Catalytic behavior in CH4 decomposition of catalysts derived from red mud: Impact of residual Na2O

Catalyst samples for CH₄ decomposition were prepared from red mud (RM) by an acid-leaching neutralization precipitation approach. Water-washing the resultant precipitates multiple times, followed by drying at 105 °C and calcination at 500 °C, resulted in a threshold of residual Na₂O, equivalent to 96% Na₂O removal. Drying the precipitate at a higher temperature of 200 °C, followed by repeated water washing, provided a deeper Na₂O removal of 99% and made the resultant samples more active for the targeted reaction. Subsequently, four catalyst samples with a simulated red mud composition and NaOH contents from 0 to 0.3 wt% were prepared and the catalytic test results revealed that the Na₂O remaining in the RM-derived catalysts did not only inhibit their activation in CH₄ but also lower their maximal activities for CH₄ decomposition. Finally, two catalysts with the same simulated red mud composition and their Na impregnated respectively on Fe₂O₃ and a mixture support of Al₂O₃-SiO₂-TiO₂ were prepared and tested to explore the effect of Na distribution on the activation behavior of RM-derived catalysts for CH₄ decomposition. The activity testing results showed that it was the Na residual dispersed on iron oxides in the RM-derived samples to significantly inhibit the activation of CH₄ decomposition.     

Balancing control of a unicycle robot with double gyroscopes using adaptive fuzzy controller

This paper presents a unicycle robot which utilizes the precession effect of a double-gyroscope for lateral balancing and designs an adaptive fuzzy controller to realize the balance control according to its dynamic model. The double gyroscope structure of the unicycle robot can eliminate the pitch angle interference caused by the precession effect and improve the robot's lateral anti-interference ability. An adaptive fuzzy controller is designed based on the dynamic equations of the unicycle robot to improve its robustness. The adaptive controller part improves the anti-interference ability of the unicycle robot, and the fuzzy controller part is used as decoupling controller to reduce the interference of coupling. Simulation and experimental results to verify the anti-interference ability and decoupling effect of the designed controller.     

建筑工业化发展的多群体演化博弈与仿真研究

新型建筑工业化具有高质量、低消耗、可循环发展等特征，其推广已上升到国家战略层面。利用演化博弈方法，建立“政府-开发商-银行” 的三方动态演化博弈模型，进行各博弈主体策略的演化稳定性分析，并针对初始状态、奖惩力度、借贷风险和开发成本等对演化结果的影响进行动态仿真。在此基础上， 考虑开发商群体的网络拓扑特征对演化真实性的影响，引入复杂网络理论， 以无标度网络为载体描述开发商个体的连接偏好和决策机制，构建政府监管下的建筑工业化扩散模型，并通过仿真深入研究相关因素对扩散深度的影响作用，最后结合仿真结果给出相应对策建议。     

Sealing behaviour of glass-based composites for oxygen transport membranes

In this study, seven different filler materials in different proportions were added to a Ba-Ca-Si glass matrix “H” to investigate new sealant with higher thermal expansion coefficient (CTE) value and good sealing performance for application in oxygen transport membrane (OTM). SrTi_0.75Fe_0.25O_3-δ (STF25) was used as an OTM, and the sealing partners were ferritic steel Aluchrom and pre-oxidized Aluchrom. Compatibility tests were carried out to investigate the feasibility of the composites. Higher CTE values were found in dilatometer tests on composite samples by adding 40 wt% Ag (HAg40) and 30 wt% Ni-Cr (HNC30). Gas-tightness measurements of sandwiched samples produced appropriate helium leakage rates in the range of 10^?6 mbar·l·s^?1. Sealing behaviour of sealants HAg40 and HNC30 were investigated by joining STF25 and as-delivered/pre-oxidized Aluchrom together. Scanning electron microscopy (SEM) on cross-sections of the joints revealed a homogeneous microstructure and good adherence of the glass sealants to support metals and STF25.     

基于改进SOA-VMD的磁声发射信号去噪算法

磁声发射（MAE）是铁磁性材料磁化过程中产生的声发射信号，在构件应力检测和微观损伤检测中有着广泛的应用。针对MAE信号非稳态、复杂性、衰减性等特点，提出海鸥算法结合变分模态分解（SOA-VMD）的去噪方法，为克服海鸥算法求解过程中易陷入局部最优解问题，利用柯西变异算子产生随机迭代过程，使改进算法即柯西变异海欧算法（CVSOA）跳出早熟收敛。采用以幅值谱熵为适应度函数，优化VMD算法中分解模态个数K和二次惩戒因子α两个参数，将含噪声的MAE信号进行VMD分解重构。经仿真信号和实际检测信号分析表明，改进后的CVSOA-VMD算法全局寻优能力和去噪性能优于传统的SOA-VMD算法，降噪后的MAE信号特征值对于不同应力下均方根、偏斜度特征值的重复性更好，可靠性更高。     

Phase constitution,microstructure and mechanical properties of a Ni-based superalloy specially designed for additive manufacturing

In this study, a kind of Ni-based superalloy specially designed for additive manufacturing (AM) was investigated. Thermo-Calc simulation and differential scanning calorimetry (DSC) analysis were used to determine phases and their transformation temperature. Experimental specimens were prepared by laser metal deposition (LMD) and traditional casting method. Microstructure, phase constitution and mechanical properties of the alloy were characterized by scanning electron microscopy (SEM), transmission scanning electron microscopy (TEM), X-ray diffraction (XRD) and tensile tests. The results show that this alloy contains two basic phases, γ/γ', in addition to these phases, at least two secondary phases may be present, such as MC carbides and Laves phases. Furthermore, the as-deposited alloy has finer dendrite, its mean primary dendrite arm space (PDAS) is about 30-45 μm, and the average size of γ' particles is 100-150 nm. However, the dendrite size of the as-cast alloy is much larger and its PDAS is 300-500 μm with secondary and even third dendrite arms. Correspondingly, the alloy displays different tensile behavior with different processing methods, and the as-deposited specimen shows better ultimate tensile stress (1,085.7±51.7 MPa), yield stress (697±19.5 MPa) and elongation (25.8%±2.2%) than that of the as-cast specimen. The differences in mechanical properties of the alloy are due to the different morphology and size of dendrites, γ', and Laves phase, and the segregation of elements, etc. Such important information would be helpful for alloy application as well as new alloy development.     

Green Measurements for Software Product Based on Sustainability Dimensions

Software is a central component in the modern world and vastly affects the environment’s sustainability. The demand for energy and resource requirements is rising when producing hardware and software units. Literature study reveals that many studies focused on green hardware; however, limited efforts were made in the greenness of software products. Green software products are necessary to solve the issues and problems related to the long-term use of software, especially from a sustainability perspective. Without a proper mechanism for measuring the greenness of a particular software product executed in a specific environment, the mentioned benefits will not be attained. Currently, there are not enough works to address this problem, and the green status of software products is uncertain and unsure. This paper aims to identify the green measurements based on sustainable dimensions in a software product. The second objective is to reveal the relationships between the elements and measurements through empirical study. The study is conducted in two phases. The first phase is the theoretical phase, where the main components, measurements and practices that influence the sustainability of a software product are identified. The second phase is the empirical study that involved 103 respondents in Malaysia investigating current practices of green software in the industrial environment and further identifying the main sustainability dimensions and measurements and their impact on achieving green software products. This study has revealed seven green measurements of software product: Productivity, Usability, Cost Reduction, Employee Support, Energy Efficiency, Resource Efficiency and Tool Support. The relationships are statistically significant, with a significance level of less than 0.01 (p = 0.000). Thus, the hypothesised relationships were all accepted. The contributions of this study revolve around the research perspectives of the measurements to attain a green software product.     

Crystallization,structure, and enhanced mechanical property of ethylene-octene elastomer crosslinked with dicumyl peroxide

Crosslinking of polyolefin elastomer (POE, ENGAGE™ 8480) with Dicumyl Peroxide (DCP) can have effects on its crystallization dynamics, crystal structure, and properties. The POE crosslinked uniformly has significantly lower crystalline ability than the one with only amorphous phase crosslinked, which, in turn, has weaker crystalline ability than neat POE. The crystallinity and melting point depend on how the POE is crosslinked. The neat POE and POE crosslinked in amorphous phase only, are investigated with DSC and in-situ tensile/synchrotron radiation (WAXD/SAXS). In situ tensile/synchrotron X-ray during a uniaxial stretching process indicates that severe crystal fragmentation is observed at a strain around 45%, and with further increase in strain. The stress in the crosslinked POE is significantly larger than neat POE. For both samples, crystal orientation increases sharply within the strain range up to 88% where orientation-induced new crystals aligned in stretching direction are observed. The long period increases more in stretching direction for the crosslinked POE, consistent with larger stress in this sample, and the stress difference is more pronounced at large strains (27.3 vs. 10.9 MPa at a strain 435%). Permanent set of the crosslinked POE is smaller, consistent with less oriented crystals observed after the test for permanent set.