^153Gd骨密度计源的研制

本文介绍了生产~(153)Gd骨密度计源的原理、工艺和结果。采用天然Eu_2O_3作靶材料,汞阴极电解法分离得的~(153)Gd,经压制、烧结法制成源芯体。源的活度>3.7×10~10Bq,放射性核纯度>99.99%。     

Gd2O2S：Ti的长余辉性能研究及机理探讨

利用高温固相法合成了一种长余辉发光材料Gd2O2S：Ti，利用XRD测试了其结构并测试了其在紫外光激发下的发光特性；停止照射，有橙色的余辉，时间接近2h。分析该磷光体的发光和余辉产生细节，认为空穴和电子的复合导致Ti^3＋的^2E→^2T2的跃迁是产生发光和余辉的原因；并根据缺陷和空位对Gd2O2S：Ti的余辉机理进行探讨，提出了余辉机理模型。     

Fabrication of Gd2O3‐MgO nanocomposite optical ceramics with varied crystallographic modifications of Gd2O3 constituent

The fabrication of Gd₂O₃‐MgO nanocomposite optical ceramics via hot‐pressing using sol‐gel derived cubic‐Gd₂O₃ and MgO nanopowders was investigated. The precursor powder calcined at 600°C had an average particle size of 12 nm. The effects of hot‐pressing temperature on constituent phases, microstructure, mid‐infrared transmittance, and microhardness were studied. The crystallographic modifications of Gd₂O₃ phase varied with the increase in sintering temperature from 1250 to 1350°C. The monoclinic‐Gd₂O₃ phase was retained for the composite sintered at 1350°C and the sample had an average grain size of 90 nm, excellent transmission (80.4%‐84.8%) over 3‐6 μm wavelength range, and enhanced hardness value of 14.1 GPa.     

用攀枝花钛矿和云南钛矿冶炼钛渣工业试验研究

通过磁性测量和X-射线衍射研究了Gd2(Co，Al)17化合物的结构和磁晶各向异性。当x≤4时，样品具有菱方Th2znl7型结构，x=5时，具有六方CaCu5型结构。随着Al浓度增加，晶格常数和单胞体积单调增大，而居里温度和自发磁化强度近似线性地减小；在x≥l时，观察到Co亚点阵的磁晶各向异性变号，室温易磁化方向由易面转变为易轴，且易轴各向异性场和各向异性常数随Al原子浓度增加出现极大值；基于补偿温度(65K)下自由粉末颗粒的磁化曲线，导出了亚点阵间的分子场系数和Gd-co交换耦合常数，结果表明，Al原子对Gd-Co交换耦合作用的影响较小。根据Al原子在Co亚点阵4种晶位的择优占位，分析了磁晶各向异性的演变。     

Ag-Pd-5Ru-Gd四元系部分相图的700℃等温截面

在Ag Pd Gd ,Ag Pd Ru ,Ag Ru Gd和Pd Ru Gd三元系合金相图的基础上 ,采用X射线衍射 ,差热分析、扫描电镜和显微金相分析等方法研究了Ag Pd Ru Gd(x(Ru) =5 % ,x(Gd) <2 5 % )四元系相图的 70 0℃等温截面。结果表明 :该截面上包含有 2个单相区 ,即Pd(Ag)和Pd3 Gd ;4个两相区 ,即Pd(Ag) (Ru) ,Pd(Ag) Pd3 Gd ,(Ru) Ag51Gd14 ,(Ru) Pd3 Gd ;3个三相区 ,即Pd(Ag) Pd3 Gd (Ru) ,Pd(Ag) Ag51Gd14 (Ru) ,Pd3 Gd Ag51Gd14 (Ru) ;1个四相区 ,即Pd(Ag) Pd3 Gd Ag51Gd14 (Ru)。未发现新的四元中间相     

Mg-6Al-1Nd-1.5Gd合金的高温蠕变机制

采用高温蠕变装置,研究了Mg-6Al-1Nd-1.5Gd合金在150、175、200℃以及50、70、90 MPa条件下的高温压缩蠕变行为,分析合金在高温蠕变过程中的蠕变机制。结果表明,Mg-6Al-1Nd-1.5Gd合金的平均应力指数及蠕变激活能分别为4.64和73.87kJ/mol,其主要蠕变机制是由位错攀移和晶界扩散共同作用,合金的蠕变本构方程为:ε=1.877×10-8σ4.641exp[-73 865/(RT)];合金在高温蠕变过程中,微观组织中的位错密度逐渐增大,出现位错缠结及位错堆积,合金蠕变后的晶粒变得粗大,金属间化合物Al3Nd和Al3Gd在晶界上出现偏聚。     

Improving the oxygen permeability of Ba0.5Sr0.5Co0.8Fe0.2O3−δ membranes by a surface-coating layer of GdBaCo2O5+δ

A GdBaCo₂O_5+δ layer was coated on the Ba_0.5Sr_0.5Co_0.8Fe_0.2O_3−δ membranes to enhance their oxygen permeability by employing the fast oxygen adsorption/desorption surface-exchange properties of the GdBaCo₂O_5+δ material. The oxygen flux of the coated and uncoated Ba_0.5Sr_0.5Co_0.8Fe_0.2O_3−δ membranes was measured in the temperature range of 600–850 °C. The results reveal that the oxygen-permeation flux of the Ba_0.5Sr_0.5Co_0.8Fe_0.2O_3−δ membranes coated by a GdBaCo₂O_5+δ layer shows significant enhancement. The GdBaCo₂O_5+δ layer coated on the oxygen desorption side (He side) has much effect than that coated on the oxygen adsorption side (air side). At 850 °C, the oxygen flux with a single coating layer on the air side can rise 16%, while a single coating on the helium side will result into a rise of 23%.     

Gd2O2SO4粉体的合成及其晶体结构确定

通过750℃,2h煅烧Gd2O3和H2SO4(摩尔比1:1)的前驱体方法合成了Gd2O2SO4粉体.利用Gd2O2SO4的X射线粉末衍射数据和Material Studio 4.0 Reflex模块中Powder solve技术和Rietveld精修方法对Gd2O2SO4的晶体结构进行了研究.研究表明:Gd2O2SO4具有空间群为PMNB(62)的正交晶系,晶胞参数为a=1.2996nm,b=0.8117nm,c=0.4184nm,V=0.440698nm3,Z=4,计算密度为6.6949g/cm3,并确定了晶胞中原子的位置,Rietveld精修得到的Rwp=9.15%.     

不同晶相Gd2O3:Eu3+荧光粉的合成与光谱性能

以尿素均相沉淀法和燃烧法相结合,以聚乙二醇(PEG)为表面活性剂,通过调节表面活性剂的用量,分别得到了立方相和单斜相的Gd2O3:Eu3 荧光粉.XRD分析表明,当PEG含量为2.5wt%时,得到了立方相的Gd2O3,当PEG含量为5wt%,350℃时就得到了单斜相的Gd2O3.SEM照片表明立方相Gd2O3:Eu3 荧光粉颗粒为球形,而单斜相Gd2O3:Eu3 荧光粉呈多孔泡末状.发射光谱中立方相和单斜相Gd2O3的最强发射峰分别位于610nm和622 nm附近,对应于Eu3 的5D0→7F2跃迁发射,其谱峰形状和位置均有所不同.激发光谱均由Eu3 的电荷迁移态(CTB),Gd2 的f-f跃迁激发以及Eu3 的f-f高能级跃迁激发峰三部分组成.