快淬纳米晶/非晶Mg2Ni1-xMnx(x=0～0.4)合金电极的电化学性能

用快淬工艺制备了纳米晶和非晶Mg2Ni型Mg2Ni1-xMnx(x=0、0.1、0.2、0.3、0.4)合金,获得长度连续,厚度约为30μm,宽度约为25mm的薄带.用XRD、HRTEM分析了快淬合金薄带的微观结构,测试了合金薄带的电化学性能及电化学交流阻抗谱(EIS),测试了电位阶跃后的阳极电流-时间相应曲线,并计算...     

An investigation on electrochemical hydrogen storage performances of Mg-Y-Ni alloys prepared by mechanical milling

The nanocrystalline and amorphous Mg2Ni-type electrode alloys with a composition of Mg20?xYxNi10 (x=0, 1, 2, 3 and 4) were fabricated by mechanical milling. Effects of Y content on the structures and e...     

Structures and electrochemical performances of La_(0.75-x)Zr_xMg_(0.25)Ni_(3.2)Co_(0.2)Al_(0.1) (x=0-0.2) electrode alloys prepared by melt spinning

The La-Mg-Ni system A2B7-type electrode alloys with nominal composition La0.75-xZrxMg0.25Ni3.2Co0.2Al0.1(x=0,0.05, 0.1,0.15,0.2)were prepared by casting and melt-spinning.The influences of melt spinning on the electrochemical performances as well as the structures of the alloys were investigated.The results obtained by XRD,SEM and TEM show that the as-cast and spun alloys have a multiphase structure,consisting of two main phases(La,Mg)Ni3 and LaNi5 as well as a residual phase LaNi2.The melt spinning leads to an obvious increase of the LaNi5 phase and a decrease of the(La,Mg)Ni3 phase in the alloys.The results of the electrochemical measurement indicate that the discharge capacity of the alloys(x≤0.1)first increases and then decreases with the increase of spinning rate,whereas for x0.1,the discharge capacity of the alloys monotonously falls.The melt spinning slightly impairs the activation capability of the alloys,but it significantly enhances the cycle stability of the alloys.     

快淬对La-Mg-Ni系A_2B_7型电极合金循环稳定性的影响

用熔体快淬工艺制备了La-Mg-Ni系A2B7型La0.75-xZrxMg0.25Ni3.2Co0.2Al0.1（x=0,0.05,0.1,0.15,0.2）电极合金。用XRD、SEM、TEM分析了铸态及快淬态合金的微观结构,用程控电池测试设备测试了铸态及快淬态合金电极的电化学循环稳定性,研究了快淬工艺对合金结构及电化学循环稳定性的影响,探讨了电极合金的失效机理。结果表明,快淬态合金均具有多相结构,包括两个主相（La,Mg）Ni3及LaNi5和一个残余相LaNi2。快淬处理可以显著改善合金的电化学循环稳定性。导致合金失效的主要原因是电极表面被电解液剧烈腐蚀以及合金电极在电化学循环过程中的粉化。     

Co替代Ni对快淬纳米晶/非晶Mg_2Ni型合金吸放氢动力学的影响

为了改善Mg2Ni型合金的吸放氢动力学性能,用Co部分替代合金中的Ni。用快淬工艺制备了纳米晶和非晶Mg20Ni10-xCox(x=0,1,2,3,4)贮氢合金,分析了铸态及快淬态合金的微观结构,测试了合金的吸放氢动力学性能。研究了Co替代Ni及快淬工艺对合金吸放氢动力学性能的影响。结果表明,在快淬合金(x=0)中没有发现非晶相,但快淬合金(x=4)显示了纳米晶/非晶结构,表明Co替代Ni提高了Mg2Ni型合金的非晶形成能力。Co替代Ni不改变合金的Mg2Ni主相,但形成了第二相MgCo2。随Co替代量的增加,合金的吸氢量先增加而后减少,但其放氢量随Co替代量的增加而单调增加。     

Influences of stoichiometric ratio B/A on structures and electrochemical behaviors of Lao.75Mg0.25Ni3.5Mx （M=Ni,Co; x=0-0.6） hydrogen storage alloys

In order to investigate the influences of the stoichiometric ratio ofB/A （A： gross A-site elements, B： gross B-site elements） and the substitution of Co for Ni on the structures and electrochemical performances of the AB3.5-4.1-type electrode alloys, the La-Mg-Ni-Co system La0.75Mg0.25Ni3.5Mx （M=Ni, Co; x= 0, 0.2, 0.4, 0.6） alloys were prepared by induction melting in a helium atmosphere. The structures and electrochemical performances of the alloys were systemically measured. The results show that the structures and electrochemical performances of the alloys are closely relevant to the B/A ratio. All the alloys exhibit a multiphase structure, including two major phases, （La, Mg）2Ni7 and LaNis, and a residual phase LaNi2, and with rising ratio B/A, the （La,Mg）2Ni7 phase decreases and the LaNi5 phase increases significantly. When ratio B/A-3.7, the alloys obtain the maximum discharge capacities. The high rate discharge（HRD） capability of the alloy （M=Ni） monotonously rises with growing B/A ratio, but that of the alloy （M=Co） first mounts up then declines. The cycle stability of the alloy （M-Co） monotonously increases with rising B/A ratio, but it first decreases slightly then increases for the alloy （M=Ni）. The discharge potential of the alloy （M=Ni） declines with increasing B/A ratio （x〉0.2）, but for the alloy （M-Co）, the result is contrary. The substitution of Co for Ni significantly ameliorates the electrochemical performances. For a fixed ratio B/A=3.7, the Co substitution enhances the discharge capacity from 365.7 to 401.8 mA.h/g, the capacity retention ratio （S100） after 100 charging-discharging cycles from 50.32% to 53.26% and the HRD from 88.65% to 90.69%.     

快淬 TiZrVMnNi 贮氢合金的电化学性能研究

对比研究了熔体旋转和常规铸态Ti0 .8Zr0 .2 Mn0 .5V0 .5Ni1.0 贮氢合金的电化学特性。发现快淬态与铸态合金的活化性能都很好 ,经过 1～ 3次充放电循环 ,就可达到最大放电容量。快淬工艺明显提高了合金的放电容量 ,并且淬速与放电容量之间在一定情况下出现峰值。快淬工艺同时改善合金的放电电压特性 ,使合金的放电平台更平 ,平台电压更高。但是快淬钛基贮氢合金的循环稳定性能和铸态合金一样差 ,放电容量在 10次内急剧衰减。     

硼对低钴AB5型贮氢合金循环寿命的影响

为了提高低钴AB5型贮氢合金的电化学循环稳定性，在低钴AB5型贮氢合金中加入微量的硼，用真空快淬工艺制备了稀土系低钴AB5型MmNi3.8Co0.4Mn0.6Al0.2Bx(x=0，0．1，0．2，0．3，0．4)贮氢合金，分析测试了铸态及快淬态合金的电化学性能及微观结构，研究了硼对铸态及快淬态合金微观结构及循环寿命的影响。结果表明，硼能大幅度提高铸态及快淬态低钴AB5型贮氢合金的电化学循环稳定性，但其作用机理是完全不同的。     

Ni50Mn27Ga23快淬薄带的马氏体相变和磁感生应变

采用快淬技术制各了非化学计量成分的Ni50Mn27Ga23多晶薄带，对快淬薄带的马氏体相变和磁感生应变进行了研究。结果表明，快淬薄带侄冷却和加热过程中仍然发牛热弹性马氏体相变及逆相变，具有典型的热弹性形状记忆效应，并且比铸态合金具有更大的应变，但是马氏体相变温度下降。快淬工艺在合金内部引入特定的内应力，使薄带形成织构，是合金获得更大相变应变和磁感卞应变的原因。热处理后，内应力大大降低，导致磁感牛应变降低。     

钎焊及钛基钎焊料的发展及应用

本文介绍了钎焊及钛基钎焊料的发展及其应用。对钎焊的特点及钎焊料应具备的性能进行了较为全面的论述。对不同状态钎焊料的性能特点进行了全面的比较，特别是对在航天、航空领域广泛应用的非晶钛基钎焊料进行了重点介绍。