复合活性氧化锌在全钢载重子午线轮胎胎侧胶中的应用

研究复合活性氧化锌部分替代间接法氧化锌在全钢载重子午线轮胎胎侧胶中的应用.结果表明：在胎侧胶中以复合活性氧化锌部分替代间接法氧化锌,胶料的焦烧时间延长,炭黑分散度提高,工艺性能良好;硫化胶的拉伸强度、拉断伸长率和撕裂强度略有增大;成品轮胎的耐久性能达到企业标准要求,且生产成本降低.     

活性氧化锌在全钢子午线轮胎胎面胶中的应用

试验研究活性氧化锌在全钢子午线轮胎胎面胶配方中的应用效果,并与普通氧化锌和纳米氧化锌进行对比.结果表明,活性氧化锌胶料的MH和MH-ML均比普通氧化锌胶料有所增大,t10和t90明显延长,与纳米氧化锌胶料差别不大;活性氧化锌硫化胶的物理性能和耐老化性能均优于普通氧化锌硫化胶,但略低于纳米氧化锌硫化胶;活性氧化锌用量不大于5份时,硫化胶的物理性能变化不明显,加入3份活性氧化锌的硫化胶耐老化性能最优.     

活性纳米碳酸钙在全钢子午线轮胎胎侧胶中的应用

试验研究活性纳米碳酸钙在全钢子午线轮胎胎侧胶中的应用。结果表明,在全钢子午线轮胎胎侧胶中添加10份活性纳米碳酸钙,胶料的硫化速度加快,硫化胶的硬度、拉断伸长率略有增大,拉伸强度、定伸应力相当,胶料生产成本降低,具有一定的经济效益。     

活性氧化锌在轮胎胎面胶中的应用

研究了活性氧化锌在轮胎胎面胶中的应用。试验结果表明 ,用 2 5份活性氧化锌替代 4份间接法氧化锌 ,胶料的焦烧时间延长 ,硫化速度下降 ;硫化胶的拉伸强度、邵尔A型硬度、撕裂强度及耐磨性有所提高 ,其它性能也满足胎面胶的性能要求 ;试验轮胎的耐久性能达到 10 5h ,速度性能达到 13 0km·h- 1 × 12 2 5h ,较原生产轮胎有所提高     

白炭黑对跑气保用轮胎胎侧支撑胶性能的影响

研究白炭黑等量替代部分炭黑对跑气保用轮胎胎侧支撑胶性能的影响。结果表明,用5～20份自炭黑等量替代炭黑（炭黑和白炭黑总用量65份）,胶料的加工性能和硫化特性变化不大;硫化胶的拉伸强度、耐屈挠龟裂性能、撕裂强度提高,压缩生热降低,可以更好地满足跑气保用轮胎对胎侧支撑胶的要求。     

纳米粘土在半钢子午线轮胎胎侧胶中的应用

研究纳米粘土在半钢子午线轮胎胎侧胶中的应用。结果表明：以一定量的纳米粘土替代炭黑N660,胶料的加工性能和硫化特性变化不大,硫化胶的拉断伸长率和撕裂强度明显增大;随着纳米粘土用量的增大,硫化胶的密度增大,定伸应力减小,耐屈挠疲劳性能提高;以纳米粘土等量替代炭黑N660,填料分散性稍好,成品轮胎的高速和耐久性能达到企业标准要求,胶料成本下降。     

EPDM J2070在轮胎胎侧胶中的应用

试验研究三元乙丙橡胶(EPDM)J2070在轮胎胎侧胶中的应用。结果表明:在胎侧胶配方中以10份EPDM J2070等量替代天然橡胶,胶料的抗硫化返原性能提高,硫化胶的物理性能和耐屈挠性能良好,耐老化性能提高;胎侧胶的耐臭氧老化性能提升两个等级,同时对成品轮胎的耐久性能无不良影响。     

特种气相法白炭黑SIDISTARR300在全钢载重子午线轮胎胎侧胶中的应用

研究特种气相法白炭黑SIDISTARR300在全钢载重子午线轮胎胎侧胶中的应用。结果表明:在全钢载重子午线轮胎胎侧胶中加入白炭黑R300,可以改善硫化胶的物理性能和耐疲劳性能;当白炭黑R300用量为3份时,硫化胶的综合物理性能较好,老化后耐疲劳性能提高;成品轮胎的耐久性能达到正常生产轮胎水平。     

纳米氧化锌在工程机械轮胎胎面上层胶和缓冲层胶中的应用

研究纳米氧化锌在工程机械轮胎胎面上层胶和缓冲层胶中的应用。结果表明:采用纳米氧化锌70%替代普通氧化锌,胶料的硫化时间延迟,密度减小;硫化胶的定伸应力、拉伸强度、撕裂强度和回弹值增大,耐磨性和耐老化性能提高,生热降低;成品轮胎的物理性能和粘合性能提高。     

绢云母粉在轮胎胶料中的应用研究

对绢云母粉在轮胎胎侧胶和帘布胶中的应用进行小配合,大配合及成品性能检测。结果表明,绢云母粉活化后对胶料的老化性能,疲劳性能,半成品粘合强度,H抽出力等性能有所改善,但焦烧时间和正硫化时间缩短;用添加10份活性绢云母粉的胎侧胶和内层帘布胶制得的轮胎成品性能达到国家标准要求。     

分解炉扩径的技术改造

我厂3号回转窑(Φ4m×60m)生产线在1996年年底由SP窑(产量912t/d)改为NSP窑(产量1320t/d),预分解系统为四级旋风预热器带离线式分解炉     

乙烯酮(双乙烯酮)下游产品废水的治理技术

乙烯酮(双乙烯酮)是十分重要的化工中间体,其下游产品较多。江苏某化工厂开发生产乙烯酮(双乙烯酮)下游产品三十多个,年生产规模三万多吨,是国内以乙烯酮(双乙烯酮)为中间体生产精细化学品的综合骨干企业。针对乙烯酮(双乙烯酮)下游产品废水特点,该厂结合企业实际,开展了产品优化,结构调整,清洁生产,资源循环利用,节水降耗等工作,从源头削减了污染物的生产。同时投资二千多万元新建预处理装置三套,6000m3/d废水生化处理装置一套,使全厂乙烯酮(双乙烯酮)下游产品的废水得到了有效的治理。     

水泥水化热测定方法综述

水泥水化热是中、低热水泥和核电工程用水泥的一项关键的技术指标。全球范围内测定水泥水化热的方法有溶解法、直接法/半绝热法、等温传导量热法三种。本文总结了中、美、欧相关方法标准,对其测试原理、仪器设备、试验过程等方面进行了比对,并对其在领域的应用做了简单的概括。     

生物油的成分分析及物性测定

以添加FeCl2的ZnCl2-KCl混合熔盐裂解纤维素和秸秆,制得生物油。采用傅立叶变换红外光谱法和气相色谱-质谱法分析生物油的成分。结果表明,生物油中成分复杂,含有氧元素、多种有机化合物,主要包括酮类、醛类、酚类及羧酸类等。测定了20～80℃生物油的密度和粘度,发现生物油的密度与温度呈较好线性关系,而生物油的粘度均大于水的粘度,且不同熔盐体系对秸秆生物油的粘度无较大影响。     

Effect of degree of deacetylation of chitosan on the kinetics of ultrasonic degradation of chitosan

The objective of the study was to explore the effect of the degree of deacetylation (DD) of the chitosan used on the degradation rate and rate constant during ultrasonic degradation. Chitin was extracted from red shrimp process waste. Four different DD chitosans were prepared from chitin by alkali deacetylation. Those chitosans were degraded by ultrasonic radiation to different molecular weights. Changes of the molecular weight were determined by light scattering, and data of molecular weight changes were used to calculate the degradation rate and rate constant. The results were as follows: The molecular weight of chitosans decreased with an increasing ultrasonication time. The curves of the molecular weight versus the ultrasonication time were broken at 1‐h treatment. The degradation rate and rate constant of sonolysis decreased with an increasing ultrasonication time. This may be because the chances of being attacked by the cavitation energy increased with an increasing molecular weight species and may be because smaller molecular weight species have shorter relaxation times and, thus, can alleviate the sonication stress easier. However, the degradation rate and rate constant of sonolysis increased with an increasing DD of the chitosan used. This may be because the flexibilitier molecules of higher DD chitosans are more susceptible to the shear force of elongation flow generated by the cavitation field or due to the bond energy difference of acetamido and β‐1,4‐glucoside linkage or hydrogen bonds. Breakage of the β‐1,4‐glucoside linkage will result in lower molecular weight and an increasing reaction rate and rate constant. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 90: 3526–3531, 2003     

Process of acceleration of filtration of viscose

Conclusions It is significant that the purification on a single passage of viscose through porous ceramic corresponds to the result of a two-stage filtration of it in industrial filter-presses with standard fillings.Kiev Combine. Kiev Technological Institute of Light Industry. Translated from Khimicheskie Volokna, No. 3, pp. 20–22, May–June, 1969.     

Approximation of temperature dependence of the modulus of elasticity of glass

A refined nonlinear value of the main parameter of a material, i.e., the elongation modulus versus the instant temperature value, was suggested for introduction into the computational algorithm of tempering stresses.