Hydraulic reactivity and cement formation of baghdadite

In this study, the hydraulic reactivity and cement formation of baghdadite (Ca₃ZrSi₂O₉) was investigated. The material was synthesized by sintering a mixture of CaCO₃, SiO₂, and ZrO₂ and then mechanically activated using a planetary mill. This leads to a decrease in particle and crystallite size and a partial amorphization of baghdadite as shown by X-ray powder diffraction (XRD) and laser diffraction measurements. Baghdadite cements were formed by the addition of water at a powder to liquid ratio of 2.0 g/ml. Maximum compressive strengths were found to be ~2 MPa after 3-day setting for a 24-h ground material. Inductively coupled plasma mass spectrometry (ICP-MS) measurements showed an incongruent dissolution profile of set cements with a preferred dissolution of calcium and only marginal release of zirconium ions. Cement formation occurs under alkaline conditions, whereas the unground raw powder leads to a pH of 11.9 during setting, while prolonged grinding increased pH values to approximately 12.3.     

Enhanced strains of Nb-doped BNKT-4ST piezoelectric ceramics via phase boundary and domain design

A strategy that constructs the morphotropic phase boundary and manipulates the domain structure has been used to design the component of 0.96[Bi_0.5(Na_0.84K_0.16)_0.5Ti_(1-x)Nb_xO₃]-0.04SrTiO₃ (BNKT-4ST-100xNb) to enhance the strain properties for actuator application. Non-equivalent Nb⁵⁺ donor doping modulates the phase transition from the mixture of rhombohedral and tetragonal phases to the pseudocubic phase and results in the coexistence of multiple phases. Moreover, the high-resolution TEM confirms the existence of polar nano regions that contribute to the macroscopic relaxor behaviour. The size of the domains is reduced with increasing Nb⁵⁺, resulting in an enhanced relaxor behaviour. The ferroelectric-relaxor transition temperature decreases from 85 to below 30 °C, implying a non-ergodic to ergodic relaxor transition. An improved strain of 0.56% and a giant normalized strain of 1120 pm/V were achieved for BNKT-4ST-1.5Nb, which were attributed to the unique domain structure in which nanodomains are embedded in an undistorted cubic matrix. Ferroelectric, antiferroelectric, and relaxor phases coexist. As the electric field is large enough, a reversible phase transition occurs. Furthermore, good temperature stability was obtained due to the stability of the nanodomains, and no degradation in strains was observed even after 10⁴ cycles, which may originate from the reversible phase transition and dynamic domain wall. The results show that this design strategy offers a reference way to improve the strain behaviour and that BNKT-4ST-100xNb ceramics could be a potential material for high-displacement actuator applications.     

Nacre-Inspired,Liquid Metal-Based Ultrasensitive Electronic Skin by Spatially Regulated Cracking Strategy

The realization of liquid metal-based wearable systems will be a milestone toward high-performance, integrated electronic skin. However, despite the revolutionary progress achieved in many other components of electronic skin, liquid metal-based flexible sensors still suffer from poor sensitivity due to the insufficient resistance change of liquid metal to deformation. Herein, a nacre-inspired architecture composed of a biphasic pattern (liquid metal with Cr/Cu underlayer) as “bricks” and strain-sensitive Ag film as “mortar” is developed, which breaks the long-standing sensitivity bottleneck of liquid metal-based electronic skin. With 2 orders of magnitude of sensitivity amplification while maintaining wide (>85%) working range, for the first time, liquid metal-based strain sensors rival the state-of-art counterparts. This liquid metal composite features spatially regulated cracking behavior. On the one hand, hard Cr cells locally modulate the strain distribution, which avoids premature cut-through cracks and prolongs the defect propagation in the adjacent Ag film. On the other hand, the separated liquid metal cells prevent unfavorable continuous liquid-metal paths and create crack-free regions during strain. Demonstrated in diverse scenarios, the proposed design concept may spark more applications of ultrasensitive liquid metal-based electronic skins, and reveals a pathway for sensor development via crack engineering.     

微波辅助孵育法富集麦胚多肽的工艺优化

目的 麦胚孵育过程中蛋白酶将蛋白质水解成肽和氨基酸，多肽具有明确的生理活性和营养调节作用。本研究以麦胚为试验原料，采用微波辅助预处理的方法，研究孵育的温度、时间、pH及料液比4种因素对孵育后的蛋白酶活力及多肽含量的影响。 方法 通过单因素和响应曲面试验进行工艺条件优化。 结果 与未进行微波辅助预处理的样品相比，微波辅助处理（600 W, 10 s）能显著提高孵育后样品中的蛋白酶酶活力（约9.4倍）和肽含量（约3.1倍）。经过微波辅助处理后，孵育温度为51.5℃、pH为4.0、时间为6.33 h、料液比为1:7时，蛋白酶活力达最高为3826.24 U/g；孵育温度为45.0 ℃、pH为4.8、时间为8 h、料液比为1:7时，肽含量达最高为262.63 mg/g。 结论 微波辅助处理能有效的激活麦胚孵育液中的内源性蛋白酶活性，促进蛋白水解反应，显著提高孵育后的肽含量。该研究结果为麦胚多肽的制备新工艺开发提供了研究基础。     

脱硫胶粉在乳化改性沥青中的应用

考察了不同规格胶粉及不同脱硫程度的脱硫胶粉对橡胶改性乳化沥青性能的影响,结果表明,采用100目胶粉即可制备出橡胶改性乳化沥青,但乳化沥青的性能较差;采用活化度为50%左右的100目脱硫胶粉制备乳化沥青时,脱硫胶粉的用量相比于胶粉可大幅提高;在通过外掺100目50%左右活化度的脱硫胶粉(质量分数15%,以沥青计,下同)和质量分数2%的苯乙烯-丁二烯-苯乙烯嵌段共聚物改性的乳化沥青中添加质量分数1%的丁苯胶乳,所制备橡胶改性乳化沥青无筛上剩余物,5 d储存稳定性为2.9%,蒸发残留物的25℃针入度、软化点和5℃延度分别为55 (0.1 mm)、64.5℃和22.5 cm,能够满足乳化改性沥青的技术指标要求。     

New exact solutions of the Tzitzéica-type equations in non-linear optics using the expa function method

One specific class of non-linear evolution equations, known as the Tzitzéica-type equations, has received great attention from a group of researchers involved in non-linear science. In this article, new exact solutions of the Tzitzéica-type equations arising in non-linear optics, including the Tzitzéica, Dodd–Bullough–Mikhailov and Tzitzéica–Dodd–Bullough equations, are obtained using the exp_a function method. The integration technique actually suggests a useful and reliable method to extract new exact solutions of a wide range of non-linear evolution equations.     

La2O3对SiO2-CaO-Al2O3-MgO熔体黏度和结构的影响

使用分析纯物质模拟微晶玻璃熔体，分别采用柱体旋转法和拉曼光谱技术研究了La2O3含量对SiO2-CaO-Al2O3-MgO熔体黏度和结构的影响规律。结果表明：熔体黏度和黏流活化能随着La2O3含量的增加而降低；拉曼光谱表明La2O3能破坏硅酸盐结构（Qn），随着La2O3含量的增加，Q1、Q2的百分含量增加，Q3的百分含量减小，Q0的百分含量基本不变，表明熔体中非桥氧数量增加，熔体聚合度降低。La2O3在熔体中起网络修饰体的作用。     

Changes in accommodative micro-fluctuations after wearing contact lenses of different optical designs

PurposeAccommodative micro-fluctuations (AMF) are small dioptric changes during accommodation. The aim of this study was to evaluate and compare changes in AMF when wearing silicone hydrogel contact lenses of two different optical designs.MethodsA multi-centre, randomised, cross-over, non-dispensing study was conducted on 68 adapted contact lens wearers aged 25–35 years to compare AMF responses to a spherical and aspheric silicone hydrogel (comfilcon A) lens designs. A Righton Speedy “i” series Auto Refractometer in accommodation analyser mode was utilized before and after reading a standard text in font size 8 on an iPhone 5 for 20 min at a 25 cm viewing distance. Phone screen brightness was set by automatic adjustment mode and ambient illumination was controlled at all sites.ResultsMean ± SD AMF change from before to after the reading task was 2.25 ± 5.6 and 0.13 ± 5.7 (relative values) for the spherical and aspheric lens designs, respectively. The difference was statistically significant (P = 0.017, Paired t-test).ConclusionsThe smaller change in AMF when using an aspheric lens design suggests reduced ciliary muscle stress when reading print on a smart phone at a close distance for short periods (20 min). Contact lens wearers who frequently use digital devices and are experiencing eye strain may benefit from switching from a spherical design to one that incorporates aspheric optics.     

柠檬酸铋合成新工艺研究

针对现有柠檬酸铋制备工艺合成时间长、能耗高、产品纯度不高等不足,介绍了一种常温下制备柠檬酸铋的新工艺。新工艺制备时间短,制备的柠檬酸铋产品质量好,合成过程产生的废水可循环利用,废气经碱液循环吸收可生产硝酸钠副产品。     

Residual strain in cadmium telluride/gallium arsenide (001) heterostructures as a function of temperature

Optical studies of residual strain in cadmium telluride (CdTe) films grown using molecular beam epitaxy on gallium arsenide (GaAs) substrate have been performed using photoreflectance techniques. Measurements have been conducted to determine the fundamental transition energy, heavy-hole and light-hole transition energy critical-point parameters in a range of temperatures between 12 and 300 K. There are problems inherent in the fabrication of optoelectronic devices using high-quality CdTe films, due to strain effects resulting from both the lattice mismatch (CdTe: 14.6%) and the thermal expansion coefficient difference. The CdTe film exhibits compressive stress causing valence-band splitting for light and heavy holes. We have used different models to fit the obtained experimental data and, although the critical thickness for the CdTe has been surpassed, the strain due to the lattice mismatch is still significant. However, the strain due to the thermal expansion is dominant. We have found that the fundamental transition energy, E₀, is affected by the compressive strain and the characteristic values are smaller than those reported. In addition, the total strain is compressive for the full measured range, since the strain due to the lattice mismatch is one order of magnitude higher than that calculated from the thermal expansion.