木质素参与有机氟硅苯丙乳液的改性后的性能研究

本文借助预乳化—半连续—种子乳液聚合法制备有机氟硅(KH-570、MBFA-12)苯丙乳液，壳层加入木质素磺酸钠(LS-Na),分别制备了有机氟硅苯丙乳液和木质素改性有机氟硅苯丙乳液。通过浸润滤纸，得到不同疏水性能的改性滤纸。通过多种表征表明，定量加入木质素可有效提升改性滤纸的疏水性，降低有机氟硅用量，维持传统乳液的基础性能。本文的木质素改性乳液可在油水分离、防水涂层等领域提供新的思路与方法。     

自交联醋苯丙防水乳液的制备与性能研究

通过种子乳液聚合法制备了有机硅改性的醋酸乙烯酯-苯乙烯-丙烯酸丁酯(醋苯丙)三元共聚防水乳液.通过对乳液红外光谱和透射电镜的分析,发现有机硅成功引入醋苯丙乳液并起到室温自交联的作用,乳胶粒为核壳结构.着重考察了有机硅用量、醋酸乙烯酯单体用量对乳液防水性能的影响.实验结果表明改性醋苯丙乳液的防水性能优于传统苯丙乳液,且成本更低.     

聚合物乳液改性含钛高炉渣免烧砖

用聚苯乙烯乳液、聚乙酸乙烯酯乳液和苯丙乳液等改性含钛高炉渣浆分别得到免烧免蒸砖试样. 考察了影响试样性能的主要因素和改性机理. 结果表明,聚乙酸乙烯酯乳液改性渣浆试样性能较好,苯丙乳液改性效果最好. 当含钛高炉渣为72%(w,下同)、苯丙乳液为10%、添加剂为18%、成型压力为30 MPa、养护时间为7 d时,渣浆试样的抗压强度和抗折强度分别达到37.7和13.9 MPa. 机理探索表明,苯丙乳液中酸根离子与渣浆中金属离子交联生成了金属络合物.     

酰肼交联体系对外交联核壳结构苯丙乳液成膜性能的影响

以双丙酮丙烯酰胺(DAAM)和己二酸二酰肼(ADH)为交联单体,采用核壳乳液聚合法对常规苯丙乳液进行改性,制备了室温外交联型苯丙乳液。着重探讨了DAAM/ADH体系对苯丙乳液粒径、稳定性、干燥时间、涂膜强度以及耐水性等影响。研究结果表明:该苯丙乳液具有较明显的核壳结构,并且涂膜具有共价交联结构;当n(ADH)∶n(DAAM)=0.75∶1时,涂膜具有相对最好的综合性能,其铅笔硬度、拉伸强度和耐水性明显提高,并且室温干燥时间也明显缩短。     

环氧酯改性苯丙树脂防锈乳液的合成研究

首先由亚麻油酸(FA)和E44按物质的量比n(FA)∶n(E44)=1∶1合成环氧酯;再以苯乙烯、甲基丙烯酸甲酯、丙烯酸丁酯为主要单体,丙烯酰胺、丙烯酸和乙烯基三(异丙氧基)硅氧烷为交联单体,环氧酯为改性单体,采用半连续种子聚合方法合成环氧酯改性有机硅苯丙乳液。研究了乳化剂的种类、用量及配比、交联单体及改性单体用量对乳液及涂膜性能的影响。确定复合乳化剂(SR-10/RP90)的最佳用量为2.5%,最佳配比为m(SR-10)∶m(RP90)=1∶1。实验发现:当丙烯酸用量为2%,丙烯酰胺用量为1.5%,乙烯基三(异丙氧基)硅氧烷用量为6%,环氧酯用量为10%,可以合成出性能优异的环氧酯改性有机硅苯丙乳液。由其制备的水性防锈涂料,具有良好的防锈性能。     

环氧改性苯丙乳液的合成及性能

采用反应性乳化剂通过种子乳液聚合法制备木器涂料用环氧树脂改性苯乙烯-丙烯酸酯微乳液.研究了乳化剂的选择与用量、环氧树脂的用量和功能单体的用量对改性苯丙乳液综合性能的影响,并用傅立叶变换红外光谱仪(FT-IR)对乳液组成进行表征.研究发现反应型乳化剂可制备纳米级乳液,且m(DSB)m(DNS-86)=31时,乳液具有好的稳定性,涂膜有较好的耐水性;得到环氧树脂以及丙烯酸的最佳添加量;性能测试表明合成的环氧树脂改性苯丙乳液具有较好的成膜性能和优异的物理机械性能.     

高阻尼性涂层用苯丙乳液的制备与性能研究

采用半连续种子乳液聚合法,以阴离子乳化剂和反应型乳化剂复配体系为复合乳化剂,引入硅烷偶联剂为改性单体,以双丙酮丙烯酰胺(DAAM)、己二酸二酰肼(ADH)为交联单体,制备出自交联苯丙乳液。采用红外光谱(FT-IR)、马尔文激光粒度仪(Mastersizer)、差示扫描量热仪(DSC)、热重分析仪(TGA)、动态热机械分析(DMA)对乳液和涂膜的结构与性能进行了表征。结果表明,适量的硅烷偶联剂可使涂膜交联密度得到适当提高,使得改性后的涂膜具有良好的耐水性、耐热性,吸水率仅为3.89%,且具有优异的阻尼性能。     

涂布纸涂料用交联型苯丙乳液的制备及应用

以双丙酮丙烯酰胺作为官能单体与其他乙烯基单体共聚,合成了含有酮羰基的苯丙乳液,再与肼混合,制备交联型苯丙乳液,用红外光谱证实了交联反应的发生,并探讨了交联反应对乳液膜性能和涂布纸性能的影响。     

复合有机硅改性苯丙乳液的性能

以苯乙烯(St)、丙烯酸异辛酯(EA)和丙烯酸丁酯(BA)为主要单体,丙烯酸(AA)为功能单体,十二烷基苯磺酸钠(SDS)和壬基酚聚氧乙烯醚(OP-10)为复合乳化剂,γ-甲基丙烯酰氧基丙基三甲氧基硅烷(KH570)、乙烯基三甲氧基硅烷(A-171)和八甲基环四氧硅烷(D4)为有机硅改性剂,通过乳液聚合合成了不同有机硅改性苯丙乳液。研究了复合乳化剂的用量及配比,软硬单体质量比,以及复合有机硅改性剂的配比与用量对苯丙乳液性能的影响,确定了合成有机硅改性苯丙乳液的较佳用量:有机硅的质量分数为6%,软单体(EA、BA)和硬单体(St)的质量比为1∶2,OP-10与SDS的质量比为3∶2,且复合乳化剂的用量为3%。通过红外光谱和热重分析对苯丙乳液,KH570、A-171或D4单一改性以及复合改性苯丙乳液进行了表征,测试了各种乳液及其涂膜的性能。结果表明,有机硅改性后苯丙乳液的综合性能明显提高,复合有机硅改性苯丙乳液的性能最好。当复合有机硅中KH570、A-171和D4的质量比为1∶2∶1时,合成的复合有机硅改性苯丙乳液的固含量为41.33%,粒径80.09 nm,黏度127 mPa·s,其漆膜硬度为2H,吸水率9.34%,失重温度区间在450~520°C,高于苯丙乳液的350~420°C以及由KH-570、A-171或D4单一改性苯丙乳液的390~430°C。     

弹性乳液的合成及在水性油墨的应用研究

采用种子聚合工艺合成了弹性乳液,研究了乳液合成过程中功能单体用量、苯丙树脂液添加量、pH缓冲剂用量以及乳化剂的选择与用量对所配制的水性油墨性能的影响,对比了所合成弹性乳液与同类进口产品所配制水性油墨的性能。结果表明,功能单体占单体质量3％,苯丙树脂液占乳浇创竞量20％,pH缓冲剂占乳液总质量0.2％,反应型非离子一阴离子乳化剂复配使用时合成的弹性乳液配制的水性油墨性能最佳,可替代同类进口产品在水性油墨上的应用。     

不同偶联剂对苯丙乳液的改性效果

采用核壳乳液聚合法,利用前期研究已确定的核壳乳液合成配方,分别将不同种类和用量的硅烷偶联剂[γ-氨丙基三乙氧基硅烷(KH-550)、γ-(2,3-环氧丙氧)丙基三甲氧基硅烷(KH-560)以及乙烯基三乙氧基硅烷(DL-151)]引入到苯丙乳液中,制得有机硅改性苯丙乳液。利用差示扫描量热分析(DSC)法、透射电镜(TEM)法和粒度分析法等多种检测手段,研究了偶联剂的种类与用量对乳液性能(包括粒径及其分布、钙离子稳定性、黏度、玻璃化转变温度及乳胶粒的核壳结构等)和乳胶膜性能(包括成膜性、吸水率、耐水性、附着力和铅笔硬度等)的影响。结果表明:乳胶粒的平均粒径最小为115 nm;DL-151和KH-560对苯丙乳液的改性效果较好,可以考虑将两者复配后共同改性苯丙乳液,以期获得综合性能较好的改性苯丙乳液。     

核/壳型含氟硅苯丙乳液的合成及性能

以氟硅偶联剂——丙烯酸六氟丁酯(HFBA)和γ-(2,3-环氧丙氧)丙基三甲氧基硅烷(KH-560)同时作为苯丙乳液的改性剂,采用种子乳液聚合法制得了核/壳型氟硅改性苯丙乳液。研究了氟硅偶联剂比例及用量对该改性乳液基本性能及应用性能的影响。结果表明:当n(HFBA)∶n(KH-560)=1∶2、w(HFBA+KH-560)=7%时,改性乳液的综合性能最佳,其平均粒径为243 nm、粒径分布较窄(多分散指数为0.237),乳胶膜的玻璃化转变温度为-18.40℃和37.81℃、吸水率(11.83%)相对最低且铅笔硬度(2H)相对较高,同时该乳胶膜具有良好的成膜性、附着力、耐水性、储存稳定性和Ca2+稳定性。     

水性油墨用室温自交联纯丙乳液的合成及应用

以甲基丙烯酸甲酯(MMA)、丙烯酸异辛酯(2-EHA)、甲基丙烯酸(MAA)、双丙酮丙烯酰胺(DAAM)为聚合单体,己二酰肼(ADH)为交联剂,采用半连续种子乳液聚合法合成软核硬壳结构的水性纯丙乳液。利用ATR-FTIR、TEM、GPC、TG、DMA表征水性纯丙乳液的结构和性能。结果表明:乳液成膜过程中DAAM中的—CO—与ADH中的—NHNH_2发生反应,交联度增加,提高了乳液膜的耐水性、热稳定性、玻璃化转变温度和油墨在双向拉伸聚丙烯(BOPP)薄膜上的附着力。当DAAM用量(以MMA和2-EHA的总质量为基准,下同)从0增加到2%,m(ADH)∶m(DAAM)=0.7∶1.0时,乳液膜的吸水率从24.2%降到7.6%,油墨的附着力从87%升至100%;当m(ADH)∶m(DAAM)从0∶1增加到0.7∶1.0,DAAM用量为2%时,乳液膜的吸水率从28.1%降至7.6%,油墨的附着力从0增至100%。当DAAM用量为2%,m(ADH)∶m(DAAM)为0.7∶1.0时,水性纯丙乳液可用作环保型水性油墨的连接料。     

Titanium dioxide grafted with silane coupling agents and its use in blue light curing ink

To improve the properties of titanium dioxide particles and realise their firm anchorage in blue light curing film, three modified titanium dioxide particles were prepared by grafting 3‐(trimethoxysilyl)propyl methacrylate, 3‐aminopropyltriethoxysilane and hexadecyltrimethoxysilane. The surface changes of titanium dioxide particles after modification were characterised. The dispersion stability, photo‐polymerisation, rheological and mechanical properties of modified titanium dioxide blue light curing inks were investigated. Results showed that compared with native titanium dioxide, modified titanium dioxide particles were more appropriate for blue light curing ink. The particle sizes of the three modified titanium dioxide particles became smaller, their surfaces exhibited hydrophobicity, and the viscosity of the modified titanium dioxide inks decreased slightly. Of the three modified titanium dioxide particles, 3‐(trimethoxysilyl)propyl methacrylate‐ and hexadecyltrimethoxysilane‐modified titanium dioxide particles exhibited better dispersion stability in blue light curing ink. In particular, 3‐(trimethoxysilyl)propyl methacrylate‐modified titanium dioxide blue light curing ink showed the best photo‐polymerisation and mechanical properties, which indicated the participation of the pigment grafted by double bonds in the blue light curable polymerisation. Using modified titanium dioxide in blue light curing ink, the dry/wet rubbing fastness of the printed fabrics improved.     

线性聚醚氨基嵌段有机硅柔软剂的应用特点

以端环氧基硅油、聚醚胺和端环氧基聚醚为主要原料,合成了线性聚醚氨基嵌段有机硅柔软剂;乳化后用于织物的整理。考察了线性聚醚氨基嵌段有机硅柔软剂对织物的白度、摩擦牢度、防水性能和撕破强力等的影响,并用FT-IR表征了产物结构。结果表明,与采用传统有机硅柔软剂氨基硅油和亲水聚醚改性硅油整理的织物相比,经线性聚醚氨基嵌段有机硅柔软剂整理织物的白度、摩擦牢度、防水性能和撕破强力等具有明显的优势,并可很好地平衡手感和亲水性之间的矛盾,具有优良的性能。     

Some properties of a thickener for preparing inkjet printing ink for nylon carpet

The properties of a thickener for nylon carpet inkjet printing are presented in this work. A water-based ink was prepared from polyacrylate-based thickener. The physical and chemical properties of the polyacrylate-based thickener used for preparing the inkjet printing ink, as well as its printing effects on carpet, were investigated. Before printing, the properties of the ink, including its surface tension, electrolyte resistance, storage stability, and percentage removal, were investigated. After printing, the efficiency of coloration of printed carpet and the fastness of printed carpet were studied. The results concerning the surface tension and percentage removal of printing ink show that the polyacrylate-based thickener printing ink is suitable for nylon carpet inkjet printing. Meanwhile, its storage stability and electrolyte resistance make it suitable for printing. The efficiency of coloration of printed carpet and the fastness of printed carpet satisfy the requirements of application at appropriate ink concentration and viscosity.     

环氧氯丙烷改性水性硝化纤维乳液的制备及性能

以硝化纤维(NC)、异佛尔酮二异氰酸酯(IPDI)和二羟甲基丙酸(DMPA)等为主要原料,制得自乳化型WNC(水性硝化纤维)乳液;然后以环氧氯丙烷(ECH)为交联改性剂,制成改性WNC乳液胶粘剂。研究结果表明:当w(DMPA)=3.5%、w(ECH)=7%时,改性WNC乳液具有优良的储存稳定性,其胶膜耐水性(吸水率为9.1%)、T型剥离强度(7.1 N/mm)、拉伸强度(14.9 MPa)和断裂伸长率(529.3%)俱佳,柔韧性和耐热性优异。     

纳米SiO_2改性苯丙乳液乳胶漆的研究

通过硅烷偶联剂改性纳米SiO2与丙烯酸丁酯、苯乙烯、甲基丙烯酸3种单体共聚,合成纳米SiO2/苯丙乳液,以其作为主要成膜物制得了乳胶漆。测试了纳米SiO2粒子改性后的微观结构,讨论纳米SiO2含量对乳胶漆的耐老化性、耐洗刷性、耐水性等的影响。     

聚氨酯型反应性乳化剂改性丙烯酸酯的合成及应用

以低聚物多元醇、异佛尔酮二异氰酸酯、二羟甲基丙酸、甲基丙烯酸β-羟乙酯、三羟甲基丙烷等为原料分别制备直链型和具有一定支化度的水性聚氨酯（WPU）。以合成的WPU作为大分子型反应性乳化剂,再辅以少量乳化剂DNS-86与丙烯酸酯单体热引发聚合,制得聚氨酯-丙烯酸酯乳液（PUA）。通过红外光谱和粒径分析等方法对PUA的结构及性能进行表征。结果表明：与直链型相比,经过支链型PU改性后的成膜物拉伸强度达到23.3MPa,粘合剂的皂洗牢度等级达到4级,干摩擦牢度达到4级,湿摩擦牢度达到3级。     

环保型苯丙上光油乳液的研制

以苯乙烯、甲基丙烯酸甲酯为硬单体,丙烯酸丁酷为软单体,以丙烯酸、甲基丙烯酸羟乙酯为功能单体,采用半连续种子乳液聚合方法,制得了一种具有核壳结构的可用于水性上光油的苯丙乳液,研究了乳化剂、交联剂、壳单体中软单体含量对乳液性能的影响及引发剂体系氧化剂和还原剂的配比和加入方式对聚合反应的影响。