Influence of SiC microstructure on its corrosion behavior in molten FLiNaK salt

The influence of the microstructure on the corrosion rate of three monolithic SiC samples in FLiNaK salt at 900 °C for 250 h was studied. The SiC samples, labeled as SiC-1, SiC-2, and SiC-3, had corrosion rates of 0.137, 0.020, and 0.043 mg/cm²h, respectively. Compared with grain size and the presence of special grain boundaries (i.e., Σ3), the content of high-angle grain boundaries (HAGBs) appeared to have the strongest influence on the corrosion rate of SiC in FLiNaK salt, since the corrosion rate increased six times as the concentration of high-angle grain boundaries increased from 19 to 32% for SiC-2 and SiC-1, respectively. These results stress the importance of controlling the content of HAGBs during the production process of SiC.     

The Age-Sensitive Efficacy of Calorie Restriction on Mitochondrial Biogenesis and mtDNA Damage in Rat Liver

Calorie restriction (CR) is the most efficacious treatment to delay the onset of age-related changes such as mitochondrial dysfunction. However, the sensitivity of mitochondrial markers to CR and the age-related boundaries of CR efficacy are not fully elucidated. We used liver samples from ad libitum-fed (AL) rats divided in: 18-month-old (AL-18), 28-month-old (AL-28), and 32-month-old (AL-32) groups, and from CR-treated (CR) 28-month-old (CR-28) and 32-month-old (CR-32) counterparts to assay the effect of CR on several mitochondrial markers. The age-related decreases in citrate synthase activity, in TFAM, MFN2, and DRP1 protein amounts and in the mtDNA content in the AL-28 group were prevented in CR-28 counterparts. Accordingly, CR reduced oxidative mtDNA damage assessed through the incidence of oxidized purines at specific mtDNA regions in CR-28 animals. These findings support the anti-aging effect of CR up to 28 months. Conversely, the protein amounts of LonP1, Cyt c, OGG1, and APE1 and the 4.8 Kb mtDNA deletion content were not affected in CR-28 rats. The absence of significant differences between the AL-32 values and the CR-32 counterparts suggests an age-related boundary of CR efficacy at this age. However, this only partially curtails the CR benefits in counteracting the generalized aging decline and the related mitochondrial involvement.     

In Vivo Albumin-Binding of a C-Functionalized Cyclam Platform for 64Cu-PET/CT Imaging in Breast Cancer Model

An improved glucose-chelator-albumin bioconjugate (GluCAB) derivative, GluCAB-2^Mal, has been synthesized and studied for in vivo ⁶⁴Cu-PET/CT imaging in breast cancer mice models together with its first-generation analogue GluCAB-1^Mal. The radioligand works on the principle of tumor targeting through the enhanced permeability and retention (EPR) effect with a supportive role played by glucose metabolism. [⁶⁴Cu]Cu-GluCAB-2^Mal (99 % RCP) exhibited high serum stability with immediate binding to serum proteins. In vivo experiments for comparison between tumor targeting of [⁶⁴Cu]Cu-GluCAB-2^Mal and previous-generation [⁶⁴Cu]Cu-GluCAB-1^Mal encompassed microPET/CT imaging and biodistribution analysis in an allograft E0771 breast cancer mouse model. Tumor uptake of [⁶⁴Cu]Cu-GluCAB-2^Mal was clearly evident with twice as much accumulation as compared to its predecessor and a tumor/muscle ratio of up to 5 after 24 h. Further comparison indicated a decrease in liver accumulation for [⁶⁴Cu]Cu-Glu-CAB-2^Mal.     

High-Pressure Reverse Osmosis for Industrial Water Recycling: Permeate-Sided Pressure Drop as Performance-Limiting Factor

In the chemical industry large amounts of saline wastewater occur. Its disposal into rivers is a considerable burden to the ecosystem. To strive for a circular economy and enable a viable raw material recycling, energy-efficient concentration processes are requisite. High-pressure reverse osmosis meets this criterion, but its industrial application demands suitable membrane elements that withstand the exceptional operation conditions and provide sufficient performance. Hence, new requirements regarding the design of spiral-wound elements arise. To identify those, specific performance-limiting effects need a better understanding.     

珠江口盆地珠一坳陷古近系高自然伽马砂岩形成机制及油气地质意义

运用放射性元素寻找油气是一种非常规油气勘探手段。近年来,在珠江口盆地珠一坳陷富烃凹陷周边古近系钻遇高自然伽马(GR)砂岩,其GR值(100~300 API)甚至大于同区泥岩的GR值(100~200 API)。为了弄清该特殊现象背后的地质意义,对珠江口盆地珠一坳陷古近系高自然伽马砂岩开展了铀(U)、钍(Th)、钾(K)等3种元素含量与GR值的相关趋势线分析,从井震特征、岩性特征及矿物成分特征等入手分析了砂岩GR值增高的主要原因及成因机制,探讨了放射性元素聚集的条件、运移通道、驱动力以及油气意义。结果表明:西江、惠州地区由U含量增高导致砂岩GR值偏高,恩平、番禺地区由K,Th含量增高导致砂岩GR值偏高;砂岩GR值增高有两大成因机制,一是地下流体带来的放射性元素离子U4+在氧化-还原面处富集后导致地层GR值偏高,这种特殊现象说明在具有连通基底大断裂旁的圈闭中,U4+的富集指示了曾经油气的存在,证实了研究区油气运移通道的有效性,对于油气藏的预测有着非常重要的指导性意义,二是地表流体带来的含放射性元素的矿物大量沉积后导致地层GR值偏高,含放射性元素矿物性质不稳定,可指示近源供给的存在,对于判断物源及沉积环境有着非常重要的意义。该研究成果为预测研究区油气成藏有利区带提供了依据。     

车门铰链系统与车门下沉刚度的相关性

针对某型车门下沉问题,通过台架试验获得车门、铰链和车身等各单因素下沉量和车门绞链系统整体下沉量,对单因素下沉量与系统整体下沉刚度进行线性拟合分析,得到车门铰链系统各单因素与系统下沉刚度的相关度排序.对前、后车门分别选取相关度较高的单因素进行优化,最终改进方案的仿真和试验结果证明该方案可有效地提升车门下沉刚度.采用定量分析法可快速找出影响下沉刚度的敏感因素,并能够快速生成优化方案,为新车型设计提供参考.     

Interfacial microstructure and mechanical properties of Ti3SiC2 ceramic and TC11 alloy joint diffusion bonded with a Cu interlayer

Reliable joints of Ti₃SiC₂ ceramic and TC11 alloy were diffusion bonded with a 50 μm thick Cu interlayer. The typical interfacial structure of the diffusion boned joint, which was dependent on the interdiffusion and chemical reactions between Al, Si and Ti atoms from the base materials and Cu interlayer, was TC11/α-Ti + β-Ti + Ti₂Cu + TiCu/Ti₅Si₄ + TiSiCu/Cu(s, s)/Ti₃SiC₂. The influence of bonding temperature and time on the interfacial structure and mechanical properties of Ti₃SiC₂/Cu/TC11 joint was analyzed. With the increase of bonding temperature and time, the joint shear strength was gradually increased due to enhanced atomic diffusion. However, the thickness of Ti₅Si₄ and TiSiCu layers with high microhardness increased for a long holding time, resulting in the reduction of bonding strength. The maximum shear strength of 251 ± 6 MPa was obtained for the joint diffusion bonded at 850 °C for 60 min, and fracture primarily occurred at the diffusion layer adjacent to the Ti₃SiC₂ substrate. This work provided an economical and convenient solution for broadening the engineering application of Ti₃SiC₂ ceramic.     

Inhibition of RANKL-Induced Osteoclastogenesis by Novel Mutant RANKL

Background: Recently, it was reported that leucine-rich repeat-containing G-protein-coupled receptor 4 (LGR4, also called GPR48) is another receptor for RANKL and was shown to compete with RANK to bind RANKL and suppress canonical RANK signaling during osteoclast differentiation. The critical role of the protein triad RANK–RANKL in osteoclastogenesis has made their binding an important target for the development of drugs against osteoporosis. In this study, point-mutations were introduced in the RANKL protein based on the crystal structure of the RANKL complex and its counterpart receptor RANK, and we investigated whether LGR4 signaling in the absence of the RANK signal could lead to the inhibition of osteoclastogenesis.; Methods: The effects of point-mutated RANKL (mRANKL-MT) on osteoclastogenesis were assessed by tartrate-resistant acid phosphatase (TRAP), resorption pit formation, quantitative real-time polymerase chain reaction (qPCR), western blot, NFATc1 nuclear translocation, micro-CT and histomorphological assay in wild type RANKL (mRANKL-WT)-induced in vitro and in vivo experimental mice model. Results: As a proof of concept, treatment with the mutant RANKL led to the stimulation of GSK-3β phosphorylation, as well as the inhibition of NFATc1 translocation, mRNA expression of TRAP and OSCAR, TRAP activity, and bone resorption, in RANKL-induced mouse models; and Conclusions: The results of our study demonstrate that the mutant RANKL can be used as a therapeutic agent for osteoporosis by inhibiting RANKL-induced osteoclastogenesis via comparative inhibition of RANKL. Moreover, the mutant RANKL was found to lack the toxic side effects of most osteoporosis treatments.     

Stress field and damage evolution in C/SiC woven composites: Image-based finite element analysis and in situ X-ray computed tomography tests

The construction and examination of meso-structural finite element models of a Chemical-Vapor-Infiltrated (CVI) C/SiC composite is carried out based on X-ray microtomography digital images (IB-FEM). The accurate meso-structural features of the C/SiC composites, which are consisted of carbon fiber tows and CVI-SiC matrix, in particular the cavity defects, are reconstructed. With the IB-FEM, the damage evolution and fracture behaviors of the C/SiC composite are investigated. At the same time, an in situ tensile test is applied to the C/SiC composite under a CT real-time quantitative imaging system, aiming to investigate the damage and failure features of the material as well as to verify the IB-FEM. The IB-FEM results indicate that material damage initially occur at the defects, followed by propagating toward the fiber-tow/SiC-matrix interfaces, ultimately, combined into macro-cracks, which is in good agreement with the in situ CT experiment results.     

Piezoelectric properties and microstructure of ceramicrete-based piezoelectric composites

Inorganic piezoelectric ceramic composite is the potential sensing element for long-term structural health monitoring due to its excellent durability and compatibility. In this study, a Ceramicrete-based piezoelectric composite is proposed preliminarily, in which the magnesium potassium phosphate cement is used as the matrix and the lead zirconate titanate particle is utilized as the functional phase. Piezoelectric properties test and microstructure analysis are performed to evaluate the testing samples. Results show that the piezoelectric performance of the composite increase with the increase of piezoelectric ceramic particle size. The value of the piezoelectric strain factor (d₃₃) can reach 83.8 pC/N, while the corresponding piezoelectric voltage factor (g₃₃) is 50.1 × 10^-3 V•m/N at the 50th day after polarization. Microstructure analysis illustrates that the interfacial transition zone (ITZ) between the matrix and the particles is dense. Moreover, the influence of aging on the composite is attributed to the continuous hydration after polarization. It indicates that the composites have a higher piezoelectric performance, which can be regarded as a promising sensing element material.