Dense pressure-sintered reaction-bonded Si₃N₄ (PSRBSN) ceramics were obtained by a hot-press sintering method. Precursor Si powders were prepared with Eu₂O₃–MgO–Y₂O₃ sintering additive. The addition of Eu₂O₃–MgO–Y₂O₃ was shown to promote full nitridation of the Si powder. The nitrided Si₃N₄ particles had an equiaxial morphology, without whisker formation, after the Si powders doped with Eu₂O₃–MgO–Y₂O₃ were nitrided at 1400 °C for 2 h. After hot pressing, the relative density, Vickers hardness, flexural strength, and fracture toughness of the PSRBSN ceramics, with 5 wt% Eu₂O₃ doping, were 98.3 ± 0.2%, 17.8 ± 0.8 GPa, 697.0 ± 67.0 MPa, and 7.3 ± 0.3 MPa m^1/2, respectively. The thermal conductivity was 73.6 ± 0.2 W m^?1 K^?1, significantly higher than the counterpart without Eu₂O₃ doping, or with ZrO₂ doping by conventional methods.     

Effects of upholstery materials on the burning behavior of real‐scale residential upholstered furniture mock‐ups

Fire spread and growth on real‐scale four cushion mock‐ups of residential upholstered furniture (RUF) were investigated with the goal of identifying whether changes in five classes of materials (barrier, flexible polyurethane foam, polyester fiber wrap, upholstery fabric, and sewing thread), referred to as factors, resulted in statistically significant changes in burning behavior. A fractional factorial experimental design plus practical considerations yielded a test matrix with 20 material combinations. Experiments were repeated a minimum of two times. Measurements included fire spread rates derived from video recordings and heat release rates (HRRs). A total of 13 experimental parameters (3 based on the videos and 10 on the HRR results), referred to as responses, characterized the measurements. Statistical analyses based on Main Effects Plots (main effects) and Block Plots (main effects and factor interactions) were used. The results showed that three of the factors resulted in statistically significant effects on varying numbers of the 13 responses. The Barrier and Fabric factors had the strongest main effects with roughly comparable magnitudes. Foam was statistically significant for fewer of the responses and its overall strength was weaker than for Barrier and Fabric. No statistically significant main effects were identified for Wrap or Thread. Multiple two‐term interactions between factors were identified as being statistically significant. The Barrier*Fabric interaction resulted in the highest number of and strongest statistically significant effects. The existence of two‐term interactions means that it will be necessary to consider their effects in approaches designed to predict the burning behavior of RUF.     

Effects of the joining process on the microstructure and properties of liquid-phase-sintered SiC-SiC joints formed with Ti foil

The joining of liquid-phase sintered SiC (LPS-SiC) ceramics was conducted using spark plasma sintering (SPS), through solid state diffusion bonding, with Ti-metal foil as a joining interlayer. Samples were joined at 1400 °C, under applied pressures of either 10 or 30 MPa, and with different atmospheres (argon, Ar, vs. vacuum). It was demonstrated that the shear strength of the joints increased with an increase in the applied joining pressure. The joining atmosphere also affected on both the microstructure and shear strength of the SiC joints. The composition and microstructure of the interlayer were examined to understand the mechanism. As a result, a SiC-SiC joining with a good mechanical performance could be achieved under an Ar environment, which in turn could provide a cost-effective approach and greatly widen the applications of SiC ceramic components with complex shape.     

Environmental effects on the strength and impact damage resistance of alumina based oxide/oxide ceramic matrix composites

In this study the effects of high temperature and moisture on the impact damage resistance and mechanical strength of Nextel 610/alumina silicate ceramic matrix composites were experimentally evaluated. Composite laminates were exposed to either a 1050°C isothermal furnace-based environment for 30 consecutive days at 6 h a day, or 95% relative humidity environment for 13 consecutive days at 67°C. Low velocity impact, tensile and short beam strength tests were performed on both ambient and environmentally conditioned laminates and damage was characterized using a combination of non-destructive and destructive techniques. High temperature and humidity environmental exposure adversely affected the impact resistance of the composite laminates. For all the environments, planar internal damage area was greater than the back side dent area, which in turn was greater than the impactor side dent area. Evidence of environmental embrittlement through a stiffer tensile response was noted for the high temperature exposed laminates while the short beam strength tests showed greater propensity for interlaminar shear failure in the moisture exposed laminates. Destructive evaluations exposed larger, more pronounced delaminations in the environmentally conditioned laminates in comparison to the ambient ones. External damage metrics of the impactor side dent depth and area directly influenced the post-impact tensile strength of the laminates while no such trend between internal damage area and residual strength could be ascertained.     

Interlaced layer thicknesses within single laser powder bed fusion geometries

The geometrical design freedoms associated with additive manufacturing techniques are currently well exploited and finding commercial application. The capability of layer-based processes to allow modification of composition and microstructure in process to achieve functional grading is currently a growing topic. In this work, a method is demonstrated for varying layer thickness within single components that allows part sections to be interlaced for the purpose of locally manipulating material and structural properties. Demonstrator geometries are explored here which exhibit the interfaces within specimens constituted of both 30 µm and 150 µm. Accordingly, a new design freedom for laser powder bed fusion is created.     

Cold plasma for the disinfection of industrial food-contact surfaces: An overview of current status and opportunities

Food safety is the primary goal for food and drink manufacturers. Cleaning and disinfection practices applied to the processing environment are vital to maintain this safety; yet, current approaches can incur costly downtime and the potential for microorganisms to grow and establish, if not effectively removed. For that reason, manufacturers are seeking nonthermal, online, and continuous disinfection processes to control the microbial levels within the processing environment. One such emerging technique, with great potential, is cold atmospheric pressure plasma (CAP). This review presents the latest advances and challenges associated with CAP-based technologies for the decontamination of surfaces and equipment found within the food-processing environment. It provides a detailed overview of the technology and a comprehensive analysis of the many CAP-based antimicrobial studies on food-contact surfaces and materials. As CAP is considered an emerging technique, many of the recent studies are still in the preliminary stages, with results obtained under widely different conditions. This lack of cohesive information and an inability to directly compare CAP systems has greatly impeded technological development. The review further explores the challenge of scaling CAP technology to meet industry needs, considering aspects such as regulatory constraints, environmental credentials, and cost of use. Finally, a discussion is presented on the future outlook for CAP technology in this area, identifying key challenges that must be addressed to promote industry uptake.     

东北地区传统发酵食品中两株植物乳杆菌的安全性评价

针对已分离的植物乳杆菌L12和L20通过体外和体内两种方法进行安全性评价。通过体外实验测定乳酸水解活性抗生素敏感性，胆盐水解酶活性，D-乳酸含量，γ溶血等指标；体内实验是对小鼠进行短期口服毒性的研究，口服0.2 mL（109 CFU/mL）的实验性细菌溶液30 d。结果表明，体外实验中，两株菌株均具有良好的抗氧化活性，对抗生素敏感性高，胆盐水解酶活性高，D-乳酸含量低，γ溶血；体内实验中灌胃给药对治疗小鼠的生长、行为、摄食量、器官重量或组织病理学分析均无不良影响。与对照组相比，益生菌组小鼠血清MDA浓度和肝脏GSH含量差异有统计学意义(P<0.05)。这些结果表明，菌株L12和L20是非致病性的，人直接食用是安全的。