Identification of the spinel (Cr,Al)3S4 in the internal sulfidation zone of Al-diffusion coatings

The thiospinel (Cr, Al)₃S₄ has been identified in the internal sulfidation zone of Al-diffusion coatings by electron diffraction in a transmission electron microscope. The Al/Cr ratio of this phase can vary over a rather broad range, obviously dependent on the Al/Cr ratio in the surrounding metallic matrix. The spinel can dissolve significant amounts of Ni and Mo, some Co but only traces of Ti. Increasing Al-content extents its stability to higher temperatures.     

再制造工程和表面工程技术在钢铁产业中的应用

阐述了再制造工程与现代钢铁产业的关系.借助再制造工程体系的先进表面技术和先进设计与管理方法,可以使钢铁设备不断得到技术改造, 延长其寿命和报废期限,提高钢铁设备的档次和附加值,是实现高效、绿色钢铁发展模式的重要途径.介绍了电镀、热喷涂等表面技术在连铸结晶器、各种辊类钢铁设备上的应用与发展,通过表面技术获得的再制造钢铁设备产品具有优异的性能和良好的经济、社会效益.     

Al2O3对CaO-Al2O3-SiO2-Na2O系微晶玻璃结构与性能的影响

利用烧结法工艺制备CaO—Al2O3-SiO2-Na2O系微晶玻璃，通过DTA、XRD、IR和SEM等分析手段，系统研究Al2O3对CaO-Al2O3-SiO2-Na2O系微晶玻璃的结晶温度、晶体结构以及性能的影响。研究表明：随着Al2O3质量分数升高，初始析晶温度升高，晶体尺寸增大、析晶率升高，微晶玻璃的表观体积密度、显微硬度和抗折强度呈先增加后降低的趋势。在本实验条件下，最佳的Al2O3质量分数为11．77％。     

高级计划与排程在MTO型企业中的应用研究

高级计划与排程是一种基于约束理论面向供应链的生产计划与排程工具，APS软件系统从ERP系统获取基础数据进行生产排程，再将排程结果送到ERP和生产系统中执行。本文在分析MTO型企业生产计划制定实施关键流程的基础上，对APS在企业生产排程中的应用方法进行了深入研究，同时探讨了系统集成的体系架构和关键实现技术。     

一种新型镍基高温合金组织及性能的研究

GH4742(俄ЭП742)合金属于典型的高合金化难变形镍基高温合金涡轮盘材料，本文通过调整Al、Ti、Nb的成分对GH4742合金进行改进，发明了一种新型镍基高温合金。利用JMatPro模拟得到平衡相图，再利用光学金相显微镜和场发射扫描电镜对合金的晶粒组织、碳化物以及γ′相分布情况进行观察，同时对力学性能进行了检测。结果表明：平衡状态下的合金从1 400 ℃到300 ℃的冷却过程中相转变可概括为L → L+γ → L+γ+MC →γ+MC+γ′ → γ+γ′+MC+μ → γ+γ′+μ+MC+M23C6 → γ+γ′+μ+MC+M23C6+σ，780 ℃下析出γ′相的质量分数为40.88%；锻造变形工艺为γ+γ′双相区变形，1 120 ℃固溶后经过标准双时效处理(850 ℃/6 h/AC＋780 ℃/6 h/AC)后的显微组织明显可见两种不同尺寸晶粒，小晶粒(13 μm)呈项链状分布于大晶粒(100 μm)周围；该合金中的碳化物主要为大尺寸、不规则形状的MC(NbC、TiC、VC)，断续穿晶和沿晶分布；强化相γ′相的分布状态也有大小两种不同尺寸，γ′I相平均直径为600 nm，γ′II相平均直径为150 nm，两种尺寸γ′相强化的良好匹配，使得该合金在具有较高强度的同时又具有较高的塑性，力学性能优异，室温抗拉强度1 478 MPa，尤其是650 ℃/863 MPa下的持久性能为194 h，远远超过GH4742合金650 ℃/823 MPa持久下50 h的标准。     

铸钢件裂纹与钢中夹杂物关系及减少措施

钢中夹杂物是铸钢裂纹产生的主要原因,同时对钢的质量和力学性能等有很大影响,必须严格控制.外来夹杂物可以根据其来源采取相应措施加以去除,而内生夹杂物却需通过脱氧工艺及钙处理工艺新技术加以控制.在冶炼过程中,要加强时脱氧、脱硫、去夹杂物、去气体等冶炼操作,并在炉后钢包内采取必要的措施,如加稀土进行变质处理等来改变夹杂物的形状,减少夹杂物,以降低铸钢裂纹倾向.     

Superplastic deformation and crystallization behavior of Cu54Ni6Zr22Ti18 metallic-glass sheet

Superplastic deformation and crystallization behavior of a Cu₅₄Ni₆Zr₂₂Ti₁₈ metallic glass were investigated. A maximum elongation of 650% was obtained at 733 K at 1 × 10⁻² s⁻¹ from the sheet fabricated by squeeze copper-mold casting method. At low strain rates, the strain-rate-sensitivity exponent value was close to 1, suggesting that Newtonian-like behavior governed the plastic flow. At a high strain rate around 10⁻² s⁻¹, a transition from Newtonian to non-Newtonian behavior took place with decrease in m value. Large strain hardening by crystallization occurred during the course of deformation. The strain hardening was found to be caused by crystallization according to the analyses of the relation of true stress vs. testing time, T-T-T diagram and DSC characteristics. The time periods up to the strain before strain hardening at 733 K for the Cu₅₄Ni₆Zr₂₂Ti₁₈ metallic glass were similar to that of the Zr₆₅Al₁₀Ni₁₀Cu₁₅ metallic glass at 696 K as 180–300 s (3–5 min). This coincidence could be explained by comparison of their T-T-T diagrams showing that the incubation times for crystallization of the Cu BMG at 733 K and for Zr BMG at 696 K are similar.     

基于模型特征的新型有限元网格划分方法研究

开孔构件的开孔形式各异,增加了其网格划分难度.另外,全六面体网格划分一直是有限元网格划分中的难点之一,实现开孔构件的全六面体网格划分具有重要的现实意义.文章基于开孔实体的参数化特征模型思想,提出了一种非自由边界分割有限元网格划分方法,可以针对开孔实体的几何特征和力学特征,对多种类型的开孔构件进行全六面体网格划分,生成的网格质量均匀、局部加密方便且疏密过渡合理.经实例应用表明,此种网格划分方法具有通用性强、简单、实用、高效等特点.     

超声显微镜技术在铜/铝摩擦焊质量控制中的应用

铜/铝摩擦焊广泛用于电力行业接线端子的制作，其焊接质量直接影响着电力系统的安全运行。通过理论分析及试验方法探讨了超声波显微镜技术在铜/铝摩擦焊质量控制中的应用可行性，同时进行超声显微镜检测试验，发现将超声显微镜技术应用在铜/铝摩擦焊检测中，检测灵敏度高、分辨率好、检测结果直观。     

碳化钨/高铬铸铁复合铸渗层耐磨特性研究

采用CO2水玻璃砂型铸渗工艺制备了碳化钨/高铬铸铁复合铸渗层试样,借助于MLD-10动载磨损试验机、扫描电镜研究了渗剂组分、粒度、工艺参数对铸渗层耐磨性的影响,结果表明:在试验条件下,渗剂中加入60～80目的20%碳化钨颗粒、40%高铬铸铁粉获得的铸渗层耐磨性能最佳.复合铸渗层适合于小能量冲击磨损的工况条件.