To save bandwidth and storage space as well as speed up data transmission, people usually perform lossy compression on images. Although the JPEG standard is a simple and effective compression method, it usually introduces various visually unpleasing artifacts, especially the notorious blocking artifacts. In recent years, deep convolutional neural networks (CNNs) have seen remarkable development in compression artifacts reduction. Despite the excellent performance, most deep CNNs suffer from heavy computation due to very deep and wide architectures. In this paper, we propose an enhanced wide-activated residual network (EWARN) for efficient and accurate image deblocking. Specifically, we propose an enhanced wide-activated residual block (EWARB) as basic construction module. Our EWARB gives rise to larger activation width, better use of interdependencies among channels, and more informative and discriminative non-linearity activation features without more parameters than residual block (RB) and wide-activated residual block (WARB). Furthermore, we introduce an overlapping patches extraction and combination (OPEC) strategy into our network in a full convolution way, leading to large receptive field, enforced compatibility among adjacent blocks, and efficient deblocking. Extensive experiments demonstrate that our EWARN outperforms several state-of-the-art methods quantitatively and qualitatively with relatively small model size and less running time, achieving a good trade-off between performance and complexity.     

Enhanced electrochemical performance of LiNi0.8Co0.1Mn0.1O2 via titanium and boron co-doping

Titanium and boron are simultaneously introduced into LiNi_0.8Co_0.1Mn_0.1O₂ to improve the structural stability and electrochemical performance of the material. X-ray diffraction studies reveal that Ti⁴⁺ ion replaces Li⁺ ion and reduces the cation mixing; B³⁺ ion enters the tetrahedron of the transition metal layers and enlarges the distance of the [LiO₆] layers. The co-doped sample has spherical secondary particles with elongated and enlarged primary particles, in which Ti and B elements distribute uniformly. Electrochemical studies reveal the co-doped sample has improved rate performance (183.1 mAh·g^-1 at 1 C and 155.5 mAh·g^-1 at 10 C) and cycle stability (capacity retention of 94.7% after 100 cycles at 1 C). EIS and CV disclose that Ti and B co-doping reduces charge transfer impedance and suppresses phase change of LiNi_0.8Co_0.1Mn_0.1O_2.     

Development of an SFMM/CGO composite electrode with stable electrochemical performance at different oxygen partial pressures

This paper carefully evaluates the electrocatalytic activity of Sr₂FeMo_0.5Mn_0.5O₆ (SFMM) double perovskite as a candidate to substitute the state-of-the-art Ni/YSZ fuel electrode. The electrochemical performance of a 40% SFMM/CGO composite electrode was studied in CO/CO₂ and H₂ with different oxygen partial pressure. Two different cell configurations are prepared at a relatively low temperature of 800 °C to increase the electrochemically active surface area. The cell was supported with a 150 μm 10Sc1CeSZ electrolyte in the first configuration. The cell in the second configuration was made by applying a 400 nm thin 8YSZ layer on 150 μm CGO electrolyte to improve the electrolyte ionic conductivity. Improving catalytic activity with increasing oxygen partial pressure is a key characteristic of the developed electrode. The polarization resistance of about 0.34 and 0.56 Ω cm² at 750 °C in 3%H₂O + H₂ and 60% CO/CO₂ makes this electrode a promising candidate for SOCs application.     

Hydraulic reactivity and cement formation of baghdadite

In this study, the hydraulic reactivity and cement formation of baghdadite (Ca₃ZrSi₂O₉) was investigated. The material was synthesized by sintering a mixture of CaCO₃, SiO₂, and ZrO₂ and then mechanically activated using a planetary mill. This leads to a decrease in particle and crystallite size and a partial amorphization of baghdadite as shown by X-ray powder diffraction (XRD) and laser diffraction measurements. Baghdadite cements were formed by the addition of water at a powder to liquid ratio of 2.0 g/ml. Maximum compressive strengths were found to be ~2 MPa after 3-day setting for a 24-h ground material. Inductively coupled plasma mass spectrometry (ICP-MS) measurements showed an incongruent dissolution profile of set cements with a preferred dissolution of calcium and only marginal release of zirconium ions. Cement formation occurs under alkaline conditions, whereas the unground raw powder leads to a pH of 11.9 during setting, while prolonged grinding increased pH values to approximately 12.3.     

微波辅助孵育法富集麦胚多肽的工艺优化

目的 麦胚孵育过程中蛋白酶将蛋白质水解成肽和氨基酸，多肽具有明确的生理活性和营养调节作用。本研究以麦胚为试验原料，采用微波辅助预处理的方法，研究孵育的温度、时间、pH及料液比4种因素对孵育后的蛋白酶活力及多肽含量的影响。 方法 通过单因素和响应曲面试验进行工艺条件优化。 结果 与未进行微波辅助预处理的样品相比，微波辅助处理（600 W, 10 s）能显著提高孵育后样品中的蛋白酶酶活力（约9.4倍）和肽含量（约3.1倍）。经过微波辅助处理后，孵育温度为51.5℃、pH为4.0、时间为6.33 h、料液比为1:7时，蛋白酶活力达最高为3826.24 U/g；孵育温度为45.0 ℃、pH为4.8、时间为8 h、料液比为1:7时，肽含量达最高为262.63 mg/g。 结论 微波辅助处理能有效的激活麦胚孵育液中的内源性蛋白酶活性，促进蛋白水解反应，显著提高孵育后的肽含量。该研究结果为麦胚多肽的制备新工艺开发提供了研究基础。     

脱硫胶粉在乳化改性沥青中的应用

考察了不同规格胶粉及不同脱硫程度的脱硫胶粉对橡胶改性乳化沥青性能的影响,结果表明,采用100目胶粉即可制备出橡胶改性乳化沥青,但乳化沥青的性能较差;采用活化度为50%左右的100目脱硫胶粉制备乳化沥青时,脱硫胶粉的用量相比于胶粉可大幅提高;在通过外掺100目50%左右活化度的脱硫胶粉(质量分数15%,以沥青计,下同)和质量分数2%的苯乙烯-丁二烯-苯乙烯嵌段共聚物改性的乳化沥青中添加质量分数1%的丁苯胶乳,所制备橡胶改性乳化沥青无筛上剩余物,5 d储存稳定性为2.9%,蒸发残留物的25℃针入度、软化点和5℃延度分别为55 (0.1 mm)、64.5℃和22.5 cm,能够满足乳化改性沥青的技术指标要求。     

胡萝卜丁中维生素C在热风辅助射频干燥过程中降解的动力学模型

目的研究热风辅助射频(hot air-assisted radio frequency,HA-RF)干燥过程中维生素C随温度变化的降解动力学模型。方法在6.5 cm极板间距和60℃热风系统条件下进行HA-RF干燥,重点研究胡萝卜丁中维生素C在干燥过程中的降解动力学,包括脱氢抗坏血酸(dehydroascorbic acid,DHAA)和抗坏血酸(ascorbic acid,AA)。总维生素C含量采用2,4-硝基苯肼分光光度法测定,AA采用2,6-二氯吲哚酚滴定法测定。结果HA-RF干燥过程中维生素C的降解规律符合一级可逆模型,其降解活化能为40.54 kJ/mol。DHAA活化能为35.83 kJ/mol,表明DHAA的稳定性低于AA。结论本研究使用的干燥温度为62.5~77.5℃,较高的干燥温度下维生素C降解速率较高,较低处理温度下的降解过程具有更好的模型适应度(R2>0.98)。     

Effect of H2O2 concentration on electrochemical growth and properties of vertically oriented ZnO nanorods electrodeposited from chloride solutions

In this work, ZnO nanostructures are electrodeposited on a transparent conducting glass from chloride baths. The influence of H₂O₂ concentration on the electrochemical characteristics has been studied using cyclic voltammetry (CV) and chronoamperometry (CA) techniques. From the analysis of the current transients on the basis of the Scharifker–Hills model, it is found that nucleation mechanism is progressive with a typical three-dimensional (3D) nucleation and growth process; independently with the concentration of H₂O₂. However, the nucleation rate of the ZnO changes with the increase of H₂O₂ concentration. The Mott–Schottky measurements demonstrate an n-type semiconductor character for all samples with a carrier density varying between 5.14×10¹⁸ cm⁻³ and 1.47×10¹⁸ cm⁻³. Scanning electron microscopy (SEM) observations show arrays of vertically aligned ZnO nanorods (NRs) with good homogeneity. The X-ray diffraction (XRD) patterns show that the ZnO deposited crystallises according to a hexagonal Würtzite-type structure and with the c-axis perpendicular to the electrode surface. The directional growth along (002) crystallographic plane is very important for deposits obtained at 5 and 7 mM of H₂O₂. The high optical properties of the ZnO NRs with a low density of deep defects was checked by UV–vis transmittance analyses, the band gap energy of films varies between 3.23 and 3.31 eV with transparency around 80–90%.     

Preparation of α-cordierite through mechanochemical activation of MgO–Al2O3–SiO2 ternary system

Samples of the ternary system MgO–Al₂O₃–SiO₂ with stoichiometric composition in relation to α-cordierite (Mg₂A_l4Si₅O₁₈), consisting of 22.2 mol% MgO, 22.2 mol% Al₂O₃, and 55.6 mol% SiO₂, were activated in a low energy mill with a constant speed of 100 rpm, in an aqueous medium. The precursors used were corundum (Al₂O₃), silica gel HF254 type 60 (SiO₂), and periclase (MgO). The objective of the present study was to evaluate the effect of mechanochemical activation on the solid-state synthesis of α-cordierite, using a low energy ball mill. Another objective was to shed light on the effect of mechanochemical activation on the steps of α-cordierite formation. For this end several grinding conditions were evaluated, varying the time and mass ratio of precursors/grinding elements, as well as calcination at different temperatures between 950 °C and 1350 °C for 2 h. The samples were analyzed for the determination of the formed phases by Infrared (IR) and X-ray Diffraction (XRD). The phases identified in uncalcined samples were brucite (Mg(OH)₂), forsterite (Mg₂SiO₄), enstatite (MgSiO₃), spinel (MgAl₂O₃), amorphous silica (SiO₂), corundum (α-Al₂O₃), and zirconia (monoclinic and tetragonal ZrO₂). The lowest temperature corresponding to the formation of α-cordierite (α-Mg₂Al₄Si₅O₁₈) was 1150 °C and a considerable amount of this phase (16.2%) was observed at this temperature, for the sample with the higher mechanochemical activation. In a solid-state reaction, α-cordierite is normally obtained at around 1400 °C, therefore, the formation of this phase at 1150 °C confirms that the mechanochemical activation method, using a low-cost ball mill, is efficient in reducing the solid-state reaction temperature.     

Inductive effect in Mn-doped ZnO nanoribon arrays grown on Ni foam: A promising key for boosted capacitive and high specific energy supercapacitors

Transition metal oxides have been explored in supercapacitor applications owing to their safety, low cost, high specific capacitance and high electrochemical activity. Among all transition metal oxides, zinc oxide based materials show remarkable response for designing the supercapacitors with high electrochemical activity. Here in, Mn doped ZnO (Zn_1-xMn_xO₃ with x = 0, 0.25, 0.50, 0.75 and 1) was synthesized by a facile hydrothermal method. Doping of Mn into the ZnO increased the surface area and decease the charge transfer resistance for the Zn_0.5Mn_0.5O₃. All the synthesized materials were characterized by x-ray diffraction (XRD), scanning electron microscopy SEM), BET, electrochemical tests and other various analytical techniques to confirm the structural, morphological, textural and suprcapacitive properties. The synthesized material Zn_0.5Mn_0.5O₃ having the porous nanoribons structure with BET surface area (2490 cm²/g). The electrochemical studies showed significantly enhanced response toward pseudocapacitive nature. The synthesized material exhibited the excellent specific capacitance (515F/g), specific energy (28.61 Wh/kg) and specific power (1000 W/kg) at current density of 2 mA/g. Such impressive and superior properties make the MnZnO₃ material as promising candidate for new generation supercapacitor applications.