VO2/GaAs异质结的制备及其光电特性研究

采用直流磁控溅射和后退火氧化工艺在p型GaAs单晶衬底上成功制备了n-VO_2/pGaAs异质结,研究了不同退火温度和退火时间对VO_2/GaAs异质结性能的影响,并分析其结晶取向、化学组分、膜层质量以及光电特性。结果表明,在退火时间2 h和退火温度693 K下能得到相变性能最佳的VO_2薄膜,相变前后电阻变化约2个数量级。VO_2/GaAs异质结在308 K、318 K和328 K温度下具有较好的整流特性,对应温度下的阈值跳变电压分别为6.9 V、6.6 V和6.2 V,该结果为基于VO_2相变特性的异质结光电器件的设计与应用提供了可行性。     

Comparison of yield and metabolites according to the types of hilling materials utilized during Glehnia littoralis sprout vegetable cultivation

Food Science and Biotechnology - Various hilling materials (rice hulls, pine sawdust, and perlite) were compared to produce sprout vegetables using beach silvertop (Glehnia littoralis Fr. Schm. ex...     

基于全U网络的混凝土路面裂缝检测算法

针对现有的混凝土裂缝检测算法在各种复杂环境中检测精度不够、鲁棒性不强的问题,根据深度学习理论和U-net模型,提出一种全U型网络的裂缝检测算法。首先,依照原U-net模型路线构建网络;然后,在每个池化层后都进行一次上采样,恢复其在池化层之前的特征图规格,并将其与池化之前的卷积层进行融合,将融合之后的特征图作为新的融合层与原U-net网络上采样之后的网络层进行融合;最后,为了验证算法的有效性,在测试集中进行实验。结果表明,所提算法的平均精确率可达到83.48%,召回率为85.08%,F1为84.11%,相较于原U-net分别提升了1.48%,4.68%和3.29%,在复杂环境中也能提取完整裂缝,保证了裂缝检测的鲁棒性。     

Optical design of the Lyman alpha based beam emission spectroscopy(LAB)diagnostic on the HL-2A tokamak

In this article, we present the optical design of a novel diagnostic on the HL-2 A tokamak, i.e. the20-channel edge Lyman-alpha beam emission spectroscopy, which is a promising solution for edge density turbulence research on tokamaks, as it offers the possibility of density fluctuation measurement with a 3.3 mm spatial resolution while maintains a high temporal resolution of1 μs. The optical path, including the reflective collection optics, the high-dispersion spectrometer, and the linear detector array, is carefully optimized to obtain a good image quality and a high throughput. The maximum root mean square radius of the collection optics is 64 μm.The detected photon flux is estimated to be about 10~(11) photons/s/channel.     

Pressure-induced transparency of MgO,Al2O3, AlN,and cBN ceramics at room temperature

The in situ axial X-ray diffraction patterns of four ceramic powder samples (MgO, Al₂O₃, AlN, and cBN) that were compressed in a diamond anvil cell under uniaxial non-hydrostatic conditions were recorded. The microscopic deviatoric stress as a function of the pressure was determined from the X-ray diffraction peak broadening analysis: the curves increased approximately linearly with the pressure at the initial compression stage and then levelled off under further compression. Pressure-induced transparency was observed in all of the samples under compression, and the pressure at the turning point on the curves of the microscopic deviatoric stress versus pressure corresponded to the pressure at which the samples became transparent. Analysis of the microstructural features of the pressure-induced transparent samples indicated that the compression caused the grains to fracture, and the broken grains bonded with each other. We demonstrated that the ceramics’ pressure-induced transparency was a process during which the grains were squeezed and broken, the pores were close between the grains, and the broken grains were re-bonded under compression.     

一种飞行计划航段自动激活方法

飞机从一个航段飞向下一个航段时,需要对下个航段是否激活进行判断.提出了一种新的飞行计划航段自动激活方法,通过获取飞机当前位置及其磁差,并结合临近的3个航路点对应位置的磁差经纬度,分别计算3个航路点与飞机位置对应的磁航向角,通过磁航向角之间做差进行比较,进而判断是否被激活.算法推导完成后,通过基于模型的系统工程工具SCADE SUITE进行了建模,并结合杰普逊航图进行了实际数据采样与仿真.仿真结果表明:该航段自动激活方法能够有效稳定地激活下一航段,比传统方法计算简便,方法实用有效.已在实际飞行中成功应用,达到了预期效果.     

减水剂类型对赤泥—矿渣基地聚物注浆材料性能的影响及机理研究

针对赤泥等固体废弃物对环境危害性大且利用率低等问题,以碱激发赤泥-矿渣基地聚物注浆材料为 研究对象,研究了不同掺量的聚羧酸(PA)减水剂、醛酮缩合物(AKC)减水剂和萘系(N)减水剂对材料凝结时间、流动 性及强度等的影响,并通过 XRD、傅里叶红外光谱及 SEM 等设备对减水剂的作用机理进行研究。 结果表明:减水剂增 强了材料的流动性但降低了材料的剪切应力;N 和 PA 减水剂能缩短材料的凝结时间,但 AKC 减水剂会延长材料的凝 结时间;N 和 AKC 减水剂能提高材料的强度,但 PA 减水剂会降低材料的强度;N 减水剂对材料的综合性能提升效果 更加明显,其最优掺量为 0. 7%;减水剂对赤泥-矿渣基地聚物性能提升的作用机理主要是促进地聚合物凝胶的形成。 研究成果为拓展赤泥在工程上的使用途径和效率提供了理论指导。