碳纳米管场发射阴极的制备及其场发射特性

采用电泳法将碳纳米管组装到电化学淀积的银台阵列上作为场发射阴极并研究了它的场发射特性.场发射特性测试结果表明:该阴极具有优异的场发射特性,开启电场为2.8V/μm,在应用电场为5.5V/μm时,发射电流密度达到1.7mA/cm2.具有优异的发射性能的原因可以归结到银台的边缘和银台类山状的表面增强了碳纳米管的场致电子发射.该阴极制备工艺简单、发射特性优异,且容易实现大面积制备,可以应用到大面积场发射显示器件中.     

利用UV曝光技术研制单根定向碳纳米管阵列冷阴极

通过普通的紫外(UV)光刻工艺,结合"变倾角缩口"新技术,研制了不同发射单元尺寸的碳纳米管(CNTs)阵列阴极。扫瞄电镜分析表明,随着缩口尺寸的依次减小(从0.6μm到0.4μm,最后到0.2μm),发射单元内CNTs的根数也不断减少。当孔径缩至0.2μm时,发射单元仅由1根~3根CNTs组成,并且大部分单元顶端均有单根CNT伸出,使得整个发射体近似于单根CNT。场发射特性测试结果表明,0.2μm发射单元尺寸的阵列阴极,开启电场约2V.μm-1;当场强为20V.μm-1时,该阵列的电流密度达到0.35A.cm-2,比1μm尺寸的阵列阴极提高了近4倍,比连续生长的薄膜CNTs阴极则高1~2个数量级。     

碳纳米管/二氧化硅复合材料制备及场发射特性研究

采用溶胶-凝胶法制备了碳纳米管/二氧化硅复合材料,并对复合材料的场发射特性进行了研究,结果表明:复合材料有很好的场发射特性,含有10%(质量分数)CNTs的复合材料开启场较低(0.98V/μm).研究了用稀HF溶液处理复合材料表面后场发射性能,发现场发射性能明显改善,开启场由0.98V/μm下降到0.73V/μm,发射电流为1mA/cm2时的电场由2.1V/μm下降到1.0V/μm.研究表明碳纳米管/二氧化硅复合材料非常适用于场发射平面显示器中的阴极.     

用玻璃粉作粘结剂制备碳纳米管厚膜及其场发射特性

研究了用涂敷法制备的碳纳米管（CNT）厚膜及其场发射特性,裂解法获得的碳纳米管与玻璃粉等混合、研磨,直接涂敷在Si基底上,经烧结后制成碳纳米管厚膜,二极结构测量的结果表明,碳纳米管厚膜有较低的开启电场（1.0～1.25V/μm）,场强为5V/μm时,电流密度达到了50μA/cm^2.该工艺的烧结过程应控制好,加热时间稍长会使CNT厚膜的场发射性能很快下降,时间过长会使CNT处在厚膜表面之下,无法有效发射电子.浆料中的玻璃粉比例增大时,碳纳米管阴极的场发射性能会有所降低.     

电泳淀积图形化碳纳米管场发射阴极及其场发射特性研究

基于电泳和半导体工艺,制备了图形化的碳纳米管场发射阴极。用较高的电场激活碳纳米管薄膜,使得碳纳米管的场发射特性有了很大的改善,讨论了这一激活过程的物理机制。研究表明,这一激活过程可能的物理机制一方面是由于碳纳米管薄膜表面形貌发生了变化,增大了碳纳米管的场增强因子;另一方面是由于碳纳米管表面吸附的气体脱附,降低了碳纳米管的表面功函数。电场激活处理后,碳纳米管薄膜的开启电场为2.1 V/μm,应用电场为6 V/μm时,电流密度达到1.19mA/cm2。该图形化的碳纳米管场发射阴极可以应用到高分辨率场发射显示器。     

碳纳米管／二氧化硅复合材料制备及场发射特性研究

采用溶胶-凝胶法制备了碳纳米管／二氧化硅复合材料，并对复合材料的场发射特性进行了研究，结果表明：复合材料有很好的场发射特性，含有10％（质量分数）CNTs的复合材料开启场较低（0．98V／μm）。研究了用稀HF溶液处理复合材料表面后场发射性能，发现场发射性能明显改善，开启场由0．98V／μm下降到0．73V／μm，发射电流为1mA／cm^2时的电场由2．1V／μm下降到1．0V／ μm。研究表明碳纳米管／二氧化硅复合材料非常适用于场发射平面显示器中的阴极。     

碳纳米管和镓掺杂碳纳米管场发射性能研究

采用催化热解方法分别 制备出碳纳米管和镓掺杂碳纳米管, 并利用丝网印刷工艺将其制备成纳米管薄膜. 对此薄膜进行低场致电子发射测试表明, 碳纳米管和镓掺杂纳米管开启电场分别为2.22和1.0V/μm, 当外加电场为2.4V/μm, 碳纳米管发射电流密度为400μA/cm², 镓掺杂纳米管发射电流密度为4000μA/cm². 可见镓掺杂碳纳米管的场发射性能优于同样条件下未掺杂时的碳纳米管. 对镓掺杂纳米管场发射机理进行了探讨.     

新型碳纳米管微焦点电子源研究

介绍了一种基于碳纳米管场发射的新型微焦点电子源技术.利用激光烧蚀镍金属表面使内部未氧化的镍金属熔化喷出暴露于基底表面,再通过化学气相沉积制备出直径约为350μm的半球壳型碳纳米管薄膜阴极.场发射测试表明,电子源具有低开启电场(<1V/μm)、高发射电流(可达1A/cm2)和高压强发射稳定等特点.通过复合石墨烯和750℃...     

类金刚石薄膜作为阴极阵列的场发射显示器研制

采用真空磁过滤弧沉积（FAD）的方法制备的金刚石（DLC）薄膜具有良好的场发射性能。通过离子束技术和微细加工技术可以实现DLC薄膜的图形化并能大大提高薄膜的场发射性能。测试表明，DLC薄膜孔洞阵列具有很好的电子场发射性能，阈值电场达到了2.1V/μm，当场强为14.3V/μm时，电流密度达到了1.23mA/cm^2。利用图形化的DLC薄膜作为阴极，设计和制作了矩阵选址单色场发射显示器（FED）样管。     

基于氧化锌纳米线表面传导场发射阴极的研究

利用热蒸发和丝网印刷技术在玻璃基底上成功制备了氧化锌纳米线表面传导场发射阴极阵列,并测试其场发射性能。扫描电镜表明,在氩气和氧气流量分别为60和1mL/min,反应温度550℃保温30min条件下制备的氧化锌纳米线均匀垂直生长在玻璃基底上,直径大约在80～200nm,长度〉7μm。场发射测试表明,在阳压2000V和阴阳间距为500μm时,ZnO纳米线表面传导场发射阴极的开启电压为70V;在栅压为96V时,电子发射效率为26.2%,高于传统报道的表面传导电子发射器件,在经过80min的老练后发射接近稳定,平均发射电流接近135μA,表明ZnO纳米线表面传导场发射阴极有着稳定高效的场发射性能。     

Insertion of triangulated surfaces into a meccano tetrahedral discretization by means of mesh refinement and optimization procedures

In this paper, we present a new method for inserting several triangulated surfaces into an existing tetrahedral mesh generated by the meccano method. The result is a conformal mesh where each inserted surface is approximated by a set of faces of the final tetrahedral mesh. First, the tetrahedral mesh is refined around the inserted surfaces to capture their geometric features. Second, each immersed surface is approximated by a set of faces from the tetrahedral mesh. Third, following a novel approach, the nodes of the approximated surfaces are mapped to the corresponding immersed surface. Fourth, we untangle and smooth the mesh by optimizing a regularized shape distortion measure for tetrahedral elements in which we move all the nodes of the mesh, restricting the movement of the edge and surface nodes along the corresponding entity they belong to. The refining process allows approximating the immersed surface for any initial meccano tetrahedral mesh. Moreover, the proposed projection method avoids computational expensive geometric projections. Finally, the applied simultaneous untangling and smoothing process delivers a high‐quality mesh and ensures that the immersed surfaces are interpolated. Several examples are presented to assess the properties of the proposed method.     

From Industry 4.0 to Research 4.0. Development of High Performance Fibers in the Light of Digitization

We associate a variety of innovations with the term ＂Industry 4.0＂. The pioneer of many 4.0 modifications forms the basisfor the trend towards the integrated di...     

The Research of Anti-Wear Properties of Organomolybdenum Compounds in the Engine Oils

A four-ball tester was used to evaluate the anti-wear performance of three kinds of organomolybdemun compounds in the engine oils, i. e., molybdenum dialkyldithiophosphate (MoDDP), molybdenum dialkyldithiocarbamate ( MoDTC), and sulphur and phosphorus freeorganomolybdeum (Molybdate). The results indicate that a low concentration of MoDDP doesn' t improve the anti-wear properties of the commercial engine oils, but a high concentration of MoDDP can obviously improve the anti-wear properties and the load-carrying capacity of the engine oils. MoDTC doesn' t improve the antiwear properties of the engine oils, but worsens the anti-wear properties of the oils. Signifi can timprove ment of frictional and wear characteristics is obtained with Molybdate added in the commercial engine oils and the formulated oils.     

Roman iron and steel: A review

ABSTRACT

The production of ferrous metal increased during the Roman Late Republican period, Principate and Empire. The direct bloomery process was used to extract the metal from its ores using slag-tapping and slag-pit furnaces. The fuel was charcoal and an air blast was introduced by bellows-operated tuyères. Iron formed as a bloom, often as a spongy mass of metal, which contained impurities from the smelting process, including unreacted ore, fuel, slag and fragments from the furnace walls, while the metal was often inhomogeneous with varied carbon contents. Blooms were either smithed directly into bars or ingots or they were broken up, which also allowed the removal of gross impurities and a selection of pieces with similar properties to be made. These could then be forge-welded together and formed into characteristically shaped ingots. Making steel in the furnace seems to have been achieved: it depended on the ore and the furnace and conditions within it. Surface carburization was also carried out. Iron and steel were used extensively in construction and for tools and weapons. Fire welding was often used to add pieces of steel to make the edges of tools and weapons, which could be heat-treated by quenching to harden them.     

Certification Institutions Expected to Update and Transfer Information on Present Standards

Standards are the basis for production enterprises to organize production, ex-factory inspection, trade (delivery) and technical exchanges, product certification, quality arbitration and supervision.……     

Synthesis of Alumina-Zirconia Nanocomposites by Solgel Process

Al₂O₃-ZrO₂ nanocomposites were developed starting with the solgel process. Composite alumina-zirconia nanopowders were synthesized from metallorganic precursors (Aluminium secondary butoxide and zirconium Iso propoxide) using the solgel process. The parameters affecting the synthesis—solvent, concentration of precursor, R/H ratio (i.e., dilution of water in solvent)—were varied as also the temperature and pH. BET and TEM were used to measure nanosize. Diffuse reflectance spectroscopy and also qualitative optical absorption led to identical particle size estimate. The variation of process parameters was used to study the effect and interdependence of process parameters. Artificial Neural Networks was used to rigorously analyze the process. Although this led to confirmation of interdependence of parameters, the presence of a single overwhelming solvent variable was also established. Then the optimal process was used to synthesize more nanopowder. To produce bulk nanocomposite the nanopowders were sintered by varying the temperature and time period. The sintered lithoids were probed with a vickers hardness tester to measure elastic modulus, hardness, and fracture toughness. The results showed high elastic modulus, modest hardness, and very high fracture toughness.     

Flow calorimeter for enthalpy increment measurements on condensed gases

A flow calorimeter for enthalpy increment measurements on condensed gases is presented. A better knowledge of the properties of the liquefied natural gas is needed, and therefore a liquid loop has been designed for our flow calorimeter. The fluid loop in the calorimeter is designed in order to avoid the two-phase region, since two phases would give compositional disturbances in the measurements. The avoidance of the two-phase region is made possible by increasing the pressure of the test fluid after the measurement section, then heating the fluid at super-critical pressure past the critical point. Finally, the fluid is throttled to the low-pressure gas state at the inlet condition of the compressor that circulates the fluid. To perform the pressure increase, a new cryogenic pump has been designed. To evaluate the new equipment, measurements were taken on liquid ethane over the temperature range 146–256 K at pressure between 0.9 and 5.1 MPa.     

Certification Becomes Important for the I Quality; and Safety Supervision of the Chinese Liquor Sector

The end of 2007, over 200 unit products of more than 80 Chinese firms have passed the quality grade certification for liquor products. These products involve distilled spirits, beer, wine, yellow wine, fruit syrup wine and others, and cover over 80% of the national top-branded liquor products.……     

Deposition and Coating Properties on CVD Tungsten

Surface characterization and microstructure studies are performed on chemical vapor deposited (CVD) tungsten coating. There is about 2 μm thickness diffusion layer of tungsten in the molybdenum substrate. The thermal shock test shows tungsten coating has good adhesion with molybdenum substrate, but the elements of oxygen and carbon in the tungsten coating have the bad affection to the adhesion. The result of high-temperature diffusion experiment is the diffusion rate from molybdenum substrate to tungsten coating is faster.