Dense and core-rim structured B4C-TiB2 ceramics with Mo-Co-WC additive

B₄C-TiB₂ ceramics (TiB₂ ranging 5~70 vol%) with Mo-Co-WC as the sintering additive were prepared by spark plasma sintering. In comparison with B₄C-TiB₂ without additive, the enhanced densification was evident in the sintered specimen with Mo-Co-WC additive. Core-rim structured grain was observed around TiB₂ grains. The interface of the rim between TiB₂ and B₄C phases demonstrated different feature: the inner borderline of the rim exhibited a smooth feature, whereas a sharp curved grain boundary was observed between the rim and the B₄C grain. The formation mechanism is discussed: the epitaxial growth of (Ti,Mo,W)B₂ rim around the TiB₂ core may occur as a result of the solid solution and dissolution-precipitation between TiB₂ phase and the sintering additive. It was revealed that the fracture toughness increased as the content of TiB₂ content increased, alongside the decreased hardness. B₄C-30 vol% TiB₂ specimen demonstrated the optimal combination of mechanical properties, reaching Vickers hardness of 24.3 GPa and fracture toughness of 3.33 MPa·m^1/2.     

巨型水轮发电机剪断销研发与质量控制

为获得设计需要的巨型水轮发电机剪断销的剪切力,得到剪切力波动受控的批量剪断销,通过拉伸试验、冲击试验、硬度试验和剪断销剪切试验等讨论了全尺寸剪断销剪切试验的可行性,分析了剪切试验时正常剪断和非正常剪断的剪断销材料性能差异,探究了剪断销的剪切力质量稳定性控制方法。结果表明:控制剪断销料坯的布氏硬度波动,可实现间接控制剪断销剪切强度的波动;通过试验总结的六步法可达到控制批量剪断销质量和剪切力波动的目的。     

Characterizations of friction welding joint interface for AISI 316

Because of heat amount is different from peripheral to central of friction welding interface, which is leaded to vary the characterizations along that interface. Current study, respectively, focused on the effect of different friction pressure on micro-structural and mechanical properties of that friction welding joint interface. Presently, these friction pressures are 110, 130, 150 and 170 MPa while kept all other conditions constant. The effects of different friction pressure on welding interface characterization were investigated by EDX, SEM, tensile, compression, impact and hardness tests. The tensile tests carried out on the standardized test piece with diameter 6 mm and 8 mm, thus, compression tests were extracted from the positions of 0°, 45° 90° with test specimen of 4 mm diameter and 6.5 mm length at weld center. Whereas, the impact test pieces were picked up in two positions, the first one is symmetrical, which it obtained to the respect of the rotation axis and the interface, on the other hand, the second one is non-symmetrical with the axis of rotation and symmetrical to the interface, for making the notch head coincide with the center of the welded joint, The obtained results showed that with reducing of friction pressure will present lack of bonding increasing from peripheral toward the welding center, which will responsible on reducing of the mechanical properties such as tensile, compression and impact strength.     

不同硬度PTMG型CPUE与硫化橡胶的性能对比研究

通过改变硬段含量、扩链系数等制备了几种不同硬度的四氢呋喃均聚醚(PTMG)浇注型聚氨酯弹性体(CPUE),讨论了PTMG型CPUE与硫化橡胶(VR)的物理机械性能、拉伸应力应变行为以及动态力学性能的区别。结果表明,随CPUE硬度的提高,材料的刚性增强,力学性能是低硬度VR的数倍。通过对CPUE硬度的调节,可以使之兼具聚氨酯和橡胶的优良性能。在玻璃态温度下CPUE的储能模量随硬度的减小而降低,但都高于VR,而且CPUE的硬度越大,二者相差越大,温度越低,相差也越大;在室温以上温度范围内,CPUE具有比VR更小的力学损耗。     

Effects of SiC content on the densification,microstructure, and mechanical properties of HfB2–SiC composites

To investigate the effects of SiC on microstructure, hardness, and fracture toughness, 0, 10, 20, and 30 vol% SiC were added to HfB₂ and sintered by SPS. Upon adding SiC to 30 vol%, relative density increased about 4%; but HfB₂ grain growth had a minimum at 20 vol% SiC. This may be due to grain boundary silicate glass, responsible for surface oxide wash out, enriched in SiO₂ with higher fraction of SiC. By SiO₂ enrichment, the glass viscosity increased and higher HfO₂ remained unsolved which subsequently lead to higher grain growth. Hardness has increased from about 13 to 15 GPa by SiC introduction with no sensible variation with SiC increase. Residual stress measurements by Rietveld method indicated high levels of tensile residual stresses in the HfB₂ Matrix. Despite the peak residual stress value at 20 vol% SiC, fracture toughness of this sample was the highest (6.43 MPa m^0.5) which implied that fracture toughness is mainly a grain size function. Tracking crack trajectory showed a mainly trans-granular fracture, but grain boundaries imposed a partial deflection on the crack pathway. SiC had a higher percentage in fracture surface images than the cross-section which implied a weak crack deflection.     

铸态Mg-xSn-1Mn合金的显微组织和阻尼性能

采用光学显微镜(OM)、维氏硬度计、热动态分析仪、X射线衍射(XRD)、多功能内耗仪等,研究了Sn含量对Mg-xSn-1Mn合金显微组织、阻尼性能和力学性能的影响。结果表明:当Sn含量从2%增加到8%时,Mg-xSn-1Mn合金的枝晶间隙呈现细化的趋势,硬度从43.84 HV0.1增加至54.00 HV0.1,呈单调增加的趋势。应变无关阻尼随着Sn含量的增加呈现先增后减的趋势,在Sn含量为4%时达到最大,应变相关阻尼则随着Sn含量的增加呈现逐渐减小的趋势。在低温阶段,相同Sn含量的合金的阻尼随着频率的增大呈现增加的趋势;但在高温下,阻尼值在低频时的上升速率比高频时快,并随着温度的升高,低频阻尼和高频阻尼趋向于相等。当Sn含量不同时,随着温度的升高,Sn含量较高的合金的阻尼值上升速率变快。     

55SiCr弹簧钢中的残留奥氏体与碳化物

通过扫描电镜(SEM)、电子背散射衍射(EBSD)、透射电镜(TEM)、X射线衍射仪(XRD)、热膨胀仪、洛氏硬度计等手段研究了弹簧钢55SiCr的组织和相变点以及残留奥氏体和碳化物在热处理过程中的组织演变。结果表明:55SiCr弹簧钢淬火后残留奥氏体以块状分布在基体上;随回火温度的升高,残留奥氏体减少并呈粒状和薄膜状分布;C在残留奥氏体中富集,使其稳定性增强;Si抑制了碳化物的析出,提高了残留奥氏体的稳定性。低温回火时,Si延缓了渗碳体析出;高温回火时,C原子扩散速率提高,促进渗碳体析出,引起体积的收缩。慢速加热回火时,C有足够的时间扩散,从而促进渗碳体的形成,使渗碳体的形成温度提前;快速加热回火时,C来不及扩散,抑制了渗碳体的析出。回火加热速率一样时,试验钢的硬度随回火温度的提高而下降。当回火温度为400 ℃时,硬度值最大为51 HRC;当回火温度为650 ℃时,硬度值最小为37 HRC。当加热速率为0.1 ℃/s时,硬度值最小为33 HRC;当加热速率为200 ℃/s时,硬度值最大为40 HRC。     

A first-principles investigation on mechanical and metallic properties of titanium carbides under pressure

The titanium carbides are potential candidates to achieve both high hardness and refractory property. We carried out a structural search for titanium carbides at three pressures of 0 GPa, 30 GPa and 50 GPa. A phase diagram of the Ti-C system at 0 K was obtained by elucidating formation enthalpies as a function of compositions, and their mechanical and metallic properties of titanium carbides were investigated systematically. We also discussed the relation of titanium concentration to the both mechanical and metallic properties of titanium carbides. It has been found that the average valence electron density and tractility improved at higher concentrations of titanium, while the degree of covalent bonding directionality decreased. To this effect, the hardness of titanium carbide decreases as the content of titanium increases. Our results indicated that the titanium content significantly affected the metallic properties of the Ti-C system.