Review: the latest advances in biomedical applications of chitosan hydrogel as a powerful natural structure with eye-catching biological properties

Journal of Materials Science - Chitosan is one of the natural cationic polymers with unique properties such as non-toxicity, biodegradability, biocompatibility, environmentally friendly that has...     

Compressive strength and wear properties of SiC/Al6061 composites reinforced with high contents of SiC fabricated by pressure-assisted infiltration

Pressure-assisted infiltration was used to synthesize SiC/Al 6061 composites containing high weight percentages of SiC. A combination of PEG and glass water was used to fabricate SiC preforms and the effect of the presence of glass water on the microstructure and mechanical properties of the preforms was evaluated by performing compression tests on the preforms. Also, the compressive strength and the hardness of the SiC/Al composites were investigated. The results revealed that the glass water improved the compressive strength of the preforms by about five times. The microstructural characterization of the composites showed that the penetration of the aluminum melt into the preforms was completed and almost no porosity could be seen in the microstructures of the composites. Moreover, the composite containing 75 wt% SiC exhibited the highest compressive strength as well as the maximum hardness. The results of the wear tests showed that increasing the SiC content reduces the wear rate so that the Al-75 wt% SiC composite has a lower wear rate and a lower coefficient of friction than those of Al-67 wt% SiC composite. This indicated higher wear resistance in these composites than the Al alloy due to the formation of a tribological layer on the surface of the composites.     

Hydrogenases, accessory genes and the regulation of [NiFe] hydrogenase biosynthesis in Thiocapsa roseopersicina

The purple (Sulphur) phototrophic bacterium, Thiocapsa roseopersicina BBS contains several [NiFe] hydrogenases, of which two are membrane bound. Mutant T. roseopersicina cells, carrying deletions in both gene clusters showed hydrogenase activity. This activity was located in the cytoplasm. The structural gene cluster hoxEFUYH was identified and sequenced. In addition, genes homologous to hupUV/hoxBC, the hydrogen sensing hydrogenase have been identified and sequenced.Regulation of hydrogenase biosynthesis was studied in detail for HydSL (renamed HynSL). A random mutagenesis system was optimised for T. roseopersicina. One of the mutations was in a gene similar to that coding for the HypF proteins in other organisms. Inactivation of the hypF gene resulted in a 60-fold increase in hydrogen evolution under nitrogen fixing conditions. In addition to hypF, the following accessory genes were identified: hydD, hupK, hypC1, hypC2, hypDE. Characterisation of the corresponding gene products and search for additional accessory genes are in progress.     

Second-order filter response with series-coupled silica microresonators

We have demonstrated an approach for fabricating a photonic filter with second-order response function. The filter consists of two germania-doped silica microtoroidal or microspherical resonators cascaded in series. We use ultraviolet irradiation to tune the mode of one microcavity to bring it close to the mode of the second microcavity. This approach produces a filter function with much sharper rolloff than can be obtained with the individual microresonators.     

Design,Facile Synthesis and Characterization of Porphyrin-Zirconium-Ferrite@SiO2 Core-Shell and Catalytic Application in Cyclohexane Oxidation

Silicon - In this study, a new magnetic ZrFe2O4@SiO2-TCPP nanocatalyst with high efficiency was used for the oxidation of cyclohexane to cyclohexanone (Ke) and cyclohexanol (Al). The mesoporous...     

Colour and COD removal from textile effluent by coagulation and advanced oxidation processes

The aim of this study was to compare the performance of coagulation, Fenton's oxidation (Fe²⁺/H₂O₂) and ozonation for the removal of chemical oxygen demand (COD) and colour from biologically pretreated textile wastewater. FeSO₄ and FeCl₃ were used as coagulants at varying doses and varying colour removal efficiency was measured. For the Fenton process, COD and colour removal efficiencies were found to be 78% and 95% for the Fenton process, and to be 64% and 71% for the Fenton-like process (Fe³⁺/H₂O₂), respectively. Ozonation experiments were conducted at different initial pH values and fixed ozone doses. Ozonation resulted in 43% COD and 97% colour removal whereas these rates increased to 54% and 99% when 5 mg/l hydrogen peroxide was added to the wastewater before ozonation at the same dose. The operating costs of all proposed treatment systems were also evaluated in this study.     

Study on the performance of Cd2+ sorption using dimethylethylenediamine-modified zinc-based MOF (ZIF-8-mmen): optimization of the process by RSM technique

ABSTRACT

Cadmium as a highly toxic metal is released into the environment through paper production, metal processing, phosphate fertilizers, insecticides, and treatment of wastewater. Cadmium also inhibits the body activities and is very toxic for kidney and other organisms. In the current study, zinc-based metal–organic framework, zeolitic imidazolate framework (ZIF)-8, was synthesized and modified by dimethylethylenediamine (ZIF-8-mmen) for the removal of cadmium. To optimize the experiments, response surface methodology was applied with three variables including pH, adsorbent dosage, and contact time using central composite design. The optimum conditions for pH, dosage, and time were 2, 0.1 g, and 89 min, respectively, with removal efficiency of 85.38%. The Langmuir isotherm (q _m = 1000 mg/g) indicates the monolayer adsorption. The kinetic studies reveal that the Lagergren model was predominant and cadmium was not chemisorbed. Thermodynamic parameters show spontaneous, endothermic, and physisorption processes.     

Effect of microwave sintering on the microstructure and electrical properties of low-voltage ZnO varistors

Coarse-grained ZnO varistors for low-voltage applications were prepared by microwave sintering technique under different soaking times of 5–150?min. For comparison, a low-voltage ZnO varistor was also prepared through a conventional sintering process. Microwave sintering remarkably enhanced the grain growth rate of ZnO varistors. Average grain size of the sample prepared by microwave sintering in 15?min was about 20?µm, which is similar to the grain size of sample prepared conventionally in 150?min time. In addition to grain growth, an increase in microwave sintering time led to precipitation of zinc titanate (Zn₂TiO₄) on the top surface of samples which sintered for long dwell times. X-ray diffraction and scanning electron microscopy results from different points of the samples declared that precipitation of Zn₂TiO₄ phase is due to the high rate of bismuth evaporation of Bi-rich liquid from top surface and the reaction between remaining titanium ions on the surface with ZnO. The results showed that increasing sintering time from 5 to 150?min increased the grain size from 14 to 33?µm, consequently, the breakdown field decreased from 90 to 27?V/mm, respectively. These changes led to a switch in the varistor application, from low to very low voltage.