综合运用植物模板法和溶胶-凝胶法制成具有藤天然生物形态的45S5玻璃陶瓷。用X射线衍射（X-ray diffraction,XRD）仪、Fourier红外光谱仪（Fourier transform infraredspectroscopy,FTIR）和扫描电子显微镜（scanning electron microsco...     

烧结条件对溶胶凝胶法制备氧化锆陶瓷纤维微观结构的影响

利用溶胶凝胶纺丝法制备了Al2O3-3Y-TZP及3Y-TZP凝胶纤维,并在工业N2中预处理后高温烧结,用SEM等分析方法考察了5wt%Al2O3添加剂、氮气预处理、烧结温度、保温时间及升温速率对纤维的微观结构的影响。结果表明:采用慢速升温可以避免裂纹等缺陷出现,加入Al2O3和N2气氛预烧结处理后,可以抑制纤维晶粒的快速生长。     

Ag/AgBr/TiO2/AC复合光催化剂的制备及其性能研究

针对TiO2光催化剂目前在实际应用中所面临的可见光利用率低及悬浮体系中光催化剂易失活、难回收的问题,我们将TiO2的改性与固定结合,首先利用溶胶-凝胶方法将TiO2光催化剂负载在多孔性载体活性炭上,然后再通过沉积-沉淀法将AgBr沉积于TiO2表面,得到最终产物Ag/AgBr/TiO2复合物光催化剂,同时利用溶胶-凝胶法在相同条件下合成纯TiO2。通过XRD、SEM和光催化降解次甲基蓝溶液来对比两者的性能。结果显示Ag/AgBr/TiO2/AC具有较好的可见光催化活性,三小时内次甲基蓝溶液的降解率达81.63%,而纯TiO2三小时内只降解了15.74%。     

基于SG法制备SiO2光纤预制棒干胶的研究

SiO2光纤预制棒是制备通信光纤的母体材料,为制备性能优良且价格低廉的SiO2光纤预制棒芯棒,本文以正硅酸乙酯和水为主要原料,乙醇为溶剂,HCl和NH3·H2O为催化剂,甲酰胺为添加剂,采用溶胶-凝胶工艺,且在不同温度(50,60,70,75,80,90℃)下经热处理制得SiO2干胶.讨论了不同摩尔比的水/正硅酸乙酯、...     

氮掺杂二氧化钛光催化降解甲基橙的研究

采用溶胶-凝胶法制备了N-TiO2多孔材料,用XRD,SEM对材料进行了结构和性能的表征,同时研究了材料对甲基橙的光降解性能.结果表明,所合成的N-TiO2是锐钛矿型,N元素进入了TiO2骨架,且样品为多孔结构;N-TiO2多孔材料对甲基橙溶液的紫外光降解2.5h可达81.7％,适当曝气可有效提高降解率.     

超临界C02干燥法工艺条件对氧化锆气凝胶结构性质的影响

以无机盐ZrOCl2·8H2O为原料,采用溶胶-凝胶过程结合超临界CO2干燥法制备了ZrO2气凝胶.采用BET、TG/DTA、XRD、TEM以及SEM等手段对样品进行了表征分析.考察了超临界CO2干燥过程中,操作压力、操作温度、CO2流率及干燥时间等工艺条件对样品比表面积、孔性质等的影响.结果表明利用本方法制备的ZrO...     

溶胶-凝胶法合成的Fe-Al氧化物纳米复合磁性颗粒

利用溶胶-凝胶法合成了Fe-Al氧化物纳米复合磁性颗粒.X射线衍射(XRD)分析表明,合成的产物为多相Fe-Al氧化物纳米复合磁性颗粒.利用振动样品磁强计(VSM)测量了所制得样品的磁化曲线,并由此得出了样品的饱和磁化强度和矫顽力.实验结果表明,在同一热处理温度下,当样品中Fe元素与Al2O3的质量比越大,所制得的Fe...     

Luminescence properties of red-emitting Ca<Subscript>2</Subscript>Al<Subscript>2</Subscript>SiO<Subscript>7</Subscript>:Eu<Superscript>3+</Superscript> nanoparticles prepared by sol-gel method

A series of red-emitting Ca2-xAl2SiO7:xEu3+(x = 1 mol.%-10 mol.%) phosphors were synthesized by the sol-gel method.The effects of annealing temperature and doping concentration on the crystal structure and luminescence properties of Ca2Al2SiO7:Eu3+ phosphors were investigated.X-ray diffraction(XRD) profiles showed that all peaks could be attributed to the tetragonal Ca2Al2SiO7 phase when the sample was annealed at 1000℃.Scanning electron microscopy(SEM) micrographs indicate that the phosphors have an irregularly rounded morphology with particles of about 200 nm.Excitation spectra showed that the strong broad band at around 258 nm and weak sharp lines in 350-490 nm were attributed to the charge transfer band of Eu3+-O2-and f-f transitions within the 4f6 configuration of Eu3+ ions,respectively.Emission spectra implied that the red luminescence could be attributed to the transitions from the 5D0 excited level to the 7FJ(J = 0,1,2,3,4) levels of Eu3+ ions with the main electric dipole transition 5D0→7F2(618 and 620 nm),and Eu3+ ions prefer to occupy a lower symmetry site in the crystal lattice.Moreover,the photoluminescence(PL) intensity was strongly dependent on both the sintering temperature and doping concentration,and the highest PL intensity was observed at an Eu3+ concentration x = 7 mol.% after annealing at 1100℃.The obtained Ca2Al2SiO7:Eu3+ phosphor may have potential application for the red lamp phosphor.     

有机硅/二氧化硅杂化涂层抗原子氧侵蚀性能研究

采用溶胶-凝胶法,以一甲基三乙氧基硅烷(MTES)和正硅酸乙酯(TEOS)为原料,乙醇为溶剂,盐酸为催化剂,通过溶胶-凝胶法制备出分子级复合的SiO2杂化有机硅树脂,浸涂在聚酰亚胺表面干燥后获得了透明致密的涂层。采用自己研制的空间综合环境地面模拟设备对试样进行了原子氧暴露实验。测试表明,溶胶-凝胶制备的有机硅/SiO2涂层抗原子氧侵蚀性能优异,抗原子氧侵蚀性能比聚酰亚胺基体提高了2个数量级以上。经AO暴露后的杂化涂层质量几乎没有发生变化。经FTIR和XPS分析表明,在原子氧暴露后涂层表面产生的是SiO2陶瓷层。SEM分析表明无涂层的聚酰亚胺原子氧暴露后表面非常粗糙,表面呈现地毯状形貌而涂覆涂层试样暴露前后表面形貌没有发生变化。采用紫外-可见光-近红外分光光度计对涂覆有机硅/SiO2涂层试样分析表明,原子氧暴露前后试样表面的光学性能也未发生变化。实验证明,制备抗原子氧侵蚀的防护涂层的溶胶-凝胶法是一种行之有效的方法。     

TiO2超疏水膜的制备及影响因素

采用溶胶-凝胶法于金属基片上制备了TiO2膜,经表面修饰低表面能物质1H,1H,2H,2H-十七氟癸基三甲氧基硅烷(FAS)后,呈现良好的超疏水性能,通过实验优化确定了最佳实验条件,得到最佳TiO2超疏水表面,其与水的接触角达到173.7°。并研究了聚乙二醇(PEG)含量、TiO2纳米粒子含量和烧结温度和时间对超疏水性能的影响。