Study on characteristics of Ni-W-B composites containing CeO2 nano-particles prepared by pulse electrodeposition

Ni-W-B composites containing CeO2 nano-particles on the surface of 45 steel were prepared by pulse electrodeposition,and the in-fluence of pulse frequency,pulse duty circle and heat treatment temperature on the structures and properties were investigated.The results in-dicated that the pulse co-deposition of Ni,W,B and CeO2 nano-particles led to Ni-W-B/CeO2 composites possessing higher microhardness and better wear resistance when heat-treated at 400 oC for 1 h.The microhardness of 636 HV and the deposition rate of 0.0281 mm/h of the as-deposited alloy were the highest at pulse frequency of 1000 Hz,pulse duty circle of 10% and pulse average current density of 10 A/dm2.The composites were mainly in the amorphous state and were partially crystallized as-deposited,and the crystallization trend was strength-ened when heat-treated at 400 oC.Decreasing pulse duty cycle from 75% to 10% was favorable to the refinement in grain structures and im-provement of microstructures.The crystal sizes of the composites were smaller by means of pulse electrodeposition.     

Li+掺杂MoO3薄膜的制备与电致-光致变色特性研究

采用过氧溶胶－凝胶法在室温下制备了具有电致变色和光致变色特性的10mol%Li掺杂MoO3薄膜。对薄膜循环安特性和光学特性的测试结果表明，经120℃处理的Li^ 掺杂MoO3薄膜具有良好的电化学性能及电致变色性能。采用Raman光谱对Li^ 掺杂MoO3薄膜光变色前后结构的分析表明，薄膜经紫外光照后结构进行了重组，有序性增强，且吸收光谱研究表明薄膜具有较好的光致变色特性。     

莫来石抑制钛酸铝材料热分解的机理研究

运用扫描电镜（SEM）、X-射线衍射仪（XRD）、能谱仪（EDS）等现代测试手段,从材质的显微结构、晶界晶相组成分析入手,对莫来石抑制钛酸铝热分解的作用机理作了较为详细的分析研究,探明莫来石抑制钛酸铝热分解的作用机理是：（1）在高温下Si^4 进入钛酸铝晶格或间隙中,形成固溶化的钛酸铝晶体,稳定了晶格;（2）因莫来石与钛酸铝间的热膨胀差异,造成较大的压应力（37.65MPa）,致使固溶化的钛酸铝晶体更趋稳定。     

MBE技术蓝宝石衬底上生长VO2薄膜及其太赫兹和金属-绝缘体相变特性研究

采用分子束外延(MBE)技术在单晶蓝宝石衬底上生长了高质量化学计量比二氧化钒(VO₂)薄膜, 通过该技术实现薄膜厚度15~60 nm精确控制。对于优化条件下VO₂薄膜, 实现了电阻率变化超过4个数量级的优异金属-绝缘体相变, 近似于之前报道高质量单晶VO₂相变特性。特别是通过太赫兹时域光谱分析了不同厚度的VO₂薄膜在太赫兹波段的光学特性。结果表明: VO₂薄膜的厚度对其在太赫兹波段的光学特性有很大影响。因此, 为了获得更优的可靠性和重复性能, VO₂薄膜的厚度必须得到精确控制。本研究结果对于下一步VO₂基太赫兹器件研究具有重要意义。     

热致变色VO2薄膜的制备及光学性能研究

利用等离子体发射光谱监测系统(PEM)控制钒的等离子强度,在石英基底上磁控溅射制备了VO2薄膜。采用XRD、XPS、SEM、紫外-可见-近红外分光光度计及傅立叶红外分光光度计研究薄膜的结构、光学及相变特性。结果表明,所制备的VO2薄膜具有(011)取向,VO2薄膜的热滞回线宽度为25℃,可见光透过率和太阳光调节率分别可达Tlum,l=34.1%、Tlum,h=35.3%和ΔTsol=6.8%,相变前后,红外光区的反射率变化最大值可达44.4%。     

二氧化钛超滤膜的制备及其渗透性能

用溶胶-凝胶工艺在涂覆两层ZrO2中间层的堇青石多孔陶瓷管上制备TiO2超滤膜。通过X射线衍射、扫描电子显微镜、孔隙度分析仪及原子力显微镜分析膜材料的形貌、厚度和孔隙率与结构。结果表明:所制备的各层膜结构完整、厚度合适且孔径分布均匀呈阶梯式递减;主晶相为锐钛矿的TiO2超滤膜,厚度为50nm,最可几孔径为15nm左右。对薄膜的渗透性能测试结果表明:所制样品对纯水的平均渗透率为131.6L/(h·m2·MPa),0.2MPa工作压力下对分子量580000右旋糖苷的截留率为94.76%。     

石墨衬底上低维ZnO纳米材料的生长(英文)

本研究成功地在石墨衬底上制备了低维ZnO材料,即一维的ZnO纳米棒和二维的ZnO薄膜。采用X射线衍射、场发射扫描电镜、光致发光谱和反射谱等测量技术对石墨衬底上制备的低维ZnO纳米材料的晶体结构、形貌和光学特性进行了表征。结果发现在室温条件下,准一维的ZnO纳米棒和二维的ZnO薄膜都表现出了较好的近带边发射,基本探测不到由杂质和缺陷等引起的深能级发光,并且这种低维ZnO材料/石墨衬底复合结构在300~800 nm光谱范围内具有较低的反射率。本实验结果对于ZnO基光电子器件性能的提高以及在太阳能电池领域的应用具有重要意义。     

光子晶体的能带结构、潜在应用和制备方法

光子晶体是指具有光子能带和能隙的一类新型材料,它具有奇特的调节光子传播状态的特性．本文将从光子晶体的能带结构、潜在应用和制备方法三方面对其进行综述性介绍．由于光子晶体有着非常广阔的应用前景,这一领域已成为当今世界范围内的研究热点．     

射频反应溅射氧化铌薄膜的电致变色性能研究

采用射频反应溅射法成功地制备了非晶态氧化铌薄膜,研究了它们的电致变色性能．这些薄膜在漂白态透明无色,而着色态则为灰褐色．循环伏安测试结果表明该薄膜具有良好的稳定性和很好的锂离子注入/抽出性能．５５０ｎｍ处的着色效率为１６．６８ｃｍ^２/Ｃ,在可见光区透过率调制幅度为２０%~３０%．结合Ｘ光电子能谱(ＸＰＳ)分析可以认为氧化铌薄膜的电致变色现象是由于锂离子和电子的共同注入与抽出,导致薄膜中的铌离子发生Ｎｂ^Ｖ和Ｎｂ^ＩＶ间的可逆氧化、还原反应引起的．     

锂掺杂MoO3薄膜的制备及电色性能的研究

采用过氧化氢溶胶－凝胶法成功地在室温下制备了纯的ＭｏＯ_３和锂掺杂的ＭｏＯ_３薄膜．通过ＴＧ－ＤＴＡ热分析、ＦＴＩＲ红外光谱分析、循环伏安和光学特性的测试,研究了薄膜成膜过程中的结构转变过程和薄膜的电化学性能及电变色性能．结果表明通过Ｌｉ^＋掺杂,ＭｏＯ_３溶胶的稳定性和ＭｏＯ_３薄膜的电化学循环稳定性都有了较大的提高．且掺杂锂的ＭｏＯ_３薄膜仍具有良好的电变色性能．