锡或锑在无取向电工钢中的研究进展

近年来,在节能减排背景之下,国内外众多研究者对无取向电工钢磁性能的提升做了大量研究。为了探索无取向电工钢磁性能提升的方法,对锡或锑对无取向电工钢磁性能的作用机制(晶粒尺寸和晶体织构的控制)进行分析。基于该作用机制,介绍锡或锑的添加对无取向电工钢磁性能的影响。经研究发现,适量的锡或锑在晶界偏聚,不会阻碍晶界的移动并且致使晶粒尺寸降低;与此同时,锡或锑在晶界偏聚不仅抑制{111}织构在原始晶界处形核及生长,还降低(100)晶粒表面能,促进(100)晶粒生长。因此,适量添加锡或锑,可使无取向电工钢铁损下降、磁感提升。最后结合生产工艺,建议无取向电工钢的研究方向应为稀土含量对高牌号无取向硅钢夹杂物尺寸和数量分布的影响,锡或锑的添加量和常化工艺参数(常化时间、常化温度)对常化晶粒尺寸的影响。     

电感耦合等离子体原子发射光谱法测定云南某矿山锑矿选矿流程样品中锑

锑在现代工业体系中占有重要地位,快速准确测定锑矿中锑含量对锑矿的采选具有重要指导意义。云南某矿山锑矿以萤石为主要伴生矿,现有的盐酸、硝酸、氢氟酸和高氯酸混酸体系无法彻底分解样品,而采用碱熔处理流程长且引入大量基体,均无法满足准确快速测定的要求。选择硫酸-氢氟酸混酸体系分解样品,再用酒石酸-盐酸混合溶液加热浸取,锑完全溶解于溶液中,选择Sb 206.833{463}nm为分析谱线,使用电感耦合等离子体原子发射光谱法(ICP-AES)测定锑。结果表明,锑的质量浓度在5.0～80 μg/mL范围内与其发射强度呈良好的线性关系,校准曲线线性相关系数r=0.999 8;方法的检出限为0.012 μg/mL。按照实验方法对锑矿石成分分析标准物质和锑矿选矿流程样品中锑进行测定,结果的相对标准偏差(RSD,n=5)为0.71%～5.7%;标准物质的认定值和测定值相一致;锑矿选矿流程样品中锑的加标回收率为97%～102%,满足国家地质矿产行业标准DZ/T 0130—2006的要求。     

浸锑石墨摩擦磨损特性研究

为使石墨产品能够应用于高温及重载条件下且能表现出良好的的耐磨性和自润滑性,使用机械加压工艺将熔融锑浸入石墨坯料气孔中制得浸锑石墨复合材料,并对浸渍前后样品的微观结构、摩擦磨损性能进行了研究,评价了浸锑石墨浸渍后磨损量及润滑性能的变化。结果表明,浸锑后磨损量减少96.6%,摩擦因数降低了45%,证明浸锑后石墨材料的摩擦磨损性能有所提高。     

Microstructure and lubrication mechanism of multilayered MoS2/Sb2O3 thin films

Multilayered MoS₂/Sb₂O₃ thin films were prepared by pulsed laser deposition on steel substrates. A rotary multi-target holder was used to switch the laser targets for alternative growth of MoS₂ and Sb₂O₃ layers providing nanometers thickness. The tribological properties of the films were measured in dry and wet environments and the wear scars were observed using a scanning electron microscope. The multilayer films showed a much longer wear life than pure MoS₂ films in wet air tribotests. Focused ion beam and transmission electron microscopies were used to investigate the cross-sectional microstructures of wear scars. Lubricious MoS₂/Sb₂O₃ tribofilms were built up on wear scar surfaces, and produced low friction. Micro-cracks occurred along the interface between the tribofilm and the neighboring/topmost Sb₂O₃ underlayer, where the Sb₂O₃ layer effectively inhibited the crack propagation perpendicular to the interface. The orientation of MoS₂ crystals in as-deposited films was mostly random and friction-induced stress oriented the MoS₂ basal planes parallel to the surface. The reorientation was confined to the topmost MoS₂ layer and was not observed below the first intact Sb₂O₃ layer.     

On the antimony-stabilized cubic structure of potassium/ammonium salts of 12-molybdophosphoric acid and its catalytic performance in the oxidehydrogenation of ethane

Potassium/ammonium salts of 12-molybdophosphoric acid were modified by the addition of an Sb⁵⁺ salt. The addition of antimony led to a remarkable increase in the thermal structural stability of the compounds obtained. The incipient destruction of the Keggin unit in the mixed potassium/ammonium salt of 12-molybdophosphoric acid was shifted from 400–420°C to 500°C. The potassium salt modified by the addition of one Sb⁵⁺ atom per KU decomposed at temperatures higher than 600°C. This property allowed the samples to be used as catalysts for high temperature, gas-phase oxidation reactions, such as the oxidehydrogenation of ethane. The compounds did not undergo structural decomposition at temperatures as high as 540°C under reaction conditions, but were poorly active and selective in ethylene formation. Therefore, antimony-stabilized compounds were further modified by the addition of transition metal ions in order to improve the catalytic performance. The addition of small amounts of iron, chromium and cerium ions led to an improvement of the catalytic performance; the compound was apparently monophasic, and characterized by the cubic crystalline structure typical of the salts of 12-molybdophosphoric acid.On leave from the Institute of Chemical Physics, Academy of Sciences, Russia.     

Formation of Zinc–Antimony-Based Spinel Phases

Formation of spinel phases in ZnO–Sb₂O₃and ZnO–Sb₂O₃–Bi₂O₃systems is studied by the use of X-ray diffraction. The formation of nonstoichiometric Zn_2.33Sb_0.67O₄phase is observed in both the systems at ∼900°C. However, in these systems, at higher temperatures ( T ≥ 1100°C), formation of the inverse spinel phase Zn₇Sb₂O₁₂is observed. The study has been extended to understand the effect of CrO₃doping on the stability of the different spinel phases in the previously mentioned systems. Interestingly, in both the systems, samples doped with CrO₃, displayed the presence of Zn_2.33Sb_0.67O₄phase <1200°C, indicating the stabilization of the spinel phase by CrO₃.     

三(苄基硫醇)锑的合成及其应用性能

以苄基硫醇、三氧化二锑 (或三氯化锑 )等为原料 ,研究了三 (苄基硫醇 )锑的最佳合成工艺条件 ,产率分别达到 90 %和 95 %。用元素分析法及红外光谱技术对产品进行了表征 ,热分析技术 (TG和DSC)研究表明 ,含合成产物的聚氯乙烯 (PVC)制品的初始分解温度在 2 2 0℃以上 ,其热分解效应为 1 1 5 5J/g。热老化研究表明 ,当合成产物添加量达 1 5份 (PVC质量为 1 0 0份 )时 ,PVC树脂的热稳定时间为 1 8min(2 0 0℃ ) ,当其与硫醇钡以质量比 3∶1复配时 ,可显著提高PVC制品的长期热稳定性     

含锑金精矿碱性硫化钠浸出锑研究与工业实践

为了回收含锑金精矿中的锑，减少锑对两段焙烧过程的影响，对浮选富集得到的含锑金精矿进行硫化钠碱性浸出锑研究。优化实验表明，在液固比1.5:1 (mL/g)，氢氧化钠用量20 g/L，硫化钠用量40 g/L，反应温度80℃，浸出30 min，锑浸出率可达98%以上。在此基础上，采用焙烧炉余热将电解贫液加温至80℃，对液固分离方式、锑电积阴阳极板和冷冻结晶装置进行工艺改造，使锑的浸出率>98%、阴极锑纯度>95%，日产锑量增加17.35%。     

Preparation of ultrafine Sb_2O_5 composite powder

ＰＲＥＰＡＲＡＴＩＯＮＯＦＵＬＴＲＡＦＩＮＥＳｂ＿２Ｏ＿３－Ｓｂ＿２Ｏ＿５ＣＯＭＰＯＳＩＴＥＰＯＷＤＥＲＤｕａｎ，Ｘｕｅｃｈｅｎ；Ｚｈａｏ，Ｔｉａｎｃｏｎｇ（ＤｅｐａｒｔｍｅｎｔｏｆＮｏｎｆｅｒｅｒｒｏｕｓＭｅｔａｌｌｕｒｇｙ．ＣｅｎｔｒａｌＳｏｕｔ...     

锂离子电池锑基负极材料研究进展

锑具有首次嵌／脱锂容量大等优点，是制备大容量高安全性锂离子电池负极潜在的优良材料。本文介绍了此系列材料的制备方法、特性及其用途。