magnesium hydride is presented. The synthesis was performed at controlled temperatures (room temperature (RT), 100, 150, 200, 250, 300, and 325 °C) while milling in a planetary ball mill under hydrogen pressure ($>$50 bar). Very mild milling conditions (250 rpm) were applied for a total milling time of 2 h, and a milling vial with a relatively small diameter (φ = 53 mm, V = ～0.06 dm³) was used. The effect of different temperatures on the synthesis kinetics and outcome were examined. The particle morphology, phase composition, reaction yield, and particle size were measured and analysed by scanning electron microscopy, X-ray diffraction, differential scanning calorimetry (DSC) techniques. The obtained results showed that increasing the temperature of the process significantly improved the reaction rate, which suggested the great potential of this technique for the mechanochemical synthesis of materials.     

Complex study of protective Cr3C2–NiAl coatings deposited by vacuum electro-spark alloying,pulsed cathodic arc evaporation,magnetron sputtering,and hybrid technology

Coatings were obtained by vacuum electro-spark alloying (VESA), pulsed cathodic arc evaporation (PCAE), magnetron sputtering (MS) techniques and VESA-PCAE-MS hybrid technology using Cr₃C₂–NiAl electrodes. The structure of the coatings was analyzed using scanning and transmission electron microscopy, X-ray diffraction and energy-dispersive spectroscopy. Mechanical properties were determined by nanoindentation, while tribological properties were assessed using pin-on-disk tribometer. Corrosion resistance was estimated by voltammetry in 1 N H₂SO₄ and 3.5%NaCl solutions. Oxidation resistance tests were performed at 800°С in air. The VESA coating had the highest thickness, low friction coefficient and high wear resistance. PCAE coating demonstrated the highest hardness (24 GPa) and elastic recovery (59%), oxidation resistance and superior corrosion resistance both in 1 N H₂SO₄ (i_corr = 70 μА/cm²) and 3.5%NaCl (i_corr = 0.74 μА/cm²) solutions. The MS coating had average mechanical properties and low corrosion current density (71 μА/cm²) in 1 N H₂SO₄. Deposition of coatings using VESA-PCAE-MS hybrid technology led to an increase in corrosion and oxidation resistance at least by 1.5 times in comparison with the VESA coating.     

机械合金化FeS/Cu复合材料的摩擦磨损性能

以FeS和CuSn8Ni1粉末为原料，利用机械合金化技术和粉末冶金技术制备了FeS/Cu复合材料，探讨了不同载荷情况下所制备的FeS/Cu复合材料的摩擦学性能及润滑膜与转移膜特征。结果表明：机械合金化提高了FeS与铜合金基体界面结合性能，进而提高了材料减摩耐磨性能；当载荷较小时，摩擦副表面接触不稳定，复合转移膜不连续，摩擦因数波动大；载荷较大时，复合转移膜易破损，材料的减摩耐磨性能变差；当载荷为150 N时，载荷适宜，材料表面软化，复合转移膜更加完整，摩擦因数较小。     

Alloying behavior and novel properties of CoCrFeNiMn high-entropy alloy fabricated by mechanical alloying and spark plasma sintering

An equiatomic CoCrFeNiMn high-entropy alloy was synthesized by mechanical alloying (MA) and spark plasma sintering (SPS). During MA, a solid solution with refined microstructure of 10 nm which consists of a FCC phase and a BCC phase was formed. After SPS consolidation, only one FCC phase can be detected in the HEA bulks. The as-sintered bulks exhibit high compressive strength of 1987 MPa. An interesting magnetic transition associated with the structure coarsening and phase transformation was observed during SPS process.     

多元合金化大断面球墨铸铁组织和性能的分析

为了提升大断面球墨铸铁综合力学性能，通过复合添加微量合金元素铜、锑、锡、钼对大断面球墨铸铁进行微合金化处理，借助金相显微镜(OM)、扫描电子显微镜(SEM)及力学性能测试等手段，研究了Cu Sb Sn Mo复合微合金化大断面球墨铸铁微观组织和力学性能。结果表明，试验球墨铸铁具有良好的综合力学性能。大断面球墨铸铁中添加铜、锑、锡、钼后优化了材料的组织结构，基体组织为珠光体＋少量牛眼状铁素体；试样石墨组织细小、圆整，分布均匀。同时，合金元素的复合加入使得其抗拉强度达到800 MPa以上，硬度约为280HB，伸长率达到5%以上。拉伸断口分析表明，微合金化大断面球墨铸铁断裂模式以解理断裂为主，伴有少量的塑性变形。     

氮化硅/石墨激光合金化涂层的组织结构与性能研究

为获得金属表面特别是高副接触金属表面含自润滑特性且具有高硬度耐磨特性的功能材料 ,研究了 45 # 钢表面激光合金化氮化硅 /石墨复合涂层的工艺方法、组织特征、界面形态及其形成机制 ,利用光学显微镜、扫描电镜和X射线能谱对所形成合金化层的元素分布和含量进行了分析 ,并对试样硬度进行了测定。结果表明 ,合金化层中元素Fe ,Co ,Si,C分布均匀 ;C含量达到了 15 6 9%,大部分以石墨的形式存在 ,具有一定的自润滑性能 ;但在形成合金化层的温度条件下 ,氮化硅分解严重 ;合金化层硬度提高的主要原因是Si Fe ,Co Fe固溶体的强化作用及高碳马氏体的生成和高硬度碳化物的存在。     

动态矩阵控制在浆料浓度控制系统中的应用

针对PTA生产中浆料配制过程这一有纯滞后、大时间常数的非线性系统，进行系统的动态机理分析，与工作点附近的线性化，在此基础上设计DMC-PID串级加前馈控制方案。目前该系统在扬子石化化工厂PTA装置上已成功投运。     

机械合金化Fe-Ni粉末的相结构

使用XRD和Moessbauer等方法，研究了在Ar气氛下机械合金化Fe—Ni粉末相结构的变化．结果表明，在机械合金化Fe64-Ni36粉末过程中，fcc相的数量随着球磨时间的增加先增加然后减少，与加乙醇球磨Fe64-Ni36的情形相同．当Ni的含量(原子分数)大于50％时，有fcc相、顺磁相和FeNi3形成，当Ni的含量低于50％时，bcc相的数量随着Ni含量减少而增加．Moessbauer谱的结果表明，因球磨时间或Fe、Ni比例的不同，Fe—Ni球磨粉末固溶体具有不同结构的原子配比。     

PTA装置压力离心机冲洗新技术

分析了仪征化纤PTA装置压力离心机运转效果不佳的原因,提出解决方案,改造实施后取得了很好的效果。     

PTA压力离心机转子的改造

介绍了PTA压力离心机的主要性能参数、工作原理、分离效果的影响因素。为了增大沉渣在过渡区及脱水区滞留的时问，同时为达到在过渡区及脱水区对沉渣加入纯净水进行再冲洗的目的，对螺旋送料转子、挡液环、进料管进行了改造。改造后，沉渣在脱水区的停留时间由0．44a增至0．72s，2．5～3t／h的冲洗水对脱水区的沉渣进行冲洗效果较好。产品中的杂质质量分数较改造前减少15％，产品优等品率提高到99％。