Dense and core-rim structured B4C-TiB2 ceramics with Mo-Co-WC additive

B₄C-TiB₂ ceramics (TiB₂ ranging 5~70 vol%) with Mo-Co-WC as the sintering additive were prepared by spark plasma sintering. In comparison with B₄C-TiB₂ without additive, the enhanced densification was evident in the sintered specimen with Mo-Co-WC additive. Core-rim structured grain was observed around TiB₂ grains. The interface of the rim between TiB₂ and B₄C phases demonstrated different feature: the inner borderline of the rim exhibited a smooth feature, whereas a sharp curved grain boundary was observed between the rim and the B₄C grain. The formation mechanism is discussed: the epitaxial growth of (Ti,Mo,W)B₂ rim around the TiB₂ core may occur as a result of the solid solution and dissolution-precipitation between TiB₂ phase and the sintering additive. It was revealed that the fracture toughness increased as the content of TiB₂ content increased, alongside the decreased hardness. B₄C-30 vol% TiB₂ specimen demonstrated the optimal combination of mechanical properties, reaching Vickers hardness of 24.3 GPa and fracture toughness of 3.33 MPa·m^1/2.     

Characterizations of friction welding joint interface for AISI 316

Because of heat amount is different from peripheral to central of friction welding interface, which is leaded to vary the characterizations along that interface. Current study, respectively, focused on the effect of different friction pressure on micro-structural and mechanical properties of that friction welding joint interface. Presently, these friction pressures are 110, 130, 150 and 170 MPa while kept all other conditions constant. The effects of different friction pressure on welding interface characterization were investigated by EDX, SEM, tensile, compression, impact and hardness tests. The tensile tests carried out on the standardized test piece with diameter 6 mm and 8 mm, thus, compression tests were extracted from the positions of 0°, 45° 90° with test specimen of 4 mm diameter and 6.5 mm length at weld center. Whereas, the impact test pieces were picked up in two positions, the first one is symmetrical, which it obtained to the respect of the rotation axis and the interface, on the other hand, the second one is non-symmetrical with the axis of rotation and symmetrical to the interface, for making the notch head coincide with the center of the welded joint, The obtained results showed that with reducing of friction pressure will present lack of bonding increasing from peripheral toward the welding center, which will responsible on reducing of the mechanical properties such as tensile, compression and impact strength.     

Effects of the film thickness and poling electric field on photovoltaic performances of (Pb,La)(Zr,Ti)O3 ferroelectric thin film-based devices

The ferroelectric photovoltaic (FPV) effect obtained in inorganic perovskite ferroelectric materials has received much attention because of its large potential in preparing FPV devices with superior stability, high open-circuit voltage (V_oc) and large short-circuit current density (J_sc). In order to obtain suitable thickness for the ferroelectric thin film as light absorption layer, in which, the sunlight can be fully absorbed and the photo-generated electrons and holes are recombined as few as possible, we prepare Pb_0.93La_0.07(Zr_0.6Ti_0.4)_0.9825O₃ (PLZT) ferroelectric thin films with different layer numbers by the sol-gel method and based on these thin films, obtain FPV devices with FTO/PLZT/Au structure. By measuring photovoltaic properties, it is found that the device with 4 layer-PLZT thin film (~300 nm thickness) exhibits the largest V_oc and J_sc and the photovoltaic effect obviously depends on the value and direction of the poling electric field. When the device is applied a negative poling electric field, both the V_oc and J_sc are significantly higher than those of the device applied the positive poling electric field, due to the depolarization field resulting from the remnant polarization in the same direction with the built-in electric field induced by the Schottky barrier, and the higher the negative poling electric field, the larger the V_oc and J_sc. At a -333 kV/cm poling electric field, the FPV device exhibits the most superior photovoltaic properties with a V_oc of as high as 0.73 V and J_sc of as large as 2.11 μA/cm². This work opens a new way for developing ferroelectric photovoltaic devices with good properties.     

不同硬度PTMG型CPUE与硫化橡胶的性能对比研究

通过改变硬段含量、扩链系数等制备了几种不同硬度的四氢呋喃均聚醚(PTMG)浇注型聚氨酯弹性体(CPUE),讨论了PTMG型CPUE与硫化橡胶(VR)的物理机械性能、拉伸应力应变行为以及动态力学性能的区别。结果表明,随CPUE硬度的提高,材料的刚性增强,力学性能是低硬度VR的数倍。通过对CPUE硬度的调节,可以使之兼具聚氨酯和橡胶的优良性能。在玻璃态温度下CPUE的储能模量随硬度的减小而降低,但都高于VR,而且CPUE的硬度越大,二者相差越大,温度越低,相差也越大;在室温以上温度范围内,CPUE具有比VR更小的力学损耗。     

Effects of SiC content on the densification,microstructure, and mechanical properties of HfB2–SiC composites

To investigate the effects of SiC on microstructure, hardness, and fracture toughness, 0, 10, 20, and 30 vol% SiC were added to HfB₂ and sintered by SPS. Upon adding SiC to 30 vol%, relative density increased about 4%; but HfB₂ grain growth had a minimum at 20 vol% SiC. This may be due to grain boundary silicate glass, responsible for surface oxide wash out, enriched in SiO₂ with higher fraction of SiC. By SiO₂ enrichment, the glass viscosity increased and higher HfO₂ remained unsolved which subsequently lead to higher grain growth. Hardness has increased from about 13 to 15 GPa by SiC introduction with no sensible variation with SiC increase. Residual stress measurements by Rietveld method indicated high levels of tensile residual stresses in the HfB₂ Matrix. Despite the peak residual stress value at 20 vol% SiC, fracture toughness of this sample was the highest (6.43 MPa m^0.5) which implied that fracture toughness is mainly a grain size function. Tracking crack trajectory showed a mainly trans-granular fracture, but grain boundaries imposed a partial deflection on the crack pathway. SiC had a higher percentage in fracture surface images than the cross-section which implied a weak crack deflection.     

A first-principles investigation on mechanical and metallic properties of titanium carbides under pressure

The titanium carbides are potential candidates to achieve both high hardness and refractory property. We carried out a structural search for titanium carbides at three pressures of 0 GPa, 30 GPa and 50 GPa. A phase diagram of the Ti-C system at 0 K was obtained by elucidating formation enthalpies as a function of compositions, and their mechanical and metallic properties of titanium carbides were investigated systematically. We also discussed the relation of titanium concentration to the both mechanical and metallic properties of titanium carbides. It has been found that the average valence electron density and tractility improved at higher concentrations of titanium, while the degree of covalent bonding directionality decreased. To this effect, the hardness of titanium carbide decreases as the content of titanium increases. Our results indicated that the titanium content significantly affected the metallic properties of the Ti-C system.     

高性能大尺寸永磁体粘合强度的测定

介绍了一种用三点弯曲试验法测定高性能大尺寸粘接永磁体粘合强度的方法，及利用布氏硬度计的加载系统，实现100％检验粘接质量的方法。     

Vapor absorption by LiBr aqueous solution in vertical smooth tubes

Heat and mass transfer in a falling film vertical in-tube absorber was studied experimentally with LiBr aqueous solution. The presented results include the effect of solution flow rate, solution subcooling and cooling water temperature on the absorption in a smooth copper tube 16.05 mm I.D. and 400 mm long. The experimental data in the previous report for a 1200-mm-long tube was also re-examined and compared. It was demonstrated by the observation of the flow in the tube that the break down of the liquid film into rivulets leads to deterioration of heat and mass transfer at lower film Reynolds number or in longer tubes. An attempt to evaluate physically acceptable heat and mass transfer coefficients that are defined with estimated temperature and concentration at the vapor–liquid interface was also presented.