电容器用铌粉和钽粉制备技术的进展

综述了铌粉和钽粉的现行生产工艺及几种新的还原方法，介绍了金属热还原反应中的电化学反应机理。钽粉的现行生产工艺几乎都用亨特法，铌粉则大部分采用铝热还原法生产。通过对亨特法还原条件、稀释剂组成等各种工艺参数的改进，已经可以制备纯度高、形态可控的金属钽粉。铌粉新还原方法的研究主要包括金属预成形热还原法、镁等蒸气还原预成形氧化物粉末的方法、镁或钠的蒸气还原氯化物蒸气的气相还原法、以液氨为介质在低温液相中均相还原铌或钽的氯化物的方法、反应媒介熔盐在强搅拌条件下的液体镁热还原金属氧化物的方法等。     

美国3年来钽铌进口情况述评

依据英国金属网公布的2003年、2004年、2005年第1季度美国钽铌原料和制品进口统计数据．评述了美国钽铌市场的状况,着重关注了中国向美国出口钽铌的情况。     

The preparation of tantalum powder using a MR-EMR combination process

In the conventional metallothermic reduction (MR) process used to obtain tantalum powder in batch-type operation, it is difficult to control the morphology and location of the tantalum deposits. In contrast, an electronically mediated reaction (EMR) process is capable of overcoming this difficulty. It has the advantage of being a continuous process, but has the disadvantage of a poor reduction yield. A process known as the MR-EMR combination process is able to overcome the shortcomings of the MR and EMR processes. In this study, an MR-EMR combination process is applied to the production of tantalum powder via sodium reduction of K₂TaF₇. In the MR-EMR combination process, the total charge passed through an external circuit and the average particle size (FSSS) increase as the reduction temperature increases. In addition, the proportion of fine particles (−325 mesh) decreases as the reduction temperature increasess. The tantalum yield improved from 65 to 74% as the reduction temperature increased. Taking into account the charge, impurities, morphology, particle size and yield, a reduction temperature of 1123 K was found to be optimum for the MR-EMR combination process.     

"牺牲"阳极法合成乙醇钽研究

研究了“牺牲“阳极法电化学合成乙醇钽过程中,添加剂种类与浓度、电解液温度、阴阳极极距和电流密度的影响.选取最佳合成条件为:四甲基氯化铵0.04 mol/L,温度为电解液的沸腾温度,极距约2 cm,电流密度220 A/m2.电合成的混合液经常压蒸馏和减压蒸馏,得到产品用红外光谱、拉曼光谱和元素分析进行表征,确定了产品为乙醇钽.电合成的电流效率大于95%,产品蒸馏时钽的直收率82.8%.     

钽粉颗粒强度的研究

研究了采用激光粒度分布仪测试电容器级团化钽粉粒度分布及强度的方法。其中心内容是:先采用3种不同比表面积、松装密度和费氏平均粒径的钠还原原粉,按3种烧结工艺制得团化钽粉。然后把烧结得到的6种试样加入纯水中,以200～300r/min进行高速搅拌并以40W,42kHz超声波振动。将激光衍射分析仪的激光束穿过经不同搅拌时间的悬浊钽粉,测得不同时间的钽粉粒径分布曲线。分析分布曲线可以获得团化钽粉的一系列信息,包括:①几种团化钽粉颗粒的相对强度;②影响团化钽粉颗粒强度的因素;③钽粉强度和其他性能如介电损耗、流动性,平均粒径及密度的关系等。     

水洗钽粉中氮的测定

针对水洗钽粉中杂质元素的干扰,采用EMGA-620W氧氮分析仪,测定了水洗钽粉中的氮,并与脉冲气相色谱法测氧氮(联测)进行了比较,认为该法快速、准确、可靠。     

High-temperature oxidation of a rapidly solidified amorphous Ta-Ir alloy

The oxidation products formed at 500 and 700°C on an amorphous Ta-44.5 at% Ir alloy in an Ar-0.1% O₂ gas mixture were characterized using SEM, XRD, EPMA, TEM, STEM, AES, and XPS. Initially, a thin (3–4 nm) layer of Ta₂O₅ formed at the surface of the alloy. Continued growth of the Ta₂O₅, which occurred very rapidly, involved diffusion of oxygen anions from the Ta₂O₅/gas interface to the alloy/Ta₂O₅ interface, where tantalum was selectively oxidized. Because the oxide grew more quickly than iridium could diffuse back into the alloy, the iridium coalesced into platelets of crystalline iridium-rich alloy that were oriented approximately parallel to the oxide/alloy interface, and which became embedded in a matrix of Ta₂O₅. The unoxidized core remained in the glassy state. The oxidation process and/or the dissolution of oxygen into the unoxidized alloy caused the alloy to become embrittled.     

钽低温离子渗氮工艺参数对渗氮层物相的影响

利用组合的二次回归正交实验设计方案 ,对钽低温离子渗氮条件下 ,表面物相及固溶体中氮的含量随渗氮温度、气氛总压力和氢氮摩尔比的变化进行了系统研究。发现表面渗氮层由化合物Ta6N2 .57、超晶格TaN0 .1和固溶体相组成。氮在钽中的固溶度随气压、温度和氢摩尔分数的增加而增加 ,化合物和超晶格相含量随温度增加而增加 ,同时化合物相随氢摩尔分数增加有一个极大值 ,该极大值随温度增加而下降。     

网状阴极法在碳钢表面沉积氮化钽薄膜的研究

介绍了一种在钢铁基体上制备氮化钽薄膜的新方法———网状阴极法。其设备简单、价格低廉。实验中发现 ,在工艺参数调配合适的条件下 ,可制备出结构为面心立方和密排六方结构的氮化钽薄膜。薄膜较致密且均匀 ,与基体结合良好。分析了优选工艺参数条件下合成的氮化钽膜的成分、组织、表面和断口形貌及结合力。     

高技术产品用无源元件与中国钽工业发展

世界高技术产品市场总体看呈增长趋势，预计2020年销售额将比2000年翻一番。以高技术产品为主要应用领域的电阻、电容、电感等无源元件，也将随着高技术产业的发展呈现出良好的市场前景，但是钽电容器市场近几年表现出骤涨急落的发展态势。由于钽电容器产能过剩，且面临着被替代的威协，因此价格将无法返回到2000年以前的水平，并呈现整体持续走低的趋势。中国的钽工业发展应注重提高企业自身的综合竞争力，加强企业间的沟通、交流与合作，维护我国钽工业的整体利益，增强环保意识，做好国外转移到我国的初级产品和低端产品生产的环保工作。