Dense and core-rim structured B4C-TiB2 ceramics with Mo-Co-WC additive

B₄C-TiB₂ ceramics (TiB₂ ranging 5~70 vol%) with Mo-Co-WC as the sintering additive were prepared by spark plasma sintering. In comparison with B₄C-TiB₂ without additive, the enhanced densification was evident in the sintered specimen with Mo-Co-WC additive. Core-rim structured grain was observed around TiB₂ grains. The interface of the rim between TiB₂ and B₄C phases demonstrated different feature: the inner borderline of the rim exhibited a smooth feature, whereas a sharp curved grain boundary was observed between the rim and the B₄C grain. The formation mechanism is discussed: the epitaxial growth of (Ti,Mo,W)B₂ rim around the TiB₂ core may occur as a result of the solid solution and dissolution-precipitation between TiB₂ phase and the sintering additive. It was revealed that the fracture toughness increased as the content of TiB₂ content increased, alongside the decreased hardness. B₄C-30 vol% TiB₂ specimen demonstrated the optimal combination of mechanical properties, reaching Vickers hardness of 24.3 GPa and fracture toughness of 3.33 MPa·m^1/2.     

Microbial susceptibility of various polymers and evaluation of thermoplastic elastomers with antimicrobial additives

The incursion of microbial growth on polymeric products can deteriorate their performance and lead to the development of undesirable staining and odors. A growing trend in the industry has aimed to reduce microbial populations on high-touch surfaces via the use of antimicrobials to protect material aesthetics and durability or to prevent the spread of pathogenic microorganisms. In this study, a variety of plastic substrates (30 unique polymer compounds), including poly(acrylonitrile-co-butadiene-co-styrene), poly(butylene terephthalate), poly(etherimide), various thermoplastic elastomers (TPEs), poly(carbonates), and poly(amides), were screened for susceptibility to microbial attack using American Society for Testing and Materials (ASTM) G21 (fungi susceptibility), Japanese Industrial Standard (JIS) Z2801, and modified ASTM E1428-15a (bacterial susceptibility) test standards. TPEs were determined to be most susceptible to microbial attack under the appropriate environmental conditions. Subsequent studies assessed the use of an antimicrobial additive, zinc pyrithione (ZPT), for potential efficacy in a variety of TPE blends for diverse target market applications. ZPT proved to be very effective in protecting TPEs, reducing Staphylococcus aureus and Escherichia coli populations by 99.9% or more in JIS Z2801 testing and inhibiting fungal growth (rating = 0) according to the ASTM G21 standard.     

Microstructure and mechanical properties of α/β-Si3N4 composite ceramics with novel ternary additives prepared via spark plasma sintering

In this study, α/β-Si₃N₄ composite ceramics with high hardness and toughness were fabricated by adopting two different novel ternary additives, ZrN–AlN–Al₂O₃/Y₂O₃, and spark plasma sintering at 1550 °C under 40 MPa. The phase composition, microstructure, grain distribution, crack propagation process and mechanical properties of sintered bulk were investigated. Results demonstrated that the sintered α/β-Si₃N₄ composite ceramics with ZrN–AlN–Al₂O₃ contained the most α phase, which resulted in a maximum Vickers hardness of 18.41 ± 0.31 GPa. In the α/β-Si₃N₄ composite ceramics with ZrN–AlN–Y₂O₃ additives, Zr₃AlN MAX-phase and ZrO phase were found and their formation mechanisms were explained. The fracture appearance presented coarser elongated β-Si₃N₄ grains and denser microstructure when 20 wt% TiC particles were mixed into Si₃N₄ matrix, meanwhile, exhibited maximum mean grain diameter of 0.98 ± 0.24 μm. As a result, the compact α/β-Si₃N₄ composite ceramics containing ZrN–AlN–Y₂O₃ additives and TiC particles displayed the optimal bending strength and fracture toughness of 822.63 ± 28.75 MPa and 8.53 ± 0.21 MPa?m^1/2, respectively. Moreover, the synergistic toughening of rod-like β-Si₃N₄ grains and TiC reinforced particles revealed the beneficial effect on the enhanced fracture toughness of Si₃N₄ ceramic matrix.     

印刷电路板缺陷检测的实际应用

电路板在我们的日常生活中非常常见,这就使得印刷电路板的缺陷检测显得尤为重要。AOI作为新兴的检测PCB板缺陷的系统,在生产实际中正在被大家熟知并且应用。相较于传统的检测方式,AOI系统比较灵活,无论是在检测时间还是系统运算上,或者是对相关技术人员的要求相较于传统方式都比较有优势,本文就AOI系统在实际中的应用展开讨论,分析并且介绍了在实际应用中的具体细则。     

New exact solutions of the Tzitzéica-type equations in non-linear optics using the expa function method

One specific class of non-linear evolution equations, known as the Tzitzéica-type equations, has received great attention from a group of researchers involved in non-linear science. In this article, new exact solutions of the Tzitzéica-type equations arising in non-linear optics, including the Tzitzéica, Dodd–Bullough–Mikhailov and Tzitzéica–Dodd–Bullough equations, are obtained using the exp_a function method. The integration technique actually suggests a useful and reliable method to extract new exact solutions of a wide range of non-linear evolution equations.     

柠檬酸铋合成新工艺研究

针对现有柠檬酸铋制备工艺合成时间长、能耗高、产品纯度不高等不足,介绍了一种常温下制备柠檬酸铋的新工艺。新工艺制备时间短,制备的柠檬酸铋产品质量好,合成过程产生的废水可循环利用,废气经碱液循环吸收可生产硝酸钠副产品。     

V2O5/RGO/Pt nanocomposite on oxytetracycline degradation and pharmaceutical effluent detoxification

The cover image is based on the Research Article V₂O₅/RGO/Pt nanocomposite on oxytetracycline degradation and pharmaceutical effluent detoxification by Mohan, H et al., DOI: 10.1002/jctb.6238 .

     

Low-temperature hot-press sintering of AlN ceramics with MgO–CaO–Al2O3–SiO2 glass additives for ceramic heater applications

Aluminum nitride (AlN) is used a ceramic heater material for the semiconductor industry. Because extremely high temperatures are required to achieve dense AlN components, sintering aids such as Y₂O₃ are typically added to reduce the sintering temperature and time. To further reduce the sintering temperature, in this study, a low-melting-temperature glass (MgO–CaO–Al₂O₃–SiO₂; MCAS) was used as a sintering additive for AlN. With MCAS addition, fully dense AlN was obtained by hot-press sintering at 1500 °C for 3 h at 30 MPa. The mechanical properties, thermal conductivity, and volume resistance of the sintered AlN–MCAS sample were evaluated and compared with those of a reference sample (AlN prepared with 5 wt% Y2O3 sintering aid sintered at 1750 °C for 8 h at 10 MPa). The thermal conductivity of AlN prepared with 0.5 wt% MCAS was 91.2 W/m?K, which was 84.8 W/m?K lower than that of the reference sample at 25 °C; however, the difference in thermal conductivity between the samples was only 14.2 W/m?K at the ceramic-heater operating temperature of 500 °C. The flexural strength of AlN–MCAS was 550 MPa, which was higher than that of the reference sample (425 MPa); this was attributed to the smaller grain size achieved by low-temperature sintering. The volume resistance of AlN–MCAS was lower than that of the reference sample in the range of 200–400 °C. However, the resistivity of the proposed AlN–MCAS sample was higher than that of the reference sample (500 °C) owing to grain-boundary scattering of phonons. In summary, the proposed sintering strategy produces AlN materials for heater applications with low production cost, while achieving the properties required by the semiconductor industry.     