Fabrication and properties of pressure-sintered reaction-bonded Si3N4 ceramics with addition of Eu2O3–MgO–Y2O3

Dense pressure-sintered reaction-bonded Si₃N₄ (PSRBSN) ceramics were obtained by a hot-press sintering method. Precursor Si powders were prepared with Eu₂O₃–MgO–Y₂O₃ sintering additive. The addition of Eu₂O₃–MgO–Y₂O₃ was shown to promote full nitridation of the Si powder. The nitrided Si₃N₄ particles had an equiaxial morphology, without whisker formation, after the Si powders doped with Eu₂O₃–MgO–Y₂O₃ were nitrided at 1400 °C for 2 h. After hot pressing, the relative density, Vickers hardness, flexural strength, and fracture toughness of the PSRBSN ceramics, with 5 wt% Eu₂O₃ doping, were 98.3 ± 0.2%, 17.8 ± 0.8 GPa, 697.0 ± 67.0 MPa, and 7.3 ± 0.3 MPa m^1/2, respectively. The thermal conductivity was 73.6 ± 0.2 W m^?1 K^?1, significantly higher than the counterpart without Eu₂O₃ doping, or with ZrO₂ doping by conventional methods.     

Influence of SiC microstructure on its corrosion behavior in molten FLiNaK salt

The influence of the microstructure on the corrosion rate of three monolithic SiC samples in FLiNaK salt at 900 °C for 250 h was studied. The SiC samples, labeled as SiC-1, SiC-2, and SiC-3, had corrosion rates of 0.137, 0.020, and 0.043 mg/cm²h, respectively. Compared with grain size and the presence of special grain boundaries (i.e., Σ3), the content of high-angle grain boundaries (HAGBs) appeared to have the strongest influence on the corrosion rate of SiC in FLiNaK salt, since the corrosion rate increased six times as the concentration of high-angle grain boundaries increased from 19 to 32% for SiC-2 and SiC-1, respectively. These results stress the importance of controlling the content of HAGBs during the production process of SiC.     

A Case Report of Germline Compound Heterozygous Mutations in the BRCA1 Gene of an Ovarian and Breast Cancer Patient

The germline carrier of the BRCA1 pathogenic mutation has been well proven to confer an increased risk of breast and ovarian cancer. Despite BRCA1 biallelic pathogenic mutations being extremely rare, they have been reported to be embryonically lethal or to cause Fanconi anemia (FA). Here we describe a patient who was a 48-year-old female identified with biallelic pathogenic mutations of the BRCA1 gene, with no or very subtle FA-features. She was diagnosed with ovarian cancer and breast cancer at the ages of 43 and 44 and had a strong family history of breast and gynecological cancers.     

Agro-Waste Generated Pd/CAP-Ash Catalyzed Ligand-Free Approach for Suzuki–Miyaura Coupling Reaction

Catalysis Letters - We converted agro-waste Custard Apple Peels (CAP) to ash via thermal treatment, on which Pd(OAc)2 was immobilized easily that produced a low-cost, highly efficient Pd/CAP-ash...     

Spectral radiance reconstruction from trichromatic camera responses based on orthogonal test and regularized algorithm

Reconstruction of spectral information based on multi‐channel image system is a significant problem in color reproduction, detection, and recognition. A spectral radiance reconstruction from trichromatic digital camera responses is researched in this article. The mapping relationship between the trichromatic imaging system response and the incident spectral radiance is analyzed. Then, in order to remove the ill‐posedness of the problem, a regularized constraint solution model of spectral radiance reconstruction matrix is established. And the spectral radiance can be reconstructed by spectral radiance reconstruction matrices and trichromatic imaging system response. Finally, the spectral radiance reconstruction matrix is estimated by the system radiometric calibration experiment. The input radiance is offered by a LCD display. A 3‐factor and 9‐level orthogonal test is designed for the calibration experiment, and a test set of 24 colors is used for precision analysis. The results show that the average relative mean error of our method is 8.69%, it is lower than that of Wiener filtering method by 2.84%. The method can reconstruct spectral radiance information effectively.     

Synthesis of nanopowders with low agglomeration by elaborating Φ values for producing Gd2O3-MgO nanocomposites with extremely fine grain sizes and high mid-infrared transparency

Refining ceramic microstructures to the nanometric range to minimize light scattering provides an interesting methodology for developing novel optical ceramic materials. In this work, we reported the fabrication and properties of a new nanocomposite optical ceramic of Gd₂O₃-MgO. The citric acid sol-gel combustion method was adopted to fabricate Gd₂O₃-MgO nanocomposites with fine-grain sizes, dense microstructures and homogeneous phase domains. Nanopowders with low agglomeration and improved sinterability can be obtained by elaborating Φ values. Further refining of the microstructure of the nanocomposites was achieved by elaborating the hot-pressing conditions. The sample sintered at 65 MPa and 1300 °C showed a quite high hardness value of 14.3 ± 0.2 GPa, a high transmittance of 80.3 %–84.7 % over the 3?6 μm wavelength range, due mainly to its extremely fine-grain size of Gd₂O₃ and MgO (93 and 78 nm, respectively) and high density.     

Tests of a Two-Stage Core at the KV-1 Test Facility: Physical Aspects and Results

Atomic Energy - The physical aspects and main results of reactor tests of a two-stage core consisting of fresh fuel assemblies and a significant number of fuel assemblies from the previous core,...     

BS960E高强钢激光-电弧复合焊接头氢脆行为研究

氢脆具有很强的微观组织敏感性,威胁着各类高强结构材料的安全服役.采用激光-电弧复合焊工艺对BS960E型高强钢进行焊接,并对接头在原位电化学充氢的条件下进行慢应变速率(10-5s-1)拉伸试验,结合微观组织和断裂特征进行分析并对接头的氢脆行为进行研究.结果 表明,焊接热循环所形成的富马氏体中的细晶区可以使接头表现出一定的氢脆敏感性,马氏体较大的氢扩散系数和较低的氢溶解度以及氢在晶界上的快速扩散是引起接头对氢脆敏感的主要原因,通过控制焊接工艺参数可抑制焊接热循环所引起的马氏体转变量,能够降低BS960E型高强钢激光-电弧复合焊接头的氢脆敏感性.     