从操作及工艺控制方面分析全钢载重子午线轮胎经常出现的胎里露线、胎圈露钢丝、胎体劈缝、胎里气泡、胎里窝气、胎趾圆角和胎侧欠硫外观质量缺陷的产生原因,并从设备改进、产品设计和工艺管理方面提出相应的解决措施.严格控制半成品尺寸、成型和硫化定型操作等可保证全钢载重子午线轮胎质量和生产效益.     

硫化活性剂AK-1在全钢载重子午线轮胎胎侧胶中的应用

研究硫化活性剂AK-1在全钢载重子午线轮胎胎侧胶中的应用。结果表明:硫化活性剂AK-1等量替代间接法氧化锌应用于全钢载重子午线轮胎胎侧胶中,胶料的硫化特性、物理性能和工艺性能以及成品轮胎的物理性能与使用间接法氧化锌的胶料和成品轮胎基本相当,满足使用要求,同时可显著降低胶料中的锌含量,满足环保法规要求。     

硫化活性剂BL-1在全钢载重子午线轮胎胎冠胶中的应用

研究硫化活性剂BL-1在全钢载重子午线轮胎胎冠胶中的应用。结果表明:在全钢载重子午线轮胎胎冠胶中采用硫化活性剂BL-1等量替代普通氧化锌,试验配方胶料的硫化特性和老化前后的物理性能与生产配方胶料相当,且满足生产工艺要求;成品轮胎的耐久性能满足相应国家标准要求;胶料中锌含量大幅减小,有利于环保,胶料成本降低。     

间苯二酚-甲醛树脂在全钢载重子午线轮胎带束层胶料中的应用

研究间苯二酚-甲醛树脂在全钢载重子午线轮胎带束层胶料中的应用。结果表明,间苯二酚-甲醛树脂替代间苯二酚应用于全钢载重子午线轮胎带束层胶料,硫化胶的物理性能变化不大,H抽出力和耐老化性能基本不变,胶料生热降低;成品轮胎耐久性能不变,解决了胶料在加工过程中出现的冒烟现象,减小环境污染。     

全钢载重子午线轮胎胎里欠硫的原因分析及改善措施

分析全钢载重子午线轮胎胎里欠硫的原因,并提出相应的改善措施。通过采取根据轮胎尺寸及胶囊的直径伸张比和断面周长伸张比选择胶囊型号、增大硫化胶囊排气线的尺寸和密度、调整预定型高度和机械手装胎位置的定位精度、增大定型压力及提高胎坯定型一次合格率等措施,降低了成品轮胎胎里欠硫缺陷的发生率,提高了轮胎质量。     

活性纳米碳酸钙在全钢子午线轮胎胎侧胶中的应用

试验研究活性纳米碳酸钙在全钢子午线轮胎胎侧胶中的应用。结果表明,在全钢子午线轮胎胎侧胶中添加10份活性纳米碳酸钙,胶料的硫化速度加快,硫化胶的硬度、拉断伸长率略有增大,拉伸强度、定伸应力相当,胶料生产成本降低,具有一定的经济效益。     

高温硫化半钢子午线轮胎外观质量缺陷的原因分析及解决措施

介绍高温硫化半钢子午线轮胎缺胶、气泡、胎圈宽窄不一、胎里露线和欠硫等外观质量缺陷的产生原因,并提出相应解决措施.通过采取严格控制胶料混炼温度、合理设置模具排气孔、定期清洗模具、调整成型压力和硫化定型高度、合理选取帘线假定伸张值以及定期检查和更换硫化胶囊等措施,轮胎外观质量缺陷明显减少,产品的一次合格率显著提高.     

抗硫化返原剂WK-901在无内胎全钢子午线轮胎胎肩垫胶中的应用

研究抗硫化返原剂WK-901在无内胎全钢子午线轮胎胎肩垫胶中的应用。结果表明,在无内胎全钢子午线轮胎胎肩垫胶中加入0.75份抗硫化返原剂WK-901,可明显减小胶料在150℃和180℃下的硫化返原率,改善胶料物理性能和耐热老化性能,降低生热,提高成品轮胎的耐久性能,减少肩空缺陷。     

多功能助剂KLF-808在全钢载重子午线轮胎中的应用

试验研究多功能助剂KLF-808在全钢载重子午线轮胎中的应用效果。结果表明,在全钢载重子午线轮胎胎面胶、下三角胶和外护胶中加入KLF-808,可以降低胶料的门尼粘度,提高胶料的抗硫化返原性能,降低硫化胶的压缩生热,提高成品轮胎的耐久性能;在胎面胶中加入KLF-808,可以提高硫化胶的耐磨和抗刺扎性能。     

氮气硫化半钢子午线轮胎欠硫产生原因及解决措施

分析氮气硫化的半钢子午线轮胎上、下胎圈,胎里和胎冠欠硫产生原因并提出相应解决措施。通过采取保证氮气硫化正常排凝和各密封部位的密封性能、在维修和更换模具后充分预热模具及保证风源压力等措施可大大减少成品轮胎欠硫的发生。采取这些措施后,由于欠硫产生的成品轮胎废品率由0.15%降至0.02%。     

分解炉扩径的技术改造

我厂3号回转窑(Φ4m×60m)生产线在1996年年底由SP窑(产量912t/d)改为NSP窑(产量1320t/d),预分解系统为四级旋风预热器带离线式分解炉     

乙烯酮(双乙烯酮)下游产品废水的治理技术

乙烯酮(双乙烯酮)是十分重要的化工中间体,其下游产品较多。江苏某化工厂开发生产乙烯酮(双乙烯酮)下游产品三十多个,年生产规模三万多吨,是国内以乙烯酮(双乙烯酮)为中间体生产精细化学品的综合骨干企业。针对乙烯酮(双乙烯酮)下游产品废水特点,该厂结合企业实际,开展了产品优化,结构调整,清洁生产,资源循环利用,节水降耗等工作,从源头削减了污染物的生产。同时投资二千多万元新建预处理装置三套,6000m3/d废水生化处理装置一套,使全厂乙烯酮(双乙烯酮)下游产品的废水得到了有效的治理。     

水泥水化热测定方法综述

水泥水化热是中、低热水泥和核电工程用水泥的一项关键的技术指标。全球范围内测定水泥水化热的方法有溶解法、直接法/半绝热法、等温传导量热法三种。本文总结了中、美、欧相关方法标准,对其测试原理、仪器设备、试验过程等方面进行了比对,并对其在领域的应用做了简单的概括。     

生物油的成分分析及物性测定

以添加FeCl2的ZnCl2-KCl混合熔盐裂解纤维素和秸秆,制得生物油。采用傅立叶变换红外光谱法和气相色谱-质谱法分析生物油的成分。结果表明,生物油中成分复杂,含有氧元素、多种有机化合物,主要包括酮类、醛类、酚类及羧酸类等。测定了20～80℃生物油的密度和粘度,发现生物油的密度与温度呈较好线性关系,而生物油的粘度均大于水的粘度,且不同熔盐体系对秸秆生物油的粘度无较大影响。     

Effect of degree of deacetylation of chitosan on the kinetics of ultrasonic degradation of chitosan

The objective of the study was to explore the effect of the degree of deacetylation (DD) of the chitosan used on the degradation rate and rate constant during ultrasonic degradation. Chitin was extracted from red shrimp process waste. Four different DD chitosans were prepared from chitin by alkali deacetylation. Those chitosans were degraded by ultrasonic radiation to different molecular weights. Changes of the molecular weight were determined by light scattering, and data of molecular weight changes were used to calculate the degradation rate and rate constant. The results were as follows: The molecular weight of chitosans decreased with an increasing ultrasonication time. The curves of the molecular weight versus the ultrasonication time were broken at 1‐h treatment. The degradation rate and rate constant of sonolysis decreased with an increasing ultrasonication time. This may be because the chances of being attacked by the cavitation energy increased with an increasing molecular weight species and may be because smaller molecular weight species have shorter relaxation times and, thus, can alleviate the sonication stress easier. However, the degradation rate and rate constant of sonolysis increased with an increasing DD of the chitosan used. This may be because the flexibilitier molecules of higher DD chitosans are more susceptible to the shear force of elongation flow generated by the cavitation field or due to the bond energy difference of acetamido and β‐1,4‐glucoside linkage or hydrogen bonds. Breakage of the β‐1,4‐glucoside linkage will result in lower molecular weight and an increasing reaction rate and rate constant. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 90: 3526–3531, 2003     

Process of acceleration of filtration of viscose

Conclusions It is significant that the purification on a single passage of viscose through porous ceramic corresponds to the result of a two-stage filtration of it in industrial filter-presses with standard fillings.Kiev Combine. Kiev Technological Institute of Light Industry. Translated from Khimicheskie Volokna, No. 3, pp. 20–22, May–June, 1969.     

Approximation of temperature dependence of the modulus of elasticity of glass

A refined nonlinear value of the main parameter of a material, i.e., the elongation modulus versus the instant temperature value, was suggested for introduction into the computational algorithm of tempering stresses.