Influence of SiC microstructure on its corrosion behavior in molten FLiNaK salt

The influence of the microstructure on the corrosion rate of three monolithic SiC samples in FLiNaK salt at 900 °C for 250 h was studied. The SiC samples, labeled as SiC-1, SiC-2, and SiC-3, had corrosion rates of 0.137, 0.020, and 0.043 mg/cm²h, respectively. Compared with grain size and the presence of special grain boundaries (i.e., Σ3), the content of high-angle grain boundaries (HAGBs) appeared to have the strongest influence on the corrosion rate of SiC in FLiNaK salt, since the corrosion rate increased six times as the concentration of high-angle grain boundaries increased from 19 to 32% for SiC-2 and SiC-1, respectively. These results stress the importance of controlling the content of HAGBs during the production process of SiC.     

Adsorption of the IFKhAN-92 Inhibitor on Chromium–Nickel Steel from Mineral Acid Solutions

Protection of Metals and Physical Chemistry of Surfaces - Impedance spectroscopy was used to study the adsorption of the IFKhAN-92 inhibitor, a triazole derivative, on cathodically polarized...     

Various Types of Combustion of a Ti + C Granular Mixture with a Different Content of the Gasifying Additive

Combustion, Explosion, and Shock Waves - This paper touches upon the effect of a polyvinyl butyral content (0–2.3%) on the combustion of a Ti + C granular...     

Low/intermediate temperature pyrolyzed polysiloxane derived ceramics with increased carbon for electrical applications

This study focuses on the chemistry, thermal stability, and electrical conductivity of low/intermediate pyrolysis temperature (700?900 °C) polysiloxane derived ceramics. These ceramics were modified with additional carbon derived from divinylbenzene (DVB) added to the precursor. Their electrical properties were investigated for potential uses in micro-electrical mechanical systems (MEMS) and anodes for lithium batteries. The microstructure and chemical composition was investigated by attenuated total reflectance Fourier transform infrared spectroscopy (ATR-FTIR), Raman spectroscopy, and x-ray photoelectron spectroscopy (XPS); thermogravimetric analysis (TGA) provided insight into the thermal stability; and electrochemical impedance spectroscopy (EIS) into the electrical properties of the material. The increase of pyrolysis temperature and carbon content lead to an enhancement of the electrical conductivity, higher than previously reported values for intermediate pyrolysis temperature SiOC polymer derived ceramics. A limit of the amount of DVB that can be added to PHMS to produce a hybrid precursor has also been obtained.     

Microstructure induced ultra-high energy storage density coupled with rapid discharge properties in lead-free Ba0.9Ca0.1Ti0.9Zr0.1O3–SrNb2O6 ceramics

Novel lead-free (1-x)Ba_0·9Ca_0·1Ti_0·9Zr_0·1O₃-xSrNb₂O₆ ceramics were synthesized via a two-step high energy ball milling process. The evolution of microstructural properties, phase transformation, and energy storage characteristics was comprehensively investigated to assess the applicability of material in multi-layered ceramic capacitors. The substitution of SrNb₂O₆ (SNO) in Ba_0·9Ca_0·1Ti_0·9Zr_0·1O₃ (BTCZ) has resulted in substantial improvement in materials density along with a small increase in the grain size of the synthesized ceramic. A thorough microstructural investigation indicates an excellent dispersibility and compatibility between BTCZ and SNO phases. With an increase in SNO substitution, a transition from typical ferroelectric to relaxor ferroelectric has been observed, which has led to a significantly slimmer ferroelectric loop along with frequency dispersive dielectric properties. The optimized composition (i.e., x = 0.10) exhibits an ultra-high recoverable energy density of 2.68 J/cm³ along with a moderately high energy efficiency of 83.4%. Further, SNO substituted samples have also shown an enhancement in breakdown strength. The improvement in energy storage performance and breakdown strength of SNO substituted BTCZ composites are mainly attributed to relatively homogeneous grain morphology, optimum grain size, microstructural density, and improved grain boundary interface.     

Self-healing capacity of Mullite-Yb2SiO5 environmental barrier coating material with embedded Ti2AlC MAX phase particles

Repetitive heating and cooling cycles inevitably cause crack damage of hot gas components of gas turbine engines, such as blades and vanes. In this study the self-healing capacity is investigated of mullite + ytterbium monosilicate (Yb₂SiO₅) as EBC material with Ti₂AlC MAX phase particles embedded as a crack-healing agent. The effect of Ti₂AlC in the EBC was compared with the self-healing ability of the mullite + Yb₂SiO₅ material. After introducing cracks by Vickers indentation on the surface of each sample, crack healing was realized by controlling the temperature and time during the post-heat-treatment process. For the mullite + Yb₂SiO₅ composite with Ti₂AlC particles, crack healing occurred at 1000 °C, while in the case of the mullite + Yb₂SiO₅ composite without Ti₂AlC, a sustained temperature of 1300 °C or higher was required. Compared with the healing of the mullite + Yb₂SiO₅ composite by the formation of a eutectic phase, the addition of Ti₂AlC promoted healing via the oxidation of Ti and Al. Notably, the surface formation of a ternary oxide of Ti–Yb–O was confirmed, which completely covered the damage area. Consequently, the addition of a Ti₂AlC MAX phase to the EBC composite resulted in a complete strength recovery, while the mullite + Yb₂SiO₅ composite without Ti₂AlC showed a strength recovery of about 80%. Furthermore, by analyzing the indentation load–displacement curve to indicate the role of Ti₂AlC, the addition of Ti₂AlC improved both the hardness and stiffness of the composite.     

Alumina-Periclase-Carbon Refractories Produced by OOO Ogneupor

Refractories and Industrial Ceramics - Technology for producing alumina-periclase-carbon refractories of the brands APUK-D and APU-D is developed and implemented. Use of complex antioxidant and...     

Corrosion behavior of T24, T92, VM12, and AISI 304 steels exposed to KCl–NaCl–K2SO4–Na2SO4 salt mixtures

The corrosion mechanisms of T24, T92, VM12, and AISI 304 steels are studied under the influence of NaCl–KCl, NaCl–Na₂SO₄, and KCl–K₂SO₄ salt mixtures in a dry air atmosphere at 650°C for 15 days. NaCl–KCl was the most aggressive deposit and AISI 304 stainless steel exhibited the highest corrosion resistance. There was no relation between the Cr content of the ferritic steels and their corrosion resistance in NaCl–KCl. In contrast, the resistance of high-Cr steels was better when exposed to NaCl–Na₂SO₄ and KCl–K₂SO₄. The high-Cr and the low-Cr steels were more susceptible to NaCl–Na₂SO₄ and to KCl–K₂SO₄, respectively.     

Dielectric performance of pyrochlore-type Bi2MgNb2-xTaxO9 ceramics: The effects of tantalum doping

The solid solutions based on the pyrochlore-type system Bi₂MgNb_2-xTa_xO₉ were formed in the compositional range х = 0–2.0 (Bi_1·6Mg_0·8Nb_1.6-tTa_tO_7.2, t = 0–1.6). The Rietveld method was used to refine the structure for Bi₂MgNb_2-xTa_xO₉ (x = 0, 1.0, 2.0). The increasing tantalum content led to the slight decrease in the cubic unit cell parameters from 10.56934 (4) Å for x = 0 and 10.54607 (3) Å for x = 2 (sp.gr. Fd-3m:2). At the same time, tantalum additions suppressed grain growth in the pyrochlore ceramics during sintering and made it possible to obtain materials with an average grain size of 1–2 μm (Bi_1·6Mg_0·8Ta_1·6O_7.2). The increase in the Ta⁵⁺ concentration led to the decrease in the dielectric permeability from 104 (Bi_1·6Mg_0·8Nb_1·6O_7.2) to 20 (Bi_1·6Mg_0·8Ta_1·6O_7.2) at room temperature, while the dielectric loss tangent remained lower than 0.002, which is due to the small grain size and the high porosity of the samples. An increase in temperature has practically no effect on the values of the dielectric permittivity in the entire frequency range. The samples have weak through conductivity. The activation energies of electrical conductivity varied in the range of 0.84–1.00 eV, and the less tantalum, the lower the activation energy. The electrical properties of the samples at 200 Hz to 1 MHz are described by the simplest parallel scheme.