碳中和背景下配电网差异化节能降耗潜力评估分

为了提高配电网差异化节能降耗效果，解决现有潜力评估方法存在的应用性能差的问题，提出碳中和背景下配电网差异化节能降耗潜力优化评估方法。根据配电网的空间结构，构建相应的等值电路模型。在该模型下，从设备损耗和运行附加损耗2个方面计算配电网的损耗量。根据损耗量计算结果，确定配电网差异化碳中和节能降耗方式。从静态和动态2个角度设置潜力评估指标，通过指标数据处理、指标权重求解等步骤，得出配电网差异化节能降耗潜力的综合量化评估结果。将设计潜力评估方法应用到配电网的差异化节能降耗改造工作中，能够有效降低配电网的实际线损量、降低区域损耗费用，并具有较高的应用价值。     

雷芬那辛的合成工艺研究

以联苯-2-基氨基甲酸哌啶-4-基酯(SM-1)为起始物料，经亲核取代、脱苄基、和4-甲酰基苯甲酸脱水反应生成酰胺中间体，最后和哌啶-4-甲酰胺脱水反应先形成希夫氏碱再经三乙酰氧基硼氢化钠还原制备雷芬那辛。通过对反应条件的控制及纯化，所得产品纯度为99.5%,总收率为45.7%,目标产物的化学结构经质谱和核磁共振确证。该工艺反应条件温和、操作简便，为雷芬那辛的合成提供了一种新选择。     

Modification of the wood-plastic composite for enhancement of formaldehyde clearance and the 3D printing application

As the formaldehyde is one of the main indoor pollutants, the purpose of this study is to effectively remove indoor formaldehyde pollution by using environmentally friendly 3D printing ornaments. The wood 3D printing filaments cellulose/polylactic acid composite (Cellu/P) was selected as the starting material, and 3-aminopropyltriethoxysilane (APTES) was used for chemical modification to obtain a series of cellulose composite materials with amino groups. The modified composite materials (APTES@Cellu/P) were characterized by Fourier transform infrared, X-ray diffraction, scanning electron microscope, energy dispersive spectroscopy, thermogravimetric analysis, and mechanical tests, and a formaldehyde removal experiment was performed. The feasibility of 3D printing was evaluated, and the process of 3D printing-functionalized customized ornaments was proposed, and then a school emblem was used for modeling, printing, and surface modification. Compared with the commercially traditional activated carbon, 3D printing-customized ornaments of APTES@Cellu/P material has a better formaldehyde removal effect, and can even avoid the secondary pollution that is common to the activated carbon.     

Sustainable phenolic thermosets coatings derived from urushiol

The over-exploitation of finite fossil resources and/or the increased environmental and sustainable awareness inspire scientists and technologists to search for inexpensive alternatives from renewable chemicals. Phenol formaldehyde (PF) resins, the oldest type of synthetic polymers with good mechanical properties and heat resistance, are widely used in the production of coatings, laminates, molding compositions, and glues. Here, biobased urushiol-derived PF resins were synthesized from the alkali-catalyzed reaction between urushiol and formaldehyde. The chemical compositions and molecular structures of resole resins were characterized by carbon-13 nuclear magnetic resonance and Fourier transform infrared spectroscopy, and their curing behaviors were studied by differential scanning calorimetry. The as-prepared urushiol-derived resole resins had methylol (Ph−CH₂OH), ortho- and para-hemiformal groups (Ph−CH₂OCH₂OH), and the para−para/ortho−para/ortho−ortho links of methylene groups (Ph−CH₂−Ph), whereas the resole resins had low curing temperatures at about 100–113°C. Additionally, given the long side alkyl group moiety on the aromatic rings of urushiol, the films of cured urushiol-derived resole resins had low glass transition temperatures of 132 ± 2°C. Furthermore, the as-prepared urushiol-derived coatings exhibited excellent physical and mechanical properties.     

镍基高温合金GH202高温氧化后的微观组织演变

研究了镍基高温合金GH202在800~1100 ℃高温氧化后晶粒、碳化物和强化相的演变过程。采用透射电子显微镜、扫描电子显微镜和电子背散射衍射对其微观结构进行了表征。结果表明：镍基高温合金的硬度随氧化温度的升高而降低，1100 ℃氧化100 h后，硬度降低了43.5%。800和900 ℃氧化后晶粒生长速度较慢，而经900 ℃氧化后晶界碳化物析出显著增加。在1000和1100 ℃氧化后，晶粒尺寸明显增大。氧化过程中晶界迁移是由晶界两侧自由能差决定，温度越高，晶界向曲率中心迁移越快，大量细小晶粒被吞并形成了大晶粒。大块状碳化物（MC）分解成大量的碳原子，与Cr原子结合形成少量的富Cr颗粒状M₂₃C₆。在900 ℃氧化150 h后，M₂₃C₆演化为富Ti的M₆C。随着氧化温度的升高，碳化物在γ相中回熔。在800、900和1000 ℃氧化后，γ′相逐渐长大，在1100 ℃氧化100 h后，完全溶解于γ相。     

Flash joining of alumina ceramics under a small current density

The ceramic joining using electric field (E-field) has garnered significant research attention due to the decreased joining barrier and enhanced reliability. However, the underlying mechanism of E-field assisted joining remains unclear. Herein, we report the rapid joining of alumina ceramics using a small current. Moreover, the E-field is applied in both perpendicular and parallel directions to the faying surfaces, demonstrating a significant difference in terms of joint strength. These results indicate that the E-field generates defects and promotes the joining process by facilitating ionic diffusion.     

A new strategy to reduce edge chipping using stress wave impedance matching

To restrain edge chipping and elucidate its mechanism during machining, the initiation of edge chipping was investigated in this study from the propagation properties of stress waves in the fractured media. Three technological principles of the support for chipping suppression were proposed to reduce the intensity of reflected extension waves, namely, the wave impedance matching, the smaller residual gap and the higher viscosity of the gap filler between the workpiece and the support. As demonstrated from the experimental results, using brass support with non-solid epoxy gap filler can significantly restrain the edge chipping of pressureless sintered silicon carbide during grinding.     

Effect of Cu-Rich Phase Precipitation on the Microstructure and Mechanical Properties of CoCrNiCux Medium-Entropy Alloys Prepared via Laser Directed Energy Deposition

CoCrNiCux (x=0.16,0.33,0.75,and 1) without macro-segregation medium-entropy alloys (MEAs) was prepared using laser directed energy deposition (LDED).The microstructure and mechanical properties of CoCrNiCux alloys with increas-ing Cu content were investigated.The results indicate that a single matrix phase changes into a dual-phase structure and the tensile fracture behaviors convert from brittle to plastic pattern with increasing Cu content in CoCrNiCux alloys.In addi-tion,the tensile strength of CoCrNiCux alloys increased from 148 to 820 MPa,and the ductility increased from 1 to 11％with increasing Cu content.The nano-precipitated particles had a mean size of approximately 20 nm in the Cu-rich phase area,and a large number of neatly arranged misfit dislocations were observed at the interface between the two phases due to Cu-rich phase precipitation in the CoCrNiCu alloy.These misfit dislocations hinder the movement of dislocations during tensile deformation,as observed through transmission electron microscopy.This allows the CoCrNiCu alloy to reach the largest tensile strength and plasticity,and a new strengthening mechanism was achieved for the CoCrNiCu alloy.Moreover,twins were observed in the matrix phase after tensile fracture.Simultaneously,the dual-phase structure with different elastic moduli coordinated with each other during the deformation process,significantly improving the plasticity and strength of the CoCrNiCu alloy.